CN102492327A - Printing article red ink - Google Patents
Printing article red ink Download PDFInfo
- Publication number
- CN102492327A CN102492327A CN2011104075592A CN201110407559A CN102492327A CN 102492327 A CN102492327 A CN 102492327A CN 2011104075592 A CN2011104075592 A CN 2011104075592A CN 201110407559 A CN201110407559 A CN 201110407559A CN 102492327 A CN102492327 A CN 102492327A
- Authority
- CN
- China
- Prior art keywords
- ink
- magenta ink
- magenta
- pigment
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to printing article red ink, which comprises a magenta pigment, a dispersant and water, wherein the magenta pigment is a combination of more than one or two of C.I. pigment red 122, C.I. pigment violet 19, C.I. pigment red 202 or C.I. pigment violet 23; and the dispersant comprises more than one or two of substances with an infrared spectrum absorption peak at position intervals (unit: cm<-1>) of 3300-3500, 2070-2170, 1600-1680, 1490-1530, 1436-1467, 1330-1370, 1270-1310, 1229-1269 and 1063-1103, and has two or more infrared spectrum absorption peaks at the interval of 2800-3000. The ink has high dispersion stability, high spray stability and high intermittent spray stability.
Description
Technical field
The present invention relates to a kind of ink, magenta ink is used in especially a kind of printing, more particularly a kind of magenta aqueous pigment ink of suitable spray ink Printing.
Background technology
Ink-jet technology is the printing technology of a kind of contactless, no pressure, no forme, mainly is divided into heat foamable formula and piezoelectric type by mode of operation.The heat foamable technology is through heated nozzle, makes ink produce bubble, is sprayed onto on the print media.Piezo technology is to utilize the characteristic that has crooked deformation under the effect of piezoelectric ceramics voltage change; When graphicinformation voltage is added on the piezoelectric ceramics; Piezoelectric ceramics will stretching vibration be out of shape along with the variation of picture information voltage, and makes the evenly ejection exactly of ink in the shower nozzle.On the basis of piezo technology; Relevant manufacturer develops convertible ink droplet minute-pressure electricity printhead technology again, and it is stronger to the controllability of ink droplet, adopts quantity of ink of this technology ejection to have only common 1/3; I is to 1.5 skin liters; And the ink droplet particulate form is more regular, the location is more accurate, and print resolution improves, and realizes the high precision printing easily.Along with the widespread use of ink-jet technology, the user prints stability and has higher requirements not only to printing precision, also print speed is had requirements at the higher level in addition.This just requires constantly development innovation ink gun technology, and continuous development is fit to the ink technology of new shower nozzle.
Generally to add components such as pigment, dispersion agent, permeate agent, wetting Agent for Printing Inks, tensio-active agent and high molecular polymer at least in the jetting ink prescription; Select appropriate component and add correct ratio to make jetting ink have good jetting stability, can make the ink jet printing article have advantages such as high glossiness, good antifriction scrape along image exquisiteness.In addition the preparation of jetting ink especially the preparation of aqueous pigment ink have certain difficulty, this is because can be by the paint ink grain diameter of shower nozzle ejection about 100 nanometers, and the pigment particles of nanoscale is very easy to reunite, and causes shower nozzle to stop up.Therefore to screen suitable dispersion agent to different pigment.There has been the dispersion agent model that much is used for colo(u)rant dispersion on the market, like the BYK series dispersion agent of Bi Ke chemistry, the solsperse series dispersion agent of Lubrizol Corp. and the AFCONA series dispersion agent of Ai Fu Kona etc.Patented claim about pigment dispersing agent also has much in addition, and is visible about the patent of dispersion agent:
Chinese patent 02803656.5 acid color dispersion agent and pigment preparation,
Chinese patent 01104937.5 pigment dispersing agent and the color compositions that contains this pigment dispersing agent,
Chinese patent 00816936.5 graft copolymer pigment dispersant,
Chinese patent 02120124.2 has the pigment combinations of modified block copolymer dispersants,
Chinese patent 200780044910.8 dispersion agents etc.
Above-mentioned patent considers that mainly a kind of dispersion agent of exploitation can make colo(u)rant dispersion more stable; Its Application Areas can be coating, printing ink or ink-jet; But for above-mentioned various dispersion agents; They also are not suitable for high precision, fireballing ink jet printing head, and are not suitable for and the new ink set system of new shower nozzle coupling.
