CN102557551A - Fluid-solid coupling similar material for model test and preparation method for material - Google Patents
Fluid-solid coupling similar material for model test and preparation method for material Download PDFInfo
- Publication number
- CN102557551A CN102557551A CN2011104270646A CN201110427064A CN102557551A CN 102557551 A CN102557551 A CN 102557551A CN 2011104270646 A CN2011104270646 A CN 2011104270646A CN 201110427064 A CN201110427064 A CN 201110427064A CN 102557551 A CN102557551 A CN 102557551A
- Authority
- CN
- China
- Prior art keywords
- admittedly
- vaseline
- coupled
- stream
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a fluid-solid coupling similar material for a model test. The material consists of the following raw materials in part by weight: 1 part of standard sand, 0.05 to 0.15 part of barite powder, 0.05 to 0.15 part of talcpowder, 0.05 to 0.125 part of cement, 0.04 to 0.12 part of vaseline, 0 to 0.15 part of silicone oil and 0.05 to 0.1 part of mixing water. Hydraulic cement and non-hydrophilic vaseline are taken as cementing agents in the material, so that the problem that the similar material is softened and disintegrated when meeting water is solved, and the strength and elastic modulus of the material can be adjusted in a wide range; the silicone oil is taken as an adjuster, so that the water physical indexes such as permeability and the like of the material can be adjusted under the condition that the mechanical indexes of the material are basically not influenced, and the physical and mechanical properties and water physical properties of the material can meet the test requirement; and compared with previous research, the invention has the advantages that: the intercoupling effect of a rock body and water is truly simulated, and the obtained geomechanical similar model test research result is more accurate.
Description
Technical field
Admittedly the present invention relates to a kind of stream-analog material and preparation method thereof that is coupled that is used for model trial, belong to materials science field.
Background technology
At present, a lot of scholars study the optimization of underground works design and constructional method in a large number through geomechanical model test, carry out the exploration of construction process mechanics rule.But present underground project model test exists significantly not enough, and analog material of the prior art only considers that mostly physical mechanics is similar, and most analog materials can be met the water disintegration, Gu can't be applied in stream-coupling model test.Admittedly for the paraffin class of the minority analog material that flow-is coupled; Also just pay attention to solving the problem that material is met the water disintegration; And very high to the temperature condition requirement, the rational adjusting of mechanical property and water has dependency, is difficult to guarantee that the physico-mechanical properties and the water rational faculty satisfy TR simultaneously.So the seepage simulation under the true hydraulic condition is not often done in the research in past, only adopt flexible loading simulation water pressure, can not reflect the practical situation under rock mass and the water coupling, admittedly stream that neither be real-analog simulation is coupled.
Summary of the invention
To above-mentioned prior art, admittedly the invention provides a kind of stream-analog material that is coupled that is used for model trial, and its preparation method is provided.Gu stream of the present invention-coupling model test analog material adopts not hydrophilic gelling material, material is met the not softening disintegration of water, satisfies similar two conditions with perviousness of solid deformation simultaneously, does not receive the temperature and humidity condition influence.
The present invention realizes through following technical scheme:
A kind of be used for model trial stream-admittedly analog material is coupled; Form by the raw material of following weight part: 1 part of standard sand, 0.05～0.15 part of ground barium sulfate, 0.05～0.15 part of talcum powder; 0.05～0.125 part of cement; 0.04～0.12 part in Vaseline, 0～0.15 part of silicone oil, 0.05～0.1 part of mixing water.
Preferably, form: 1 part of standard sand, 0.085 part of ground barium sulfate, 0.085 part of talcum powder, 0.065 part of cement, 0.075 part in Vaseline, 0.05 part of silicone oil, 0.1 part of mixing water by the raw material of following weight part.
The particle diameter of said standard sand is less than 5mm.
Said ground barium sulfate fineness is 625 orders.
Talcous fineness is 1250 orders.
Said cement is that ultimate compression strength is the high-quality white portland cement of 32.5MPa.
Said Vaseline is the nontoxic medical grade Vaseline of white.
Said silicone oil is the methyl-silicone oil of viscosity 1500.
Affiliated mixing water is conventional water, plays mix.
Admittedly the said preparation method who is used for the stream-analog material that is coupled of model trial, step is following:
(1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline and silicone oil in proportion;
(2) standard sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
(3) add mixing water, fully stir;
(4) add regulator silicone oil, mix thoroughly;
(5) Vaseline is heated to 45 ℃～60 ℃, makes it molten for liquid;
(6), and fully stir with liquid Vaseline and the resulting material mixing of step (4);
(7) cool off 5～10min under the room temperature, admittedly promptly get be used for model trial stream-analog material is coupled.
