CN102410407A - Light-resisting and oxygen-resisting plastic piping material - Google Patents
Light-resisting and oxygen-resisting plastic piping material Download PDFInfo
- Publication number
- CN102410407A CN102410407A CN2011102231045A CN201110223104A CN102410407A CN 102410407 A CN102410407 A CN 102410407A CN 2011102231045 A CN2011102231045 A CN 2011102231045A CN 201110223104 A CN201110223104 A CN 201110223104A CN 102410407 A CN102410407 A CN 102410407A
- Authority
- CN
- China
- Prior art keywords
- resisting
- oxygen
- resistance
- light
- plastic tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light-resisting and oxygen-resisting plastic piping material, which comprises three layers, wherein both the outer layer and the inner layer are polypropylene random copolymer layers; and the middle layer is a light-resisting and oxygen-resisting layer. The light-resisting and oxygen-resisting plastic piping material is characterized in that: the light-resisting and oxygen-resisting layer comprises the following components in part by weight: 100 to 200 parts of polypropylene random copolymer resin, 5 to 20 parts of light-resisting material, 10 to 50 parts of oxygen-resisting material, 0.5 to 3 parts of color masterbatch, 0.1 to 3 parts of antioxidant and 0.1 to 2 parts of ultraviolet light stabilizer. A light-resisting and oxygen-resisting effect is achieved by adding the light-resisting and oxygen-resisting layer positioned in the middle of a pipe wall, so the application range of the piping material is widened, and the service life of the piping material is prolonged.
Description
Technical field
The present invention relates to a kind of plastic tube, particularly relate to a kind of resistance photoresistance oxygen plastic tube with three-decker.
Background technique
Along with the progress of society and improving constantly of human living standard, PA tube is because have good mechanical performance and sanitation performance, replaces metal tube gradually and serves masses.Because the transmission of light of polypropylene material own, oxygen permeability are all good, after receiving solar radiation and tube wall oxygen flow,, thereby influence water quality even blocking pipe tube wall inboard breed bacteria and algae easily, make troubles to people's life.
Summary of the invention
The object of the invention is exactly the defective that exists to existing technology, provides that a kind of processability is good, mechanical strength is high, the resistance photosensitiveness is strong, the good polypropylene stable state composite pipe of resistance oxygen property.
The present invention is achieved in that
A kind of resistance photoresistance oxygen plastic tube comprises three-decker, and outer and internal layer is the atactic copolymerized polypropene material layer, and the mesosphere is resistance light, oxidation prevention material layer.
Wherein, the mesosphere wall thickness is 20%~30% of a pipe wall thickness, and the internal layer wall thickness is not more than outer wall thickness.
Wherein the atactic copolymerized polypropene material is the P-R material.
Resistance light, oxidation prevention material layer comprise following component: atactic copolymerized polypropene resin: 100~200 weight portions; Resistance luminescent material 5~20 weight portions; Oxygen barrier material 10~50 weight portions; Look female 0.5~3 weight portion; Antioxidant 0.1~3 weight portion; Ultraviolet light stabilizers 0.1~2 weight portion.
Scheme further is: said resistance luminescent material is one or more mixing in titanium dioxide, cerium oxide, the zirconium oxide.
Scheme further is: said oxygen barrier material is one or more the combination in PVDC (polyvinylidene chloride), EVOH (ethylene/vinyl alcohol copolymer), PEN (PEN), MXD6 (polyamide) or derivatives thereof.
Said look mother is a blue masterbatch.
Said antioxidant is antioxidant 168 or antioxidant 1010.
Said ultraviolet light stabilizers is UV-531.
This resistance photoresistance oxygen plastic tube can once be directly formed to tubing through coextrusion technology, processes very convenient.
Specifically can be with reference to following steps:
(1) according to the accurate raw materials weighing of prescription;
(2) all raw material is all needed oven dry processing in dryer before processing;
(3) raw material after will drying are discharged into homogenizer and stir mixing time 5 minutes;
(4) batch mixing is discharged in twin-screw or the single screw extrusion machine hopper through feeder, each section of extruder temperature is provided with sees shown in the table 1:
Each section of table 1 twin-screw temperature/℃
Annotate: feeding: 7Hz; Engine speed: 240r/min.
(5) vacuum sizing: the tubing of extruding through twin-screw passes through the calibration sleeve sizing, and gets into the vacuum cooling tank, and water temperature is divided two sections, and first section water temperature is at 65~75 ℃, and second section water temperature is at 20~25 ℃, and degree of vacuum remains on-0.2MPa;
(6) coding is printed;
(7) fixed length cutting is batched;
(8) pack after the assay was approved.
