CN102528024A - Method for preparing insulated iron powder used by soft magnetic composite materials - Google Patents
Method for preparing insulated iron powder used by soft magnetic composite materials Download PDFInfo
- Publication number
- CN102528024A CN102528024A CN2012100189207A CN201210018920A CN102528024A CN 102528024 A CN102528024 A CN 102528024A CN 2012100189207 A CN2012100189207 A CN 2012100189207A CN 201210018920 A CN201210018920 A CN 201210018920A CN 102528024 A CN102528024 A CN 102528024A
- Authority
- CN
- China
- Prior art keywords
- iron powder
- insulated
- magnetic composite
- purity
- concentration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for preparing insulated iron powder used by soft magnetic composite materials belongs to the technical field of magnetic function materials and powder metallurgy. The process is that a cladding process includes: adding high-purity iron powder with concentration of 0.1-5g/ml for industrialized production into hexafluorotitanic acid or hexafluorozirconic acid cladding solution with concentration of 0.002-0.05g/ml, stirring for 5-60 minutes for reacting at temperature of 20-70 DEG C, filtering and washing, and drying at 50-120 DEG C to obtain insulated iron powder. The method for preparing insulated iron powder used by soft magnetic composite materials has the advantages of being simple in preparing process, high in efficiency and complete in cladding. An insulated cladding layer on the surface of the iron powder can effectively reduce magnetic loss of powder cores of the soft magnetic composite materials, and comprehensive performance of the powder cores can be regulated by controlling thickness of the insulated layer.
Description
Technical field
The invention belongs to magnetic functional material and powder metallurgical technology, particularly a kind of soft-magnetic composite material is with the preparation method of insulated iron powder.
Background technology
Soft-magnetic composite material (Soft Magnetic Composites; Hereinafter to be referred as SMC) manufacturing of employing PM technique; Metal powder granulates (like straight iron powder) by surface insulation is formed; Can one the step be pressed into parts with complicated shape, and have good three-dimensional isotropism magnetic property and thermal characteristics, and lower eddy-current loss under the high frequency; Can in some have the motor of work under motor and the upper frequency of complicated shape and magnetic circuit, be used as core material, can bring revolutionary variation to the electrical convertors and generators design when obtaining extensive use.Development along with electronics miniaturization and high frequencyization; Micro machine, low-power machine and anti-electromagnetic interference element etc. are widely used in automobile, robot, office and the home automation device, and the application of SMC in these fields with special performance will produce huge economic benefit.
Insulated iron powder is the important source material of preparation SMC magnetic core, directly has influence on the serviceability and the structural strength of magnetic core.In recent years, external leading company has successively developed insulated iron powder, like Sweden
The Somaloy of AB company
TMKIPMG270H of the ATOMET EM-1 of serial, Canadian QMP company and Japanese JFE company etc., and applied for related patent U.S. Patent No. in China.Patent (the application number: 03811970.6 of the Robert Bosch Co., Ltd (Robert Bosch GmbH) of Germany; Publication number: CN1656575A) and the patent (application number: 97192452.X of Sweden
AB company; Publication number: CN1211943A) (application number: 200480025248.8, publication number: CN1845805A) all adopt phosphating process to obtain insulated iron powder in the technology; The patent of Japan JFE company (application number: 200480025248.8, publication number: CN1518011A) adopt phosphalugel to coat soft magnetic powder in the technology and make the insulation soft magnet powder.Japan TDK Corp. (application number: 97102244.5, publication number: CN1167990A) successfully made the soft magnetism coated composite powder of forming by iron powder and silicon titanyl rete through in iron powder, adding silica, silicone resin and organic titanic compound.In addition; Domestic also have similar patented technology to occur; Patented technology (application number: 200610040493.7 like Tianyi Superfine Metal Powders Co., Ltd., Jiangsu; Publication number: CN1895820A) provide a kind of with adopting physical method to prepare the method for nano silicon coating carbonyl iron powder behind coupling agent, ammoniacal liquor modified carbonyl iron powder or the silica surface; The technology of Huzhou Keda Magnetoelectric Co. Ltd. (application number: 200710186855.8, publication number: the CN101226807A) SMC of adopted Prepared by Sol Gel Method silica and organic polymer compound inslation cladding iron powder.
Above method prepares insulated iron powder and all more or less has some problems, and like the easy embrittlement of insulating film layer, to coat inhomogeneous, complicated process of preparation, efficient low etc., the SMC insulation soft magnetic powder of further seeking excellent performance is very important.Up to the present, domesticly do not see the report that adopts hexafluoro metatitanic acid and hexafluoro zirconate to carry out the processing of iron powder insulating.
Summary of the invention
The object of the present invention is to provide the preparation method of a kind of soft-magnetic composite material (SMC) with insulated iron powder.Prepared fluorine titanium/zirconic acid molysite inorganic insulating membrane can improve the resistivity of iron powder on the one hand, plays insulating effect, can reduce the magnetic loss of SMC significantly; This dielectric film resistance to elevated temperatures is better on the other hand, can stand heat-treated more than 550 ℃ and can not damage, and the heat treatment under this temperature can further reduce the coercivity and the magnetic loss of SMC magnetic core.This method has the advantage that technology is simple, coating is even, efficient is high.
