CN102566127A - Forming method for liquid crystal cell for 3D (three-dimensional) liquid crystal glasses - Google Patents
Forming method for liquid crystal cell for 3D (three-dimensional) liquid crystal glasses Download PDFInfo
- Publication number
- CN102566127A CN102566127A CN2012100250332A CN201210025033A CN102566127A CN 102566127 A CN102566127 A CN 102566127A CN 2012100250332 A CN2012100250332 A CN 2012100250332A CN 201210025033 A CN201210025033 A CN 201210025033A CN 102566127 A CN102566127 A CN 102566127A
- Authority
- CN
- China
- Prior art keywords
- liquid crystal
- ito glass
- ito
- glass
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a forming method for a liquid crystal cell for 3D (three-dimensional) liquid crystal glasses, which includes the steps: cleaning, photoetching, arranging PS (photoresist spacer) supporting columns, coating PI (polyimide) films, forming the cell, cutting, injecting, sealing, performing visual inspection or/and electrical inspection, and the like. The forming method for the liquid crystal cell for the 3D liquid crystal glasses utilizes the PS supporting columns arranged on lower ITO (indium-tin oxide) glass to replace resin powder balls in an original liquid crystal cell, so that the cell thickness is supported. When the cell thickness is small, the PS supporting columns are sufficiently and fixedly adhered with the glass surface and cannot be separated from the glass to vibrate, so that noise of a liquid crystal screen is avoided.
Description
Technical field
The present invention relates to a kind of forming liquid crystal box method, relate in particular to a kind of 3D liquid crystal glasses forming liquid crystal box method.
Background technology
Existing one-tenth box technology, the thick control of box mainly relies on size, density and the homogeneity of the support powder between two sheet glass to guarantee.The technology of dusting is at the identical sphere of powder of a slice sprinkling particle diameter on glass, is divided into doing spray and two kinds of technologies of wet shot.Doing spray, is that the resin sphere of powder is sprayed in spray gun through pressing sky or nitrogen, and under effect of electric field, the sphere of powder is scattered in the ito glass surface.The homogeneity of powder is to control through parameters such as the distance of spray gun and glass, spray gun pressure, electric field intensity and distribution (spray gun voltage, steel wire voltage), settling times.The density of powder is through how much controlling of the amount of dusting once.Wet shot is that the resin sphere of powder is mixed with volatile organic solvent in proportion, and mixed liquor is sprayed at glass surface, and organic solvent volatilization back glass stays the sphere of powder.The homogeneity of powder is to control through parameters such as the distance of spray gun and glass, the time of dusting, settling times.The density of powder is how much controlling through powder ratio in the mixed liquor.The sphere of powder of two kinds of spray processing formation has common deficiency; At first; The sphere of powder is unfixing between two sheet glass, and it can move under external force (like ultrasound wave etc.) effect, when being used in the 3D glasses; When two sheet glass gaps less than 4 microns, the high-speed switch of liquid crystal display can cause the vibrations of the sphere of powder and produce the noise of screen; Secondly, be to guarantee the powder unanimity that is evenly distributed, the some places powder is many, and the some places powder is few, even the powder clustering phenomena is arranged.
Summary of the invention
In order to overcome the deficiency of above-mentioned prior art, the present invention provides a kind of 3D liquid crystal glasses forming liquid crystal box method, may further comprise the steps,
Clean, clean ito glass and dry with as the following ito glass that is arranged at 3D liquid crystal glasses liquid crystal cell lower floor and be arranged at the last ito glass on 3D liquid crystal glasses liquid crystal cell upper strata;
Photoetching, on cleaning up ito glass and down on the ito glass respectively photoetching make the ITO figure.
