CN102504566A - Preparation method for silicon-plastic material and application thereof on aspect of garbage bin - Google Patents
Preparation method for silicon-plastic material and application thereof on aspect of garbage bin Download PDFInfo
- Publication number
- CN102504566A CN102504566A CN2011103645527A CN201110364552A CN102504566A CN 102504566 A CN102504566 A CN 102504566A CN 2011103645527 A CN2011103645527 A CN 2011103645527A CN 201110364552 A CN201110364552 A CN 201110364552A CN 102504566 A CN102504566 A CN 102504566A
- Authority
- CN
- China
- Prior art keywords
- preparation
- silicon
- waste
- smelting furnace
- plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method for a silicon-plastic material and an application thereof on the aspect of a garbage bin. The preparation method comprises the following steps of: (1) putting waste plastic and pulverized fuel ash into a smelting furnace in the weight ratio of (3-5):1; (2) heating the smelting furnace to 150-200 DEG C till the plastic the pulverized fuel ash are smelted into paste, and uniformly stirring; and (3) casting a pasty melt onto a mold for molding to obtain a plate form, a revolving form or a basin form, and cooling. In the invention, industrial domestic solid waste such as waste plastic, pulverized fuel ash and the like are adopted, so that secondary pollution is avoided in a production process; a product is nontoxic, tasteless and resistant to aging, acids, alkalis and impact, and has the characteristics of saving in energy, environmental friendliness, easiness for processing raw materials and products, low production cost and the like; the tenet of recovering waste is represented completely; and the method belongs to an environmentally-friendly project.
Description
Technical field
The present invention relates to the silicon moulding material, especially a kind of preparation method of silicon moulding material and the application aspect refuse container thereof.
Background technology
At present, make refuse container and mainly adopt plastics, stainless steel, iron plate and timber, kaolin etc., the refuse container cost that plastics, stainless steel, iron plate and timber are made is higher, is prone to stolen; Though the refuse container that kaolin is made is with low cost, work-ing life is short, is prone to cracked.Therefore, it is very necessary studying a kind of environmental protection and energy saving, refuse container material with low cost.
Through retrieval; Find the two piece publications close with application of the present invention; 1, a kind of making method of silicon plastic well lid (CN101712192A) is processed by following raw materials by weight percent: Vilaterm 70%, flyash 25%, softening agent 1.5%, coupling agent 1.5%, Triple Pressed Stearic Acid 2%; Its making method is: Vilaterm powder and flyash are mixed, add softening agent, coupling agent and Triple Pressed Stearic Acid, be heated to 180 ℃ and stir, drop into mechanical pressing in the mould that is provided with Framework Of Steel Reinforcement.2, a kind of silicon plastic composite template and working method (CN101338077); It mainly is made up of plastics, flyash, bamboo bar, earlier plastic grain is handled and processed to waste or used plastics, adopts the exhaust high-speed mixer of heating in proportion above-mentioned plastic grain and flyash to be mixed; The additive that adding is made up of lime carbonate, potter's clay, inhibitor, anti-fosterization agent, promotor, stablizer and coupling agent forms raw material; Raw material is put into the compound forcing machine of pulsation extruding exhaust, heat, after plasticizing is extruded to 100 ℃-220 ℃; Be aided with the bamboo bar by proportioning, through the mould compound extrusion forming.
Above-mentioned two pieces of patent documentations, though also be to be main raw material with plastics machine flyash, technology is comparatively complicated, and for hardness and the intensity that improves the silicon moulding material has adopted various additives, in smelting process, produces obnoxious flavour and contaminate environment easily.
Summary of the invention
The objective of the invention is to overcome the weak point of prior art, the preparation method and the application aspect refuse container thereof that a kind of environmental protection and energy saving are provided, prepare silicon moulding material simple, with low cost.
The present invention realizes that the technical scheme of purpose is following:
A kind of preparation method of silicon moulding material, preparing method's step is:
(1) with waste or used plastics and flyash according to 3-5: 1 part by weight is put into smelting furnace;
(2) smelting furnace is heated to 150-200 ℃, planar until plastics and flyash are melted to, stir;
(3) planar melts is poured into moulding in the model, processes template, rotary type or basin type, cooling gets final product.
And, in step (1), be added to the pigment of raw material gross weight 0.5-1%.
A kind of application of the silicon moulding material being made refuse container.
Advantage of the present invention and positively effect are:
1, the present invention all adopts industry such as plastic waste and flyash, life solid waste; Do not produce secondary pollution in the production process; Product is nontoxic, tasteless, ageing-resistant, acid and alkali-resistance, shock resistance; Characteristics such as the processing with save energy, protection environment, raw material and product is simple, low production cost have embodied the aim of " utilization of waste material " fully, belong to the environmental protection project.
2, technology of the present invention is simple, makes easily, and technical requirements is low, adopts simple smelting furnace to get final product, and material source is easy, and the rubbish container of made can be discarded in use for some time, eliminates white pollution, and novelty is stronger.
Embodiment
Below in conjunction with specific embodiment the present invention is made further detailed description, following examples are descriptive, are not determinate, can not limit protection scope of the present invention with this.
Embodiment 1:
A kind of preparation method of silicon moulding material, step is:
(1) waste or used plastics and flyash are put into smelting furnace according to 5: 1 part by weight;
(2) smelting furnace is heated to 200 ℃, planar until plastics and flyash are melted to, stir;
(3) planar melts is poured into moulding in the model, processes template, rotary type or basin type, cooling gets final product.
(4) modes such as the template of making, rotary type or basin type material employing screw are packed on the refuse container skeleton, can make silicon plastic refuse bucket.
Embodiment 2:
A kind of preparation method of silicon moulding material, step is:
(1) waste or used plastics and flyash are put into smelting furnace according to 4: 1 part by weight, be added to the pigment of gross weight 1% simultaneously;
(2) smelting furnace is heated to 190 ℃, planar until plastics and flyash are melted to, stir;
(3) planar melts is poured into moulding in the model, processes template, rotary type or basin type, cooling gets final product.
(4) modes such as the template of making, rotary type or basin type material employing screw are packed on the refuse container skeleton, can make silicon plastic refuse bucket.
Embodiment 3:
A kind of preparation method of silicon moulding material, step is:
(1) waste or used plastics and flyash are put into smelting furnace according to 3: 1 part by weight;
(2) smelting furnace is heated to 180 ℃, planar until plastics and flyash are melted to, stir;
(3) planar melts is poured into moulding in the model, processes template, rotary type or basin type, cooling gets final product.
(4) modes such as the template of making, rotary type or basin type material employing screw are packed on the refuse container skeleton, can make silicon plastic refuse bucket.
Claims (3)
1. the preparation method of a silicon moulding material, it is characterized in that: preparing method's step is:
(1) with waste or used plastics and flyash according to 3-5: 1 part by weight is put into smelting furnace;
(2) smelting furnace is heated to 150-200 ℃, planar until plastics and flyash are melted to, stir;
(3) planar melts is poured into moulding in the model, processes template, rotary type or basin type, cooling gets final product.
2. the preparation method of silicon moulding material according to claim 1 is characterized in that: the pigment that in step (1), is added to raw material gross weight 0.5-1%.
3. application of the silicon moulding material being made refuse container.