CN102382479A - Star-shaped modified emulsified asphalt and preparation method of same - Google Patents
Star-shaped modified emulsified asphalt and preparation method of same Download PDFInfo
- Publication number
- CN102382479A CN102382479A CN2010102696758A CN201010269675A CN102382479A CN 102382479 A CN102382479 A CN 102382479A CN 2010102696758 A CN2010102696758 A CN 2010102696758A CN 201010269675 A CN201010269675 A CN 201010269675A CN 102382479 A CN102382479 A CN 102382479A
- Authority
- CN
- China
- Prior art keywords
- star
- asphalt
- modified emulsifying
- mixing
- emulsifying asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to star-shaped modified emulsified asphalt and a preparation method of the star-shaped modified emulsified asphalt in the field of a building technology. The star-shaped modified emulsified asphalt contains the components in percent by weight: 3-5% of arene, 3-8% of modifier, 2-5% of emulsifier, 1-3% of reinforcer, 3-10% of solubilizer, 20-50% of water and 30-60% of heavy-traffic asphalt. The preparation method includes the steps: firstly, conducting the following operations as follows: A. stirring the arene with the solubilizer, then adding the modifier and conducting stirring; B. adding the emulsifier and the reinforcer in water and then conducting stirring; C. heating the heavy-traffic asphalt; and secondly, mixing the products obtained from the A, B and C operations in the step 1 simultaneously, and then enabling the mixture to pass through a colloid mill, thus obtaining the star-shaped modified emulsified asphalt. The property of the star-shaped modified emulsified asphalt far exceeds the national standard, the application range of the emulsified asphalt is expanded greatly and the using effect of the emulsified asphalt is improved.
Description
Technical field
The present invention relates to a kind of emulsified bitumen of technical field of buildings, be specifically related to a kind of star-like modified emulsifying asphalt and preparation method thereof.
Background technology
Along with the development of construction work, the mileage number of highway in China increases greatly.Highway pavement adopts pitch or cement as the road surface gelatinous material in a large number, is connected relatively more difficult between the brea bed or between brea bed and the cement layer.Modified emulsifying asphalt can be widely used in the making and routine servicing engineering of advanced road; Modified emulsifying asphalt is used to connect brea bed or connects brea bed and cement layer can be obtained effect preferably; But the connection effect of modified emulsifying asphalt is desirable not enough in the prior art, is further improved.
Summary of the invention
First purpose of the present invention is to provide a kind of star-like modified emulsifying asphalt, and its component and weight percentage are: aromatic hydrocarbons 3-5%, properties-correcting agent 3-8%, emulsifying agent 2-5%, toughener 1-3%, solubility promoter 3-10%, water 20-50%, heavy traffic paving asphalt 30-60%.
Preferably, said aromatic hydrocarbons is the naphthenic petroleum hydrocarbon.
Preferably, said properties-correcting agent is one or more the mixing in the styrene-butadiene block copolymer.
Preferably, said emulsifying agent is one or more the mixing in the polyamines class tensio-active agent.
Preferably, said emulsifying agent is one or more the mixing in the following combination: 12 tertiary amines, 14 tertiary amines, 16 tertiary amines, 18 tertiary amines and dodecyl dimethyl tertiary amine.
Preferably, said toughener is one or more the mixing in the organosulfur based compound.
Preferably, said toughener is one or more the mixing in thioether, the mercaptan.
Preferably, said fusing assistant is ETHYLE ACETATE, white oil or its mixing.
The invention still further relates to the preparation method of aforementioned star-like modified emulsifying asphalt, comprise the steps:
1, operate as follows respectively:
A, aromatic hydrocarbons and fusing assistant are stirred, add properties-correcting agent then, and stir;
B, emulsifying agent, toughener are added in the entry, and stir;
C, heavy traffic paving asphalt is heated;
2, the product with A, B and C operation gained in the step 1 mixes simultaneously, crosses colloidal mill afterwards, promptly gets star-like modified emulsifying asphalt.
In the step 1, said being heated to be is heated to 110-120 ℃.
The present invention has following beneficial effect: the aromatic hydrocarbons that contains in the modified emulsifying asphalt of the present invention makes and can form stable mixture between properties-correcting agent, the heavy traffic paving asphalt that properties-correcting agent group and heavy traffic paving asphalt group are able to bridge joint; The performance of star-like remodeling emulsified bitumen of the present invention is considerably beyond national standard, expanded the use range of emulsified bitumen greatly and improved the result of use of emulsified bitumen.
Embodiment
Below in conjunction with specific embodiment, the present invention is described further.Should be understood that following examples only are used to the present invention is described but not are used to limit scope of the present invention.As not having specified otherwise, the per-cent in following examples is weight percentage.
The mechanical means information of using in following examples is following: colloidal mill is the JM-L50 model of Wenzhou, Zhejiang colloidal mill factory; Stirrer is Wujin, Changzhou laboratory stirrer of machine works from all directions; Temperature control system is that TM is used in the laboratory; Metering system is the Shanghai 9903-3 of a precision instrumentation company type;
Heavy traffic paving asphalt in following examples all meets JTG F40-2004 standard-required.
The aromatic hydrocarbons that relates in following examples all meets JTG F40-2004 standard-required.