Summary of the invention
The objective of the invention is to, provide a kind of printing to use magenta ink, the magenta ink that adopts the present invention to obtain has good dispersion stabilization, jetting stability and interrupted injection stability.In order to obtain good print quality, can contain silicon-type tensio-active agent and glycol ether simultaneously in the ink, and contain the high molecular polymer that improves the image crocking resistance simultaneously, and the stably dispersing performance of ink keeps good.
The technical scheme that the present invention adopts is:
A kind of magenta ink; This ink comprises magenta pigment, dispersion agent and water; Wherein said magenta pigment is one or more compsns in C.I. pigment red 122, C.I. pigment violet 19, C.I. Pigment red 202 or the C.I. pigment Violet 23, and said dispersion agent comprises that one or more all have an infrared spectrum absorpting peak between following location registration zone
3300cm
-1To 3500cm
-1
2070cm
-1To 2170cm
-1
1600cm
-1To 1680cm
-1
1490cm
-1To 1530cm
-1
1436cm
-1To 1476cm
-1
1330cm
-1To 1370cm
-1
1270cm
-1To 1310cm
-1
1229cm
-1To 1269cm
-1
1063cm
-1To 1103cm
-1,
And at 2800cm
-1To 3000cm
-1The interval has the material of two or more infrared spectrum absorpting peaks.
Preferably, in this ink, with respect to the ink gross weight, the mass percent of said magenta pigment is 1%-6%; The mass percent of said dispersion agent is 0.5%-10%;
Meeting dispersion agent of the present invention gives an example like the SAF DT-531 product of Shanghai Sang Jing chemical industry ltd.
Preferably, also contain mass percent (with respect to the ink total mass) in this magenta ink and be 1%-8% glycol ether or glycol ether compsn, preferably, wherein glycol ether has following structure:
m=1~2,n=1~4
Perhaps have following structure:
m=1~4,n=1~4
More preferably, described glycol ether is terepthaloyl moietie n-butyl ether, Diethylene Glycol n-butyl ether, triethylene glycol n-butyl ether, TEG n-butyl ether, terepthaloyl moietie tertbutyl ether, Diethylene Glycol tertbutyl ether, glycol isopropyl ether, Diethylene Glycol isopropyl ether, propylene glycol monomethyl ether, propylene-glycol ethyl ether, glycol tertiary butyl ether, propylene glycol n-propyl ether, propylene glycol n-butyl ether, Ucar 35 isopropyl ether, dipropylene glycol n-butyl ether, dipropylene glycol n-propyl ether or dipropylene glycol isopropyl ether.Said glycol ether compsn is the two or more mixtures in the above-mentioned glycol ether.
Preferably, this magenta ink also contains mass percent (with respect to the ink total mass) and is the high molecular polymer of 0.5%-7%, and wherein the second-order transition temperature Tg of high molecular polymer is greater than 50 ℃, and weight-average molecular weight Mw is greater than 5000;
More preferably, as the high molecular polymer that improves the ink rub resistance, can enumerate high molecular polymers such as acrylic acid or the like, styrene-propene acids, polyurethanes, polyester, rosin or modified rosin class, silicone based or polyolefin-wax emulsion.For obtaining the ideal crocking resistance, the weight-average molecular weight of high molecular polymer should be greater than 5000, and second-order transition temperature Tg should be greater than 50 ℃; Concrete for example like the commercial goods: the Joncryl HPD 696 of BASF AG (Tg=88, Mw=16000), Joncryl611 (Tg=50, Mw=8100), Joncryl 678 (Tg=85; Mw=8600), Joncryl HPD 71 (Tg=128; Mw=17250), Joncryl HPD196 (Tg=85, Mw=9200), Joncryl 67 (Tg=73, Mw=12500), JoncrylHPD690 (Tg=102; Mw=16500) Joncryl 678 (Tg=85, Mw=8600) etc.
Preferably, this magenta ink also contains mass percent (with respect to the ink total mass) and is the tensio-active agent of 0.5-3.0%; More preferably, said tensio-active agent is silicone based tensio-active agent, more preferably, contains a kind of in following four kinds of structures in the said silicone based surfactant molecule at least:
As silicone based tensio-active agent, can be selected from BYK345, BYK346, BYK347, BYK348 of Bi Ke chemical company or the like.
