CN102557162A - Biological activating water treatment agent - Google Patents
Biological activating water treatment agent Download PDFInfo
- Publication number
- CN102557162A CN102557162A CN2012100105324A CN201210010532A CN102557162A CN 102557162 A CN102557162 A CN 102557162A CN 2012100105324 A CN2012100105324 A CN 2012100105324A CN 201210010532 A CN201210010532 A CN 201210010532A CN 102557162 A CN102557162 A CN 102557162A
- Authority
- CN
- China
- Prior art keywords
- percent
- water
- treatment agent
- water treatment
- conventional material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a biological activating water treatment agent, which consists of the following components in percentage by weight: 0.5 to 1 percent of magnesium oxide, 25 to 45 percent of silicon oxide, 6 to 8 percent of alumina, 0.5 to 1 percent of titanium oxide, 10 to 20 percent of titanium carbide, 0.8 to 1.5 percent of nickel, 10 to 30 percent of zeolite, 10 to 25 percent of rose quartz, 2 to 5 percent of copper and the balance of clay. The biological activating water treatment agent has functions of oxygenating, activating and sterilizing, and has effects of building a body, improving immunity and promoting the growth of plants and animals. After the nickel is added, the conventional material is changed from a static state to a dynamic state, and more negative ions are generated; after the zeolite is added, the speed of the conventional material can be improved; the rose quartz has piezoelectric properties and has an effect of increasing the amplitude of the conventional material; and after the copper is added, the activity of the conventional material can be exerted. When the biological activating water treatment agent is put into a filter element of a water purifier, the biological activating water treatment agent generates small molecular group water, emits far infrared rays and micro-electrolyzes water, and can be applied to water vats, fishponds, seed soaking or direct drinking.
Description
Technical field
The invention belongs to the tap water technical field, particularly a kind of bioactivation water conditioner.
Background technology
Water is Source of life, no matter be animal or plant, all keeps the most basic vital movement with water.Along with the development of society and the raising of people's life water article, to the quality of tap water, effect require increasingly high, yet problems such as employed water ubiquity water quality anoxic in the life, aging, degeneration.
Disclose a kind of " oxygenation activated water treatment agent and manufacture craft thereof " among the CN1616356A, this technology makes treatment agent can become small-micelle water with the macromolecular mass water crack, and the activity of water is improved, and increases the dissolved oxygen content in the water.But negative ion distributes with the oxygenation activating velocity slowly in the treatment agent, and it is slow that the macromolecular mass water crack is become the speed of small-micelle water; Solidify with potter's clay separately, the difference of hardness of treatment agent, fall slag easily.
Summary of the invention
The technical problem that the present invention will solve provides a kind of bioactivation water conditioner; Negative ion distributes with the oxygenation activating velocity slow in the activated water treatment agent to solve in the past; The speed that the macromolecular mass water crack is become small-micelle water is slow, and difference of hardness, the easy problem of weathering.
Technical solution of the present invention is:
A kind of bioactivation water conditioner, by weight composed of the following components:
Natural manganese dioxide 0.5%～1%
Silicon oxide 25%～45%
Aluminum oxide 6%～8%
Titanium oxide 0.5%～1%
Titanium carbide 10%～20%
Nickel 0.8%～1.5%
Zeolite 10%～30%
Rose quartzy 10%～25%
Copper 2%～5%
The potter's clay surplus.
This bioactivation water conditioner has the oxygenation activation, and the function of sterilization plays the effect that animal and plant growth was healthy and strong, was promoted in health.Wherein, nickel belongs to reflective material; Have magnetic and good plasticity-, can impel original material to be become dynamically by static state after increasing nickel, produce more negative ion, it is faster to impel negative ion to distribute speed, and can remove peculiar smell.Zeolite belongs to the quick-acting material; Can quicken the speed of original material after adding zeolite, can sterilization.The rose quartz belongs to amplification property material, and piezoelectric property is arranged, and can play the amplification effect to original material behind the adding rose quartz.Copper belongs to conductive of material; After adding copper, can bring into play the activity of original material, play and strengthen solidifying and accelerating conduction, the hardness of treatment agent is strengthened, prolong work-ing life, also has the effect of sterilization, and simultaneously, the speed that makes negative ion produce small-micelle water accelerates.This bioactivation water conditioner is placed in the filter element of water purifier, produces small-micelle water, and is emitting far-infrared and to the little electrolysis of water, can be applicable to water vat, fishpond, seed soaking or directly drinks.Can improve immunizing power after people's long-term drinking, can improve vegeto-animal yield and quality behind the plant-animal life-time service, reduce the usage quantity of feed, fertilizer.
