CN102477236A - Flash silver/fluorocarbon finish paint and manufacturing method thereof - Google Patents
Flash silver/fluorocarbon finish paint and manufacturing method thereof Download PDFInfo
- Publication number
- CN102477236A CN102477236A CN2010105587930A CN201010558793A CN102477236A CN 102477236 A CN102477236 A CN 102477236A CN 2010105587930 A CN2010105587930 A CN 2010105587930A CN 201010558793 A CN201010558793 A CN 201010558793A CN 102477236 A CN102477236 A CN 102477236A
- Authority
- CN
- China
- Prior art keywords
- percent
- agent
- flash
- silver
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to flash silver/fluorocarbon finish paint and a manufacturing method thereof. The flash silver/fluorocarbon finish paint is made from the following materials in percentage by weight: 60 to 70 percent of fluorocarbon resin, 5 to 8 percent of xylene, 1 to 2 percent of an anti-settling agent, 0.1 to 0.2 percent of a dispersing agent, 0.2 to 0.3 percent of a defoaming agent, 6 to 7 percent of flash silver powders, 3 to 5 percent of butyl ester, 2 to 3 percent of pma solution, 0.4 to 0.6 percent of a levelling agent, and 15 to 20 percent of CBA solution. Owing to the formula and process provided by the invention, the flash silver/fluorocarbon finish paint has the advantage of excellent quality and can be widely applied in different operating environments.
Description
Technical field
The present invention relates to silver-colored fluorine carbon finishing paint of a kind of flash of light and complete processing thereof.
Background technology
The silver-colored fluorine carbon finishing paint that glistens receives widely with its excellent performance to be used, but present flash of light silver fluorine carbon finishing paint exists quality not good mostly, and the shortcoming of complex manufacturing needs further to improve.
Summary of the invention
The present invention is directed to above-mentioned defective, purpose is to provide a kind of can make flash of light silver guaranteed prescription of fluorine carbon finishing paint quality and the complete processing thereof that processes.
Technical scheme of the present invention is: the weight ratio of each material of the present invention is: fluorocarbon resin 60-70%, YLENE 5-8%, anti-settling agent 1-2%, dispersion agent 0.1-0.2%, skimmer 0.2-0.3%, flash of light silver powder 6-7%, fourth fat 3-5%, pma solution 2-3%, flow agent 0.4-0.6%, CBA solution 15-20%.
The glisten complete processing of silver-colored fluorine finish paint, carry out according to the following steps:
1) fluorocarbon resin, YLENE are fed in the reaction kettle in proportion, speed change was disperseed 4-6 minute then;
2) anti-settling agent, dispersion agent, skimmer, flash of light silver powder are dropped into 1) in reaction kettle in, speed change was disperseed 10-15 minute then;
3) fourth fat, pma solution, flow agent, CBA solution are dropped into 2) in reaction kettle in, speed change was disperseed 5-10 minute then;
4) censorship.
The flash of light silver fluorine carbon finishing paint that comes out according to prescription of the present invention and explained hereafter has the advantage of good quality, can be widely used in various environments for use.
Embodiment
Embodiment one
The weight ratio of each material of the present invention is: fluorocarbon resin 60%, YLENE 6%, anti-settling agent 2%, dispersion agent 0.2%, skimmer 0.3%, flash of light silver powder 7%, fourth fat 5%, pma solution 3%, flow agent 0.5%, CBA solution 16%.
The glisten complete processing of silver-colored fluorine finish paint, carry out according to the following steps:
1) fluorocarbon resin, YLENE are fed in the reaction kettle in proportion, speed change was disperseed 5 minutes then;
2) anti-settling agent, dispersion agent, skimmer, flash of light silver powder are dropped into 1) in reaction kettle in, speed change was disperseed 12 minutes then;
3) fourth fat, pma solution, flow agent, CBA solution are dropped into 2) in reaction kettle in, speed change was disperseed 12 minutes then;
4) censorship.
Embodiment two
The weight ratio of each material of the present invention is: fluorocarbon resin 65%, YLENE 5%, anti-settling agent 1%, dispersion agent 0.2%, skimmer 0.2%, flash of light silver powder 6%, fourth fat 3%, pma solution 2%, flow agent 0.6%, CBA solution 17%.
The glisten complete processing of silver-colored fluorine finish paint, carry out according to the following steps:
1) fluorocarbon resin, YLENE are fed in the reaction kettle in proportion, speed change was disperseed 3 minutes then;
2) anti-settling agent, dispersion agent, skimmer, flash of light silver powder are dropped into 1) in reaction kettle in, speed change was disperseed 15 minutes then;
3) fourth fat, pma solution, flow agent, CBA solution are dropped into 2) in reaction kettle in, speed change was disperseed 14 minutes then;
4) censorship.
Claims (2)
1. silver-colored fluorine carbon finishing paint glistens; It is characterized in that the weight ratio of each material is: fluorocarbon resin 60-70%, YLENE 5-8%, anti-settling agent 1-2%, dispersion agent 0.1-0.2%, skimmer 0.2-0.3%, flash of light silver powder 6-7%, fourth fat 3-5%, pma solution 2-3%, flow agent 0.4-0.6%, CBA solution 15-20%.
2. the complete processing of silver-colored fluorine finish paint of glistening is characterized in that, carries out according to the following steps:
1) fluorocarbon resin, trimethylbenzene are fed in the reaction kettle in proportion, speed change was disperseed 4-6 minute then;
2) anti-settling agent, dispersion agent, skimmer, flash of light silver powder are dropped into 1) in reaction kettle in, speed change was disperseed 10-15 minute then;
3) fourth fat, pma solution, flow agent, CBA solution are dropped into 2) in reaction kettle in, speed change was disperseed 5-10 minute then;
4) censorship.