The PS support column is provided with, and makes the PS support column being formed on the ITO figure of ito glass, and said PS support column adopts epoxy resin;
The PI film applies, at last ito glass, apply PI liquid respectively on the ITO figure of ito glass down, be coated on ito glass, down reach with the last PI film that forms directed usefulness by the certain orientation friction with flannelette respectively behind the PI liquid hot setting of ito glass under the PI film;
Become box, get ito glass and frame adhesive is set, will go up ito glass and down ito glass fit and with frame adhesive curing to process sylphon;
Cutting cuts into unit box to whole sylphon;
Perfusion vacuumizes unit box, from the perfusing hole perfusion liquid crystal of unit box;
Seal, perfusing hole is sealed with ultraviolet curing glue;
Estimate or/and electrical measurement is checked the outward appearance and the display graphics of product through light platform and electrical measurement machine;
Of the present inventionly further be improved to, said 3D liquid crystal glasses forming liquid crystal box method is further comprising the steps of, pastes polaroid in the top and bottom of liquid crystal cell.
Of the present inventionly further be improved to, may further comprise the steps during said PS support column is provided with,
Clean, clean the following ito glass that the ITO figure is arranged, the Impurity removal of the ITO patterned surface that descends ito glass is clean;
Drip glue, drip row's epoxy resin liquid on following ito glass surface;
Frictioning is evenly scraped completely whole following ito glass with glue scraping plate with epoxy resin liquid;
Spin coating is placed on the following ito glass that is coated with epoxy resin liquid on the spin coater, and ito glass and high speed rotating form the PS film of consistency of thickness at following ito glass face thereby vacuum suction is stayed;
Preliminary drying covers together the solvent evaporates in the epoxy resin liquid is fallen to make the face of PS film and glass;
Exposure, design is transferred to down the dot pattern on the mask plate on the ito glass through ultraviolet exposure by the dot pattern equidistant, that diameter is consistent on the mask plate;
Develop, removed by the part of ultraviolet radiation, the epoxy resin solid that on following ito glass surface, forms equal altitudes, column is as the PS support column through developer solution.
Clean the developer solution of ito glass remained on surface and the photosensitive material of dissolving under cleaning with DI water.
Solidify, will descend the moisture oven dry in ito glass and the epoxy resin through high temperature.
Of the present inventionly further be improved to, the rotating speed of said spin coater is greater than 600 circle per minutes.
Of the present inventionly further be improved to, said thickness is less than 4 microns.
Of the present inventionly further be improved to, the preliminary drying temperature in the said soft-bake step is lower than 100 degree.
Of the present inventionly further be improved to, adopt DI water to clean in the said cleaning step.
Of the present inventionly further be improved to, in the said PI film coating step, the solidification temperature of said PI liquid is 250 ℃.
Compared to prior art, the present invention adopts the PS support column that is arranged at down ito glass to replace the resin sphere of powder in original liquid crystal cell, plays the thick supporting role of box.Enough again bonding firmly under the thick situation of thin box with glass surface, can not separate to produce and vibrate with glass, the result then can not produce the noise of liquid crystal display.
Description of drawings
Fig. 1 is the structural representation of 3D liquid crystal glasses liquid crystal cell of the present invention.
Fig. 2 is the process flow diagram of 3D liquid crystal glasses forming liquid crystal box method of the present invention.
Fig. 3 is the process flow diagram that the PS support column of PS in the 3D liquid crystal glasses forming liquid crystal box method of the present invention is provided with.
Embodiment
See also Fig. 1 to Fig. 3; The invention provides a kind of 3D liquid crystal glasses liquid crystal cell 10; Comprise ITO (Indium-Tin Oxide; Tin indium oxide) glass 11, time ito glass 12, PS (photoresist spacer, photonasty clearance material) support column 13, last PI (polyimide, polyimide) film 15, following PI film 16, liquid crystal 21 and frame adhesive 23.
