CN102505559A - 一种阻然安全型烟用接装原纸的制备方法 - Google Patents

一种阻然安全型烟用接装原纸的制备方法 Download PDF

Info

Publication number
CN102505559A
CN102505559A CN2011103521115A CN201110352111A CN102505559A CN 102505559 A CN102505559 A CN 102505559A CN 2011103521115 A CN2011103521115 A CN 2011103521115A CN 201110352111 A CN201110352111 A CN 201110352111A CN 102505559 A CN102505559 A CN 102505559A
Authority
CN
China
Prior art keywords
retardant
flame
paper
cigarette
fire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103521115A
Other languages
English (en)
Inventor
计皓
张琦
陈万平
王大望
毛仁华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG KAIFENG PAPER INDUSTRY Co Ltd
Original Assignee
ZHEJIANG KAIFENG PAPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG KAIFENG PAPER INDUSTRY Co Ltd filed Critical ZHEJIANG KAIFENG PAPER INDUSTRY Co Ltd
Priority to CN2011103521115A priority Critical patent/CN102505559A/zh
Publication of CN102505559A publication Critical patent/CN102505559A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种卷烟接装纸的制备方法。一种阻然安全型烟用接装原纸的制备方法，该方法以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，其中在抄纸机烘干部施涂阻燃成份，阻燃成份由变性淀粉和无卤磷氮系阻燃剂构成，按重量配比计变性淀粉：无卤磷氮系阻燃剂为1：1～1：8；所述的磷氮系阻燃剂选自磷酸三聚氰胺盐、三聚氰胺多聚磷酸盐、2,4,8,10-四氧-3,9-二磷螺环[5,5]十一烷-3,9-二氧-3,9-二三聚氰胺盐、双(2,6,7-三氧-1-磷-双环[2,2,2]辛烷-1-氧甲基)磷酸酯三聚氰胺盐中的一种或多种。本发明产品的优点在于：工艺简单、产品质量稳定，阻燃效果突出，不仅提高纸的阻燃性能，而且改善纸的表面强度，是烟用接装原纸更新换代产品。