Of the present invention be used for model trial stream-admittedly analog material is coupled; The cement of the employing hydraulicity and non-hydrophilic Vaseline are as jointing compound; Solved the problem of analog material chance water softening disintegration, the intensity of material and Young's modulus can be regulated in a big way; Adopt silicone oil as regulator, can under the situation of the mechanical index that does not influence material basically, regulate the rational index of water such as perviousness of material, guarantee that the physico-mechanical properties and the water rational faculty of material can both satisfy TR.Material significant parameter scope such as table 1, stress-strain(ed) curve under single shaft resistance to compression condition such as accompanying drawing 1.
Table 1
Of the present invention be used for model trial stream-admittedly analog material is coupled; Admittedly studied the technical scheme and the preparation method of the stream-analog material that is coupled that can be used for model trial; Solve traditional analog material and met the problem of water softening disintegration; Be difficult to independent adjusting admittedly improved conventional flow-the be coupled analog material physico-mechanical properties and the water rational faculty, the defective of the rational analog simulation degree of water difference.Be applied in the model trial admittedly should flow-be coupled analog material, compared with forefathers research, real simulation the effect of intercoupling of rock mass and water, the geomechanics layer during similar model test achievement in research that is drawn is more accurate.
Selection standard sand of the present invention, ground barium sulfate, talcum powder, cement, Vaseline, silicone oil are as moity; Wherein, Cement guarantees that softening disintegration does not take place material, simultaneously as hydraulic binding agent under the effect of water; Cement is also apparent in view to the perviousness influence of material, and the intensity of material and PQ can be regulated in the larger context; Vaseline is as the plasticity jointing compound, mainly is intensity and the Young's modulus of regulating analog material, and along with the increase of content, its regulating effect and cement to intensity and Young's modulus is opposite, guaranteed that like this Mechanical Properties of Materials can effectively regulate and control; Silicone oil is as regulator; Guaranteed the non-wetting ability of material, the mixing water in the material can fully be reacted with cement, reduced the requirement of material curing condition; And silicone oil can be implemented on the basis that does not influence the mechaanical property of materials basically; The rational index of the water of material is regulated, improved the analog simulation degree of the rational aspect of material water greatly, admittedly expanded the range of application of this stream-analog material that is coupled.In addition, regulate the proportion of ground barium sulfate and talcum powder and standard sand, internal friction angle and the cohesion that can regulate material.
Admittedly the technical scheme of the stream-analog material that is coupled in the model trial that the present invention proposes has the following advantages:
1, can realize that softening disintegration does not take place analog material under the effect of water, for the coupling of real simulation rock mass and water provides possible;
2, can under the prerequisite of the bulk property that does not influence material, regulate and control the single index of rational index of water and mechanical property separately through regulating material mixture ratio, rock mass different classes of for simulating, different PQs provide maybe;
3, can in a big way, regulate the intensity and the perviousness of material, all kinds of rock mass that can simulate intermediate intensity.
4, the character to material has realized " major control, the reverse adjusting ", has solved composition and has changed the dependency to material properties influence, has improved the analog simulation degree of material greatly.
Description of drawings
Fig. 1 is the Complete Stress-Strain Curve figure of material under single shaft resistance to compression condition of embodiment 1.
Embodiment
Below in conjunction with embodiment the present invention is further described.
The used standard sand particle diameter of embodiments of the invention is less than 5mm; And grating is even; The ground barium sulfate fineness is 625 orders, and talcous fineness is 1250 orders, and cement is that ultimate compression strength is the high-quality white portland cement of 32.5MPa; Vaseline is the nontoxic medical grade Vaseline of white, and silicone oil is the methyl-silicone oil of viscosity 1500.
Embodiment 1 preparation be used for model trial stream-admittedly analog material is coupled
Prescription is: standard sand 320g, ground barium sulfate 32g, talcum powder 32g, cement 20.8g, Vaseline 24g, silicone oil 16g, mixing water 32g.
Preparation process is:
1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline, silicone oil and mixing water in proportion;
2) sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
3) add mixing water, fully stir;
4) add regulator silicone oil, mix thoroughly;
5) Vaseline is heated to 50 ℃, makes it molten for liquid;
6), and fully stir with liquid Vaseline and material mixing;
7) cool off 10min under the room temperature, promptly get.
The correlation parameter of this proportioning: severe 2.14g/cm
3, ultimate compression strength 0.61MPa, tensile strength 0.058MPa, Young's modulus 37MPa, PQ 5.36 * 10
-6Cm/s.
Embodiment 2 preparation be used for model trial stream-admittedly analog material is coupled
Prescription is for being: standard sand 320g, ground barium sulfate 32g, talcum powder 32g, cement 20.8g, Vaseline 24g, silicone oil 0, mixing water 24g.
Preparation process is:
1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline and mixing water in proportion;
2) sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
3) add mixing water, fully stir;
4) Vaseline is heated to 50 ℃, makes it molten for liquid;
5), and fully stir with liquid Vaseline and material mixing;
6) cool off 10min under the room temperature, promptly get.
The correlation parameter of this proportioning: severe 1.92g/cm
3, ultimate compression strength 0.44MPa, tensile strength 0.042MPa, Young's modulus 13MPa, PQ 8.61 * 10
-5Cm/s.
