CN102464930A - Water-in-water multicolor latex paint - Google Patents
Water-in-water multicolor latex paint Download PDFInfo
- Publication number
- CN102464930A CN102464930A CN201010534519XA CN201010534519A CN102464930A CN 102464930 A CN102464930 A CN 102464930A CN 201010534519X A CN201010534519X A CN 201010534519XA CN 201010534519 A CN201010534519 A CN 201010534519A CN 102464930 A CN102464930 A CN 102464930A
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- pigment
- kaolin
- multicolor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to water-in-water multicolor latex paint, which is composed of, by weight: 30-40% of deionized water, 25-35% of kaolin, 0.1-0.2% of an auxiliary agent AMP95, 5-10% of a dispersant rutile titanium dioxide, 15-25% of a film forming material silicone-acrylate emulsion, 3-7% of an anionic wetting agent, and a small amount of a pigment. The water-in-water multicolor latex paint of the invention is free of the defects of disoperation on environments and walls as well as short service life of oil-in-water paint, has no problems of low simulation degree and great construction difficulty of all water-based paint, and overcomes various lesions of other granite color paint, thus being paint with long service life, strong simulation property, and excellent performances.
Description
Technical field
The present invention relates to a kind of colored hilllock color coating material, relate in particular to a kind of water bag water multi-colour emulsoid paint.
Background technology
Flower hilllock color coating material has three types on oil-in-water-type, water-in-water type and full water-based type at present at home; Oil-in-water-type flower hilllock color coating material is because it can't overcome environmental protection requirement; And the as easy as rolling off a log facing basic unit that makes comes to harm, and heat insulating effect is seriously reduced, and its work-ing life is shorter; The appearance of film that full water-based type coating generates does not obviously have the nature sense, and fidelity is poor, and difficulty of construction is big.Both do not have " oil-in-water-type " to the infringement of environment, body of wall and useful life period short defective; The problem that fidelity is poor, difficulty of construction is big that does not have " full water-based type " again; The various focuses of other flower hilllock color coating material have been overcome; Become a weathering resistance overlength, extremely strong, the various performance of emulation property and be excellent coating and since its characteristic it become the product that a utmost point has the market competitiveness.
Summary of the invention
The present invention provides a kind of long service life, water bag water multi-colour emulsoid paint that emulation property is strong in order to overcome the above problems.
Technical scheme of the present invention is: be made up of deionized water, kaolin, auxiliary agent A MP95, dispersion agent rutile titanium white powder, filmogen organosilicon crylic acid latex, negatively charged ion wetting agent and pigment; The weight percent that each composition accounts for total mass is respectively: deionized water 30-40%, kaolin 25-35%, AMP95 auxiliary agent 0.1-0.2%; White titanium pigment 5-10%; Organosilicon crylic acid latex 15-25%, negatively charged ion wetting agent 3-7%, pigment is a small amount of.
The present invention both do not had oil-in-water-type coating to the infringement of environment, body of wall and useful life period short defective; The problem that fidelity is poor, difficulty of construction is big that does not have full water-based type coating again; Overcome the various focuses of other flower hilllock color coating material, become a kind of long service life, emulation property extremely strong, various performance is excellent coating.
Embodiment
Embodiment 1
Water bag water multicolor finish is made up of deionized water, kaolin, auxiliary agent A MP95, dispersion agent rutile titanium white powder, filmogen organosilicon crylic acid latex, negatively charged ion wetting agent and pigment, and the weight percent that each composition accounts for total mass is respectively: deionized water 30%; Kaolin 25%; AMP95 auxiliary agent 0.1%, white titanium pigment 5%, organosilicon crylic acid latex 15%; Negatively charged ion wetting agent 3%, pigment is a small amount of.
Embodiment 2
Water bag water multicolor finish is made up of deionized water, kaolin, auxiliary agent A MP95, dispersion agent rutile titanium white powder, filmogen organosilicon crylic acid latex, negatively charged ion wetting agent and pigment, and the weight percent that each composition accounts for total mass is respectively: deionized water 35%; Kaolin 30%; AMP95 auxiliary agent 0.15%, white titanium pigment 8%, organosilicon crylic acid latex 20%; Negatively charged ion wetting agent 5%, pigment is a small amount of.
Embodiment 3
Water bag water multicolor finish is made up of deionized water, kaolin, auxiliary agent A MP95, dispersion agent rutile titanium white powder, filmogen organosilicon crylic acid latex, negatively charged ion wetting agent and pigment, and the weight percent that each composition accounts for total mass is respectively: deionized water 40%; Kaolin 35%; AMP95 auxiliary agent 0.2%, white titanium pigment 10%, organosilicon crylic acid latex 25%; Negatively charged ion wetting agent 7%, pigment is a small amount of.
Claims (1)
1. water bag water multi-colour emulsoid paint, it is characterized in that: be made up of deionized water, kaolin, auxiliary agent A MP95, dispersion agent rutile titanium white powder, filmogen organosilicon crylic acid latex, negatively charged ion wetting agent and pigment, the weight percent that each composition accounts for total mass is respectively: deionized water 30-40%; Kaolin 25-35%; AMP95 auxiliary agent 0.1-0.2%, white titanium pigment 5-10%, organosilicon crylic acid latex 15-25%; Negatively charged ion wetting agent 3-7%, pigment is a small amount of.