CN102563332A - Kraft paper clad steel wire for seat frame, manufacturing method and application thereof - Google Patents
Kraft paper clad steel wire for seat frame, manufacturing method and application thereof Download PDFInfo
- Publication number
- CN102563332A CN102563332A CN2012100117783A CN201210011778A CN102563332A CN 102563332 A CN102563332 A CN 102563332A CN 2012100117783 A CN2012100117783 A CN 2012100117783A CN 201210011778 A CN201210011778 A CN 201210011778A CN 102563332 A CN102563332 A CN 102563332A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- kraft paper
- paper
- spring steel
- clad steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of paper clad steel wires, particularly, a kraft paper clad steel wire used for a seat frame, a manufacturing method and application of the kraft paper clad steel wire. The kraft paper clad steel wire comprises flame retardant kraft paper and a spring steel wire, and is characterized in that a normal diameter of the steel wire is 1.85-2.15mm; the flame retardant kraft paper is covered and bonded on the outer side of the spring steel wire in a rotation structure; the normal diameter of the wound paper clad steel wire is 3.8-4.0mm; and the flame-retardant kraft paper is covered and bonded on the surface of the spring steel wire by steps of straightening, wrapping, swelling, cutting and the like. The kraft paper clad steel wire used for a seat frame of the invention reduces the leakage of galvanization and parkerising waste gas and waste water to a greater extent, reduces the cost of the production process, strengthens the bonding force of the product, has corrosion resistance, can be cut freely according to the requirements of users in the actual application without influencing the quality of the paper clad steel wire, and can be applied to a plurality of occasions such as corrosion resistance, needing adhesive and the like.
Description
[technical field]
The present invention relates to paper bag wire technique field, a kind of specifically kraft paper Baogang silk and production method and application that is used for chair framework.
[background technique]
Existing steel wire, the steel wire toughness that especially is used for connecting the sofa base serpentine spring is not enough, use for a long time yielding, and under the environment of humidity, the easy corrosion of steel wire, thereby shortened the working life of sofa.Original A level (Spring Steel Wire) adopts plating zinc on surface and phosphatization in practical application, Galvanized Steel Wire is the skeleton of seat, and apparent motion is frequent, therefore needs paper bag steel wire Adhesion force strong.In addition, in course of working, cause zinc-plated leaked liquid, influence air quality, human body is worked the mischief.
[summary of the invention]
The objective of the invention is to solve the deficiency of existing technology, a kind of kraft paper Baogang silk and production method that is used for chair framework is provided, and make it can be used in more occasions that get more.
For realizing a kind of kraft paper Baogang silk that is used for chair framework of above-mentioned purpose design; Comprise fire-retardant kraft paper and Spring Steel Wire; It is characterized in that described steel wire latus rectum is 1.85～2.15mm; Described fire-retardant kraft paper coats with rotational structure and sticks in outside the described Spring Steel Wire, and the paper bag steel wire latus rectum after the winding is 3.8～4.0mm.
Described Spring Steel Wire plating zinc on surface and phosphatization.
The present invention also comprises a kind of method of making kraft paper Baogang silk, comprises paper bag steel wire machine, it is characterized in that coating said Spring Steel Wire surface with fire-retardant kraft paper, and this method may further comprise the steps:
Step 1 is twisted described Spring Steel Wire directly in paper bag steel wire machine;
Step 3, it is upright that described kraft paper Baogang silk is risen, the kraft paper of fastening coating;
Step 4 is cut the kraft paper Baogang silk of step 3.
After step 4, pack tightly the fire-retardant kraft paper that twines on the steel wire of cutting back, carry out finished product packing.
Above-mentioned kraft paper Baogang silk also can be used for one or more in anticorrosion occasion, the sticking occasion of employing Bond.
The present invention compares with existing technology and has the following advantages:
Reduce leaking of zinc-plated and phosphatization waste gas water to a greater extent, environmental protection has ensured again that simultaneously the operator's is healthy.
Reduced the production process cost.
Through the application of paper bag steel wire, strengthened the Adhesion force of product, and had erosion-resisting performance.
This product can cut arbitrarily according to user's request in practical application, does not influence the paper bag wire quality.