Main processes of the present invention: high-purity iron powder → insulating is handled (mechanical agitation) → filtration → washing → oven dry → insulated iron powder.For solving the problems of the technologies described above the technical scheme that adopts be: certain density iron powder is joined stirring reaction certain hour in fluotitanic acid or the fluorine zirconic acid treatment fluid; Control certain reaction condition makes the certain thickness high-quality fluorine titanium of iron powder coated with uniform/zirconates clad.Concrete processing step is following:
(1) preparation coats treatment fluid, and be specially: hexafluoro metatitanic acid or hexafluoro zirconate are solute, and absolute ethyl alcohol or acetone are solvent, and the control solute concentration is 0.002～0.05g/ml;
(2) high-purity iron powder is joined in the coating treatment fluid, controlling iron powder concentration simultaneously is 0.1～5g/ml, and control treatment fluid temperature is 20～70 ℃, mechanical agitation reaction 5～60min;
(3) filtration washing, and obtain insulated iron powder in 50～120 ℃ of dryings.
Described high-purity iron powder is one or more the composition in purity 99% above atomized iron powder, reduced iron powder, electrolytic iron powder or the carbonyl iron dust.
As preferably, the solvent in the above-mentioned steps (1) can be absolute ethyl alcohol or acetone, and is preferably absolute ethyl alcohol; Solute concentration is preferably 0.005～0.01g/ml.
As preferably, the high-purity iron powder in the above-mentioned steps (2) can be atomized iron powder, reduced iron powder, electrolytic iron powder and carbonyl iron dust, and is preferably water-atomized iron powder, and its purity height and suppression performance are good, and concentration is preferably 0.1～2g/ml; The treatment fluid temperature is preferably 30～60 ℃; Reaction time is preferably 20～30min.
The raw material iron powder provides basic magnetic property for the SMC magnetic core, and the concentration of treatment fluid, reaction temperature and time can directly influence the quality and the thickness of dielectric film, and further have influence on the final performance of magnetic core.Insulating film layer thickness increases in the certain limit, and the magnetic loss of magnetic core significantly reduces, but magnetic conductivity also can be lost; Surpass the certain thickness scope, its magnetic property will worsen rapidly, and magnetic conductivity significantly reduces, and magnetic loss increases.Control suitable treatment process and condition, can make the excellent insulated iron powder of actual required magnetic property.
The invention has the advantages that:
1, the insulating barrier on iron powder surface has good resistance to elevated temperatures, has improved insulated iron powder to be subject to insulating barrier and the too low problem of heat treatment temperature all the time;
2, the prepared SMC magnetic core of the present invention has good comprehensive magnetic property, and can adjust according to actual needs;
3, technology is simple, and efficient is high, is suitable for industrial applications.
The specific embodiment
Below in conjunction with specific embodiment, further set forth the present invention, but embodiment does not limit the present invention, and do not address part and be applicable to prior art in the invention.
Embodiment 1
Getting a certain amount of hexafluoro metatitanic acid solution joins and is made into reactant liquor in the absolute ethyl alcohol; Control hexafluoro metatitanic acid concentration is 0.005g/ml; Heating in water bath for reaction liquid temp to 30 ℃ is that high-purity atomized iron powder (controlling its concentration is 0.2g/ml) of 99.5% joins mechanical agitation reaction 30min in the reactant liquor with purity, after the centrifugal filtration with absolute ethanol washing 3 times; Place 50 ℃ of fully dryings, make insulated iron powder.Iron powder becomes Paint Gloss in the surface after insulating is handled, glossiness is also better, and clad is evenly complete.The magnetic property of the made magnetic core of iron powder was found before and after contrast coated and handles; The maximum relative permeability of insulated iron powder magnetic core becomes 291 by 328; Magnetic loss when magnetic strength 1T frequency 50Hz drops to 6.8W/kg by 9.1W/kg; And the magnetic loss when magnetic strength 1T frequency 400Hz drops to 85.2W/kg by 212W/kg, and magnetic loss has reduced by 60%.
Embodiment 2
What the raw material iron powder adopted atomized iron powder and reduced iron powder mass ratio 1: 1 mixes iron powder, purity 99.3%.Get a certain amount of hexafluoro zirconate solution and join and be made into reactant liquor in the anhydrous propanone, control hexafluoro zirconate concentration is 0.05g/ml, heating in water bath for reaction liquid temp to 60 ℃; The mixing iron powder of preparation is joined in the reactant liquor; Control iron powder concentration is 5g/ml, and mechanical agitation reaction 60min washs 3 times with anhydrous propanone after the centrifugal filtration; Place 120 ℃ of fully dryings, make insulated iron powder.The magnetic property of the made magnetic core of iron powder found that the maximum relative permeability of insulated iron powder magnetic core becomes 263 by 318 before and after contrast coated and handles, and the magnetic loss when magnetic strength 1T frequency 400Hz drops to 63.5W/kg by 201W/kg.
