Abstract

The invention discloses a production method of a jet black Chengni inkstone, solving the problems that the production method of the Chengni inkstone has been lost for many years and the color can not be artificially controlled. The production method comprises the following steps: airing and drying the ancient silt from the Hutuo river in Wutai county in Shanxi province; putting the dried ancient silt into a water tank to be soaked for two hours; stirring the soaked ancient silt to form mud; filtering the mud; kneading and beating the filtered mud to form a mud pie; putting the mud pie into a mould to prepare a blank; putting the blank into a fireproof box and burying the complete blank with coal dust; and putting the fireproof box into a kiln, controlling the kiln temperature to be 980-1050 DEG C and firing the blank for 72 hours, thus obtaining the jet black Chengni inkstone. The production method has the following beneficial effects: the production method carries forward the traditions and brings forth new ideas; the long lost production process of the Chengni inkstone is restored; and the produced Chengni inkstone has fine quality and both shape and color.

Description

The production method of the black sedimentary clay inkstone platform of black jade

Technical field

The present invention relates to a kind of production method of sedimentary clay inkstone platform, be specially the production method of the black sedimentary clay inkstone platform of a kind of black jade.

Background technology

Sedimentary clay inkstone is one of China's four major famous inkstones, it and Duanxi inkstone, inhales inkstone, the Taohe River inkstone and is called China's " four major famous inkstones ".Sedimentary clay inkstone is opened the meticulous beginning of China's inkstone circle.Its predecessor is the Tao Yan in ancient times.The enlightenment that ancients are produced by brick, eaves tile is manufactured meticulously in conjunction with Tao Yanzai, satisfies the step distillation and is sedimentary clay inkstone.This inkstone starts from the Tang Dynasty, and the Song dynasty is developed into the peak, and progressively decline after this is lost at last.The characteristics of sedimentary clay inkstone are that matter is hard fine and smooth, and hard water storage does not dry up and not dry, carefully and not sliding, and going through trembles with fear does not ice, and send out China ink benefit milli, and are deep or light suitable, gentle calmness, and there is multiple different colours in the refined U.S.A of color and luster.Say in " study four spectrums ": " after the Song dynasty, the exploitation natural stone is chiseled inkstone, type sedimentary clay inkstone, also name ' sedimentary clay inkstone '.Its category has ' yellow eel is yellow ', ' crust green ', ' mineral granule ', ' rose violet ', ' bean cotyledon sand ' etc. "; The expert on historical relics points out: " because of the weather of the source of silt and manufacturing process, fire the color that the difference of the duration and degree of heating is had nothing in common with each other." it seems that ancients are not is to have a mind to fire shades of colour, but objective formation in the sintering procedure, the formation of color has contingency, non-artificial can control.

Sintering procedure that the sedimentary clay inkstone platform is concrete and technology, then just lost to the Qing Dynasty.The ancient sedimentary clay inkstone of finding today is very rare, and top grade difficulty is especially asked, and traces it to its cause, probably with regard to being that manufacture craft is complicated and output is very low.

Summary of the invention

The present invention is directed to the problem that sedimentary clay inkstone platform production method is lost and the inkstone color can't artificially be controlled, the production method of the black sedimentary clay inkstone platform of a kind of black jade is provided.

The present invention realizes through following steps: the production method of the black sedimentary clay inkstone platform of a kind of black jade may further comprise the steps: the heavy mud airing of Gu that will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done; The heavy mud of Gu after drying is put into water vat to be soaked two hours; The heavy mud of Gu after soaking is stirred into mud; Mud is filtered; Mud after filtering is carried out kneading pat, make it be shaped to walk; Walk is put into mould process blank; Blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with coal dust; Fire-resistant box is put into kiln, and the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained the black sedimentary clay inkstone platform of black jade.

The present invention holds Gu and innovates, and has recovered the production technology of lost sedimentary clay inkstone platform for a long time, and the sedimentary clay inkstone platform quality of producing is fine and smooth; Solid thick Gu; Shape system is various, and has realized the purpose of artificial control sedimentary clay inkstone platform appearance luster on this basis, and the sedimentary clay inkstone platform shape and color of producing has both.Said production method possesses operability, realizes for those skilled in the art are easy.The present invention follows the example of folk tradition technology; Explore through a large amount of experiments and technology for many years; Successfully realized the suitability for industrialized production of sedimentary clay inkstone platform; The sedimentary clay inkstone platform of being produced has the multiple good characteristic of putting down in writing in the ancient books, and has obtained breakthrough on this basis, has realized the control to sedimentary clay inkstone platform appearance colour.The sedimentary clay inkstone platform that burns out can combine color and shape system, makes it have more artistic effect.The present invention protects precious cultural heritage among the people also significant for carrying forward folk tradition technology.

The specific embodiment

The production method of the black sedimentary clay inkstone platform of a kind of black jade may further comprise the steps: the heavy mud airing of Gu that (a) will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done; (b) the heavy mud of the Gu after will drying is put into water vat and was soaked two hours; (c) the heavy mud of the Gu after will soaking stirs into mud; (d) mud is filtered; (e) mud after filtering is carried out kneading and pat, make it be shaped to walk; (f) walk is put into mould and process blank; (g) blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with coal dust; (h) fire-resistant box is put into kiln, the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained the black sedimentary clay inkstone platform of black jade.The said filtration of step (d) is carried out in two steps, and the first step adopts 10000-hole sieve to filter, and the mud after second step will filter is packed into and sling in the cloth bag, filters out moisture wherein.

Take from the heavy mud of Gu in the domestic Hutuohe River in Wutai County, Shanxi Province, fine and glossy and flexibility is arranged, contain ten several mineral materials in the mud; Very careful mud through staying behind 10000-hole sieve filtration and the cloth bag filtration moisture is exactly clear mud; Clear mud is carried out the kneading beating make it be shaped to walk, put into mould again and process the inkstone blank, can require carry out Carving Machining this moment according to art, makes it possess various shape systems; Said coal dust is the coal that is milled to powdery; When firing, the inkstone blank in the fire-resistant box is all buried with coal dust; Temperature in the kiln is controlled between 980 ℃ ~ 1050 ℃ (can select 980 ℃, 990 ℃, 1000 ℃, 1050 ℃); Keep the fire-resistant box that this temperature range will be equipped with blank to fire 72 hours, the quality that just can obtain having black jade black pool is fine and smooth, Fa Mo and do not decrease the sedimentary clay inkstone platform of milli.

Claims

1. the production method of the black sedimentary clay inkstone platform of black jade is characterized in that, may further comprise the steps:

(a) the heavy mud airing of Gu that will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done;

(b) the heavy mud of the Gu after will drying is put into water vat and was soaked two hours;

(c) the heavy mud of the Gu after will soaking stirs into mud;

(d) mud is filtered;

(e) mud after filtering is carried out kneading and pat, make it be shaped to walk;

(f) walk is put into mould and process blank;

(g) blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with coal dust;

(h) fire-resistant box is put into kiln, the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained the black sedimentary clay inkstone platform of black jade.

2. the production method of the black sedimentary clay inkstone platform of black jade as claimed in claim 1 is characterized in that said filtration step carries out in two steps, and the first step adopts 10000-hole sieve to filter, and the mud after second step will filter is packed into and sling in the cloth bag, filters out moisture wherein.