CN102560282A - 一种渗氮齿轮钢及其热处理方法 - Google Patents

一种渗氮齿轮钢及其热处理方法 Download PDF

Info

Publication number
CN102560282A
CN102560282A CN2012100288999A CN201210028899A CN102560282A CN 102560282 A CN102560282 A CN 102560282A CN 2012100288999 A CN2012100288999 A CN 2012100288999A CN 201210028899 A CN201210028899 A CN 201210028899A CN 102560282 A CN102560282 A CN 102560282A
Authority
CN
China
Prior art keywords
gear
percent
nitriding
hardness
heat treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100288999A
Other languages
English (en)
Inventor
杜树芳
杜威
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012100288999A priority Critical patent/CN102560282A/zh
Publication of CN102560282A publication Critical patent/CN102560282A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种渗氮齿轮钢及其热处理方法，属于材料及热处理，所述渗氮齿轮钢化学成分质量配比为C 0.10％-0.25％、Cr 0.3％-1.0％、Ni 3.0％-4.0％、Mn 1.0％-2.0％、Si 0.2％-0.5％、Al 0.5％-1.5％、Mo 0.2％-0.6％、V 0.1％-0.3％、P≤0.030％、S≤0.030％、余量为Fe和其他残留元素和不可避免杂质；所述热处理方法包括齿轮粗车后固溶处理，半精车和粗滚(剃)齿后去应力退火以及精滚(剃)齿或粗磨齿后渗氮处理.本发明提供用于制造高速重载精密齿轮的新钢种和取代常规渗碳淬火的渗氮方法，齿轮表面硬度700-1000HV，心部硬度38-45HRC，省去淬火工序，工艺简单，齿轮变形小，质量稳定，废品率低，大大提高生产效率。

Description

一种渗氮齿轮钢及其热处理方法
本发明属于材料及热处理，是一种用于制造渗氮齿轮的新钢种及其达到齿轮使用性能的热处理方法
齿轮的使用性能和可靠性靠齿轮材料和热处理质量保证，对于要求高速、连续运行安全可靠性高的中大型齿轮，常用12CrNi3、12Cr2Ni4钢等材料制造，并采用渗碳淬火工艺。这类材料齿轮需经多次渗碳和多次淬火回火，造成齿轮变形很大，工艺复杂，质量不稳定，废品率高，生产周期长。
本发明涉及一种省去渗碳淬火，采用渗氮处理方法制造齿轮的新钢种及其热处理方法，省去渗碳淬火采用空冷固溶处理，根本上杜绝了齿轮变形，采用渗氮处理达到齿轮表面硬化而心部同时经过时效硬化，确保了齿轮的使用性能和精度。
采用本发明制造齿轮，可以大大简化工艺和提高生产效率，根本上解决齿轮变形，质量稳定，废品率很低。本发明也适用于制造压铸模具和塑料模具。

Claims (4)

1.一种渗氮齿轮钢及其热处理方法，所述渗氮齿轮钢化学成分质量配比为C 0.10％-0.25％、Cr 0.3％-1.0％、Ni 3.0％-4.0％、Mn 1.0％-2.0％、Si 0.2％-0.5％、Al 0.5％-1.5％、Mo 0.2％-0.6％、V 0.1％-0.3％、P≤0.030％、S≤0.030％、余量为Fe和其他残留元素和不可避免杂质；所述热处理方法包括固溶处理、去应力退火和渗氮处理。
2.按权利要求1所述热处理方法，其特征在于齿轮粗车后进行固溶处理：840-900℃保温2-4小时空冷，硬度28-33HRC。
3.按权利要求1所述热处理方法，其特征在于齿轮半精车和粗滚(剃)齿后去应力退火：580-600℃保温5-10小时炉冷。
4.按权利要求1所述热处理方法，其特征在于齿轮精滚(剃)齿或粗磨齿后渗氮处理：离子渗氮或气体渗氮，500-550℃保温20-100小时，齿轮表面硬度700-1000HV，心部硬度38-45HRC，渗层深度0.5-1.0mm。 
CN2012100288999A 2012-01-30 2012-01-30 一种渗氮齿轮钢及其热处理方法 Pending CN102560282A (zh)