Last ito glass 11 comprises top glass substrate 111 and goes up ITO film 113 that following ito glass 12 comprises that lower glass substrate 121 reaches ITO film 123 down.The 3D liquid crystal glasses liquid crystal cell 10 of present embodiment also can be provided with polaroid 25, following polaroid 27.Last polaroid 25, polaroid 27 can fit in top glass substrate 111 and lower glass substrate 121 respectively down.Following polaroid 27, lower glass substrate 121, down ITO film 123, liquid crystal 21, go up ITO film 113, top glass substrate 111, go up polaroid 25 and set gradually from the bottom to top.Top glass substrate 111 and lower glass substrate 121 adopt frame adhesive 23 to be bonded with each other.Last ito glass 11, the sealing of fitting of ito glass 12 and frame adhesive 23 forms airtight inner chamber down, and liquid crystal 21 is filled in the airtight inner chamber.
Said PS support column is arranged in the said closed cavity; Said PS support column is fixedly connected on said ITO film and supports the said ito glass 11 of going up; Said PI film 16 down is covered in said PS support column and reaches ITO film 123 down, and the said PI film 15 of going up is covered in the said ITO film 113 of going up.PS (photoresist spacer, photonasty clearance material) support column 13 adopts epoxide resin material.PS (photoresist spacer, photonasty clearance material) support column 13 is to be formed by liquid-solidization of epoxy resin.Last PI film 15 reaches down, and PI film 16 is formed by PI liquid hot setting.
After liquid crystal 21 charged into, liquid crystal molecule presented continuous 90 degree distortion configurations in liquid crystal cell.The pitch p of liquid crystal molecule satisfies the relation of following formula with respect to light wavelength λ in the said liquid crystal cell:
p>4d，p>λ/Δn，Δn=?n
e-n
o
D is a liquid crystal layer box thickness, n
oBe ordinary refraction index, n
eBe the extraordinary ray refractive index, Δ n is the refractive index anisotropy.10 one-tenth cassette methods of a kind of 3D liquid crystal glasses liquid crystal cell, 10 one-tenth cassette methods of said 3D liquid crystal glasses liquid crystal cell may further comprise the steps:
Clean, clean ito glass (Indium-Tin Oxide, tin indium oxide) and dry with as the following ito glass 12 that is arranged at 3D liquid crystal glasses liquid crystal cell 10 lower floors and be arranged at the last ito glass 11 on 3D liquid crystal glasses liquid crystal cell 10 upper stratas.ITO glass can be selected according to requirement of products.Following ito glass 12 can adopt clean-out system and DI water (Deionization Water, deionized water) to clean, and can will descend the impurity on ito glass 12 surfaces and greasy dirt to clean through physics or chemical method.After cleaning, following ito glass 12 needs water is removed and drying, to guarantee the crudy of next step.
Photoetching, on cleaning up ito glass 11 and down on the ito glass 12 (Indium-Tin Oxide, tin indium oxide) respectively photoetching make the ITO figure.Photoetching method is identical with existing ito glass photoetching method, and the ITO figure is formed through photoetching by the following ITO film 123 of following ito glass 12, comprises and steps such as gluing, exposure, development, etching repeats no more at this.The ITO figure divides adjustment of the printing plate figure and following domain shape, and last ito glass 11 adopts and carries out photoetching with following ito glass 12 identical methods.
PS (photoresist spacer, photonasty clearance material) support column 13 is provided with, and in the present embodiment, PS support column 13 adopts epoxy resin.In this step, be formed at the PS support column 13 of making the epoxy resin material on the ITO figure of ito glass.
PI (polyimide; Polyimide) film applies; At last ito glass 11, apply PI (polyimide respectively on the ITO figure of ito glass 12 down; Polyimide) liquid, be coated on ito glass 11, down behind the PI liquid hot setting of ito glass 12 respectively with flannelette by last PI film 15 and the following PI film 16 of certain orientation friction to form directed usefulness.The solidification temperature of PI liquid is 250 ℃.Last PI film reaches down, and the PI film is used for making the liquid crystal 21 of liquid crystal cell to reach the specific direction orientations in PI film edge down at last PI film.In the present embodiment, the PI film was to be formed by liquid-solidization of PI that is coated on ito glass 11, following ito glass 12 respectively under last PI film reached.
