CN102584029B - Tempered glass decorating plate manufactured through digital painting and manufacture method thereof - Google Patents
Tempered glass decorating plate manufactured through digital painting and manufacture method thereof Download PDFInfo
- Publication number
- CN102584029B CN102584029B CN201210028706.XA CN201210028706A CN102584029B CN 102584029 B CN102584029 B CN 102584029B CN 201210028706 A CN201210028706 A CN 201210028706A CN 102584029 B CN102584029 B CN 102584029B
- Authority
- CN
- China
- Prior art keywords
- screen
- substrate
- sdueegee
- printing
- nip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a tempered glass decorating plate manufactured through digital painting and a manufacture method thereof. The tempered glass decorating plate manufactured through the digital painting comprises a substrate and is characterized in that the substrate is made of a tempered glass material, a gloss oil prime coating agent is printed on the substrate, a pattern layer is painted on the surface of the gloss oil prime coating agent, and a protective coating layer is printed on the pattern layer. The manufacture method combines a screen printing technology principle to increase gloss oil prime coating agent so as to improve adhesive force of digital painting ink on the tempered glass material and resolve the problem that the digital painting cannot be processed on the hard tempered glass material. In addition, by means of follow-up printing protective coating layer production process, the production cost is reduced, the production efficiency is improved, a developing period is short, and the tempered glass decorating plate is formed without a mould, produced in a personalized mode, flexible in shape and size, attractive, elegant and suitable for the fields of household appliances, household decoration, advertising media and the like.
Description
Technical field
The invention belongs to printing packaging technical field, specifically relate to a kind of tempered-glass decorative plate that adopts numerial code spray drawing making and preparation method thereof.
Background technology
UV numerial code spray drawing is a kind of widely used image making technology, but UV numerial code spray drawing cannot be applied on toughened glass for a long time always, and its major cause is that UV digital jet ink stress due to UV resin wherein in solidification process is large.The stress of UV digital jet ink in solidification process is from aspect two: the one, and dope layer volumetric shrinkage in solidification process, there are differences in distortion with ground, thereby produce stress on the interface between coating and ground; The 2nd, UV digital jet ink UV is cured as rapid reaction, and material is very exothermic at short notice, and this thermopositive reaction meeting causes the structural inhomogeneity of coated material itself, causes the internal stress of coating itself.These weakness are on the base material of porous, as showed not out on timber or paper.But at metal, obvious on the hard and level and smooth base material such as pottery and glass.Based on two above reasons, carry out UV numerial code spray drawing at this rigid substrate surface of toughened glass and be difficult to realize, UV ink is very easy to peeling off phenomenon.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of tempered-glass decorative plate that adopts numerial code spray drawing making and preparation method thereof is provided, it can either ensure high-precision pattern effect, solved again the problem that cannot carry out UV numerial code spray drawing on this hard material of toughened glass time, UV ink can be peeled off, that the pattern of air brushing has is wear-resisting, the characteristic of scratch resistance, resistance to solvent, water boiling resistance.
According to technical scheme provided by the invention: a kind of tempered-glass decorative plate that adopts numerial code spray drawing to make; comprise substrate; it is characterized in that: described substrate is toughened glass material; on substrate, be printed with gloss oil silane coupling agent; on gloss oil silane coupling agent face, air brushing has patterned layer, is printed with supercoat in patterned layer.
As a further improvement on the present invention, the thickness of described substrate is 2 ~ 5mm.
As a further improvement on the present invention, the material of described gloss oil silane coupling agent is two component epoxy series plastics gloss oil.
As a further improvement on the present invention, described two component epoxy series plastics gloss oil comprises host and two kinds of compositions of solidifying agent, host is wherein epoxy resin gloss oil, it is mainly to be formed by epoxy resin, the agent of vinylformic acid levelling, modification fluorine defoamer, butyl ester mixed grinding, solidifying agent is polyamide curing agent, and the weight percentage of host is 80 ~ 88%, polyamide curing agent weight percentage be 12 ~ 20%, host and polyamide curing agent are uniformly mixed, and within curing reaction 5-10 minute, use.Described two component epoxy series plastics gloss oil also can directly adopt outsourcing product, host can adopt common epoxy resin varnish, as the XB-100 type of Changzhou Wujin Xin Bang coating company limited, polyurethane curing agent can adopt the XB-101 type of Changzhou Wujin Xin Bang coating company limited.
