CN102443306A - 一种胶水粉 - Google Patents
一种胶水粉 Download PDFInfo
- Publication number
- CN102443306A CN102443306A CN2011103161340A CN201110316134A CN102443306A CN 102443306 A CN102443306 A CN 102443306A CN 2011103161340 A CN2011103161340 A CN 2011103161340A CN 201110316134 A CN201110316134 A CN 201110316134A CN 102443306 A CN102443306 A CN 102443306A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion powder
- powder
- glue
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种胶水粉,由下列组分组成,各组分的重量份为:轻质纳米碳酸钙50-70、羟丙基甲基纤维素10-15、乙烯/醋酸乙烯共聚胶粉4-7、秸秆灰烬5-10、丙烯酰胺10-15、甲酸钙1-2、聚羧酸系高性能减水剂1-2、木质素1-2、硅烷基憎水剂4-6凹凸棒土3-5、钛白粉1-3、气相二氧化硅3-5。制备时以轻质碳酸钙作为载体,将羟丙基甲基纤维素、乙烯/醋酸乙烯共聚胶粉、甲酸钙、减水剂、憎水剂、木质素、聚丙烯酰胺、秸秆灰烬等融合在一起制成白色粉末。本发明的胶水粉具有无毒、无污染、无气味、无放射性、无碱性的特点。适用的温度范围大。用其配制的涂料,施工方便,不尿线,流平性好,不卷皮,成膜快。
Description
技术领域
本发明涉及建筑材料领域,具体涉及一种胶水粉。
背景技术
建筑业当中所使用的胶水与普通的胶水不同,其要求有较高的附着能力,以及保持粘性的时间足够长。当前市场上使用的建筑胶水有两种生产方式,一种是生产厂家直接将聚乙烯醇、丙烯酰胺等化工材料生产的液体包装后投放市场;另一种由生产厂家将PVA、EVA、CMC等高分子聚合物胶粉加工成建筑胶水后分装投放市场。这两种生产方式需要的包装物大,不够节能;投放市场贮运成本高,不够经济;生产的产品使用不方便;其生产的胶水成分中有甲醛、氨、防腐剂等有毒物质,不环保;产品在运输过程中,易破损,会造成资源浪费;胶水品质低,调制的腻子附着力差、易卷皮、脱落等;针对外墙等基材使用胶水调制的水泥基材料,由于水泥基毛细管吸水原因易造成膨胀、开裂、风化、污染、霉变及冻融循环时导致剥落等问题。目前很多厂家都针对建筑胶水的原料组分进行了改进及更新,如安徽省建筑科学研究设计院采用乳胶粉、甲基纤维素、消泡剂、粘结剂、白水泥等原料生产的新型环保建筑腻子胶粉,其专门用于代替劣质的建筑胶水配置内、外墙腻子。但现有技术的建筑用胶水粉(固体胶水),除了其附着能力强弱不一,同时普遍存在污染环境的缺点,有的长时间接触会对建筑工人的身体造成损害。
发明内容
本发明提供一种胶水粉,采用轻质碳酸钙基物质作为载体,由多种高分子材料,辅以多功能助剂,科学配方而成 ,具有无毒、无污染、无气味、无放射性、无碱性的特点。
为了达到上述目的,本发明所采用的技术方案为:
一种胶水粉,由下列组分组成,各组分的重量份为:
轻质纳米碳酸钙 50-70
羟丙基甲基纤维素 10-15
乙烯/醋酸乙烯共聚胶粉 4-7
秸秆灰烬 5-10
丙烯酰胺 10-15
甲酸钙 1-2
聚羧酸系高性能减水剂 1 -2
木质素 1-2
硅烷基憎水剂 4-6
凹凸棒土 3-5
钛白粉 1-3
气相二氧化硅 3-5。
所述木质素长度为1mm。