Preferably, when often not using, stop up, also comprise mass percent (with respect to the ink total mass) in the magenta ink according to the invention and be the difficult evaporable solvent of 4%-30% high boiling point because of volatile dry causes shower nozzle for making ink; This kind solvent can be given an example like USP Kosher, terepthaloyl moietie, Diethylene Glycol, triglycol, n-propyl alcohol, 1,2-Ucar 35,1, ammediol, 1; 4-butyleneglycol, 1; 5-pentanediol, 1,2-pinakon, 1,6-pinakon, TriMethylolPropane(TMP), Macrogol 200, PEG 400, Polyethylene Glycol-600,2-pyrrolidone, 1; 2, the mixture of one or more in 6-hexanetriol, tetramethylolmethane or the urea.
Preferably, can also contain mass percent (with respect to the ink total mass) in this magenta ink and be the pH regulator agent of 0.05%-1%, like ammoniacal liquor, triethylamine, diethylolamine, trolamine, sodium hydroxide, Pottasium Hydroxide etc.
Preferably, can also contain mass percent (with respect to the ink total mass) in this magenta ink for the sterilant of 0.01%-0.3%, as 1, the 2-benzisothiazole-3-ketone.
This magenta ink can also contain metal ion chelation agent, UV light absorber as required.
The present invention also provides the application of above-mentioned magenta ink in spray ink Printing.
Use dispersion agent described in the invention that quinacridine ketone pigment is had dissemination preferably; Quinacridine ketone pigment such as C.I. pigment red 122, C.I. pigment violet 19 and C.I. Pigment red 202 use dispersion agent described in the invention that the C.I. pigment Violet 23 is also had dissemination preferably in addition.
The beneficial effect that the present invention had:
Magenta ink provided by the invention has good dispersion stabilization, jetting stability and interrupted injection stability.Than the ink of prior art, be more suitable for high precision, fireballing ink jet printing head.
Contain the silicon-type tensio-active agent in the ink set of the present invention, can prevent that black liquid from spreading and sinking in oozes, improves ejection stability and to the wettability of medium; Also contain glycol ether in the ink of the present invention, thereby can improve the perviousness of ink medium; Contain glossiness, crocking resistance that high molecular polymer can further improve image in the ink of the present invention; Through the addition of preferred surfactant, glycol ether and high molecular polymer, can obtain good print quality (improving jetting stability and image sophistication); Can realize above-mentioned polycomponent coexistence in the prescription through preferred dispersants, and make ink have good dispersion stabilization.
Description of drawings
Fig. 1 is the ir spectra spectrogram of dispersion agent Dispers 760W (enlightening high product);
Fig. 2 is the ir spectra spectrogram of dispersion agent Jeffsperse X3204 (the graceful product of Hensel);
Fig. 3 is the ir spectra spectrogram of dispersion agent SAF DT-531 (Shanghai Sang Jing chemical industry);
Embodiment:
Below in conjunction with specific embodiment the present invention is described further, but does not limit protection scope of the present invention.
The umber that embodiment 1-3 and comparative example 1-2 are mentioned is parts by weight.
Embodiment 1:
With 18 parts of C.I. pigment red 122s; 9,40 parts of dispersion agent SAFDT-531 of 18 parts of C.I. pigment violet 1s and 224 parts of deionized waters mix with the high speed shear whisking appliance, obtain shearing dispersion liquid; Again above-mentioned shearing dispersion liquid is ground with shredder and disperseed 2 hours, obtain dispersion liquid A.
With 4 parts of 2-pyrrolidone, 12 parts of USP Kosher, 1 part of BYK348,1 part of Joncryl67,0.2 part of sodium hydroxide and 41.8 parts of deionized waters mix, and obtain ink solution.
The ink solution of preparation is added drop-wise among 40 parts of above-mentioned dispersion liquid A, and after mixing, the use aperture is that 0.5 micron strainer filters, and obtains the magenta aqueous pigment ink.
Embodiment 2:
36 parts of C.I. pigment violet 19,40 parts of dispersion agent SAF DT-531 and 224 parts of deionized waters are mixed with the high speed shear whisking appliance, obtain shearing dispersion liquid, above-mentioned shearing dispersion liquid is ground with shredder disperseed 2 hours again, obtain dispersion liquid B.
