CN102442040A - Molding method of fiber product and finished product thereof - Google Patents
Molding method of fiber product and finished product thereof Download PDFInfo
- Publication number
- CN102442040A CN102442040A CN2010105041866A CN201010504186A CN102442040A CN 102442040 A CN102442040 A CN 102442040A CN 2010105041866 A CN2010105041866 A CN 2010105041866A CN 201010504186 A CN201010504186 A CN 201010504186A CN 102442040 A CN102442040 A CN 102442040A
- Authority
- CN
- China
- Prior art keywords
- plastic carrier
- fiber
- preimpregnation material
- fibre
- fiber preimpregnation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a molding method of a fiber product and a finished product thereof. The molding method comprises the following steps of: preparing a plastic carrier; coating a layer of interface adhesive on a special-shaped surface of the plastic carrier; preparing at least one fiber pre-preg material containing the interface adhesive; stabilizing the fiber pre-preg material by using the plastic carrier; and performing hot pressing on the fiber pre-preg material and the plastic carrier till the fiber pre-preg material is boned with a hot melt interface and is attached to the surface of the plastic carrier. The fiber pre-preg material is positioned by taking the plastic carrier as a support, and three-dimensional (3D) appearance change can be realized by performing a one-time hot pressing procedure, so that the appearance is not limited, the procedure can be shortened, and the economic benefit is enhanced greatly.
Description
Technical field
The present invention relates to a kind of fibre, particularly relate to a kind of forming method and finished product thereof of fibre.
Background technology
Carbon fiber is a kind of fiber that is made up of carbon atom, and " lines " are extremely very thin, though diameter approximately has only 0.005 millimeter～0.01 millimeter; Intensity but can reach 7～9 times of steel, and therefore weight is less than 1/4 of steel; Taken into account lightweight and high-intensity demand, added its special braiding lines, made carbon fiber product; Become the synonym of high texture, and be widely used in various product.
Because carbon cloth is softness and tool is not qualitative quite, therefore, carbon fiber product in the past all is with manual type, with carbon cloth binding to desired thickness in layer, cuts, is hot pressed into predetermined shape again.Not only labor intensive, time, and appearance is subject to the bonding mode, the variation of deflection can only be arranged, and can not be directed against demand, has the appearance of three-dimensional (3D) to change, and adds the cost height, causes price also high.
Announcing No. 590888 " manufacturing approach of plastic composites and composite product " patent of invention case, No. 572825 " method of forming composite goods and this composite " patent of invention case of bulletin, No. 512830 " it is the object of structural wood that the fibrous composite of tool high interfacial strength reaches with this composite " patent of invention case of bulletin with TaiWan, China is example; Though can form a composite wood with the heating and pressurizing mode with other material layer and fibrous material layer; Reach the purpose that reduces cost; But still can be because of being to cohere layer by layer with manual work; Cut again, hot-forming, make appearance be subject to the bonding mode equally, the variation of deflection can only be arranged; And can not be directed against demand, there is the appearance of three-dimensional (3D) to change.
Consult Fig. 1, Fig. 2; Be example with No. 317926 " the fastening combined structure of working of plastics and carbon fiber spare " novel patent case of TaiWan, China patent in addition; Mainly be to be furnished with one deck bond 12, then, in advance this carbon fiber spare 11 be contained in the die cavity 21 of a mould 2 carbon fiber spare 11 1 surfaces coated; This working of plastics 13 of ejection formation makes this working of plastics 13 be combined as a whole with this carbon fiber spare 11 through this bond 12 again.
Yet, because this carbon fiber spare 11 is a kind of weaving cotton cloth, soft and the mobile or distortion because of external force easily of matter; Therefore; Though aforementioned die cavity 21 can be any moulding, the pressure in the time of can penetrating because of this working of plastics 13 has and pushes the situation that the fine part 11 of this carbon produces fold; So, still be not suitable for appearance variations such as moulding concave, convex fluctuating.
Summary of the invention
The objective of the invention is is providing a kind of and can simplify processing procedure, reducing cost, and has the forming method and the finished product thereof of the fibre that three-dimensional (3D) appearance changes.
The forming method of fibre of the present invention comprises the following step, step 1: purchase a plastic carrier.Step 2: be coated with a bed boundary glue in compromise face of this plastic carrier.Step 3: purchase the fiber of a slice at least preimpregnation material that impregnation has interface glue.Step 4: stablize this fiber preimpregnation material with this plastic carrier.Step 5: this fiber preimpregnation material of hot pressing and this plastic carrier close the interface agglutination of this fiber preimpregnation material and hot melt, and are obedient to the surface of this plastic carrier.
The forming method of fibre of the present invention, this plastic carrier are that plastics and fiber mixing form.
The forming method of fibre of the present invention, the content of fiber is greater than 40% in this plastic carrier.
The forming method of fibre of the present invention, this plastic carrier are with shoot mode machine-shaping.
