CN102371472B - A kind of manufacturing process of copper word - Google Patents
A kind of manufacturing process of copper word Download PDFInfo
- Publication number
- CN102371472B CN102371472B CN201110255330.1A CN201110255330A CN102371472B CN 102371472 B CN102371472 B CN 102371472B CN 201110255330 A CN201110255330 A CN 201110255330A CN 102371472 B CN102371472 B CN 102371472B
- Authority
- CN
- China
- Prior art keywords
- word
- edge strip
- solder
- word edge
- limit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of manufacturing process of copper word, comprise the following steps: (1) plate digital control cuts; (2) sheet material after Numerical control cutting cuts into edge strip by hydraulic plate shears, then cuts into word edge strip; (3) according to the situation designated size of concrete word; (4) size is copied to above word edge strip; (5) the word edge strip fluting of size is indicated; (6) the word edge strip after cross-notching adopts soldering; (7) the word edge strip flatiron after scolding tin; (8) solder acid is smeared with solder acid peg wood to the word edge strip after flatiron; (9) the word edge strip after solder acid process is slotted again; (10) word of solder acid to word edge strip is smeared with in the groove of limit, limit with solder acid peg wood; (11) taking-up solder acid peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn paste tin bar, the face of word edge strip and limit are welded together, last copper word finished product.Working (machining) efficiency of the present invention is high, successful, and speed of welding is fast.
Description
Technical field
The invention belongs to mechanical manufacturing field, particularly a kind of manufacturing process of copper word.
Background technology
Metal word comprises copper word, iron word, stainless steel letters, titanium word etc., beautiful in colour, effect is eye-catching, the change of high temperature resistant, weatherability and not yielding, not fugitive color, rainproof, fire prevention, anti-pyrophorisity.
Metal word was all sticky by glue usually or realized with rivet in the past, glued by glue and show metal word, by rivet, metal riveting is got up to show metal word, these metal words exist fixes the problems such as insecure, and making metal word is at present all first make metal decking and base plate usually, then makes three-dimensional surrounding edge, then weld, last polishing plating, when making panel and base plate, Metal Cutting is with the most use is at present CUT and gas flame cuttiug.
Summary of the invention
Object of the present invention is just to provide a kind of manufacturing process of copper word, effectively improves operating efficiency, practical, and successful, speed of welding is exceedingly fast.
For achieving the above object, the concrete scheme of the inventive method is: by metal in cutting, deform in welding process the word that is shaped.
The manufacturing process realizing described a kind of copper word mainly comprises the following steps:
(1) sheet material is cut by numerical control cutting machine numerical control;
(2) sheet material after Numerical control cutting cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width further, and concrete word edge strip width should be formulated according to the actual conditions of concrete word;
(3) according to the situation designated size of concrete word, i.e. location, word angle;
(4) size is copied to above word edge strip;
(5) indicate the word edge strip fluting of size, make it bend;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear solder acid with solder acid peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin;
(9) the word edge strip after solder acid process is slotted again;
(10) word of solder acid to word edge strip is smeared with in the groove of limit, limit with solder acid peg wood;
(11) taking-up solder acid peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in solder acid, tin bar pasted by solder horn after cleaning, be positioned over again and smeared in the limit groove of solder acid, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
Described solder acid is protochloride zinc (Zncl
2).
In the present invention, described sheet material can be the one in copper coin, bavin copper coin, brass sheet and galvanized iron sheet.
In the present invention, described Numerical control cutting can be the one in Water Cutting, the cutting of diversion and laser cutting.
The beneficial effect that the present invention has: working (machining) efficiency improves ten times, practical, successful, can carry out the welding of various position easily, and speed of welding is fast, and welding material scope is wide.