With 4 parts of 2-pyrrolidone, 12 parts of USP Kosher, 1 part of BYK348,1 part of Joncryl67,0.2 part of sodium hydroxide and 51.8 parts of deionized waters mix, and obtain ink solution.
The ink solution of preparation is added drop-wise among 30 parts of above-mentioned dispersion liquid B, and after mixing, the use aperture is that 0.5 micron strainer filters, and obtains the magenta aqueous pigment ink.
Embodiment 3
With 30 parts of C.I. pigment Violet 23s, 35 parts of dispersion agent SAF DT-531 and 235 parts of deionized waters mix with the high speed shear whisking appliance, obtain shearing dispersion liquid, above-mentioned shearing dispersion liquid is ground with shredder disperseed 2 hours again, obtain dispersion liquid C.
With 4 parts of 2-pyrrolidone, 12 parts of USP Kosher, 1 part of BYK348,1 part of Joncryl67,0.2 part of sodium hydroxide and 41.8 parts of deionized waters mix, and obtain ink solution.
The ink solution of preparation is added drop-wise among 40 parts of above-mentioned dispersion liquid C, and after mixing, the use aperture is that 0.5 micron strainer filters, and obtains the magenta aqueous pigment ink.
Comparative example 1:
With 18 parts of C.I. pigment red 122s; 18 parts of C.I. pigment violet 19,40 parts of dispersion agent Dispers 760w and 224 parts of deionized waters mix with the high speed shear whisking appliance, obtain shearing dispersion liquid; Again above-mentioned shearing dispersion liquid is ground with shredder and disperseed 2 hours, obtain dispersion liquid D.
With 4 parts of 2-pyrrolidone, 12 parts of USP Kosher, 1 part of BYK348,1 part of Joncryl67,0.2 part of sodium hydroxide and 41.8 parts of deionized waters mix, and obtain ink solution.
The ink solution of preparation is added drop-wise among 40 parts of above-mentioned dispersion liquid D, and after mixing, the use aperture is that 0.5 micron strainer filters, and obtains the magenta aqueous pigment ink.
Comparative example 2
With 18 parts of C.I. pigment red 122s; 9,45 parts of dispersion agent JeffsperseX3204 of 18 parts of C.I. pigment violet 1s and 219 parts of deionized waters mix with the high speed shear whisking appliance, obtain shearing dispersion liquid; Again above-mentioned shearing dispersion liquid is ground with shredder and disperseed 2 hours, obtain dispersion liquid E.
With 4 parts of 2-pyrrolidone, 12 parts of USP Kosher, 1 part of BYK348,1 part of Joncryl67,0.2 part of sodium hydroxide and 41.8 parts of deionized waters mix, and obtain ink solution.
The ink solution of preparation is added drop-wise among 40 parts of above-mentioned dispersion liquid E, and after mixing, the use aperture is that 0.5 micron strainer filters, and obtains the magenta aqueous pigment ink.
For more intuitive explanation, the form with form is following with the prescription of each example below:
The formula table of table 1 embodiment 1-3, comparative example 1-2
(wherein numeric representation mass fraction)
|
Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | |
The 2-pyrrolidone | 4 | 4 | 4 | 4 | 4 |
USP Kosher | 12 | 12 | 12 | 12 | 12 |
BYK?348 | 1 | 1 | 1 | 1 | 1 |
Joncryl?67 | 1 | 1 | 1 | 1 | 1 |
Sodium hydroxide | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 |
Deionized water | 41.8 | 51.8 | 41.8 | 41.8 | 41.8 |
|
40 | ||||
|
30 | ||||
|
40 | ||||
|
40 | ||||
|
40 |
The test result explanation:
Can find out that according to table 2 test result the magenta ink that the employing method that the present invention write down obtains has good dispersion stabilization.The method that adopts the present invention in addition and write down is embodiment 2 for example, not only can obtain good dispersion stabilization, and ink also has good jetting stability and interrupted injection stability.
