CN102555642A - Method for manufacturing activated carbon process product - Google Patents
Method for manufacturing activated carbon process product Download PDFInfo
- Publication number
- CN102555642A CN102555642A CN2011104106196A CN201110410619A CN102555642A CN 102555642 A CN102555642 A CN 102555642A CN 2011104106196 A CN2011104106196 A CN 2011104106196A CN 201110410619 A CN201110410619 A CN 201110410619A CN 102555642 A CN102555642 A CN 102555642A
- Authority
- CN
- China
- Prior art keywords
- activated carbon
- parts
- powder
- polishing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an activated carbon process product. The method comprises the following process steps of: 1, mixing 6 to 9 parts of activated carbon powder, 4 to 7 parts of carboxy styrene-butadiene latex, 1 to 3 parts of bowlder powder, 1 to 3 parts of activating agent and 1 to 2 parts of water according to a weight ratio to obtain an activated carbon matrix; 2, stirring in a stirrer for 30 to 45 minutes; 3, pressing into a mold through pressure; 4, putting into an oven at the temperature of between 60 and 90 DEG C, and baking for 24 to 30 minutes; 5, taking out, and polishing; and 6, adhering negative ion powder onto the polished product. The activated carbon obtained by the process method is processed to form artware and is placed at home, the adsorption effect of the activated carbon can be enhanced by the adsorption effect of the activated carbon in combination with the activating agent, air is cleaned, and the bowlder powder can collect energy to form an electromagnetic field, so that indoor microcirculation can be realized, and the adsorption energy of the activated carbon on harmful gas is increased.
Description
Technical field
The present invention relates to a kind of preparation method of activated carbon process goods, activated carbon process goods especially a kind of environmental protection, that have negative ion powder belong to handicraft preparation method technical field.
Background technology
Active carbon is the very extensive and internationally recognized drug abuse material of a kind of purposes; It has very flourishing pore structure, special surface functional group, stable physics and chemical property; Be a kind of good adsorbent, catalyst and catalyst carrier, can be used for fields such as gas defence, filtration.Along with development of science and technology, the progress of society, people's living standard improves day by day, but people's living environment more and more polluted, and in order to safeguard people's life and health, need take certain measure.At present, finishing becomes the part of family life, but just fit up indoor, can produce like harmful substances such as formaldehyde, benzene, sulfur dioxide, if the such gas of generation in the house ornamentation, people hang up one's hat receiving the serious health threat.
Summary of the invention
The objective of the invention is to: preparation method a kind of environmental protection, that have negative ion powder, can adsorb the activated carbon process goods of pernicious gas is provided; Solve existing not environmental protection of handicraft; Influence healthy technical problem, thereby can effectively solve the problem that exists in the above-mentioned prior art.
The object of the invention realizes through following technical proposals: a kind of preparation method of activated carbon process goods comprises following technical process:
The first step: with 6-9 part activated carbon powder, 4-7 part carboxylic styrene butadiene latex, 1-3 part jade powder, 1-3 part activator, 1-2 part water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 30-45 minute;
The 3rd step: it is pressed in the mould with pressure;
The 4th step: put into the baking box of 60-90 degree, stoving time 24-30 hour;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up.
As a kind of optimal way:
The first step: with 7 parts of activated carbon powders, 6 parts of carboxylic styrene butadiene latexs, 2 parts of jade powder, 2 parts of activators, 1.5 parts of water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 35 minutes;
The 3rd step: it is pressed in the mould with pressure;
The 4th step: put into the baking box of 80 degree, stoving time 25 hours;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up.
As a kind of optimal way, in above-mentioned the 3rd step, said source pressure is exerted pressure in hydraulic press.
As further optimal way, in above-mentioned the 4th step, putting into oven temperature is 75 degree, and stoving time is 26 hours.
As further optimal way, in above-mentioned the 6th step, said negative ion powder is: the bi-component organic silica gel soaks gained through alkaline solution.
Compared with prior art, beneficial effect of the present invention: will be processed into handicraft through the active carbon that process of the present invention obtains, and place at home; Suction-operated through active carbon combines activator can strengthen the suction-operated of active carbon; It is more effective to purify air, and has also added the jade powder that human body is had health-care effect, can focused energy form electromagnetic field; Make indoor generation microcirculation, increased the absorption energy of active carbon pernicious gas.
The specific embodiment
In order to make the object of the invention, technical scheme and advantage clearer,, the present invention is further elaborated below in conjunction with embodiment.Should be appreciated that specific embodiment described herein only in order to explanation the present invention, and be not used in qualification the present invention.
