CN102557553A - Marine light filling dressing - Google Patents
Marine light filling dressing Download PDFInfo
- Publication number
- CN102557553A CN102557553A CN201110441445XA CN201110441445A CN102557553A CN 102557553 A CN102557553 A CN 102557553A CN 201110441445X A CN201110441445X A CN 201110441445XA CN 201110441445 A CN201110441445 A CN 201110441445A CN 102557553 A CN102557553 A CN 102557553A
- Authority
- CN
- China
- Prior art keywords
- cement
- reducing agent
- rubber powder
- water reducing
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Marine light filling dressing is formed by mixing and stirring 8-20 meshes quartz sand, general silicon 42.5# cement, expanded perlite, ceramic sand, rubber powder, tartaric acid and an efficient water reducing agent. The raw materials comprise, by weight, 15%-25% of the 8-20 meshes quartz sand, 25%-35% of the general silicon 42.5# cement, 5%-7% of the expanded perlite, 25%-35% of the ceramic sand, 5%-7% of the rubber powder, 2% of the tartaric acid and 2% of the efficient water reducing agent. The marine light filling dressing has the advantages of being light in weight, small in density, good in adiabatic and fire-proof performance and the like.
Description
Technical field
[0001] the present invention relates to a kind of dressing peculiar to vessel, relate in particular to a kind of filling dressing.
Background technology
At present; Need utilize other material to carry out levelling for liner part and other insulation of the arcuate part of boats and ships, moist space ceramic tile, the thermal region that breaks etc.; This material is packing material; Existing packing material mainly is a sand-stone concrete, though sand-stone concrete plays certain filling effect, in practical application, still exists not enough.Because the weight of sand-stone concrete is bigger, not only makes troubles, and increased construction area and even ship weight undoubtedly after the construction to construction; Sand-stone concrete belongs to the macrobead material, and its density is bigger, then can't realize filling for the zone that the less need of size are filled; In addition, the disconnected heat of sand-stone concrete and fire-resistant effect are unsatisfactory.
Summary of the invention
The object of the present invention is to provide a kind of not only in light weightly, density is little, and disconnected heat is good with fire performance, and easy construction, is prone to preserve the lightweight filling dressing peculiar to vessel of economy and durability.
A kind of lightweight peculiar to vessel is filled dressing, and it is by 8～20 order silica sands, general silicon 42.5 cement, pearlstone; Pottery sand, rubber powder, the product that tartrate and high efficiency water reducing agent mix together; Its raw material weight component is: 8～20 order silica sands 15%～25%, general silicon 42.5 cement 25%～35%, pearlstone 5%～7%; Pottery sand 25%～35%, rubber powder 5%～7%, tartrate 2% and high efficiency water reducing agent 2%.
The lightweight peculiar to vessel that the present invention relates to is filled dressing, and its raw material i.e. 8～20 order silica sands, general silicon 42.5 cement; Pearlstone, pottery sand, rubber powder; Tartrate and high efficiency water reducing agent can directly be obtained by market, utilize stirrer to stir after above-mentioned raw materials is mixed by proportioning and get final product.
The present invention is applicable to that liner part and other of UPP deck, arcuate part, engine control room, the moist space ceramic tile part of boats and ships need to be incubated, the zone of disconnected thermal effect.During construction, remove earlier dirt, paint, dust, moisture, wet goods above the deck, the mixed with the present invention and water are pressed 3:1 stirs can construct after the stirring (filling levelling) after the mixing; Proportion≤1000kg/m3 of the present invention, construction thickness>=25mm.
The present invention compared with prior art has following advantage:
1, in light weight, it is light by 1/2～1/6 to mix earth than general sandstone;
2, density is little, can realize the zone of the less filling of size is realized filling;
3, have disconnected preferably heat and resistivity against fire;
4, construction cost is practiced thrift in easy construction, is prone to preserve.
Description of drawings
The present invention does not have accompanying drawing
Embodiment
Embodiment 1
A kind of lightweight peculiar to vessel is filled dressing, and it is by 8～20 order silica sands, general silicon 42.5 cement, pearlstone; Pottery sand, rubber powder, the product that tartrate and high efficiency water reducing agent mix together; Its raw material weight component is: 8～20 order silica sands 25%, general silicon 42.5 cement 30%, pearlstone 5%; Pottery sand 30%, rubber powder 6%, tartrate 2% and high efficiency water reducing agent 2%.
Embodiment 2
A kind of lightweight peculiar to vessel is filled dressing, and it is by 8～20 order silica sands, general silicon 42.5 cement, pearlstone; Pottery sand, rubber powder, the product that tartrate and high efficiency water reducing agent mix together; Its raw material weight component is: 8～20 order silica sands 20%, general silicon 42.5 cement 35%, pearlstone 6%; Pottery sand 30%, rubber powder 5%, tartrate 2% and high efficiency water reducing agent 2%.
Embodiment 3
A kind of lightweight peculiar to vessel is filled dressing, and it is by 8～20 order silica sands, general silicon 42.5 cement, pearlstone; Pottery sand, rubber powder, the product that tartrate and high efficiency water reducing agent mix together; Its raw material weight component is: 8～20 order silica sands 15%, general silicon 42.5 cement 35%, pearlstone 5%; Pottery sand 35%, rubber powder 6%, tartrate 2% and high efficiency water reducing agent 2%.
Claims (1)
1. a lightweight peculiar to vessel is filled dressing, and it is characterized in that: it is by 8～20 order silica sands, general silicon 42.5 cement, pearlstone; Pottery sand, rubber powder, the product that tartrate and high efficiency water reducing agent mix together; Its raw material weight component is: 8～20 order silica sands 15%～25%, general silicon 42.5 cement 25%～35%, pearlstone 5%～7%; Pottery sand 25%～35%, rubber powder 5%～7%, tartrate 2% and high efficiency water reducing agent 2%.