CN102358867A - Fragrant foaming candle - Google Patents
Fragrant foaming candle Download PDFInfo
- Publication number
- CN102358867A CN102358867A CN 201110281842 CN201110281842A CN102358867A CN 102358867 A CN102358867 A CN 102358867A CN 201110281842 CN201110281842 CN 201110281842 CN 201110281842 A CN201110281842 A CN 201110281842A CN 102358867 A CN102358867 A CN 102358867A
- Authority
- CN
- China
- Prior art keywords
- foaming
- candle
- wax liquid
- minutes
- liquid paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fragrant foaming candle, which is prepared by the following steps of: (1) heating paraffin at 75-85 DEG C for 18-20 min to obtain liquid paraffin and adding essence into the liquid paraffin; (2) injecting the liquid paraffin from step (1) into a foaming machine and stirring for foaming; (3) cooling the liquid paraffin; (4) continuing stirring for foaming to obtain foaming liquid paraffin; (5) injecting the foaming liquid paraffin into a die or a container, inserting a cotton wick inside and cooling the foaming liquid paraffin for 12-15 min to obtain a solid candle; coating a layer of liquid paraffin with 75-85 DEG C and 1-20mm on the solid candle surface and flattening a liquid paraffin surface; continuing cooling for 12-15 min and demoulding to obtain the fragrant foaming candle. Compared with a same volume foaming candle, the fragrant foaming candle of the invention consumes 50% less paraffin, so as to reduce production costs substantially and save valuable petroleum resource.
Description
Technical field
The present invention relates to a kind of candle, especially a kind of fragrance foaming candle.
Background technology
Common candle in the middle of the prior art is that paraffin is placed on the fusing of heating in the container, and the wax liquid after the fusing is cast in the special mould, and cooling makes it moulding.Same container, the about 950kg/m of candle density after the moulding
3, the density of the foaming candle after the moulding is 500 kg/m
3Common candle with volume is compared with the foaming candle, and the used paraffin of common candle is the nearly twice of foaming candle.
Summary of the invention
The objective of the invention is to overcome the deficiency that exists in the prior art, a kind of fragrance foaming candle is provided, density is low, component is lighter, can reduce production costs significantly, and the while is the petroleum resources of saves valuable also.
According to technical scheme provided by the invention, said fragrance foaming candle, characteristic is to comprise following process step:
(1) paraffin was heated under 75 ~ 85 ℃ temperature condition 18 ~ 20 minutes, obtain wax liquid; In wax liquid, add the essence that is equivalent to wax liquid quality 1 ~ 2%;
(2) the wax liquid that step (1) is obtained injects to stir in the foaming machine and foams, and stirring velocity is 100 ~ 150 rev/mins, and foamed time is 8 ~ 10 minutes;
(3) the wax liquid in the step (2) is cooled to 57 ~ 59 ℃;
(4) the wax liquid that continues step (3) is obtained stirs foaming, and stirring velocity is 1380 ~ 1440 rev/mins, and churning time is 4 ~ 5 minutes, obtains foamed wax liquid;
(5) foamed wax liquid is injected in mould or the container, the middle cotton wick that inserts makes the liquid cooling of spumescence wax but obtain solid-state candle, and be 12 ~ 15 minutes cooling time; Add the lid layer temperature on the surface of solid-state candle and be 75 ~ 85 ℃ wax liquid, the thickness of wax liquid is 1 ~ 2mm, makes the surfacing of wax liquid; Continue cooling after 12 ~ 15 minutes, the demoulding promptly obtains described fragrance foaming candle.
The density of said fragrance foaming candle is 490 ~ 500 kg/m
3
The present invention compares paraffin that the foaming candle with volume expends and will practice thrift closely 50%, can reduce production costs significantly, simultaneously the also petroleum resources of saves valuable.
Embodiment
Below in conjunction with specific embodiment the present invention is described further.