[description of drawings]
Fig. 1 is a partial structurtes schematic representation of the present invention;
Fig. 2 is the schematic cross-section of paper bag steel wire of the present invention;
Among the figure: 1. Spring Steel Wire 2. fire-retardant kraft paper
[embodiment]
In conjunction with accompanying drawing the present invention is further specified, the manufacturing technology of this device is very clearly concerning this professional people.
Embodiment:
Choose steel wire:
Can divide three rank supplies of material according to spring working stress state steel wire: the B level is used for the low stress spring, and the C level is used for medium stress spring, and the D level is used for heavily stressed spring.The finished product steel wire is examined tensile strength, is reversed, twines and crooked four performances, and the mechanical property of common specification is following:
1. the B level of the D level steel wire of Φ≤4.0mm and Φ≤6.0mm, the specimen surface of C level steel wire after equaling to twine 2 circles on the plug of steel wire diameter, twining must not crack and rupture.
2. the D level steel wire of Φ＞4.0mm twines 2 circles on the plug of 2 times of steel wire diameter, and the specimen surface after the winding must not crack and rupture.
3. the steel wire of Φ＞6.00mm should carry out the bending check, and sample, must not crack and rupture after the bending to different direction bending 900 along the R=10mm circular arc.
B level and C level steel wire are generally selected 70 (67A, 72A) or 65Mn (67B) for use, and the D level selects for use T9XtA and T8MnA (82B) to produce.
What this was selected for use is the Spring Steel Wire of 72A level.
Equipment choosing paper bag steel wire machine.
The lineal system of strand:
Described Spring Steel Wire is twisted in paper bag steel wire machine directly.
Wrapped system:
Described kraft paper rotation stickup is coated on the straight Spring Steel Wire of strand.
Erection system rises:
It is upright that described kraft paper Baogang silk is risen, the kraft paper of fastening coating;
Diced system:
The kraft paper Baogang silk of step 3 is cut.
The structure of steel wire that obtains comprises following kind:
A: the steel wire latus rectum is 1.85mm, and described fire-retardant kraft paper coats with rotational structure and sticks in outside the described Spring Steel Wire, and the paper bag steel wire latus rectum after the winding is 3.8mm.
B: the steel wire latus rectum is 2.15mm, and described fire-retardant kraft paper coats with rotational structure and sticks in outside the described Spring Steel Wire, and the paper bag steel wire latus rectum after the winding is 4.0mm.
C: the steel wire latus rectum is 2.0mm, and described fire-retardant kraft paper coats with rotational structure and sticks in outside the described Spring Steel Wire, and the paper bag steel wire latus rectum after the winding is 3.9mm.
Claims (5)
1. kraft paper Baogang silk that is used for chair framework; Comprise fire-retardant kraft paper and Spring Steel Wire; It is characterized in that described steel wire latus rectum is 1.85～2.15mm; Described fire-retardant kraft paper coats with rotational structure and sticks in outside the described Spring Steel Wire, and the paper bag steel wire latus rectum after the winding is 3.8～4.0mm.
2. a kind of kraft paper Baogang silk that is used for chair framework as claimed in claim 1 is characterized in that described Spring Steel Wire plating zinc on surface and phosphatization.
3. a method of making kraft paper Baogang silk comprises paper bag steel wire machine, it is characterized in that coating said Spring Steel Wire surface with fire-retardant kraft paper, and this method may further comprise the steps:
Step 1 is twisted described Spring Steel Wire directly in paper bag steel wire machine;
Step 2 is coated on described kraft paper rotation stickup on the straight Spring Steel Wire of strand;
Step 3, it is upright that described kraft paper Baogang silk is risen, the kraft paper of fastening coating;
Step 4 is cut the kraft paper Baogang silk of step 3.
4. a kind of method of making kraft paper Baogang silk as claimed in claim 3 is characterized in that described method is further comprising the steps of, after step 4, packs tightly the fire-retardant kraft paper that twines on the steel wire of cutting back, carries out finished product packing.
5. the application of a kraft paper Baogang silk is characterized in that described kraft paper Baogang silk can be used for anticorrosion occasion, adopts in the Bond bonding occasion one or more.