Through on the basis of conventional polypropylene pipe, be positioned at tube wall middle resistance light, oxidation prevention material layer through increase, reach resistance light, resistance oxygen effect, using scope and the working life that can improve tubing.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is elaborated.
Shown in accompanying drawing 1, a kind of resistance photoresistance oxygen plastic tube comprises three-decker; Skin 1 is the atactic copolymerized polypropene material layer with internal layer 3, and mesosphere 2 is resistance light, oxidation prevention material layer, wherein; The mesosphere wall thickness is 20%~30% of a pipe wall thickness, and the internal layer wall thickness is not more than outer wall thickness.
Because an emphasis of the present invention provides the concrete prescription in mesosphere, therefore, specify the prescription and the resistance photoresistance oxygen effect thereof in mesosphere through several embodiments.
Embodiment one
The prescription in mesosphere is:
Atactic copolymerized polypropene (PP-R) resin: 150 weight portions;
Anatase thpe white powder (TiO2) 15 weight portions;
Ethylene/vinyl alcohol copolymer (EVOH) 20 weight portions;
Blue masterbatch 1 weight portion;
Antioxidant 168 0.2 weight portions;
Ultraviolet light stabilizers UV-531 0.2 weight portion.
Embodiment two
The prescription in mesosphere is:
Atactic copolymerized polypropene (PP-R) resin: 150 weight portions;
Zircon (ZrO2) 20 weight portions;
Polyvinylidene chloride (PVDC) 20 weight portions;
Blue masterbatch 1 weight portion;
Antioxidant (1010) 0.2 weight portions;
Ultraviolet light stabilizers (UV-531) 0.3 weight portion.
Embodiment three
The prescription in mesosphere is:
Atactic copolymerized polypropene (PP-R) resin: 150 weight portions;
Cerium oxide (CeO2) 20 weight portions;
PEN (PEN) 15 weight portions;
Blue masterbatch 1.2 weight portions;
Antioxidant (1010) 0.2 weight portions;
Ultraviolet light stabilizers (UV-531) 0.3 weight portion.
In addition, the random copolymerization polypropylene pipe that does not add resistance light, oxidation prevention material layer is routine as a comparison, and the performance measurement of being correlated with obtains mensuration result as shown in the table.
The steam transit dose: at a certain temperature, make the both sides of sample form a specific psychrometric difference, water vapour sees through sample and gets into a dry side, measures over time through measuring the moisture vapor transmission cup loss of weight, thereby obtains the moisture-vapor transmission and the moisture permeable coefficient of sample.
Resistance photosensitiveness: with a kind of photosensitive film (ASA sensitivity: 3200) overlay on the sample to be tested, then with 10
5The light of reining in passes sample irradiation to be tested.By following grade, evaluate the resistance photosensitiveness of sample to be tested with the sensitivity of photosensitive film:
The embodiment's performance parameter that records is following:
Performance | Embodiment one | Embodiment two | Embodiment three | Comparative Examples |
Resistance photosensitiveness (grade) | 5 | 5 | 4 | 3 |
Tensile strength (MPa) | 89.4 | 82.8 | 76 | 79.5 |
Stretch modulus (MPa) | 1642 | 1475 | 1777 | 1670 |
The steam transit dose | 0.52 | 0.57 | 0.61 | 2.3 |
Claims (7)
1. one kind is hindered photoresistance oxygen plastic tube; Comprise three-decker; Outer and internal layer is the atactic copolymerized polypropene material layer, and the mesosphere is resistance light, oxidation prevention material layer, and it is characterized in that: said resistance light, oxidation prevention material layer comprise following component: the atactic copolymerized polypropene resin: 100~200 weight portions; Resistance luminescent material 5~20 weight portions; Oxygen barrier material 10~50 weight portions; Look female 0.5~3 weight portion; Antioxidant 0.1~3 weight portion; Ultraviolet light stabilizers 0.1~2 weight portion.
2. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: said resistance luminescent material is one or more mixing in titanium dioxide, cerium oxide, the zirconium oxide.
3. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: said oxygen barrier material is one or more the combination among PVDC, EVOH, PEN, the MXD6.
4. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: said look female is blue masterbatch.
5. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: said antioxidant is antioxidant 168 or antioxidant 1010.
6. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: said ultraviolet light stabilizers is UV-531.
7. according to the said resistance photoresistance of claim 1 oxygen plastic tube, it is characterized in that: the mesosphere wall thickness is 20%~30% of a pipe wall thickness, and the internal layer wall thickness is not more than outer wall thickness.