Embodiment one: a kind of fragrance foaming candle comprises following process step:
(1) paraffin was heated under 75 ℃ temperature condition 18 minutes, obtain wax liquid; In wax liquid, add the essence that is equivalent to wax liquid quality 1%;
(2) the wax liquid that step (1) is obtained injects to stir in the foaming machine and foams, and stirring velocity is 100 rev/mins, and be 8 minutes cooling time;
(3) the wax liquid in the step (2) is cooled to 57 ℃;
(4) the wax liquid that continues step (3) is obtained stirs foaming, and stirring velocity is 1380 rev/mins, and churning time is 4 minutes, obtains foamed wax liquid;
(5) foamed wax liquid is injected in mould or the container, the middle cotton wick that inserts makes the liquid cooling of spumescence wax but obtain solid-state candle, and be 12 minutes cooling time; Add the lid layer temperature on the surface of solid-state candle and be 75 ℃ wax liquid, the thickness of wax liquid is 1mm, makes the surfacing of wax liquid; Continue cooling after 12 minutes, the demoulding promptly obtains described fragrance foaming candle, and the density of said fragrance foaming candle is 490 kg/m
3
Embodiment two: a kind of fragrance foaming candle comprises following process step:
(1) paraffin was heated under 85 ℃ temperature condition 20 minutes, obtain wax liquid; In wax liquid, add the essence that is equivalent to wax liquid quality 2%;
(2) the wax liquid that step (1) is obtained injects to stir in the foaming machine and foams, and stirring velocity is 150 rev/mins, and be 10 minutes cooling time;
(3) the wax liquid in the step (2) is cooled to 59 ℃;
(4) the wax liquid that continues step (3) is obtained stirs foaming, and stirring velocity is 1440 rev/mins, and churning time is 5 minutes, obtains foamed wax liquid;
(5) foamed wax liquid is injected in mould or the container, the middle cotton wick that inserts makes the liquid cooling of spumescence wax but obtain solid-state candle, and be 15 minutes cooling time; Add the lid layer temperature on the surface of solid-state candle and be 85 ℃ wax liquid, the thickness of wax liquid is 2mm, makes the surfacing of wax liquid; Continue cooling after 15 minutes, the demoulding promptly obtains described fragrance foaming candle, and the density of said fragrance foaming candle is 500 kg/m
3
Embodiment three: a kind of fragrance foaming candle comprises following process step:
(1) paraffin was heated under 80 ℃ temperature condition 19 minutes, obtain wax liquid; In wax liquid, add the essence that is equivalent to wax liquid quality 1.5%;
(2) the wax liquid that step (1) is obtained injects to stir in the foaming machine and foams, and stirring velocity is 120 rev/mins, and be 9 minutes cooling time;
(3) the wax liquid in the step (2) is cooled to 58 ℃;
(4) the wax liquid that continues step (3) is obtained stirs foaming, and stirring velocity is 1400 rev/mins, and churning time is 4.5 minutes, obtains foamed wax liquid;
(5) foamed wax liquid is injected in mould or the container, the middle cotton wick that inserts makes the liquid cooling of spumescence wax but obtain solid-state candle, and be 13 minutes cooling time; Add the lid layer temperature on the surface of solid-state candle and be 80 ℃ wax liquid, the thickness of wax liquid is 1.5mm, makes the surfacing of wax liquid; Continue cooling after 13 minutes, the demoulding promptly obtains described fragrance foaming candle, and the density of said fragrance foaming candle is 495 kg/m
3
Claims (2)
1. a fragrance foaming candle is characterized in that, comprises following process step:
(1) paraffin was heated under 75 ~ 85 ℃ temperature condition 18 ~ 20 minutes, obtain wax liquid; In wax liquid, add the essence that is equivalent to wax liquid quality 1 ~ 2%;
(2) the wax liquid that step (1) is obtained injects to stir in the foaming machine and foams, and stirring velocity is 100 ~ 150 rev/mins, and be 8 ~ 10 minutes cooling time;
(3) the wax liquid in the step (2) is cooled to 57 ~ 59 ℃;
(4) the wax liquid that continues step (3) is obtained stirs foaming, and stirring velocity is 1380 ~ 1440 rev/mins, and churning time is 4 ~ 5 minutes, obtains foamed wax liquid;
(5) foamed wax liquid is injected in mould or the container, the middle cotton wick that inserts makes the liquid cooling of spumescence wax but obtain solid-state candle, and be 12 ~ 15 minutes cooling time; Add the lid layer temperature on the surface of solid-state candle and be 75 ~ 85 ℃ wax liquid, the thickness of wax liquid is 1 ~ 2mm, makes the surfacing of wax liquid; Continue cooling after 12 ~ 15 minutes, the demoulding promptly obtains described fragrance foaming candle.
2. fragrance foaming candle as claimed in claim 1 is characterized in that: the density of said fragrance foaming candle is 490 ~ 500 kg/m
3