CN102423896A - Method for producing turtledove grey mud inkstone - Google Patents
Method for producing turtledove grey mud inkstone Download PDFInfo
- Publication number
- CN102423896A CN102423896A CN2011103036143A CN201110303614A CN102423896A CN 102423896 A CN102423896 A CN 102423896A CN 2011103036143 A CN2011103036143 A CN 2011103036143A CN 201110303614 A CN201110303614 A CN 201110303614A CN 102423896 A CN102423896 A CN 102423896A
- Authority
- CN
- China
- Prior art keywords
- mud
- inkstone
- blank
- turtledove
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing a turtledove grey mud inkstone, which solves the problems that the mud inkstone production method has been lost for years and the color of the inkstone cannot be controlled manually. The method for producing the turtledove grey mud inkstone comprises the following steps of: airing ancient mud in the Hutuo River in the region of Wutai County, Shanxi Province; soaking the aired ancient mud in a water vat for two hours; stirring the soaked ancient mud to form slurry; filtering the slurry; rubbing and patting the filtered slurry to form a mud pie; putting the mud pie in a mould to produce a blank; putting the blank in a flame-retardance box, burying the blank with powdered coking coal; and putting the flame-retardance box in a kiln, controlling the temperature of the kiln to be between 980 and 1,050 DEG C, burning for 72 hours to obtain the turtledove grey mud inkstone. The production method inherits the tradition and makes innovations, and restores the mud inkstone production process which has been lost for a long time; and the produced mud inkstone has excellent texture, nice color and shape.
Description
Technical field
The present invention relates to a kind of production method of sedimentary clay inkstone platform, be specially a kind of production method of ringdove ash sedimentary clay inkstone platform.
Background technology
Sedimentary clay inkstone is one of China's four major famous inkstones, it and Duanxi inkstone, inhales inkstone, the Taohe River inkstone and is called China's " four major famous inkstones ".Sedimentary clay inkstone is opened the meticulous beginning of China's inkstone circle.Its predecessor is the Tao Yan in ancient times.The enlightenment that ancients are produced by brick, eaves tile is manufactured meticulously in conjunction with Tao Yanzai, satisfies the step distillation and is sedimentary clay inkstone.This inkstone starts from the Tang Dynasty, and the Song dynasty is developed into the peak, and progressively decline after this is lost at last.The characteristics of sedimentary clay inkstone are that matter is hard fine and smooth, and hard water storage does not dry up and not dry, carefully and not sliding, and going through trembles with fear does not ice, and send out China ink benefit milli, and are deep or light suitable, gentle calmness, and there is multiple different colours in the refined U.S.A of color and luster.Say in " study four spectrums ": " after the Song dynasty, the exploitation natural stone is chiseled inkstone, type sedimentary clay inkstone, also name ' sedimentary clay inkstone '.Its category has ' yellow eel is yellow ', ' crust green ', ' mineral granule ', ' rose violet ', ' bean cotyledon sand ' etc. "; The expert on historical relics points out: " because of the weather of the source of silt and manufacturing process, fire the color that the difference of the duration and degree of heating is had nothing in common with each other." it seems that ancients are not is to have a mind to fire shades of colour, but objective formation in the sintering procedure, the formation of color has contingency, non-artificial can control.
Sintering procedure that the sedimentary clay inkstone platform is concrete and technology, then just lost to the Qing Dynasty.The ancient sedimentary clay inkstone of finding today is very rare, and top grade difficulty is especially asked, and traces it to its cause, probably with regard to being that manufacture craft is complicated and output is very low.
Summary of the invention
The present invention is directed to the problem that sedimentary clay inkstone platform production method is lost and the inkstone color can't artificially be controlled, a kind of production method of ringdove ash sedimentary clay inkstone platform is provided.
The present invention realizes through following steps: a kind of production method of ringdove ash sedimentary clay inkstone platform may further comprise the steps: the heavy mud airing of Gu that will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done; The heavy mud of Gu after drying is put into water vat to be soaked two hours; The heavy mud of Gu after soaking is stirred into mud; Mud is filtered; Mud after filtering is carried out kneading pat, make it be shaped to walk; Walk is put into mould process blank; Blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with ground coking coal; Fire-resistant box is put into kiln, and the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained ringdove ash sedimentary clay inkstone platform.