Embodiment
Embodiment 1
Choose raw material according to weight ratio:
Natural manganese dioxide 0.5%
Silicon oxide 40%
Aluminum oxide 8%
Titanium oxide 0.5%
Titanium carbide 20%
Nickel 1%
Zeolite 10%
Rose quartzy 10%
Copper 5%
Potter's clay 5%
Above-mentioned raw materials is mixed the back pulverize, cross 100 mesh sieves, inject mould, compression moulding, the stainless steel casing of behind 400 ℃ of following high temperature sinterings, packing into is promptly processed water activating device.
Embodiment 2
Choose raw material according to weight ratio:
Natural manganese dioxide 1%
Silicon oxide 35%
Aluminum oxide 6%
Titanium oxide 1%
Titanium carbide 10%
Nickel 0.8%
Zeolite 28%
Rose quartzy 14.2%
Copper 2%
Potter's clay 2%
Above-mentioned raw materials is mixed the back pulverize, cross 200 mesh sieves, inject mould, compression moulding, the stainless steel casing of behind 400 ℃ of following high temperature sinterings, packing into is promptly processed water activating device.
Embodiment 3
Choose raw material according to weight ratio:
Natural manganese dioxide 0.8%
Silicon oxide 25%
Aluminum oxide 7%
Titanium oxide 0.7%
Titanium carbide 13%
Nickel 1.5%
Zeolite 16%
Rose quartzy 25%
Copper 3%
Potter's clay 8%
Above-mentioned raw materials is mixed the back pulverize, cross 250 mesh sieves, inject mould, compression moulding, the stainless steel casing of behind 400 ℃ of following high temperature sinterings, packing into is promptly processed water activating device.
Testing method:
1, gets 0.6ml source water to the nuclear-magnetism pipe, test
17O NMR also obtains the peak width at half value of its signal.
2, will be soaked in according to the water activating device that embodiment 3 processes in the water source, when 5 minutes, 15 minutes, 30 minutes and 60 minutes, get in 0.6ml water sample to the nuclear-magnetism pipe respectively, test
17O NMR also obtains the peak width at half value of its signal, and each time point is all tested 3 times.
3, the water activating device of processing with the CN1616356A method soaks as reference substance and is soaked in the water source, when 5 minutes, 15 minutes, 30 minutes and 60 minutes, gets in 0.6ml water sample to the nuclear-magnetism pipe test respectively
17O NMR also obtains the peak width at half value of its signal, and each time point is all tested 3 times.
(annotate: test source water is ordinary tap water to test result.）
Source water
17O NMR signal peak width at half is 81.6Hz (adopting the MV of 3 tests); The water activating device that source water is processed with embodiment 3 soaks after 5 minutes it
17O NMR signal peak width at half reduces (75.0Hz) to some extent, soaks after 15 minutes it
17O NMR signal peak width at half significantly reduces (46.9Hz), thereafter along with the growth of soak time its
17O NMR signal peak width at half no longer changes (being respectively 46.9Hz and 45.5Hz when 30 minutes and 60 minutes) basically; Source water soaks after 5 minutes it with reference substance
17O NMR signal peak width at half reduces (77.5Hz) equally to some extent, thereafter along with soak time 15 minutes, 30 minutes and 60 minutes the time its
17O NMR signal peak width at half continues slowly to reduce (being respectively 75.2Hz, 71.6Hz and 67.7Hz).Explain that the water activating device that the present invention processes is fast with the speed that the macromolecular mass water crack becomes small-micelle water, negative ion distributes with the oxygenation activating velocity fast, and oxygenation effect is good.
Claims (1)
1. bioactivation water conditioner is characterized in that by weight composed of the following components:
Natural manganese dioxide 0.5%～1%
Silicon oxide 25%～45%
Aluminum oxide 6%～8%
Titanium oxide 0.5%～1%
Titanium carbide 10%～20%
Nickel 0.8%～1.5%
Zeolite 10%～30%
Rose quartzy 10%～25%
Copper 2%～5%
The potter's clay surplus.