CN102582208A - Pmma/abs复合板材生产工艺 - Google Patents
Pmma/abs复合板材生产工艺 Download PDFInfo
- Publication number
- CN102582208A CN102582208A CN2011104431101A CN201110443110A CN102582208A CN 102582208 A CN102582208 A CN 102582208A CN 2011104431101 A CN2011104431101 A CN 2011104431101A CN 201110443110 A CN201110443110 A CN 201110443110A CN 102582208 A CN102582208 A CN 102582208A
- Authority
- CN
- China
- Prior art keywords
- pmma
- abs
- raw material
- composite board
- abs composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种PMMA/ABS复合板材生产工艺,再生产时首先向PMMA原料中按重量百分比加入1%-5%的聚酯接枝改性硅酮助剂进行混炼,然后在通过挤出机挤压PMMA原料、ABS原料,并进行复合形成PMMA/ABS复合板材。该生产工艺在PMMA原料中加入聚酯接枝改性硅酮助剂进行混炼,能改善PMMA的表面性能,提高PMMA表面耐刮擦、耐磨损、光滑性、憎水性,并降低表面摩擦系数,这样加入该助剂后形成的PMMA板与ABS板复合后可直接形成PMMA/ABS复合板材,无需再在PMMA板表面设置防划伤保护层,这样就可有效简化工艺,提高生产效率,降低企业的生产成本。
Description
技术领域
本发明涉及一种复合板材生产工艺,特别涉及一种耐刮擦、耐磨损PMMA/ABS复合板材生产工艺。
背景技术
目前生产耐刮擦、耐磨损PMMA/ABS复合板材主要采用如下三步:1生产PMMA板材;2)采用HARD-COATING(表面硬化)设备在提高PMMA板材表面形成耐刮擦、耐磨损的防划伤保护层;3)把PMMA板材与ABS板材用胶水粘合在一起形成耐刮擦、耐磨损PMMA/ABS复合板材。上述生产工艺工序复杂,生产环境不友好,生产效率较低。再有生产成本很高,设备价格昂贵,尤其是HARD-COATING设备投资巨大,会给企业的生产运营带来很大的压力。
发明内容
针对上述现有技术的不足,本发明要解决的技术问题是提供一种无需使用HARD-COATING设备在PMMA板材表面形成耐刮擦、耐磨损的防划伤保护层,就可实现耐刮擦、耐磨损PMMA/ABS复合板材生产的工艺。
为解决上述技术问题,本发明采用如下技术方案:
一种PMMA/ABS复合板材生产工艺,再生产时首先向PMMA原料中按重量百分比加入1%-5%的聚酯接枝改性硅酮助剂进行混炼,然后在通过挤出机挤压PMMA原料、ABS原料,并进行复合形成PMMA/ABS复合板材。
优选的,向PMMA原料中加入聚酯接枝改性硅酮助剂按重量百分比为3%。
优选的,所述PMMA原料、ABS原料采用模内复合共挤工艺形成PMMA/ABS复合板材。
优选的,所述PMMA/ABS复合板材中PMMA材料、ABS材料厚度的复合比为8∶92。
上述技术方案具有如下有益效果:该PMMA/ABS复合板材生产工艺在PMMA原料中加入聚酯接枝改性硅酮助剂进行混炼,聚酯接枝改性硅酮助剂是多功能的塑料改性助剂,特别能改善PMMA的表面性能,提高PMMA表面耐刮擦、耐磨损、光滑性、憎水性,并降低表面摩擦系数,而且由于是有机接枝的锚固作用,其与PMMA的相容性非常好,不会迁移、析出。这样加入该助剂后形成的PMMA板与ABS板复合后可直接形成PMMA/ABS复合板材,而无需再在PMMA板表面设置防划伤保护层,这样就可有效简化工艺,提高生产效率,而且可节省企业购买HARD-COATING设备的资金,降低企业的生产成本。
具体实施式
下面以具体实施例对本发明的实施步骤进行详细介绍:
采用该PMMA/ABS复合板材生产工艺生产PMMA/ABS复合板材时,首先向PMMA原料中按重量百分比加入1%-5%的聚酯接枝改性硅酮助剂进行混炼,经过多次的试验PMMA中添加3%聚酯接枝改性硅酮助剂,性价比最高。然后采用采用模内复合共挤工艺挤压PMMA原料、ABS原料,并进行复合形成PMMA/ABS复合板材。PMMA原料、ABS原料采用模内复合共挤工艺形成PMMA/ABS复合板材,这样可确保板材复合均匀,而不采用通常的复合体复合再到模内。
挤压PMMA原料、ABS原料的两个挤出机直径分别为120MM和45MM,螺杆L/D比分别为36和38,这样可有效保证挤出机的挤出量相匹配及物料充分熔融。在挤压过程中挤出机上应加装熔体计量泵,确保挤出无波动平稳。精密模具的开发采用双层衣架型,确保精密复合。为确保耐刮擦、耐磨损PMMA/ABS复合板最佳,PMMA/ABS复合板材中PMMA材料、ABS材料厚度的复合比为8∶92。
该PMMA/ABS复合板材生产工艺在PMMA原料中加入聚酯接枝改性硅酮助剂进行混炼,聚酯接枝改性硅酮助剂是多功能的塑料改性助剂,特别能改善PMMA的表面性能,提高PMMA表面耐刮擦、耐磨损、光滑性、憎水性,并降低表面摩擦系数,而且由于是有机接枝的锚固作用,其与PMMA的相容性非常好,不会迁移、析出。这样加入该助剂后形成的PMMA板与ABS板复合后可直接形成PMMA/ABS复合板材,而无需再在PMMA板表面设置防划伤保护层,这样就可有效简化工艺,提高生产效率,而且可节省企业购买HARD-COATING设备的资金,降低企业的生产成本。
以上对本发明实施例所提供的一种PMMA/ABS复合板材生产工艺的合成方法进行了详细介绍,对于本领域的一般技术人员,依据本发明实施例的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制,凡依本发明设计思想所做的任何改变都在本发明的保护范围之内。
Claims (4)
1.一种PMMA/ABS复合板材生产工艺,其特征在于:在生产时首先向PMMA原料中按重量百分比加入1%-5%的聚酯接枝改性硅酮助剂进行混炼,然后在通过挤出机挤压PMMA原料、ABS原料,并进行复合形成PMMA/ABS复合板材。
2.根据权利要求1所述的PMMA/ABS复合板材生产工艺,其特征在于:向PMMA原料中加入聚酯接枝改性硅酮助剂按重量百分比为3%。
3.根据权利要求1所述的PMMA/ABS复合板材生产工艺,其特征在于:所述PMMA原料、ABS原料采用模内复合共挤工艺形成PMMA/ABS复合板材。
4.根据权利要求1所述的PMMA/ABS复合板材生产工艺,其特征在于:所述PMMA/ABS复合板材中PMMA材料、ABS材料厚度的复合比为8∶92。