Embodiment 1
The component of the star-like modified emulsifying asphalt of present embodiment and weight percent are: naphthenic petroleum hydrocarbon 3%, star-shaped sbs (styrene-butadiene block copolymer) 4%, ten two tertiary amine 2%; Mercaptan 2%; ETHYLE ACETATE 2%, water 20%, road is with 70# heavy traffic paving asphalt 67%.
The preparation method of said modified emulsifying asphalt comprises the steps:
1, operate as follows respectively:
A, aromatic hydrocarbons and ETHYLE ACETATE are stirred, add star-shaped sbs then, and stir;
B, 12 tertiary amines, mercaptan are added in the entry, and stir;
C, heavy traffic paving asphalt is heated to 110 ℃;
2, the product with A, B and C operation gained in the step 1 mixes simultaneously, crosses colloidal mill afterwards, promptly gets star-like modified emulsifying asphalt.
Embodiment 2
The component of the star-like modified emulsifying asphalt of present embodiment and weight percent are: naphthenic petroleum hydrocarbon 4%, star-shaped sbs (styrene-butadiene block copolymer) 6%, dodecyl dimethyl tertiary amine 3%; Mercaptan 2%; White oil 2%, water 30%, road is with 70# heavy traffic paving asphalt 53%.
The preparation method of said modified emulsifying asphalt comprises the steps:
1, operate as follows respectively:
A, naphthenic petroleum hydrocarbon and white oil are stirred, add star-shaped sbs then, and stir;
B, dodecyl dimethyl tertiary amine, mercaptan are added in the entry, and stir;
C, heavy traffic paving asphalt is heated to 115 ℃;
2, the product with A, B and C operation gained in the step 1 mixes simultaneously, crosses colloidal mill afterwards, promptly gets star-like modified emulsifying asphalt.
Embodiment 3
The component of the star-like modified emulsifying asphalt of present embodiment and weight percent are: naphthenic petroleum hydrocarbon 4%, and star-shaped sbs (styrene-butadiene block copolymer) 8%, emulsifying agent 4%, thioether 2%, fusing assistant 2%, water 30%, road is with 70# heavy traffic paving asphalt 50%;
Said emulsifying agent is that mixing in 1: 1 gets by 16 tertiary amines and 18 tertiary amines by mass ratio;
Said fusing assistant is that mixing in 1: 2 gets by ETHYLE ACETATE and white oil by mass ratio.
The preparation method of said modified emulsifying asphalt comprises the steps:
1, operate as follows respectively:
A, naphthenic petroleum hydrocarbon and fusing assistant are stirred, add star-shaped sbs then, and stir;
B, emulsifying agent, toughener are added in the entry, and stir;
C, heavy traffic paving asphalt is heated to 120 ℃;
2, the product with A, B and C operation gained in the step 1 mixes simultaneously, crosses colloidal mill afterwards, promptly gets star-like modified emulsifying asphalt.
Embodiment 4
Test detects; By the People's Republic of China's industry standard---T0605-1993, T0606-2000, T0662-2000, T0616-1993 standard among highway engineering pitch and the asphalt experiment rules JTJ052-2000 detect; Detected result is seen table 1; Can know that by table 1 performance of star-like remodeling emulsified bitumen of the present invention is considerably beyond national standard, expand the use range of emulsified bitumen greatly and improved the result of use of emulsified bitumen.
Table 1
Test subject | 5 ℃ of ductilities | Softening temperature | Recovery of elasticity | Adhesivity |
Embodiment 1 | 34 centimetres | 80℃ | 85% | 5 grades |
Embodiment 2 | 38 centimetres | 82℃ | 88% | 5 grades |
Embodiment 3 | 45 centimetres | 86℃ | 90% | 5 grades |
Claims (10)
1. a star-like modified emulsifying asphalt is characterized in that, its component and weight percentage are: aromatic hydrocarbons 3-5%, properties-correcting agent 3-8%, emulsifying agent 2-5%, toughener 1-3%, solubility promoter 3-10%, water 20-50%, heavy traffic paving asphalt 30-60%.
2. star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, said aromatic hydrocarbons is the naphthenic petroleum hydrocarbon.
3. star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, said properties-correcting agent is one or more the mixing in the styrene-butadiene block copolymer.
4. star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, said emulsifying agent is one or more the mixing in the polyamines class tensio-active agent.
5. star-like modified emulsifying asphalt as claimed in claim 4 is characterized in that, said emulsifying agent is one or more the mixing in the following combination: 12 tertiary amines, 14 tertiary amines, 16 tertiary amines, 18 tertiary amines and dodecyl dimethyl tertiary amine.
6. star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, said toughener is one or more the mixing in the organosulfur based compound.
7. star-like modified emulsifying asphalt as claimed in claim 6 is characterized in that, said toughener is one or more the mixing in thioether, the mercaptan.
8. star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, said fusing assistant is ETHYLE ACETATE, white oil or its mixing.
9. a method for preparing star-like modified emulsifying asphalt as claimed in claim 1 is characterized in that, comprises the steps:
1, operate as follows respectively:
A, aromatic hydrocarbons and fusing assistant are stirred, add properties-correcting agent then, and stir;
B, emulsifying agent, toughener are added in the entry, and stir;
C, heavy traffic paving asphalt is heated;
2, the product with A, B and C operation gained in the step 1 mixes simultaneously, crosses colloidal mill afterwards, promptly gets star-like modified emulsifying asphalt.
10. preparation method as claimed in claim 9 is characterized in that, in the step 1, said being heated to be is heated to 110-120 ℃.