CN102383178A - Stripping solution for vehicle connector electroplated terminal plating - Google Patents
Stripping solution for vehicle connector electroplated terminal plating Download PDFInfo
- Publication number
- CN102383178A CN102383178A CN2011103520485A CN201110352048A CN102383178A CN 102383178 A CN102383178 A CN 102383178A CN 2011103520485 A CN2011103520485 A CN 2011103520485A CN 201110352048 A CN201110352048 A CN 201110352048A CN 102383178 A CN102383178 A CN 102383178A
- Authority
- CN
- China
- Prior art keywords
- added
- sulfuric acid
- sodium acetate
- ammonium fluoride
- tta
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a stripping solution for vehicle connector electroplated terminal plating, and the stripping solution mainly comprises the following components: 120-170 ml of sulfuric acid with a concentration mass fraction of 98%, 70-100 ml of hydrogen peroxide with a concentration mass fraction of 30%, 90-100 g of ammonium fluoride, 30-50 g of sodium acetate, 5-8 g of corrosion inhibitors, 0.2-0.5 g of polyvinyl alcohol with a molecular weight of 6000-10000; sulfuric acid is added slowly into 0.5 L water; polyvinyl alcohol is added, stirred and dissolved; the solution is allowed to stand and is cooled; when the temperature is below 30 DEG C, ammonium fluoride, sodium acetate, and the corrosion inhibitor are added, stirred and dissolved; hydrogen peroxide is added; and finally water is added to obtain a volume of 1 L. With the combined effect of sulfuric acid and hydrogen peroxide, an oxidation-reduction reaction is performed with metallic tin; an oxide layer is dissolvd by ammonium fluoride and sodium acetate, which facilitates further reaction of the tin layer; the organic polymer substance can allow the tin layer reaction to perform uniformly, allow a stripping layer to be bright; and the corrosion inhibitor can ensure that over-corrosion of a substrate copper layer does not occur.
Description
Technical field
The present invention relates to a kind of decoating liquid that is used for automobile connector assembly plated terminals coating.
Background technology
When automobile connector assembly plated terminals and copper strips, eleetrotinplate and tin alloy coat are more.In electroplating process, can produce bad coating, at this moment just need electroplate again then with bad decoating under the situation that does not injure base material.
Summary of the invention
The technical problem that the present invention will solve provides a kind of decoating liquid that is used for automobile connector assembly plated terminals coating.
Technical scheme of the present invention is: a kind of decoating liquid that is used for automobile connector assembly plated terminals coating, and decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is sulfuric acid 120 ~ 170ml of 98%, the concentration massfraction is 30% ydrogen peroxide 50 70 ~ 100 ml; Neutral ammonium fluoride 90 ~ 100g, sodium acetate 30 ~ 50 g, inhibiter are 5 ~ 8 g; Molecular weight is 6000 ~ 10000 Z 150PH 0.2 ~ 0.5 g, and sulfuric acid is slowly added in the 0.5L water, adds Z 150PH; Leave standstill cooling after the stirring and dissolving, temperature is lower than 30 ℃, and Neutral ammonium fluoride, sodium acetate and inhibiter are added; Add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
2. the decoating liquid that is used for automobile connector assembly plated terminals coating according to claim 1; It is characterized in that: said inhibiter is the mixture of benzotriazole BTA and TTA TTA, and the mass ratio of benzotriazole BTA and TTA TTA is 1 ~ 2:9.
The invention has the beneficial effects as follows: decoating liquid is for being master's acidic oxidation property liquid with sulfuric acid and ydrogen peroxide 50, and is minimum to copper matrix corrosion property, steps back the matrix surface light.Sulfuric acid and ydrogen peroxide 50 acting in conjunction, with metallic tin generation redox reaction, Neutral ammonium fluoride and sodium acetate dissolve zone of oxidation; Be beneficial to the further reaction of tin layer; The organic polymer material can make the reaction of tin layer evenly carry out, and makes strip aspect light, and inhibiter guarantees that excessive erosion does not take place matrix copper layer.Decoating liquid can spray bad product, immersion treatment, generally can the stripping of tin and tin alloy coat is clean in one minute, and it is bigger that this prescription can make every liter of product move back the tin amount, and the decoating liquid preparation is simple, easily operation.
