CN102507850A - 玩具填充物燃烧率的测试方法 - Google Patents
玩具填充物燃烧率的测试方法 Download PDFInfo
- Publication number
- CN102507850A CN102507850A CN2011103540385A CN201110354038A CN102507850A CN 102507850 A CN102507850 A CN 102507850A CN 2011103540385 A CN2011103540385 A CN 2011103540385A CN 201110354038 A CN201110354038 A CN 201110354038A CN 102507850 A CN102507850 A CN 102507850A
- Authority
- CN
- China
- Prior art keywords
- filling material
- burning
- testing
- candle
- toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出一种玩具填充物燃烧率的测试方法,该方法包括步骤:准确称取适量的填充物,均匀填充或平铺到燃烧架子或燃烧网格里;于一定的测试环境下,将蜡烛点燃,然后将点燃的蜡烛的焰心顶端与燃烧架子或燃烧网格一端的表面接触S1秒或直至填充物被点燃;移开蜡烛,让上述填充物在持续自燃的状态下燃烧S2秒;熄灭火焰,测量出被燃烧掉的填充物的尺寸,从而算出填充物的燃烧率。本发明具有操作简单、结果直观、计算简便的优点。
Description
技术领域
本发明涉及一种系统检测与分析测试方法,具体是指一种玩具填充物燃烧率的测试方法。
背景技术
欧美发达国家对儿童教育及日常生活都给与高度的重视,对于平时玩耍的玩具都有极高的要求。所以,欧美比较成熟的玩具行业对于他们的产品在满足玩具法规要求基础上,根据自身产品的特点,制定一系列的行业标准要求,这些要求不仅增强了产品的安全性能,而且对产品质量也有极高的要求。
关于填充玩具内部填充物的清洁度,在美国宾夕法尼亚州有专门的法规——《宾夕法尼亚州填充玩具法规47.317》进行规定:污垢和其他外来物质不超过质量的1.0%;油和油脂成分不超过质量的1.0%;铅含量不超过0.002%;砷含量不超过0.0002%;氨含量不超过5.0%;尿素含量不超过1.0%;石头或其他硬质杂质,或带锐利尖端、边缘的杂物不可存在;不可存在静电以及填充物可能进入耳朵或鼻孔;表面燃烧率<4in2/s(1in=0.0254m)。目前,针对填充玩具清洁度要求—燃烧速度的测试,常见的测试产品易燃性法规有美国玩具安全标准ASTM F963及美国消费品安全委员会联邦法案,但测量结果都是以单位长度来表征的,尚未有以单位面积来表征燃烧速度的方法或对类似填充物料类燃烧速度的测试方法。
发明内容
本发明提出一种符合法规要求的、完善可行的以单位面积来表征玩具填充物燃烧速度的测试方法,以解决目前测量结果都是以单位长度来表征玩具填充物燃烧速度的技术问题。
本发明采用如下技术方案实现:一种玩具填充物燃烧率的测试方法,该方法步骤包括:
准确称取适量的填充物,均匀填充或平铺到燃烧架子或燃烧网格里;
于一定的测试环境下,将蜡烛点燃,然后将点燃的蜡烛的焰心顶端与燃烧架子或燃烧网格一端的表面接触S1秒或直至填充物被点燃;
移开蜡烛,让上述填充物在持续自燃的状态下燃烧S2秒;
熄灭火焰,测量出被燃烧掉的填充物的尺寸,从而算出填充物的燃烧率。
较优的,所述燃烧架子或燃烧网格设置有多个相同尺寸的正方形网格。
较优的,所述填充物为松散型填充材料或固体粒子类填充材料。
较优的,所述测试环境是:温度为18-28oC,相对湿度为20-80%。
较优的,所述时间S1为5秒。
较优的,所述蜡烛时直径至少为1英寸、点燃后的火焰高度至少为5/8 英寸的石蜡蜡烛。
较优的,所述燃烧时间S2为60秒。
较优的,所述熄灭火焰是用非破坏性灭火器或水将蜡烛的火焰熄灭。
较优的,所述测量为观察被燃烧掉的填充物在所述燃烧架子或燃烧网格上占有多少个正方形网格的数量。
与现有技术相比,本发明具有如下特征:操作简单,燃烧架子或燃烧网格的尺寸非常直观,因此,检测员可以快捷、准确地计算出测试结果。