Become box, get ito glass 11 and stamp sealing epoxy resin glue as frame adhesive 23, adopt the silk screen process mode printing ITO electrode conduction point glue on the ito glass 12 down equally with the silk screen process mode.To go up ito glass 11 and down ito glass 12 fit and frame adhesive 23 solidified to process sylphon.During applying alignment mark can be set, and press the alignment mark contraposition and fit.During curing can to two blocks of glass exert pressure with so that liquid crystal 21 box thickness keep evenly.
Cutting cuts into unit box to whole sylphon.
Perfusion vacuumizes unit box, from the perfusing hole perfusion liquid crystal 21 of unit box.
Seal, perfusing hole is sealed with ultraviolet curing glue.
Estimate or/and electrical measurement is checked the outward appearance and the display graphics of product through light platform and electrical measurement machine.
Paste polaroid, paste polaroid respectively according to product requirement, accomplish production of products in the top and bottom of liquid crystal cell.
On following ito glass 12, carrying out 13 settings of PS support column may further comprise the steps:
Clean, clean the following ito glass 12 that the ITO figure is arranged with DI water (Deionization Water, deionized water), the Impurity removal of ITO patterned surface is clean.
Drip glue, drip row's epoxy resin liquid on following ito glass 12 surfaces with minim pipette, the dropping liquid amount is by pressing empty pressure size to control.Epoxy resin liquid can adopt the mixed liquor of liquid-state epoxy resin or epoxy resin and solvent configuration.
Frictioning is evenly scraped completely whole following ito glass 12 with glue scraping plate with epoxy resin liquid.It is understandable that, can be through surperficial gap of glue scraping plate and following ito glass 12 and glue scraping plate translational speed being set to obtain the thickness and the homogeneity of required epoxy resin liquid.
Spin coating will have the following ito glass 12 of epoxy resin liquid to be placed on the spin coater, and ito glass 12 and high speed rotating are at 12 PS films that form consistency of thickness of following ito glass thereby vacuum suction is stayed.The rotating speed of high speed rotating is greater than 600 circle per minutes.The controllable film thickness of PS film is built in below 4 microns.
Preliminary drying so that the solvent evaporates in the epoxy resin liquid is fallen, covers together the face of PS film and glass.The preliminary drying temperature is lower than 100 degree.
Exposure, design through ultraviolet exposure, is transferred to the dot pattern on the mask plate on glass by the dot pattern equidistant, that diameter is consistent on the mask plate.Epoxy resin liquid is photosensitive material, receive the radiation of ultraviolet after, it is crosslinked that molecule takes place, and becomes soluble substance.
Develop, removed by the part of ultraviolet radiation, the epoxy resin solid that on following ito glass 12 surfaces, forms equal altitudes, column is as PS support column 13 through developer solution.Because the film thickness monitoring of PS film is below 4 microns, thereby the height of the PS support column 13 that forms after the sensitization of PS film is also less than 4 microns.
Clean the developer solution of ito glass 12 remained on surface and the photosensitive material of dissolving under cleaning with DI water.
Curing will descend ito glass 12 and the moisture in the epoxy resin to dry through high temperature, the bonding strength of ito glass 12 and epoxy resin under improving simultaneously.
The present invention adopts the PS support column that is arranged at down ito glass 12 to replace the resin sphere of powder in original liquid crystal cell, plays the thick supporting role of box.Enough again bonding firmly under the thick situation of thin box with glass surface, can not separate to produce and vibrate with glass, the result then can not produce the noise of liquid crystal display.
Above content is to combine concrete preferred implementation to the further explain that the present invention did, and can not assert that practical implementation of the present invention is confined to these explanations.For the those of ordinary skill of technical field under the present invention, under the prerequisite that does not break away from the present invention's design, can also make some simple deduction or replace, all should be regarded as belonging to protection scope of the present invention.The present invention does not address part and is applicable to prior art.