The forming method of fibre of the present invention; This step 3 comprises step 3-1, with fibrous a slice impregnation one interface glue of weaving cotton cloth, forms this fiber preimpregnation material; Step 3-2; Form the thin film of printing opacity light in this fiber preimpregnation material one surface, this film is with coating, pastes wherein a kind of mode, is formed on the surface of this fiber preimpregnation material.
The forming method of fibre of the present invention, the hot pressing temperature of this step 5 are higher than 160 ℃, and hot pressing time circle was in 2～10 minutes, and hot pressing pressure circle is in 5～200kg/cm
2
The finished product of fibre of the present invention comprises a plastic carrier, a slice fiber preimpregnation material, an and interface glue at least.This plastic carrier has a compromise face.This fiber preimpregnation material is obedient to the surface of this plastic carrier.This interface glue is formed between this plastic carrier and this fiber preimpregnation material, and behind hot melt, involutory plastic carrier and this fiber preimpregnation material in conjunction with bearing a pressure.
The finished product of fibre of the present invention also includes the thin film that is formed on this fiber preimpregnation material one surface and is used for printing opacity.
The finished product of fibre of the present invention, this film have a surface and the bed boundary glue that combines with this fiber preimpregnation material that is formed on towards this fiber preimpregnation material.
The finished product of fibre of the present invention, this plastic basis material also have at least one the moulding portion that is formed on this surface and in three dimensions, changes.
Effect of the present invention is to be support with this plastic carrier, makes this fiber preimpregnation material keep the location, and can be with a hot pressing processing procedure, and the appearance with three-dimensional (3D) changes, and not only moulding is unrestricted, and can shorten processing procedure, significantly promotes economic benefit.
Description of drawings
Fig. 1 is a cutaway view, and No. 317926 case of Chinese patent is described;
Fig. 2 is a cutaway view, and a finished product of patent case is described;
Fig. 3 is a sectional exploded view, and the forming method of the present invention's one fibre and a preferred embodiment of finished product thereof are described;
Fig. 4 is the preferred embodiment is stablized a fiber preimpregnation cloth with a plastic carrier a cutaway view;
Fig. 5 is a cutaway view of a finished product in the preferred embodiment;
Fig. 6 is a flow chart of the preferred embodiment; And
A stereogram of this finished product in Fig. 7 the preferred embodiment.
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is elaborated:
Consult Fig. 3, Fig. 4, and Fig. 5, a preferred embodiment of the finished product of fibre of the present invention comprises a plastic carrier 3, a slice fiber preimpregnation material 4, a bed boundary glue 5 and a slice film 6.
This plastic carrier 3 has a surface 31 of abnormity, and is formed with several moulding portions 32 that in three-dimensional (3D) space, change.In this preferred embodiment, this plastic carrier 3 be plastics and content greater than the fiber mixing more than 40% after, one-body molded with the injection molding mode, have high rigidity, and shock-resistant.
This fiber preimpregnation material 4 is followed the fluctuating of these plastic carrier 3 moulding portions 32, is obedient to the surface 31 of this plastic carrier 3.In this preferred embodiment, be with fibrous a slice impregnation one interface glue of weaving cotton cloth, form this fiber preimpregnation material 4.Aforementioned fibers can be that carbon fiber, glass fibre, polyester fiber (polyester fiber), nylon fiber, Ke Weila fiber (Kevlar fiber), cotton textured fiber are wherein a kind of.
This interface glue 5 is formed on 4 of this plastic carrier 3 and this fiber preimpregnation materials, is used to combine this plastic carrier 3 and this fiber preimpregnation material 4.This interface glue 5 can be epoxy resin, phenolic resins, acryl resin, thermoplasticity polyamine base Ethyl formate resin (Thermoplastic Polyurethane, TPU), nylon resin, ABS resin (Acrylonitrile Butadiene Styrene), polycarbonate resin, polyvinyl resin, acrylic resin, sarin ionization resin (Surlyn) is wherein a kind of and these a combination.
This film 6 is the transparent resin of one deck thermoplasticity and printing opacity at this preferred embodiment, can be formed on this fiber preimpregnation material 4 one surfaces 41 to be coated with, to paste wherein a kind of mode, has the high grade of transparency, uvioresistant, reaches characteristics such as shock-resistant.In this preferred embodiment; This film 6 can be epoxy resin, nylon resin, (Acrylonitrile Butadiene Styrene) is wherein a kind of for ABS resin, and has a surface and the bed boundary glue 61 that combines with this fiber preimpregnation material that is formed on towards this fiber preimpregnation material 4.
Consult Fig. 6 and Fig. 3, Fig. 4, the forming method of fibre of the present invention is to be instrument with a mould 7 and hot-press arrangement (figure does not show), and this mould 7 has two involutory modules 71, and is formed on several die cavitys 72 of 71 of aforementioned modules.Below promptly combine explanation of embodiment step as back:
Step 81: purchase more than one plastic carrier 3.
Step 82: 31 these interface glue 5 of coating in the surface of this plastic carrier 3.
