CN102558629A - Ageing-resistant and cold-resistant rubber - Google Patents
Ageing-resistant and cold-resistant rubber Download PDFInfo
- Publication number
- CN102558629A CN102558629A CN2011104192524A CN201110419252A CN102558629A CN 102558629 A CN102558629 A CN 102558629A CN 2011104192524 A CN2011104192524 A CN 2011104192524A CN 201110419252 A CN201110419252 A CN 201110419252A CN 102558629 A CN102558629 A CN 102558629A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- ageing
- rubber
- promotor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ageing-resistant and cold-resistant rubber. The rubber comprises the following components in part by weight: 100 parts of chloroprene rubber, 20 to 30 parts of carbon black, 2 to 8 parts of anti-ageing agent, 1 to 2 parts of accelerator, 10 to 20 parts of plasticizing softener, 3 to 8 parts of zinc oxide, 1 to 2 parts of stearic acid and 1 to 2 parts of paraffin. The ageing-resistant and cold-resistant rubber can be used for a long time at low temperature and has high ageing resistance, and the breaking strength, breaking elongation and hardness of the rubber at low temperature are basically unchanged compared with those of the rubber at normal temperature.
Description
Technical field
The present invention relates to rubber materials, relate in particular to a kind of ageing-resistant arctic rubber.
Background technology
The rubber that under coldcondition, uses, sclerosis prematurely easily, embrittlement, the aging and forfeiture peculiar elasticity of rubber and lose use value.In the prior art, rubber hardens under-20 ℃～-30 ℃ environment, embrittlement, and is aging, influenced its result of use and work-ing life greatly, give produce and life bring very big unfavorable.
Summary of the invention
In order to overcome above-mentioned deficiency, technical problem to be solved provides a kind of ageing-resistant arctic rubber just in the present invention.
For solving the problems of the technologies described above, the technical scheme that the present invention adopted is following:
A kind of ageing-resistant arctic rubber, it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 20～30 parts
Anti-aging agent: 2～8 parts
Promotor: 1～2 part
Plasticising tenderizer: 10～20 parts
Zinc oxide: 3～8 parts
Triple Pressed Stearic Acid: 1～2 part
Paraffin: 1～2 part.
As screening formulation, above-mentioned ageing-resistant arctic rubber, it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 25 parts
Anti-aging agent: 6 parts
Promotor: 1.8 parts
Plasticising tenderizer: 15 parts
Zinc oxide: 5 parts
Triple Pressed Stearic Acid: 1.5 parts
Paraffin: 1.5 parts.
Described anti-aging agent is preferably any one or a few among anti-aging agent 4020, antioxidant 4010NA or the antioxidant A W.
Described promotor is preferably any one or a few among accelerant CZ, captax or the promotor TT.
Described plasticising tenderizer is preferably any one or a few in machine oil, neck xylylene dibutylester or the silicone oil.
Beneficial effect: ageing-resistant arctic rubber of the present invention can use at low temperatures for a long time, and basic no change when its tensile strength at yield, tensile yield, hardness and normal temperature has good ageing-resistant performance.
Embodiment
Embodiment 1
A kind of ageing-resistant arctic rubber, it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 25 parts
Anti-aging agent 4020:6 part
Advance agent CZ:1 part
0.8 part of promotor TT
7 parts in machine oil
Silicone oil: 8 parts
Zinc oxide: 5 parts
Triple Pressed Stearic Acid: 1.5 parts
Paraffin: 1.5 parts.
Above-mentioned recipe ingredient is carried out mixing processing: rubber, starting material weighing-section banburying-a section are opened refining-following sheet-two section banburying-two and section are opened the ageing-resistant arctic rubber of refining-following sheet-promptly get.
Embodiment 2
A kind of ageing-resistant arctic rubber, it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 20 parts
Antioxidant 4010NA: 2 parts
Captax: 1 part
Neck xylylene dibutylester: 10 parts
Zinc oxide: 3 parts
Triple Pressed Stearic Acid: 1 part
Paraffin: 1 part.
Above-mentioned recipe ingredient is carried out mixing processing: rubber, starting material weighing-section banburying-a section are opened refining-following sheet-two section banburying-two and section are opened the ageing-resistant arctic rubber of refining-following sheet-promptly get.
Embodiment 3
A kind of ageing-resistant arctic rubber, it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 30 parts
4 parts of antioxidant 4010NAs
Antioxidant A W:4 part
Promotor TT:2 part
Silicone oil: 20 parts
Zinc oxide: 8 parts
Triple Pressed Stearic Acid: 2 parts
Paraffin: 2 parts.
Above-mentioned recipe ingredient is carried out mixing processing: rubber, starting material weighing-section banburying-a section are opened refining-following sheet-two section banburying-two and section are opened the ageing-resistant arctic rubber of refining-following sheet-promptly get.
The foregoing description does not limit the present invention in any way, and every employing is equal to the technical scheme that replacement or the mode of equivalent transformation obtain and all drops in protection scope of the present invention.
Claims (5)
1. ageing-resistant arctic rubber is characterized in that it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 20～30 parts
Anti-aging agent: 2～8 parts
Promotor: 1～2 part
Plasticising tenderizer: 10～20 parts
Zinc oxide: 3～8 parts
Triple Pressed Stearic Acid: 1～2 part
Paraffin: 1～2 part.
2. ageing-resistant arctic rubber according to claim 1 is characterized in that it comprises the component of following parts by weight:
X 050: 100 parts
Carbon black: 25 parts
Anti-aging agent: 6 parts
Promotor: 1.8 parts
Plasticising tenderizer: 15 parts
Zinc oxide: 5 parts
Triple Pressed Stearic Acid: 1.5 parts
Paraffin: 1.5 parts.
3. ageing-resistant arctic rubber according to claim 1 and 2 is characterized in that: described anti-aging agent is any one or a few among anti-aging agent 4020, antioxidant 4010NA or the antioxidant A W.
4. ageing-resistant arctic rubber according to claim 1 and 2 is characterized in that: described promotor is any one or a few among accelerant CZ, captax or the promotor TT.
5. ageing-resistant arctic rubber according to claim 1 and 2 is characterized in that: described plasticising tenderizer is any one or a few in machine oil, neck xylylene dibutylester or the silicone oil.