Embodiment 3
What the raw material iron powder adopted atomized iron powder and carbonyl iron dust mass ratio 1: 1 mixes iron powder, purity 99.4%.Get a certain amount of hexafluoro metatitanic acid solution and join and be made into reactant liquor in the absolute ethyl alcohol, control hexafluoro metatitanic acid concentration is 0.02g/ml, heating in water bath for reaction liquid temp to 50 ℃; The mixing iron powder of preparation is joined in the reactant liquor; Control iron powder concentration is 2g/ml, mechanical agitation reaction 5min, after the centrifugal filtration with absolute ethanol washing 3 times; Place 80 ℃ of fully dryings, make insulated iron powder.The maximum relative permeability of the prepared magnetic core of iron powder became 225 by 302 before and after contrast coated and handles, and the magnetic loss when magnetic strength 1T frequency 400Hz drops to 92W/kg by 196W/kg.
Embodiment 4
The raw material iron powder adopts reduced iron powder, purity 99.4%.Get a certain amount of hexafluoro zirconate solution and join and be made into reactant liquor in the absolute ethyl alcohol, control hexafluoro zirconate concentration is 0.002g/ml, heating in water bath for reaction liquid temp to 70 ℃; Iron powder is joined in the reactant liquor; Controlling its concentration is 0.5g/ml, mechanical agitation reaction 20min, after the centrifugal filtration with absolute ethanol washing 3 times; Place 80 ℃ of fully dryings, make insulated iron powder.The maximum relative permeability of the magnetic core that makes is 268, and the magnetic loss when magnetic strength 1T frequency 400Hz is 106W/kg.
Embodiment 5
The raw material iron powder adopts electrolytic iron powder, purity 99.2%.Get a certain amount of hexafluoro zirconate solution and join and be made into reactant liquor in the absolute ethyl alcohol, control hexafluoro zirconate concentration is 0.01g/ml, heating in water bath for reaction liquid temp to 40 ℃; Iron powder is joined in the reactant liquor; Controlling its concentration is 1g/ml, mechanical agitation reaction 30min, after the centrifugal filtration with absolute ethanol washing 3 times; Place 80 ℃ of fully dryings, make insulated iron powder.The maximum relative permeability of the magnetic core that makes is 239, and the magnetic loss when magnetic strength 1T frequency 400Hz is 96W/kg.
Embodiment 6
The raw material iron powder adopts carbonyl iron dust, purity 99.0%.Get a certain amount of hexafluoro metatitanic acid solution and join and be made into reactant liquor in the anhydrous propanone, control hexafluoro metatitanic acid concentration is 0.01g/ml, heating in water bath for reaction liquid temp to 50 ℃; Iron powder is joined in the reactant liquor; Controlling its concentration is 2g/ml, and mechanical agitation reaction 20min washs 3 times with anhydrous propanone after the centrifugal filtration; Place 70 ℃ of fully dryings, make insulated iron powder.The maximum relative permeability of the magnetic core that makes is 187, and the magnetic loss when magnetic strength 1T frequency 400Hz is 90.6W/kg.
Claims (5)
1. a soft-magnetic composite material is with the preparation method of insulated iron powder, and it is characterized in that: processing step is following:
(1) preparation coats treatment fluid: hexafluoro metatitanic acid or hexafluoro zirconate are solute, and absolute ethyl alcohol or acetone are solvent, and the control solute concentration is 0.002～0.05g/ml;
(2) high-purity iron powder is joined in the coating treatment fluid, controlling high-purity iron powder concentration simultaneously is 0.1～5g/ml, and control treatment fluid temperature is 20～70 ℃, mechanical agitation reaction 5～60min;
(3) filtration washing, and obtain insulated iron powder in 50～120 ℃ of dryings.
2. soft-magnetic composite material according to claim 1 is characterized in that with the preparation method of insulated iron powder: described high-purity iron powder is one or more the composition in purity 99% above atomized iron powder, reduced iron powder, electrolytic iron powder or the carbonyl iron dust.
3. soft-magnetic composite material according to claim 1 is characterized in that with the preparation method of insulated iron powder: the solvent in the step (1) is an absolute ethyl alcohol; The concentration of hexafluoro metatitanic acid or hexafluoro zirconate is 0.005～0.01g/ml.
4. soft-magnetic composite material according to claim 1 and 2 is characterized in that with the preparation method of insulated iron powder: the high-purity iron powder concentration in the step (2) is 0.1～2g/ml, and reaction temperature is 30～60 ℃, and the reaction time is 20～30min.
5. soft-magnetic composite material according to claim 1 and 2 is characterized in that with the preparation method of insulated iron powder: described high-purity iron powder is an atomized iron powder.