CN102408641A - Molding process of plastic sectional material - Google Patents
Molding process of plastic sectional material Download PDFInfo
- Publication number
- CN102408641A CN102408641A CN2011102228678A CN201110222867A CN102408641A CN 102408641 A CN102408641 A CN 102408641A CN 2011102228678 A CN2011102228678 A CN 2011102228678A CN 201110222867 A CN201110222867 A CN 201110222867A CN 102408641 A CN102408641 A CN 102408641A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- molding
- stirring
- granulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a molding process of a plastic sectional material. The process comprises the following steps: 1) preparing materials: 100 parts of polystyrene resin, 4-5 parts of thermal stabilizing agent, 5-10 parts of modifier, 0.5 part of triphenyl polyphosphate, 7-9 parts of titanium white, 0.5-1 part of fine lubricating agent and 10-30 parts of inorganic filling material; 2) mixing and stirring: putting all the raw materials in a blender and stirring at the temperature of 100-120 DEG C; 3) pelleting: repeatedly smelting the mixed material at the temperature below a thermal decomposition point; and 4) molding: molding in a mould at the temperature of about 180-200 DEG C. The plastic sectional material manufactured by applying the process provided by the invention has high hard density, strong impact resistance, good toughness, bright surface like a mirror, natural and elegant lines, fastness, no deading and no ageing.
Description
Technical field
The present invention relates to a kind of polymeric material field, specifically is a kind of moulding process of plastic material.
Background technology
Plastic extruding forming process allocation material of the prior art, stirring, granulation, moulding.Prescription in the proportioning process is wherein selected resin, softening agent, thermo-stabilizer, lubricant, stopping composition and other auxiliary agents for use.Softening agent is prone to make product in fusion process, to influence its banburying because soft, after the moulding, because of the continuous volatilization of softening agent can impel the product accelerated deterioration.Even if plastic prod takes secondary processing to improve surface smoothness, also can only be the japanning glazing, because the major ingredient of pool lacquer is a resin, contain rare Chinese catalpa agent of volatility extra-heavy again, be easy to fade, delustering.Product color is dull, matt, secondary processing cost is higher, effect is also poor.
Summary of the invention
In order to overcome above-mentioned defective, the present invention provides a kind of moulding process of novel plastic material.
Technical scheme of the present invention is achieved in that a kind of moulding process of plastic material, and step is following:
1) batching: with polystyrene resin is 100 parts, thermo-stabilizer 4-5 part, and properties-correcting agent 5-10 part, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, white titanium pigment 7-9 part is moistened O.5-1 part of smart agent, inorganic fillings 10-30 part;
2) mix stirring: above-mentioned each raw material is dropped in stirrer, and temperature is controlled at 100-120 ℃;
3) granulation: above-mentioned stirring material is put following temperature, melt back then in thermolysis;
4) moulding: in die for molding, temperature is controlled at about 180-200 ℃.
The polystyrene resin that consists of of said step 1) raw material is 100 parts, 4 parts of thermo-stabilizers, and 5 parts of properties-correcting agent, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, 8 parts of white titanium pigments moisten O.5 part of smart agent, 15 parts of inorganic fillings.
In the said step 3) granulation process, the each time of granulation material when ultimate temperature is in 2-4 second.
The invention has the beneficial effects as follows: use the hard density height of plastic material that technology of the present invention is made, strong shock resistance, good toughness, surface-brightening such as mirror, lines are graceful, colour-fast naturally, not delustering, aging.
Embodiment
Below in conjunction with specific embodiment the present invention is further explained.
Embodiment 1
The moulding process step of plastic material is following:
1) batching: with polystyrene resin is 100 parts, 4 parts of thermo-stabilizers, and 5 parts of properties-correcting agent, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, 7 parts of white titanium pigments moisten O.5 part of smart agent, 18 parts of inorganic fillings;
2) mix stirring: above-mentioned each raw material is dropped in stirrer, and temperature is controlled at 100 ℃;
3) granulation: above-mentioned stirring material is put following temperature, melt back then in thermolysis;
4) moulding: in die for molding, temperature is controlled at about 200 ℃.
Embodiment 2
The moulding process step of plastic material is following:
1) batching: with polystyrene resin is 100 parts, 5 parts of thermo-stabilizers, and 10 parts of properties-correcting agent, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, 9 parts of white titanium pigments moisten 1 part of smart agent, 30 parts of inorganic fillings;
2) mix stirring: above-mentioned each raw material is dropped in stirrer, and temperature is controlled at 120 ℃;
3) granulation: above-mentioned stirring material is put following temperature, melt back then in thermolysis;
4) moulding: in die for molding, temperature is controlled at about 180 ℃.
The above; Be merely the preferable embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any technician who is familiar with the present technique field is equal to replacement or change according to technical scheme of the present invention and inventive concept thereof in the technical scope that the present invention discloses, all should be encompassed within protection scope of the present invention.
Claims (3)
1. the moulding process of a plastic material, it is characterized in that: step is following:
1) batching: with polystyrene resin is 100 parts, thermo-stabilizer 4-5 part, and properties-correcting agent 5-10 part, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, white titanium pigment 7-9 part is moistened O.5-1 part of smart agent, inorganic fillings 10-30 part;
2) mix stirring: above-mentioned each raw material is dropped in stirrer, and temperature is controlled at 100-120 ℃;
3) granulation: above-mentioned stirring material is put following temperature, melt back then in thermolysis;
4) moulding: in die for molding, temperature is controlled at about 180-200 ℃.
2. the moulding process of plastic material according to claim 1, it is characterized in that: the polystyrene resin that consists of of said step 1) raw material is 100 parts, 4 parts of thermo-stabilizers; 5 parts of properties-correcting agent, 0.5 part of polyphosphoric acid triphenylmethyl methacrylate, 8 parts of white titanium pigments; Moisten O.5 part of smart agent, 15 parts of inorganic fillings.
3. the moulding process of plastic material according to claim 1 is characterized in that: in the said step 3) granulation process, the each time of granulation material when ultimate temperature is in 2-4 second.