Embodiment 3 preparation be used for model trial stream-admittedly analog material is coupled
Prescription is: standard sand 320g, ground barium sulfate 32g, talcum powder 32g, cement 40g, Vaseline 38.4g, silicone oil 12.8g, mixing water 32g.
Preparation process is:
1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline, silicone oil and mixing water in proportion;
2) sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
3) add mixing water, fully stir;
4) add regulator silicone oil, mix thoroughly;
5) Vaseline is heated to 50 ℃, makes it molten for liquid;
6), and fully stir with liquid Vaseline and material mixing;
7) cool off 10min under the room temperature, promptly get.
The correlation parameter of this proportioning: severe 2.12g/cm
3, ultimate compression strength 0.92MPa, tensile strength 0.090MPa, Young's modulus 116MPa, PQ 3.66 * 10
-7Cm/s.
Embodiment 4 preparation be used for model trial stream-admittedly analog material is coupled
Prescription is: standard sand 320g, ground barium sulfate 16g, talcum powder 48g, cement 20.8g, Vaseline 24g, silicone oil 16g, mixing water 32g.
Preparation process is:
1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline, silicone oil and mixing water in proportion;
2) sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
3) add mixing water, fully stir;
4) add regulator silicone oil, mix thoroughly;
5) Vaseline is heated to 50 ℃, makes it molten for liquid;
6), and fully stir with liquid Vaseline and material mixing;
7) cool off 10min under the room temperature, promptly get.
The correlation parameter of this proportioning: severe 2.03g/cm
3, ultimate compression strength 0.59MPa, tensile strength 0.058MPa, Young's modulus 37MPa, PQ 5.58 * 10
-6Cm/s.
Prescription is: standard sand 320g, ground barium sulfate 48g, talcum powder 16g, cement 20.8g, Vaseline 24g, silicone oil 16g, mixing water 32g.
Preparation process is:
1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline, silicone oil and mixing water in proportion;
2) sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;
3) add mixing water, fully stir;
4) add regulator silicone oil, mix thoroughly;
5) Vaseline is heated to 50 ℃, makes it molten for liquid;
6), and fully stir with liquid Vaseline and material mixing;
7) cool off 10min under the room temperature, promptly get.
The correlation parameter of this proportioning: severe 2.19g/cm
3, ultimate compression strength 0.60MPa, tensile strength 0.058MPa, Young's modulus 38MPa, PQ 5.19 * 10
-6Cm/s.
Though above-mentioned combination embodiment specific embodiments of the invention is described; But be not restriction to protection domain of the present invention; One of ordinary skill in the art should be understood that; On the basis of technical scheme of the present invention, those skilled in the art need not pay various modifications that creative work can make or distortion still in protection scope of the present invention.
Claims (9)
- One kind be used for model trial stream-admittedly analog material is coupled; It is characterized in that: form: 1 part of standard sand, 0.05～0.15 part of ground barium sulfate, 0.05～0.15 part of talcum powder by the raw material of following weight part; 0.05～0.125 part of cement; 0.04～0.12 part in Vaseline, 0～0.15 part of silicone oil, 0.05～0.1 part of mixing water.
- 2. according to claim 1 be used for model trial stream-admittedly analog material is coupled; It is characterized in that: form: 1 part of standard sand, 0.085 part of ground barium sulfate, 0.085 part of talcum powder by the raw material of following weight part; 0.065 part of cement; 0.075 part in Vaseline, 0.05 part of silicone oil, 0.1 part of mixing water.
- 3. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2, it is characterized in that: the particle diameter of said standard sand is less than 5mm.
- 4. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2, it is characterized in that: said ground barium sulfate fineness is 625 orders.
- 5. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2, it is characterized in that: talcous fineness is 1250 orders.
- 6. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2 is characterized in that: said cement is that ultimate compression strength is the high-quality white portland cement of 32.5MPa.
- 7. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2 is characterized in that: said Vaseline is the nontoxic medical grade Vaseline of white.
- 8. admittedly the stream-analog material that is coupled that is used for model trial according to claim 1 and 2, it is characterized in that: said silicone oil is the methyl-silicone oil of viscosity 1500.
- 9. admittedly each described preparation method who is used for the stream-analog material that is coupled of model trial in the claim 1～8, it is characterized in that: step is following:(1) strictness takes by weighing standard sand, ground barium sulfate, talcum powder, cement, Vaseline and silicone oil in proportion;(2) standard sand, ground barium sulfate, talcum powder and four kinds of fine materials of cement are mixed and stir;(3) add mixing water, fully stir;(4) add silicone oil, mix thoroughly;(5) Vaseline is heated to 45 ℃～60 ℃, makes it molten for liquid;(6), and fully stir with liquid Vaseline and the resulting material mixing of step (4);(7) cool off 5～10min under the room temperature, admittedly promptly get be used for model trial stream-analog material is coupled.