Table 2 magenta ink test result
|
Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | |
D50/ initial (nanometer) | 78 | 85 | 76 | 81 | 82 |
D50/2 is (nanometer) after week | 78 | 90 | 84 | 90 | 91 |
Dispersion stabilization | Well | Well | Well | Well | Well |
Jetting stability is estimated | Well | Well | Well | Well | Well |
Interrupted injection stability | Well | Well | Well | Extreme difference | Extreme difference |
The testing method explanation
IR spectroscopy: use Fourier transformation infrared spectrometer that dispersion agent is tested, resolution setting is 4cm
-1, scanning times is set at 16.
Jetting stability is estimated: use Epson Stylus Pro 7910 stamping machines that ink to be measured is carried out continous inkjet output; After 5 square metres of continuous outputs; The inspection condition of nozzles; The intact not broken string of nozzle is recorded as good, and there have 1 to 5 nozzle broken string to be recorded as to be poor, has more than 5 nozzle broken strings to be recorded as extreme difference.
Interrupted injection estimation of stability: use Epson Stylus Pro 7910 stamping machines that ink to be measured is carried out continous inkjet output; After 5 square metres of continuous outputs; Left standstill stamping machine 12 hours, and checked condition of nozzles afterwards, the intact not broken string of nozzle is recorded as good; There have 1 to 5 nozzle broken string to be recorded as to be poor, has more than 5 nozzle broken strings to be recorded as extreme difference.
Dispersion stabilization is estimated: at first use dynamic laser scattering particle size analyzer to measure the granularity of ink, it is initial to be labeled as D50/; Then ink sealing to be measured is placed in the incubator of 60 ℃ of constant temperature, two weeks back taking-up ink to be measured still uses dynamic laser scattering particle size analyzer to measure the granularity of ink once more, is labeled as D50/2 after week; If changing, the granularity difference of twice measurement is recorded as well less than 10 nanometers, medium if the variation of the granularity difference of twice measurement is recorded as less than 30 nanometers greater than 10 nanometers, and poor if the variation of the granularity difference of twice measurement is recorded as greater than 30 nanometers.
Claims (10)
1. magenta ink; It is characterized in that: this ink comprises magenta pigment, dispersion agent and water; Wherein said magenta pigment is one or more compsns in C.I. pigment red 122, C.I. pigment violet 19, C.I. Pigment red 202 or the C.I. pigment Violet 23, and said dispersion agent comprises that one or more all have an infrared spectrum absorpting peak between following location registration zone
3300cm
-1To 3500cm
-1
2070cm
-1To 2170cm
-1
1600cm
-1To 1680cm
-1
1490cm
-1To 1530cm
-1
1436cm
-1To 1476cm
-1
1330cm
-1To 1370cm
-1
1270cm
-1To 1310cm
-1
1229cm
-1To 1269cm
-1
1063cm
-1To 1103cm
-1,
And at 2800cm
-1To 3000cm
-1The interval has the material of two or more infrared spectrum absorpting peaks.
2. according to the said a kind of magenta ink of claim 1, it is characterized in that: the mass percent of said magenta pigment is 1%-6%; The mass percent of said dispersion agent is 0.5%-10%.
3. according to claim 1 or 2 said a kind of magenta inks, it is characterized in that: described dispersion agent is the SAF DT-531 product of Shanghai Sang Jing chemical industry ltd.
5. according to each described a kind of magenta ink of claim 1-4; It is characterized in that: this magenta ink also contains the high molecular polymer that mass percent is 0.5%-7%; Wherein the second-order transition temperature Tg of high molecular polymer is greater than 50 ℃, and weight-average molecular weight Mw is greater than 5000.
6. according to each said a kind of magenta ink of claim 1-5, it is characterized in that: this magenta ink also contains the tensio-active agent that mass percent is 0.5-3.0%.
7. according to each said a kind of magenta ink of claim 1-6, it is characterized in that: said tensio-active agent is silicone based tensio-active agent, more preferably, contains a kind of in following four kinds of structures in the said silicone based surfactant molecule at least:
8. according to each said a kind of magenta ink of claim 1-7, it is characterized in that: also comprising mass percent in the said magenta ink is the difficult evaporable solvent of 4%-30% high boiling point.
9. according to each said a kind of magenta ink of claim 1-7, it is characterized in that: also containing mass percent in this magenta ink is the pH regulator agent of 0.05%-1%.
10. each described a kind of magenta ink application in spray ink Printing of claim 1-9.