CN102558814A - Modified polymeric carbon ester material for preparing capacitor housing - Google Patents
Modified polymeric carbon ester material for preparing capacitor housing Download PDFInfo
- Publication number
- CN102558814A CN102558814A CN2011104237008A CN201110423700A CN102558814A CN 102558814 A CN102558814 A CN 102558814A CN 2011104237008 A CN2011104237008 A CN 2011104237008A CN 201110423700 A CN201110423700 A CN 201110423700A CN 102558814 A CN102558814 A CN 102558814A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs
- drying
- carbon ester
- polycarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified polymeric carbon ester material for a capacitor housing. The modified polycarbonate material comprises compositional raw materials with the weight parts as follows: 56 to 75 parts of polycarbonate, 15 to 25 parts of acrylonitrile butadiene styrene (ABS) resin, 2 to 4 parts of ABS-g-maleic anhydride (MAH) compatilizer, 3 to 8 parts of toughening agent MBS (methyl methacrylate-butadiene-styrene), 3 to 4 parts of flame retardants STB, 3 to 4 parts of organosilicon flame retardants, 0.1 to 0.5 part of linear aliphatic epoxy resin, 1 to 2 parts of acrylate and 0.1 to 0.3 part of composite antioxidants B215. The capacitor housing of a locomotive, which is processed by using the material disclosed by the invention, has the advantages of light weight, low cost and high electric strength, and has low probability of deformation.
Description
Technical field
The present invention relates to the engineering plastics field, be specifically related to a kind of modification that is used to prepare capacitor casing and gather the carbon ester material.
Background technology
Be used for the electrical condenser on the power vehicle at present, its shell shell adopts stainless steel or ABS engineering plastics to process usually.The former housing is heavy, and cost is high, is prone to get rusty, and very easily produces the housing puncture again and draws fiery phenomenon, is substituted by the ABS material just gradually.Though and the ABS material housing is in light weight, the wall thickness of the housing that this material is processed must be more than 5cm, and side resistance to deformation temperature is not low; Yielding, but when wall was too thick, difficulty of processing increased; Waste product is many during production, and qualification rate is low, has increased production cost; The ABS material is prone to suction simultaneously, causes the capacitor casing insulating property to reduce, and dielectric strength descends.
Summary of the invention
In order to overcome above-mentioned deficiency, the invention provides a kind of modification that is used to prepare capacitor casing and gather the carbon ester material, adopt this modification to gather the injection molded locomotive capacitor casing of carbon ester material and have good processability, not yielding and the big characteristics of dielectric strength.
The technical scheme that adopts for the present invention of realization above-mentioned purpose is following:
Be used to prepare the modified polycarbonate material of capacitor casing, it is characterized in that: the weight part of its constitutive material is following:
Polycarbonate 56-75 part, ABS resin 15-25 part, ABS-g-MAH compatilizer 2-4 part; Toughner MBS 3-8 part, fire retardant STB 3-4 part, organic silicon fibre retardant 3-4; Line style aliphatic category epoxy resin 0.1-0.5 part, propenoate 1-2 part, composite antioxidant B215 0.1-0.3 part.
The described modification that is used to prepare capacitor casing gathers the carbon ester material, and it is characterized in that: the weight part of its constitutive material is following:
70 parts of polycarbonate, 22 parts of ABS resins, 3 parts of ABS-g-MAH compatilizers, 5 parts of toughner MBS, 3 parts of fire retardant STB, organic silicon fibre retardant 4,0.4 part of line style aliphatic category epoxy resin, 1 part of propenoate, 0.3 part of composite antioxidant B215.
The described modification that is used to prepare capacitor casing gathers the preparation method of carbon ester material, it is characterized in that, specifically may further comprise the steps:
(1) takes by weighing each starting material respectively;
(2) starting material that take by weighing are mixed according to formula rate;
(3) compound is put into carried out drying in the drying machine, drying temperature is 75-85 ℃, and be 8-10 hour time of drying;
(4) drying is good batch mixing drops into twin screw extruder, and extruding pelletization, the barrel zone temperature of forcing machine are 210-270 ℃.