Embodiment
Embodiment 1
A kind of decoating liquid that is used for automobile connector assembly plated terminals coating, decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is 98% sulfuric acid 120 ml, the concentration massfraction is 30% ydrogen peroxide 50 70 ml; Neutral ammonium fluoride 90 g, sodium acetate 30 g, inhibiter are 5 ~ 8 g; Inhibiter is the mixture of benzotriazole BTA and TTA TTA, benzotriazole BTA 0.5 g, TTA TTA 4.5 g; Molecular weight is 6000 ~ 10000 Z 150PH 0.2 g, and sulfuric acid is slowly added in the 0.5L water, adds Z 150PH; Leave standstill cooling after the stirring and dissolving, temperature is lower than 30 ℃, and Neutral ammonium fluoride, sodium acetate and inhibiter are added; Add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
Embodiment 2
A kind of decoating liquid that is used for automobile connector assembly plated terminals coating, decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is 98% sulfuric acid 170ml, the concentration massfraction is 30% ydrogen peroxide 50 100 ml; Neutral ammonium fluoride 100g, sodium acetate 50 g, inhibiter are that inhibiter is the mixture of benzotriazole BTA and TTA TTA; Benzotriazole BTA 0.8g, TTA TTA7.2 g, molecular weight are 6000 ~ 10000 Z 150PH 0.5 g; Sulfuric acid is slowly added in the 0.5L water, add Z 150PH, leave standstill cooling after the stirring and dissolving; Temperature is lower than 30 ℃; Neutral ammonium fluoride, sodium acetate and inhibiter are added, add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
Embodiment 3
A kind of decoating liquid that is used for automobile connector assembly plated terminals coating, decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is 98% sulfuric acid 150ml, the concentration massfraction is 30% ydrogen peroxide 50 80 ml; Neutral ammonium fluoride 95g, sodium acetate 40 g, inhibiter are the mixture of benzotriazole BTA and TTA TTA; Benzotriazole BTA0.6 g, TTA TTA 6.6 g, molecular weight are 6000 ~ 10000 Z 150PH 0.4 g; Sulfuric acid is slowly added in the 0.5L water, add Z 150PH, leave standstill cooling after the stirring and dissolving; Temperature is lower than 30 ℃; Neutral ammonium fluoride, sodium acetate and inhibiter are added, add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
Embodiment 4
A kind of decoating liquid that is used for automobile connector assembly plated terminals coating, decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is sulfuric acid 120 ~ 170ml of 98%, the concentration massfraction is 30% ydrogen peroxide 50 70 ~ 100 ml; Neutral ammonium fluoride 90 ~ 100g, sodium acetate 30 ~ 50 g, inhibiter are 5 ~ 8 g; Inhibiter is the mixture of benzotriazole BTA and TTA TTA, and the mass ratio of benzotriazole BTA and TTA TTA is 1 ~ 2:9, and molecular weight is 6000 ~ 10000 Z 150PH 0.2 ~ 0.5 g; Sulfuric acid is slowly added in the 0.5L water, add Z 150PH, leave standstill cooling after the stirring and dissolving; Temperature is lower than 30 ℃; Neutral ammonium fluoride, sodium acetate and inhibiter are added, add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
Claims (2)
1. decoating liquid that is used for automobile connector assembly plated terminals coating, it is characterized in that: decoating liquid mainly contains following one-tenth and is grouped into: the concentration massfraction is sulfuric acid 120 ~ 170ml of 98%, the concentration massfraction is 30% ydrogen peroxide 50 70 ~ 100 ml; Neutral ammonium fluoride 90 ~ 100g, sodium acetate 30 ~ 50 g, inhibiter are 5 ~ 8 g; Molecular weight is 6000 ~ 10000 Z 150PH 0.2 ~ 0.5 g, and sulfuric acid is slowly added in the 0.5L water, adds Z 150PH; Leave standstill cooling after the stirring and dissolving, temperature is lower than 30 ℃, and Neutral ammonium fluoride, sodium acetate and inhibiter are added; Add ydrogen peroxide 50 after the stirring and dissolving, add water at last and be settled to 1L.
2. the decoating liquid that is used for automobile connector assembly plated terminals coating according to claim 1; It is characterized in that: said inhibiter is the mixture of benzotriazole BTA and TTA TTA, and the mass ratio of benzotriazole BTA and TTA TTA is 1 ~ 2:9.