CN102452200A - Composite base fabric of hot-rolling stereotypes carpet and production method thereof - Google Patents
Composite base fabric of hot-rolling stereotypes carpet and production method thereof Download PDFInfo
- Publication number
- CN102452200A CN102452200A CN2010105304518A CN201010530451A CN102452200A CN 102452200 A CN102452200 A CN 102452200A CN 2010105304518 A CN2010105304518 A CN 2010105304518A CN 201010530451 A CN201010530451 A CN 201010530451A CN 102452200 A CN102452200 A CN 102452200A
- Authority
- CN
- China
- Prior art keywords
- acupuncture
- rolling
- fiber
- base fabric
- base cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to composite base fabric of a hot-rolling stereotypes carpet and a production method thereof. The base fabric consists of needling fabric and base fabric composite needling. The needling fabric is needled by 4-6 layers of nonwoven fabric. The base fabric consists of polypropylene fiber with the melting point at 150 DEG C and fiber with the melting point greater than 200 DEG C which are mixed. The base fabric of the product in the invention mixed by the polypropylene fiber with low melting point and conventional fiber has the functions of ventilation, moisture absorption, bacteria prevention and antifungus performance, integrates sanitariness and environmental protection and has good abrasive resistance and standing hardness. The invention is simple and convenient in technological operation and has high work efficiency.
Description
Technical field
The present invention relates to a kind of compound base cloth and production method thereof, relate in particular to compound base cloth of a kind of rolling and molding carpet and production method thereof.
Background technology
The traditional carpet base cloth is the PP base cloth mostly, on the ground blanket base cloth, often want napping, and the napping effect of PP base cloth is relatively poor; Kind and color are also relatively more dull, can not satisfy the different demands of different people, simultaneously because carpet mainly plays decoration and place mat effect; In use through regular meeting unintentionally with water droplet on carpet; In the course of time carpet can be mouldy, and breed bacteria more easily influences people's health.
Summary of the invention
The present invention provides a kind of ventilative, health, compound base cloth of rolling and molding carpet and production method thereof wear-resisting, convenient for production in order to overcome the above problems.
Technical scheme of the present invention is: described base cloth is made up of acupuncture lining and base fabric composite acupuncture; The nonwoven acupuncture that described acupuncture lining is the 4-6 layer forms, and described base fabric is that the fiber mixing that 150 ℃ polypropylene fiber and fusing point is higher than 200 ℃ forms by fusing point.
The compound base cloth production method of a kind of rolling and molding carpet, implement according to the following steps:
1), face and fiber are sent into bale opener mixed cotton, shredding, combing processing;
2), multiple fiber mixing is processed web, be mixed with web cementation after heat bonding processing of low melting point polypropylene fiber;
3), the product that obtains of step be will go up and pre-needling, purl thorn, main acupuncture carried out;
4), the product behind the composite acupuncture is carried out the high temperature hot rolling, examine the pin operation again, inspection acupuncture quality;
5), with the finished product combing rolling that obtains.
Described polypropylene fiber and fusing point are higher than the ratio 1: 4 of 200 ℃ fiber.
Product base fabric of the present invention adopts low-melting polypropylene fiber and conventional fibre to mix, and has the function of ventilative, moisture absorption, fungi-proofing, mildew-resistant, integrates the wholesomeness and the feature of environmental protection, and good wearability and high stiff degree are arranged.
Technological operation of the present invention is easy, high efficiency.
The specific embodiment
Compound base cloth of a kind of rolling and molding carpet and production technology thereof; Described base cloth is made up of acupuncture lining and base fabric composite acupuncture; The nonwoven acupuncture that described acupuncture lining is the 4-6 layer forms; Described base fabric is that the fiber mixing that 150 ℃ polypropylene fiber and fusing point is higher than 200 ℃ forms by fusing point, and described polypropylene fiber and fusing point are higher than the ratio 1: 4 of 200 ℃ fiber.Implement according to the following steps:
1), face and fiber are sent into bale opener mixed cotton, shredding, combing processing;
2), multiple fiber mixing is processed web, be mixed with web cementation after heat bonding processing of low melting point polypropylene fiber;
3), the product that obtains of step be will go up and pre-needling, purl thorn, main acupuncture carried out;
4), the product behind the composite acupuncture is carried out the high temperature hot rolling, examine the pin operation again, inspection acupuncture quality;
5), with the finished product combing rolling that obtains.
Claims (3)
1. compound base cloth of rolling and molding carpet; It is characterized in that: described base cloth is made up of acupuncture lining and base fabric composite acupuncture; The nonwoven acupuncture that described acupuncture lining is the 4-6 layer forms, and described base fabric is that the fiber mixing that 150 ℃ polypropylene fiber and fusing point is higher than 200 ℃ forms by fusing point.
2. compound base cloth production method of rolling and molding carpet is characterized in that: implement according to the following steps:
1), face and fiber are sent into bale opener mixed cotton, shredding, combing processing;
2), multiple fiber mixing is processed web, be mixed with web cementation after heat bonding processing of low melting point polypropylene fiber;
3), the product that obtains of step be will go up and pre-needling, purl thorn, main acupuncture carried out;
4), the product behind the composite acupuncture is carried out the high temperature hot rolling, examine the pin operation again, inspection acupuncture quality;
5), with the finished product combing rolling that obtains.
3. the compound base cloth of rolling and molding carpet according to claim 1 is characterized in that: described polypropylene fiber and fusing point are higher than the ratio 1: 4 of 200 ℃ fiber.