Beneficial effect of the present invention:
Modification of the present invention gathers the carbon ester material, has to have the dual characteristics that gathers carbon ester material and ABS material concurrently, adopts this modification to gather the injection molded locomotive capacitor casing of carbon ester material and has good processability, the not yielding and big characteristics of dielectric strength.
Embodiment
A kind of modification that is used to prepare capacitor casing gathers the carbon ester material, and the weight part of its constitutive material is following:
70 parts of polycarbonate, 22 parts of ABS resins, 3 parts of ABS-g-MAH compatilizers, 5 parts of toughner MBS, 3 parts of fire retardant STB, organic silicon fibre retardant 4,0.4 part of line style aliphatic category epoxy resin, 1 part of propenoate, 0.3 part of composite antioxidant B215.
The modification that is used to prepare capacitor casing gathers the preparation method of carbon ester material, specifically may further comprise the steps:
(1) takes by weighing each starting material respectively;
(2) starting material that take by weighing are mixed according to formula rate;
(3) compound is put into carried out drying in the drying machine, drying temperature is 80 ℃, and be 8 hours time of drying;
(4) drying is good batch mixing drops into twin screw extruder, and extruding pelletization, the barrel zone temperature of forcing machine are 210-270 ℃.
Experimental data
Modification of the present invention gathers the carbon ester material and the ABS properties of materials contrasts like following table:
Performance | Modified polycarbonate of the present invention | ABS |
Tensile strength | 68-75mPa | 40-55mPa |
Bending strength | 97-122mPa | 30-65mPa |
The notch shock toughness | 72-83KJ/m 2 | 15-35KJ/m 2 |
Water-intake rate | 0.4-0.6% | 1.1% |
Heat-drawn wire | 136-152 | 95 |
Second-order transition temperature | 150 | 110 |
Embrittlement temperature | -105-130 | -25 |
Can be found out that by last table the tensile strength of modified polycarbonate, bending strength, notch shock toughness all obviously are superior to the ABS material, heat-drawn wire and second-order transition temperature are higher than the ABS material, and water-intake rate is lower than the ABS material.
Therefore the capacitor casing intensity that becomes with modified polycarbonate materials processed of the present invention is good, is ABS material housing 2-3 times, and is not yielding; Dielectric strength is big, and operable TR is wide, and good processability; Dimensional stability is good, the wall phenomenon that do not contract, and the wall thickness processing of housing is unaffected; Can increase the wall thickness of housing on demand, it is light to have case weight simultaneously, the characteristics that cost is low.
Claims (3)
1. be used to prepare the modified polycarbonate material of capacitor casing, it is characterized in that: the weight part of its constitutive material is following:
Polycarbonate 56-75 part, ABS resin 15-25 part, ABS-g-MAH compatilizer 2-4 part; Toughner MBS 3-8 part, fire retardant STB 3-4 part, organic silicon fibre retardant 3-4; Line style aliphatic category epoxy resin 0.1-0.5 part, propenoate 1-2 part, composite antioxidant B215 0.1-0.3 part.
2. the modification that is used to prepare capacitor casing according to claim 1 gathers the carbon ester material, and it is characterized in that: the weight part of its constitutive material is following:
70 parts of polycarbonate, 22 parts of ABS resins, 3 parts of ABS-g-MAH compatilizers, 5 parts of toughner MBS, 3 parts of fire retardant STB, organic silicon fibre retardant 4,0.4 part of line style aliphatic category epoxy resin, 1 part of propenoate, 0.3 part of composite antioxidant B215.
3. the modification that is used to prepare capacitor casing as claimed in claim 1 gathers the preparation method of carbon ester material, it is characterized in that, specifically may further comprise the steps:
(1) takes by weighing each starting material respectively;
(2) starting material that take by weighing are mixed according to formula rate;
(3) compound is put into carried out drying in the drying machine, drying temperature is 75-85 ℃, and be 8-10 hour time of drying;
(4) drying is good batch mixing drops into twin screw extruder, and extruding pelletization, the barrel zone temperature of forcing machine are 210-270 ℃.