Description

一种阻然安全型烟用接装原纸的制备方法
本专利申请是发明专利申请（申请号：201010141780.3，申请日2010年04月07日，发明创造名称：一种阻然安全型烟用接装原纸及其制备方法）的分案申请。
技术领域
本发明涉及一种卷烟接装纸的制备方法。
背景技术
无论在哪个国家，随意丢弃的烟蒂都是引发火灾的重要原因之一，烟蒂火种落地可导致房屋烧毁、工厂爆炸和森林失火，造成生命、财产等方面的重大损失。卷烟接装原纸，是生产滤嘴香烟时，将滤嘴与烟支卷接在一起的专用基纸。过去采用的烟用接装原纸，不具有阻燃特性，给自然环境留下较大的火灾隐患。
中国发明专利（申请号为：200410047091.0）公开了一种卷烟行业中可防火自熄安全型卷烟及其制备方法。卷烟水松纸上涂覆有阻燃剂涂液的阻燃涂层环带，涂层环带位置位于烟支烟丝与嘴棒连接处。其制备为在卷烟水松纸印刷凹印机上，阻燃剂涂液放置在卷烟水松纸印刷凹印机任意一组或多组墨槽中，将阻燃剂涂液涂附在卷烟水松纸上后，分切成盘，再在卷烟机上卷接成烟支。
中国发明专利（申请号为：200910098165.6）公开了一种阻燃卷烟纸及其制备方法，阻燃卷烟纸的长度方向上设有至少两个低透气度区，所谓低透气度区是在普通卷烟纸上设有低透气度薄层而形成的;低透气度薄层的材料主要包括乙基纤维素。阻燃卷烟纸的制备方法，包括调制、放卷、印刷、收卷步骤，其中调制是将5%～25%乙基纤维素、1%～1.5%分散剂和94%～73.5%溶剂在高速搅拌下调制用于低透气度薄层的材料，使之呈油墨状;印刷是采用印刷技术将调制好的呈油墨状的材料印刷到卷烟纸上，形成均匀的低透气度薄层;放卷和收卷的速度为50M/MIN～150M/MIN。
发明内容
为了解决烟用接装原纸不具有阻燃特性的技术缺陷，本发明的一个目的是提供一种阻然安全型烟用接装原纸，该阻燃烟用接装原纸具有阻燃特性，由阻燃烟用接装原纸生产的烟蒂具备不抽吸时自行熄灭功能。本发明的另外一个目的是提供上述的接装原纸的制备方法。
为了实现上述的第一个目的，本发明采用了以下的技术方案：
一种阻然安全型烟用接装原纸，该接装原纸的表面施涂有阻燃成份，阻燃成份的固形物为接装原纸重量的3%～10%，阻燃成份由变性淀粉和无卤磷氮系阻燃剂构成，按重量配比计变性淀粉：无卤磷氮系阻燃剂为1：1～1：8。 
作为优选，上述的阻燃成份的固形物为接装原纸重量的5%～9%。
作为优选，上述的无卤磷氮系阻燃剂为1：2～1：5。
作为优选，上述的磷氮系阻燃剂选自磷酸三聚氰胺盐、三聚氰胺多聚磷酸盐(MPP)、2，4，8，10-四氧-3，9-二磷螺环[5，5]十一烷-3，9-二氧-3，9-二三聚氰胺盐(CN-329)、双(2，6，7-三氧-1-磷-双环[2，2，2]辛烷-1-氧甲基)磷酸酯三聚氰胺盐中的一种或多种。
为了实现上述的第二个目的，本发明采用了以下的技术方案：
一种制备上述的阻然安全型烟用接装原纸的制备方法，该方法以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，其中在抄纸机烘干部施涂阻燃成份。
本发明由于采用了上述的技术方案，制备方法简单易行，使其在原有生产烟用接装原纸的工艺过程中增加较低成本即可实现。本发明产品的优点在于：工艺简单、产品质量稳定，阻燃效果突出，不仅提高纸的阻燃性能，而且改善纸的表面强度，是烟用接装原纸更新换代产品。
具体实施方式
下面将结合具体实施例对本发时作进一步说明，但不限于实施例。
实施例1
以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，其中在抄纸机烘干部施涂阻燃成份，然后进行后续干燥、分切，得到阻燃烟用接装原纸产品。
阻燃成份的配置实例：
磷酸三聚氰胺盐       100g
变性淀粉             35g
水                   1000g
将改性淀粉35克，溶于700克水中，搅拌分散均匀，加温到80-90℃，此温度下糊化20分钟，加水稀释到1000克，然后加入100克磷酸三聚氰胺盐，继续搅拌进一步溶解制成溶夜。
用量：固形物对纸5%～9%的施加量，施涂液的浓度依基纸的吸附量而定，二者之间成反比。
实施例2
以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，其中在抄纸机烘干部施涂阻燃成份，然后进行后续干燥、分切，得到阻燃烟用接装原纸产品。
阻燃成份的配置实例：
三聚氰胺多聚磷酸盐   120g
变性淀粉             40g
水                   1000g
将改性淀粉40克，溶于700克水中，搅拌分散均匀，加温到80-90℃，此温度下糊化20分钟，加水稀释到1000克，然后加入120克三聚氰胺多聚磷酸盐，继续搅拌进一步溶解制成溶夜。
用量：固形物对纸5%-9%的施加量，施涂液的浓度依基纸的吸附量而定，二者之间成反比。
实施例3
以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，其中在抄纸机烘干部施涂阻燃成份，然后进行后续干燥、分切，得到阻燃烟用接装原纸产品。
阻燃成份的配置实例：
三聚氰胺多聚磷酸盐   60g
磷酸三聚氰胺盐       50g
变性淀粉             25g
水                   1000g
将改性淀粉25克，溶于700克水中，搅拌分散均匀，加温到80-90℃，此温度下糊化20分钟，加水稀释到1000克，然后加入三聚氰胺多聚磷酸盐60g、磷酸三聚氰胺盐50g，继续搅拌进一步溶解制成溶夜。
用量：固形物对纸5%-9%的施加量，施涂液的浓度依基纸的吸附量而定，二者之间成反比。
试验例
阻燃烟用接装原纸检测结果及阻燃效果的评价。
测试条件：温度20度，湿度60%
阻燃效果以烟支在静态燃烧下，能息行熄灭数或氧指数指标来衡量
检测结果与评价
  NO1 NO2 NO3
20支香烟，点燃后置于静态燃烧箱内燃烧至滤嘴时，可自行熄灭数量 20支 19支 18支
NO1：实施例1
NO2：实施例2
NO3：实施例3。

Claims (3)

1.一种阻然安全型烟用接装原纸的制备方法，其特征在于：该接装原纸以漂白化学木浆为原纸浆料，经打浆、净化、筛选、抄纸制备而成，在抄纸机烘干部施涂所述的阻燃成份，阻燃成份的固形物为接装原纸重量的3%～10%，阻燃成份由变性淀粉和无卤磷氮系阻燃剂构成，按重量配比计变性淀粉：无卤磷氮系阻燃剂为1：1～1：8；所述的磷氮系阻燃剂选自磷酸三聚氰胺盐、三聚氰胺多聚磷酸盐、2,4,8,10-四氧-3,9-二磷螺环[5,5]十一烷-3,9-二氧-3,9-二三聚氰胺盐、双(2,6,7-三氧-1-磷-双环[2,2,2]辛烷-1-氧甲基)磷酸酯三聚氰胺盐中的一种或多种。
2.根据权利要求1所述的一种阻然安全型烟用接装原纸的制备方法，其特征在于阻燃成份的固形物为接装原纸重量的5%～9%。
3.根据权利要求1所述的一种阻然安全型烟用接装原纸的制备方法，其特征在于按重量配比计变性淀粉：无卤磷氮系阻燃剂为1：2～1：5。
CN2011103521115A 2010-04-07 2010-04-07 一种阻然安全型烟用接装原纸的制备方法 Pending CN102505559A (zh)