制备方法:本发明以轻质碳酸钙作为载体,将羟丙基甲基纤维素、乙烯/醋酸乙烯共聚胶粉、甲酸钙、减水剂、憎水剂、木质素、聚丙烯酰胺、秸秆灰烬等融合在一起 制成的白色粉末。
本发明溶于水后,其高分子材料及助剂依附轻质碳酸钙形成一种高性能的胶连体。本发明体积小、储运方便、操作简易、环保节能,其具有以下优点:
1、提高腻子的保水性,延长腻子的凝结时间。
2、提高腻子的施工和易性,增加腻子的柔韧性。
3、提高腻子的引气性、流动性和可再分散性。
4、提高腻子的抗裂强度及耐磨性。
5、提高腻子稠度、粘接力及粘接强度。
6、提高腻子致密性,减少毛细孔对水的吸收,防止渗水,有效抑制基材的泛碱。
7、具有无毒、无污染、无气味、无放射性、无碱性的特点。
用其配制的涂料,施工方便,不尿线,流平性好,不卷皮,成膜快。
具体实施方式
一种胶水粉,由下列组分组成,各组分的重量份为:
轻质纳米碳酸钙 50-70
羟丙基甲基纤维素 10-15
乙烯/醋酸乙烯共聚胶粉 4-7
秸秆灰烬 5-10
丙烯酰胺 10-15
甲酸钙 1-2
聚羧酸系高性能减水剂 1 -2
木质素 1-2
硅烷基憎水剂 4-6
凹凸棒土 3-5
钛白粉 1-3
气相二氧化硅 3-5。
憎水剂为聚二甲基硅氧烷和烷氧基硅烷的聚合物。木质素长度为1mm。
一年四季当中环境温度的波动比较大,冬季气温低于-10℃,而夏季墙体温度超过60℃以上,本发明的胶水粉调制的腻子适应的温度范围大,能适应大温度范围的原理如下:
1、墙体极易吸水,腻子要易批,具有一定的保湿性,不使腻子骨料等产生分离泌水,使用轻质碳酸钙,延缓了水泥的水合过程,使得水泥凝结硬化过程变慢,腻子的凝聚时间相应得到延长。
2、使用木质素、丙烯酰胺等,增强墙体的抗裂作用。
3、胶水粉中的减水剂使腻子减少用水量,改善流动性,增强稳定性。
4、由于水泥基材料极易发生毛细管吸水现象,加入憎水剂,延缓水泥水合过程中水泥硅酸钙mCaOSiO2nH2O的形成,延长水泥颗粒之间的空隙存在时间,便于水泥基材料固化,当基材固化后,基材显著降低水的吸收及通过水渗入到基材的盐分,抑制泛碱现象。
5、硬化的基材材料结构主要由水泥石相和聚合物相构成,通过无机颗粒与聚合物颗粒间的界面粘接在一起。乙烯/醋酸乙烯共聚胶粉,玻璃化温度较低,具有较高的柔韧性,能很好的与水泥石胶接在一起。
6、秸秆灰烬的平均粒径仅为水泥平均粒径的1%,渗入水泥腻子中,能很好的填充于水泥颗粒孔隙之中,使腻子更致密;另还与游离的氢氧化钙结合,形成稳定的硅酸钙水合物,从而提高了腻子的抗渗性。
本发明生产过程中将配方内相应组分依次加入失重混合机中,搅拌10-15min,由提升机提起,通过自动化包装机计量包装,然后即可投入市场使用。
使用方法:按照胶水粉与水的质量比为:1:(40-50)的比例配制成胶水,具体操作如下:
首先在搅拌桶里面加入清洁水倒,在不断搅拌的情况下将胶水粉徐徐加入水中,继续搅拌到胶水粉完全溶解,然后静置10-20分钟让胶性完全反应即可使用。
实验数据
本发明的胶水粉主要技术指标检测如下表:
粘度 | 180剥离强度 | 低温稳定性 | 压剪胶接强度 | 附着力 | 干燥时间 |
22.25Pa | 65N/25num | 0℃,24h部分凝胶化,室温下恢复到流动状态 | 5.0MPa | 100% | 4h |
Claims (2)
1.一种胶水粉,其特征在于:由下列组分组成,各组分的重量份为:
轻质纳米碳酸钙 50-70
羟丙基甲基纤维素 10-15
乙烯/醋酸乙烯共聚胶粉 4-7
秸秆灰烬 5-10
丙烯酰胺 10-15
甲酸钙 1-2
聚羧酸系高性能减水剂 1 -2
木质素 1-2
硅烷基憎水剂 4-6
凹凸棒土 3-5
钛白粉 1-3
气相二氧化硅 3-5。
2.根据权利要求1所述的胶水粉(固体胶水),其特征在于:所述木质素长度为1mm。