Claims (8)
1. 3D liquid crystal glasses forming liquid crystal box method is characterized in that: may further comprise the steps,
Clean, clean ito glass and dry with as the following ito glass that is arranged at 3D liquid crystal glasses liquid crystal cell lower floor and be arranged at the last ito glass on 3D liquid crystal glasses liquid crystal cell upper strata;
Photoetching, on cleaning up ito glass and down on the ito glass respectively photoetching make the ITO figure;
The PS support column is provided with, and makes the PS support column being formed on the ITO figure of ito glass, and said PS support column adopts epoxy resin;
The PI film applies, at last ito glass, apply PI liquid respectively on the ITO figure of ito glass down, be coated on ito glass, down reach with the last PI film that forms directed usefulness by the certain orientation friction with flannelette respectively behind the PI liquid hot setting of ito glass under the PI film;
Become box, get ito glass and frame adhesive is set, will go up ito glass and down ito glass fit and with frame adhesive curing to process sylphon;
Cutting cuts into unit box to whole sylphon;
Perfusion vacuumizes unit box, from the perfusing hole perfusion liquid crystal of unit box;
Seal, perfusing hole is sealed with ultraviolet curing glue;
Estimate or/and electrical measurement is checked the outward appearance and the display graphics of product through light platform and electrical measurement machine;
According to the said 3D liquid crystal glasses of claim 1 forming liquid crystal box method, it is characterized in that: said 3D liquid crystal glasses forming liquid crystal box method is further comprising the steps of, pastes polaroid in the top and bottom of liquid crystal cell.
2. according to the said 3D liquid crystal glasses of claim 1 forming liquid crystal box method, it is characterized in that: during being provided with, said PS support column may further comprise the steps,
Clean, clean the following ito glass that the ITO figure is arranged, the Impurity removal of the ITO patterned surface that descends ito glass is clean;
Drip glue, drip row's epoxy resin liquid on following ito glass surface;
Frictioning is evenly scraped completely whole following ito glass with glue scraping plate with epoxy resin liquid;
Spin coating is placed on the following ito glass that is coated with epoxy resin liquid on the spin coater, and ito glass and high speed rotating form the PS film of consistency of thickness at following ito glass face thereby vacuum suction is stayed;
Preliminary drying covers together the solvent evaporates in the epoxy resin liquid is fallen to make the face of PS film and glass;
Exposure, design is transferred to down the dot pattern on the mask plate on the ito glass through ultraviolet exposure by the dot pattern equidistant, that diameter is consistent on the mask plate;
Develop, removed by the part of ultraviolet radiation, the epoxy resin solid that on following ito glass surface, forms equal altitudes, column is as the PS support column through developer solution;
Clean the developer solution of ito glass remained on surface and the photosensitive material of dissolving under cleaning with DI water.
3. solidify, will descend the moisture oven dry in ito glass and the epoxy resin through high temperature.
4. according to the said 3D liquid crystal glasses of claim 3 forming liquid crystal box method, it is characterized in that: the rotating speed of said spin coater is greater than 600 circle per minutes.
5. according to the said 3D liquid crystal glasses of claim 3 forming liquid crystal box method, it is characterized in that: said thickness is less than 4 microns.
6. according to the said 3D liquid crystal glasses of claim 3 forming liquid crystal box method, it is characterized in that: the preliminary drying temperature in the said soft-bake step is lower than 100 degree.
7. according to the said 3D liquid crystal glasses of claim 1 forming liquid crystal box method, it is characterized in that: adopt DI water to clean in the said cleaning step.
8. according to the said 3D liquid crystal glasses of claim 1 forming liquid crystal box method, it is characterized in that: in the said PI film coating step, the solidification temperature of said PI liquid is 250 ℃.