Step 83:, form this fiber preimpregnation material 4 with the fibrous impregnation interface glue of weaving cotton cloth.
Step 84: repeatedly put this film 6 in the surface 41 of this fiber preimpregnation material 4.
Step 85: this plastic carrier 3 is received in the die cavity 72 of this module 71, and cooperate the quantity of this plastic carrier 3, with this fiber preimpregnation material 4 more than plastic carrier 3 stable a slices.
Step 86: involutory aforementioned modules 71 makes this fiber preimpregnation material 4 be subject to this plastic carrier 3 and this die cavity 72, and with pliability own, follows the moulding portion 32 of this plastic carrier 3 to rise and fall.
Step 87: with this mould 7 of this hot-press arrangement hot pressing.Hot pressing temperature is higher than 160 ℃, and hot pressing time circle was in 2～10 minutes, and hot pressing pressure circle is in 5～200kg/cm
2, whereby, the interface glue of impregnation can be because high temperature and hot melt in the interface glue of this interface glue 5, this film 6 61 and this fiber preimpregnation material 4, makes that this fiber preimpregnation material 4 and this plastic carrier 3, this film 6 are fixed to be one, and is obedient to the surface 31 of this plastic carrier 3.
Step 88: open this mould 7, and take out a finished product 9 as shown in Figure 7.
According to aforementioned, through ganoid film 6, the braiding lines that high-visible this finished product 9 is special; The visual effect that not only has the fibrid goods, and, can take into account lightweight and high-intensity demand equally with the finished product 9 of the plastic carrier that is mixed with fiber 3 with these fiber preimpregnation material 4 be combined intos; Importantly; The present invention can make this fiber preimpregnation material 4 follow the moulding portion 32 of this plastic carrier 3 to rise and fall, and the appearance with three-dimensional (3D) changes, and fully highlights commodity competitiveness of the present invention.
Can know that according to the above the forming method of fibre of the present invention and finished product thereof have advantage and effect:
The present invention is to be support with this plastic carrier 3, make softness not tool fiber preimpregnation qualitatively material 4 can keep the location, and with a hot pressing processing procedure; Cooperate die cavity 72 quantity of this mould 7, obtain more than one finished product 9, make this finished product 9 have three-dimensional (3D) appearance change; Not only unrestricted, the surface of moulding need not application, just can obtain smooth surface, smooth finished product 9, and can simplify processing procedure and manpower; Reach structural form, take into account lightweight, high strength at the same time and can have an X-rayed under the situation of demands such as braiding lines the consumption of minimizing fiber with composite; And then can reduce cost, and significantly promote productivity effect, and economic benefit.
Claims (10)
1. the forming method of a fibre is characterized in that it comprises the following step:
Step 1: purchase a plastic carrier;
Step 2: a compromise face in said plastic carrier is coated with a bed boundary glue;
Step 3: purchase the fiber of a slice at least preimpregnation material that impregnation has interface glue;
Step 4: stablize said fiber preimpregnation material with said plastic carrier; And
Step 5: hot pressing said fiber preimpregnation material and said plastic carrier close the interface agglutination of said fiber preimpregnation material and hot melt, and are obedient to the surface of said plastic carrier.
2. the forming method of fibre according to claim 1 is characterized in that, said plastic carrier is that plastics and fiber mixing form.
3. the forming method of fibre according to claim 2 is characterized in that, the content of fiber is greater than 40% in the said plastic carrier.
4. according to the forming method of claim 1 or the described fibre of claim 2, it is characterized in that said plastic carrier is with shoot mode machine-shaping.
5. the forming method of fibre according to claim 1 is characterized in that, said step 3 comprises step 3-1; With fibrous a slice impregnation one interface glue of weaving cotton cloth; Form said fiber preimpregnation material, step 3-2 is in the thin film of said fiber preimpregnation material one surface formation printing opacity light; Said film is with coating, pastes wherein a kind of mode, is formed on the surface of said fiber preimpregnation material.
6. the forming method of fibre according to claim 1 is characterized in that, the hot pressing temperature of said step 5 is higher than 160 ℃, and hot pressing time circle was in 2～10 minutes, and hot pressing pressure circle is in 5～200kg/cm
2
7. the finished product of a fibre is characterized in that it comprises:
A plastic carrier has a compromise face;
At least a slice fiber preimpregnation material is obedient to the surface of said plastic carrier; And
One interface glue is formed between said plastic carrier and said fiber preimpregnation material, and behind hot melt, involutory plastic carrier and the said fiber preimpregnation material in conjunction with bearing a pressure.
8. the finished product of fibre according to claim 7 also includes the thin film that is formed on said fiber preimpregnation material one surface and is used for printing opacity.
9. the finished product of fibre according to claim 8 is characterized in that, said film has a surface and the bed boundary glue that combines with said fiber preimpregnation material that is formed on towards said fiber preimpregnation material.
10. the finished product of fibre according to claim 7 is characterized in that, said plastic basis material also has at least one the moulding portion that is formed on said surface and in three dimensions, changes.