The present invention holds Gu and innovates, and has recovered the production technology of lost sedimentary clay inkstone platform for a long time, and the sedimentary clay inkstone platform quality of producing is fine and smooth; Solid thick Gu; Shape system is various, and has realized the purpose of artificial control sedimentary clay inkstone platform appearance luster on this basis, and the sedimentary clay inkstone platform shape and color of producing has both.Said production method possesses operability, realizes for those skilled in the art are easy.The present invention follows the example of folk tradition technology; Explore through a large amount of experiments and technology for many years; Successfully realized the suitability for industrialized production of sedimentary clay inkstone platform; The sedimentary clay inkstone platform of being produced has the multiple good characteristic of putting down in writing in the ancient books, and has obtained breakthrough on this basis, has realized the control to sedimentary clay inkstone platform appearance colour.The sedimentary clay inkstone platform that burns out can combine color and shape system, makes it have more artistic effect.The present invention protects precious cultural heritage among the people also significant for carrying forward folk tradition technology.
The specific embodiment
A kind of production method of ringdove ash sedimentary clay inkstone platform may further comprise the steps: the heavy mud airing of Gu that (a) will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done; (b) the heavy mud of the Gu after will drying is put into water vat and was soaked two hours; (c) the heavy mud of the Gu after will soaking stirs into mud; (d) mud is filtered; (e) mud after filtering is carried out kneading and pat, make it be shaped to walk; (f) walk is put into mould and process blank; (g) blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with ground coking coal; (h) fire-resistant box is put into kiln, the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained ringdove ash sedimentary clay inkstone platform.The said filtration of step (d) is carried out in two steps, and the first step adopts 10000-hole sieve to filter, and the mud after second step will filter is packed into and sling in the cloth bag, filters out moisture wherein.
Take from the heavy mud of Gu in the domestic Hutuohe River in Wutai County, Shanxi Province, fine and glossy and flexibility is arranged, contain ten several mineral materials in the mud; Very careful mud through staying behind 10000-hole sieve filtration and the cloth bag filtration moisture is exactly clear mud; Clear mud is carried out the kneading beating make it be shaped to walk, put into mould again and process the inkstone blank, can require carry out Carving Machining this moment according to art, makes it possess various shape systems; Said coking coal powder is powdered coking coal; When firing, the inkstone blank in the fire-resistant box is all buried with coking coal powder; Temperature in the kiln is controlled between 980 ℃ ~ 1050 ℃ (can select 980 ℃, 990 ℃, 1000 ℃, 1050 ℃); Keep the fire-resistant box that this temperature range will be equipped with blank to fire 72 hours, the quality that just can obtain having ringdove ash color and luster is fine and smooth, Fa Mo and do not decrease the sedimentary clay inkstone platform of milli.
Claims (2)
1. the production method of a ringdove ash sedimentary clay inkstone platform is characterized in that, may further comprise the steps:
(a) the heavy mud airing of Gu that will take from the domestic Hutuohe River in Wutai County, Shanxi Province is done;
(b) the heavy mud of the Gu after will drying is put into water vat and was soaked two hours;
(c) the heavy mud of the Gu after will soaking stirs into mud;
(d) mud is filtered;
(e) mud after filtering is carried out kneading and pat, make it be shaped to walk;
(f) walk is put into mould and process blank;
(g) blank is put into fire-resistant box, the blank in the fire-resistant box is all buried with ground coking coal;
(h) fire-resistant box is put into kiln, the kiln temperature control was fired 72 hours at 980 ℃ ~ 1050 ℃, obtained ringdove ash sedimentary clay inkstone platform.
2. the production method of ringdove as claimed in claim 1 ash sedimentary clay inkstone platform is characterized in that said filtration step carries out in two steps, and the first step adopts 10000-hole sieve to filter, and the mud after second step will filter is packed into and sling in the cloth bag, filters out moisture wherein.