Disclosed all characteristics in this specification, or the step in disclosed all methods or the process are except the speciality of mutual repulsion and/or the step; All can make up by any way; Only if special narration all can be replaced by other equivalences or the alternative features with similar purpose, promptly; Only if special narration, an embodiment in a series of equivalences of each characteristic or the similar characteristics.
The preparation method of the activated carbon process goods that the embodiment of the invention provides for the ease of explanation, only shows the part relevant with the embodiment of the invention.
Comprise following technical process:
The first step: with 6-9 part activated carbon powder, 4-7 part carboxylic styrene butadiene latex, 1-3 part jade powder, 1-3 part activator, 1-2 part water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 30-45 minute;
The 3rd step: it is pressed in the mould with pressure;
The 4th step: put into the baking box of 60-90 degree, stoving time 24-30 hour;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up.
Embodiment 1:
Comprise following technical process:
The first step: with 7 parts of activated carbon powders, 6 parts of carboxylic styrene butadiene latexs, 2 parts of jade powder, 2 parts of activators, 1.5 parts of water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 35 minutes;
The 3rd step: with pressure it is pressed in the mould, said source pressure is exerted pressure in hydraulic press;
The 4th step: put into the baking box of 80 degree, stoving time 25 hours;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up, said negative ion powder is: the bi-component organic silica gel soaks gained through alkaline solution.
Embodiment 2:
Comprise following technical process:
The first step: with 8 parts of activated carbon powders, 5 parts of carboxylic styrene butadiene latexs, 1.5 parts of jade powder, 1.5 parts of activators, 1.3 parts of water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 42 minutes;
The 3rd step: with pressure it is pressed in the mould, said source pressure is exerted pressure in hydraulic press;
The 4th step: put into the baking box of 85 degree, stoving time 28 hours;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up, said negative ion powder is: the bi-component organic silica gel soaks gained through alkaline solution.
Embodiment 3:
Comprise following technical process:
The first step: with 9 parts of activated carbon powders, 4 parts of carboxylic styrene butadiene latexs, 1.8 parts of jade powder, 1.8 parts of activators, 1.8 parts of water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 42 minutes;
The 3rd step: with pressure it is pressed in the mould, said source pressure is exerted pressure in hydraulic press;
The 4th step: putting into oven temperature is 75 degree, and stoving time is 26 hours.
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up, said negative ion powder is: the bi-component organic silica gel soaks gained through alkaline solution.
Carry out carrying out again after manual secondary is carved the activated carbon process goods of above-mentioned technical process gained painted; The handicraft that gets final product exquisitely will be processed into handicraft through the active carbon that process of the present invention obtains, and place at home; Suction-operated through active carbon combines activator can strengthen the suction-operated of active carbon; It is more effective to purify air, and has also added the jade powder that human body is had health-care effect, can focused energy form electromagnetic field; Make indoor generation microcirculation, increased the absorption energy of active carbon pernicious gas.
The above is merely preferred embodiment of the present invention, not in order to restriction the present invention, all any modifications of within spirit of the present invention and principle, being done, is equal to and replaces and improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. the preparation method of activated carbon process goods is characterized in that:
Comprise following technical process:
The first step: with 6-9 part activated carbon powder, 4-7 part carboxylic styrene butadiene latex, 1-3 part jade powder, 1-3 part activator, 1-2 part water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 30-45 minute;
The 3rd step: it is pressed in the mould with pressure;
The 4th step: put into the baking box of 60-90 degree, stoving time 24-30 hour;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up.
2. the preparation method of activated carbon process goods as claimed in claim 1 is characterized in that: comprise following technical process:
The first step: with 7 parts of activated carbon powders, 6 parts of carboxylic styrene butadiene latexs, 2 parts of jade powder, 2 parts of activators, 1.5 parts of water by weight being mixed and made into the active carbon matrix;
Second step: in agitator, stirred 35 minutes;
The 3rd step: it is pressed in the mould with pressure;
The 4th step: put into the baking box of 80 degree, stoving time 25 hours;
The 5th step: after the taking-up, polishing, polishing;
The 6th step: the gluing above that negative ion powder of going up.
3. the preparation method of activated carbon process goods as claimed in claim 1 is characterized in that: in above-mentioned the 3rd step, said source pressure is exerted pressure in hydraulic press.
4. the preparation method of activated carbon process goods as claimed in claim 1 is characterized in that: in above-mentioned the 4th step, putting into oven temperature is 75 degree, and stoving time is 26 hours.
5. like the preparation method of the described activated carbon process goods of arbitrary claim in claim 1 or 2, it is characterized in that: in above-mentioned the 6th step, said negative ion powder is: the bi-component organic silica gel soaks gained through alkaline solution.