附图说明
图1是本发明的测试流程示意图。
图2是本发明燃烧架子的结构示意图。
图3是本发明燃烧网格的结构示意图。
具体实施方式
常见的填充物主要分为两类:一类是松散型填充材料,如聚酯纤维、合成泡沫、棉花等;另一类则是固体粒子类填充材料。若是松散型填充材料则使用燃烧架子,若为固体粒子类填充材料则使用燃烧网格。
如图1所示,本发明包括如下测试步骤:准确称取适量的填充物,将其均匀填充或平铺到燃烧架子或燃烧网格里;于一定的测试环境下,将点燃蜡烛的焰心顶端与填充物架子一端的表面接触S1秒或直至填充物被点燃;移开蜡烛,让上述填充物在持续自燃的状态下燃烧S2秒;熄灭火焰,通过量度燃烧掉的格子来计算填充物的燃烧率(或燃烧速度)。
实验数据与结果
实例1
准确称取10克聚酯纤维填充材料,将它均匀填充到燃烧架子(如图2所示)里,将架子放置在无风且每次测试后可通风及方便清理的地方,其测试环境的温度为18-28oC,相对湿度为20-80%;手持点燃蜡烛,用焰心顶端与样品架子一端的表面接触5秒钟或直至样品被点燃;移开蜡烛,让样品在持续自燃的火焰下燃烧60秒。用水熄灭火焰后,计算得到总共烧掉4平方英寸(2英寸*2英寸),则其燃烧速度为0.07平方英寸/每秒(4平方英寸/ 60秒)。
实例2
准确称取10克棉花填充材料,将它均匀填充到燃烧架子(如图2所示)里,将架子放置在无风且每次测试后可通风及方便清理的地方,其测试环境的温度为18-28oC,相对湿度为20-80%;手持点燃蜡烛,用焰心顶端与样品架子一端的表面接触5秒钟或直至样品被点燃;移开蜡烛,让样品在持续自燃的火焰下燃烧60秒。用水熄灭火焰后,计算得到总共烧掉6平方英寸(3英寸*2英寸),则其燃烧速度为0.1平方英寸/每秒(6平方英寸/ 60秒)。
实例3
准确称取10克热塑性塑料珠子填充材料,将它均匀平铺到燃烧网格(如图3所示)上,将网格放置在无风且每次测试后可通风及方便清理的地方,其测试环境的温度为18-28oC,相对湿度为20-80%;手持点燃蜡烛,用焰心顶端与样品网格一端的表面接触5秒钟或直至样品被点燃;移开蜡烛,让样品在持续自燃的火焰下燃烧60秒。用水熄灭火焰后,计算得到总共烧掉3平方英寸(2英寸*1.5英寸),则其燃烧速度为0.05平方英寸/每秒(3平方英寸/ 60秒)。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (9)
1. 一种玩具填充物燃烧率的测试方法,其特征在于,该方法步骤包括:
准确称取适量的填充物,均匀填充或平铺到燃烧架子或燃烧网格里;
于一定的测试环境下,将蜡烛点燃,然后将点燃的蜡烛的焰心顶端与燃烧架子或燃烧网格一端的表面接触S1秒或直至填充物被点燃;
移开蜡烛,让上述填充物在持续自燃的状态下燃烧S2秒;
熄灭火焰,测量出被燃烧掉的填充物的尺寸,从而算出填充物的燃烧率。
2.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述燃烧架子或燃烧网格设置有多个相同尺寸的正方形网格。
3.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述填充物为松散型填充材料或固体粒子类填充材料。
4.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述测试环境是:温度为18-28oC,相对湿度为20-80%。
5.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述时间S1为5秒。
6.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述蜡烛是直径至少为1英寸、点燃后的火焰高度至少为5/8 英寸的石蜡蜡烛。
7.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于:所述燃烧时间S2为60秒。
8.根据权利要求1所述的玩具填充物燃烧率的测试方法,其特征在于,所述熄灭火焰的步骤是使用非破坏性灭火器或水将蜡烛的火焰熄灭。
9.根据权利要求2所述的玩具填充物燃烧率的测试方法,其特征在于,所述测量出被燃烧掉的填充物的尺寸的步骤是观察被燃烧掉的填充物在所述燃烧架子或燃烧网格上占有多少个正方形网格的数量。