Detailed description of the invention
For making to have a better understanding and awareness method of the present invention and effect of reaching, in order to preferred embodiment detailed description, be described as follows:
Embodiment 1
(1) copper coin is by numerical control cutting machine Water Cutting;
(2) copper coin of Water Cutting cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width further, and concrete word edge strip width should be formulated according to the actual conditions of concrete word;
(3) according to the situation designated size of concrete word, i.e. location, word angle;
(4) size is copied to above word edge strip;
(5) indicate the word edge strip fluting of size, make it bend;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear protochloride zinc with protochloride zinc peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin;
(9) the word edge strip after the process of protochloride zinc is slotted again;
(10) word of protochloride zinc to word edge strip is smeared with in the groove of limit, limit with protochloride zinc peg wood;
(11) taking-up protochloride zinc peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in protochloride zinc, tin bar pasted by solder horn after cleaning, be positioned over again smear the sub-zinc of superchlorination limit groove in, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
Embodiment 2
(1) bavin copper coin is by the cutting of numerical control cutting machine diversion;
(2) the bavin copper coin after the cutting of diversion cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width further, and concrete word edge strip width should be formulated according to the actual conditions of concrete word;
(3) according to the situation designated size of concrete word, i.e. location, word angle;
(4) size is copied to above word edge strip;
(5) indicate the word edge strip fluting of size, make it bend;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear protochloride zinc with protochloride zinc peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin;
(9) the word edge strip after the process of protochloride zinc is slotted again;
(10) word of protochloride zinc to word edge strip is smeared with in the groove of limit, limit with protochloride zinc peg wood;
(11) taking-up protochloride zinc peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in protochloride zinc, tin bar pasted by solder horn after cleaning, be positioned over again smear the sub-zinc of superchlorination limit groove in, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
Embodiment 3
(1) brass sheet is by numerical control cutting machine laser cutting;
(2) brass sheet after laser cutting cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width further, and concrete word edge strip width should be formulated according to the actual conditions of concrete word;
(3) according to the situation designated size of concrete word, i.e. location, word angle;
(4) size is copied to above word edge strip;
(5) indicate the word edge strip fluting of size, make it bend;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear protochloride zinc with protochloride zinc peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin;
(9) the word edge strip after the process of protochloride zinc is slotted again;
(10) word of protochloride zinc to word edge strip is smeared with in the groove of limit, limit with protochloride zinc peg wood;
(11) taking-up protochloride zinc peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in protochloride zinc, tin bar pasted by solder horn after cleaning, be positioned over again smear the sub-zinc of superchlorination limit groove in, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
Embodiment 4
(1) galvanized iron sheet is by numerical control cutting machine Water Cutting;
(2) galvanized iron sheet after Water Cutting cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width further, and concrete word edge strip width should be formulated according to the actual conditions of concrete word;
(3) according to the situation designated size of concrete word, i.e. location, word angle;
(4) size is copied to above word edge strip;
(5) indicate the word edge strip fluting of size, make it bend;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear protochloride zinc with protochloride zinc peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin;
(9) the word edge strip after the process of protochloride zinc is slotted again;
(10) word of protochloride zinc to word edge strip is smeared with in the groove of limit, limit with protochloride zinc peg wood;
(11) taking-up protochloride zinc peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in protochloride zinc, tin bar pasted by solder horn after cleaning, be positioned over again smear the sub-zinc of superchlorination limit groove in, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
In sum, be only preferred embodiment of the present invention, be not used for limiting scope of the invention process, all equalizations of doing according to the feature described in the claims in the present invention scope and spirit change and modify, and all should be included in right of the present invention.
Claims (3)
1. a manufacturing process for copper word, comprises the following steps, and it is characterized in that:
(1) sheet material is cut by numerical control cutting machine numerical control;
(2) sheet material after Numerical control cutting cuts into edge strip by hydraulic plate shears, then cuts into the word edge strip of respective width;
(3) according to the situation designated size of concrete word;
(4) size is copied to above word edge strip;
(5) the word edge strip fluting of size is indicated;
(6) the word edge strip after cross-notching adopts soldering, gives the word edge strip scolding tin after fluting with tin bar;
(7) the word edge strip flatiron after scolding tin;
(8) smear solder acid with solder acid peg wood to the word edge strip after flatiron, the word edge strip after being evenly put on flatiron wants the place of scolding tin, and wherein solder acid is protochloride zinc Zncl
2;
(9) the word edge strip after solder acid process is slotted again;
(10) word of solder acid to word edge strip is smeared with in the groove of limit, limit with solder acid peg wood;
(11) taking-up solder acid peg wood smear after word edge strip, through the solder horn of coal stove high-temperature heating, solder horn cleans fast in solder acid, tin bar pasted by solder horn after cleaning, be positioned over again and smeared in the limit groove of solder acid, move equably in the groove of limit, the face of word edge strip and limit are welded together, last copper word finished product.
2. the manufacturing process of a kind of copper word as claimed in claim 1, is characterized in that: described sheet material is the one in bavin copper coin, brass sheet.
3. the manufacturing process of a kind of copper word as claimed in claim 1, is characterized in that: described Numerical control cutting is the one in Water Cutting, the cutting of diversion and laser cutting.