As a further improvement on the present invention, the material of described supercoat is single-component oleic series resin ink.
As a further improvement on the present invention, the component of described single-component oleic series resin gloss oil is acrylic resin modified.
A making method that adopts the tempered-glass decorative plate of numerial code spray drawing making, is characterized in that comprising the steps:
(1) choose the substrate of being made by toughened glass material, substrate is sent in Semi-automatic screen process press, adopt silk screen at substrate surface printing varnish silane coupling agent, in printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience does not contact screen printing forme except nip with stock, ink is under the squeeze effect of sdueegee, pass through mesh, bite stock from moving nip, after finishing printing, sending into light wave drying tunnel, is drying and processing 7 ~ 8 minutes under the condition of 170 DEG C ~ 180 DEG C in temperature,
(2) substrate that prints gloss oil silane coupling agent is lain on digit inkjet printer service platform, figure is processed by air brushing software RIP, on gloss oil silane coupling agent face, pass through the mode printing pattern layer of six look numerial code spray drawings, air brushing precision is between 1500 ~ 3000DPI, and the solid machine of 1000W UV light being carried by spray drawing apparatus in air brushing process solidifies simultaneously; Air brushing environment is controlled at 15 DEG C ~ 30 DEG C of temperature, humidity 40% ~ 65%;
(3) substrate of spraying good pattern layer is sent in Semi-automatic screen process press, adopt silk screen in patterned layer, to print supercoat, in printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience does not contact screen printing forme except nip with stock, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, sending into light wave drying tunnel, is drying and processing 7 ~ 8 minutes under the condition of 170 DEG C ~ 180 DEG C in temperature, obtains tempered-glass decorative board finished product.
The present invention compared with prior art, advantage is: zygomite reticulated printing know-why of the present invention, increase gloss oil silane coupling agent to improve the sticking power of digital jet ink on toughened glass material, solve the difficult problem that numerial code spray drawing cannot be processed on this hard material of toughened glass, and by follow-up printing supercoat production technique, reduce production costs, improve production efficiency, construction cycle is short, without making mould molding, personalized production, product design dimensional change is flexible, elegant in appearance, be applicable to household electrical appliance, house decoration, the fields such as advertisement media.
Brief description of the drawings
Fig. 1 is the cross section structure schematic diagram of tempered-glass decorative plate of the present invention.
Embodiment
Below in conjunction with concrete drawings and Examples, the invention will be further described.
Embodiment 1: cabinet air-conditioner decoration panel
(1) choose the substrate 1 that the thickness be made up of toughened glass material is 3.0mm, use Semi-automatic screen process press to carry out printing varnish silane coupling agent 2, gloss oil silane coupling agent 2 adds 360 order glitter powders allotments of 5% weight percent to form by two component epoxy series plastics gloss oil, described two component epoxy series plastics gloss oil contain certain catch special gene; Adopt 150 order silk screens, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, send into light wave drying tunnel, drying and processing 7 minutes under the condition of 170 DEG C of temperature;
(2) substrate 1 that prints gloss oil silane coupling agent 2 is lain on digit inkjet printer service platform, figure is processed by air brushing software RIP, on 2 of gloss oil silane coupling agents by the mode printing pattern layer 3 of six look numerial code spray drawings, air brushing precision 2500DPI, the solid machine of the 1000W UV light being carried by spray drawing apparatus in air brushing process solidifies simultaneously; Air brushing environment is controlled at 25 DEG C of temperature, humidity 50%;
(3) substrate 1 of spraying good pattern layer 3 is sent in Semi-automatic screen process press, adopt 200 order silk screens, in patterned layer 3, print supercoat 4, the material of supercoat 4 is single-component acrylic resin ink, and the component of this single-component acrylic resin gloss oil is special acrylic resin modified; In printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, sending into light wave drying tunnel, is drying and processing 7 minutes under the condition of 180 DEG C in temperature, obtains tempered-glass decorative board finished product.
Embodiment 2: air-conditining decoration panel
(1) choose the substrate 1 that the thickness be made up of toughened glass material is 2.0mm, use Semi-automatic screen process press to carry out printing varnish silane coupling agent 2, gloss oil silane coupling agent 2 adopts two component epoxy series plastics gloss oil, and described two component epoxy series plastics gloss oil contains some special gene; Adopt 250 order silk screens, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, send into light wave drying tunnel, drying and processing 7 minutes under the condition of 175 DEG C of temperature;
(2) substrate 1 that prints gloss oil silane coupling agent 2 is lain on digit inkjet printer service platform, figure is processed by air brushing software RIP, on 2 of gloss oil silane coupling agents by the mode printing pattern layer 3 of six look numerial code spray drawings, air brushing precision 1500DPI, the solid machine of the 1000W UV light being carried by spray drawing apparatus in air brushing process solidifies simultaneously; Air brushing environment is controlled at 15 DEG C of temperature, humidity 40%;
(3) substrate 1 of spraying good pattern layer 3 is sent in Semi-automatic screen process press, adopt 200 order silk screens, in patterned layer 3, print supercoat 4, the material of supercoat 4 is single-component oleic series resin ink, and the component of this single-component oleic series resin gloss oil is special acrylic resin modified; In printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, sending into light wave drying tunnel, is drying and processing 7 minutes under the condition of 175 DEG C in temperature, obtains tempered-glass decorative board finished product.
Embodiment 3: refrigerator decorative panel
(1) choose the substrate 1 that the thickness be made up of toughened glass material is 5.0mm, use Semi-automatic screen process press to carry out printing varnish silane coupling agent 2, gloss oil silane coupling agent 2 adopts two component epoxy series plastics gloss oil, and described two component epoxy series plastics gloss oil contains some special gene; Adopt 300 order silk screens, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, send into light wave drying tunnel, drying and processing 8 minutes under the condition of 180 DEG C of temperature;
(2) substrate 1 that prints gloss oil silane coupling agent 2 is lain on digit inkjet printer service platform, figure is processed by air brushing software RIP, on 2 of gloss oil silane coupling agents by the mode printing pattern layer 3 of six look numerial code spray drawings, air brushing precision 3000DPI, the solid machine of the 1000W UV light being carried by spray drawing apparatus in air brushing process solidifies simultaneously; Air brushing environment is controlled at 30 DEG C of temperature, humidity 65%;
(3) substrate 1 of spraying good pattern layer 3 is sent in Semi-automatic screen process press, adopt 200 order silk screens, in patterned layer 3, print supercoat 4, the material of supercoat 4 is single-component acrylic resin ink, and the component of this single-component oleic series resin gloss oil is special acrylic resin modified; In printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience screen printing forme is not contacted with stock except nip, ink is under the squeeze effect of sdueegee, by mesh, bite stock from moving nip; After finishing printing, sending into light wave drying tunnel, is drying and processing 8 minutes under the condition of 180 DEG C in temperature, obtains tempered-glass decorative board finished product.
Claims (1)
1. a making method that adopts the tempered-glass decorative plate of numerial code spray drawing making, is characterized in that comprising the steps:
(1) choose the substrate (1) of being made by toughened glass material, substrate (1) is sent in Semi-automatic screen process press, adopt silk screen at substrate surface printing varnish silane coupling agent (2), in printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience does not contact screen printing forme except nip with stock, ink is under the squeeze effect of sdueegee, pass through mesh, bite stock from moving nip, after finishing printing, sending into light wave drying tunnel, is drying and processing 7 ~ 8 minutes under the condition of 170 DEG C ~ 180 DEG C in temperature,
(2) substrate (1) that prints gloss oil silane coupling agent (2) is lain on digit inkjet printer service platform, figure is processed by air brushing software RIP, on gloss oil silane coupling agent (2) face, pass through the mode printing pattern layer (3) of six look numerial code spray drawings, air brushing precision is between 1500 ~ 3000DPI, and the solid machine of 1000W UV light being carried by spray drawing apparatus in air brushing process solidifies simultaneously; Air brushing environment is controlled at 15 DEG C ~ 30 DEG C of temperature, humidity 40% ~ 65%;
(3) substrate (1) that sprays good pattern layer (3) is sent in Semi-automatic screen process press, adopt silk screen at patterned layer (3) upper printing supercoat (4), in printing process, through transmission rig transferring power, allow sdueegee push at the volley ink and screen printing forme, make screen printing forme and stock form a nip, because silk screen has high tensile, sdueegee is produced to power screen resilience does not contact screen printing forme except nip with stock, ink is under the squeeze effect of sdueegee, pass through mesh, bite stock from moving nip, after finishing printing, sending into light wave drying tunnel, is drying and processing 7 ~ 8 minutes under the condition of 170 DEG C ~ 180 DEG C in temperature, obtains tempered-glass decorative board finished product.