CN1023572C - Compound spheroidizing inoculant - Google Patents
Compound spheroidizing inoculant Download PDFInfo
- Publication number
- CN1023572C CN1023572C CN 92108915 CN92108915A CN1023572C CN 1023572 C CN1023572 C CN 1023572C CN 92108915 CN92108915 CN 92108915 CN 92108915 A CN92108915 A CN 92108915A CN 1023572 C CN1023572 C CN 1023572C
- Authority
- CN
- China
- Prior art keywords
- spheroidizing
- inoculant
- alloy
- compound
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a composite spheroidizing modifier which is especially suitable for producing as-cast ferritic spheroidal graphite cast iron. The composite spheroidizing modifier is prepared from an RE-Si-Mg alloy and non-metal materials, such as graphite, CaF2, etc., by physical and mechanical mixing according to certain particle distribution and compounding ratio. The present invention integrates the functions of spheroidizing, desulphurization, inoculation and graphitizing deterioration, and has the advantages of stable spheroidizing reaction and high Mg absorption rate. The spheroidal iron produced by the composite spheroidizing modifier has the advantages of excellent metallurgical structure and good comprehensive mechanical property.
Description
The present invention relates to a kind of additive of producing spheroidal graphite cast iron, particularly a kind of spheroidizing inoculant of producing casting ferrite with nodular cast iron that is applicable to.
Nodulizing agent is the important additives of producing spheroidal graphite cast iron.In certain sense, the technical feature of nodulizing agent has determined the Manufacturing Technology of Nodular Cast Iron level to a great extent.Present spheriodization process thereof, home and abroad generally adopt the metal alloy nodulizing agent, mainly contain rare earth magnesium ferrosilicon alloy series and nickel magnesium alloy series etc.There is following several respects problem aborning:
1, reaction is fierce.
The alloy nodulizer that uses produces strong magnesium light and volume of smoke because of reacting fierce when the spheroidizing of stokehold at present, and operating environment is seriously polluted.
2, specific absorption is low.
Because reaction is fierce, causes a large amount of magnesium scaling loss, thereby the specific absorption of magnesium in molten iron reduced, generally have only about 50%, both caused nodularization quality instability easily, waste a large amount of magnesium resources again.
3, function singleness.
The nodulizing agent that uses generally only has the nodularization function at present, breeds with metamorphism and then need use other additive, and just production has brought big difficulty to spheroidal graphite cast iron for this.Also added inoculant elements such as number of C a, Ba, Sr in the nodulizing agent that has, but cost is very high, is difficult to promote the use of.
4, silicon content height.
Because the restriction of smelting technology, the silicon content of alloy nodulizer is limit because of the whole silicon amount of spheroidal graphite cast iron generally all more than 40%, makes pregnant amount have to reduce, and does not reach the purpose that fully breeds.Because nodulizing agent is brought a large amount of element silicons into, caused the higher foundry returns of silicon content to be difficult to recycle.In like manner, the use of the high trade mark pig iron also is restricted.Hindered the benign cycle development that spheroidal graphite cast iron is produced.
5, the contradiction of the use granularity of nodulizing agent is difficult to solve.
Because the little meeting of granularity makes speed of response too fast, too drastic, to have to amplify and use granularity, thereby caused melting performance bad again, a large amount of nodulizing agents does not melt and floats to the molten iron surface combustion, and both waste material easily caused abnormal nodularizing again.
The purpose of this invention is to provide a kind of novel compound spheroidizing inoculant, it can overcome the shortcoming that present widely used nodulizing agent exists effectively, thereby guarantees the stability and the reliability of spheriodizing technique in the spheroidal graphite cast iron production, to improve its quality product.
The present invention is achieved in that
With the re-si-mg alloy is nodulizing agent, and graphite is moderator and nucleating agent, CaF
2Or CaO, Ca
2C is a sweetening agent, carries out the physical mechanical mixing and makes this compound spheroidizing inoculant by certain particle distribution and proportioning.Its material mixture ratio and size-grade distribution are:
After table is seen literary composition
Wherein, the chemical ingredients of re-si-mg alloy is:
Re 0.5~3%
Ca 1~4%
Mg 8~13%
Si 38~42%
The Fe surplus
The effect of each the composition constituent element in this compound spheroidizing inoculant is:
Re both can play auxiliary nodularization and inoculation(effect), the tendency that can avoid excessive rare earth to cause graphite shape to worsen again at its given content range; Ca has stronger inoculation(effect) in given content, help promoting cast ferrite growth, can reduce the activity of Kg again, controls reaction speed and the specific absorption of Kg of improving.
Graphite can reduce the seepage velocity of molten iron to spheroidizing inoculant as moderator and nucleating agent, forms the state of reaction successively, thereby has controlled spheroidizing reacion speed and time; Graphite spreads under the stirring of the magnesium vapor that spheroidizing reacion takes place and fuses in the molten iron, can increase a large amount of non-spontaneous nucleations, plays effective inoculation, crystal grain thinning and promotion graphitizing.
With CaF
2Or CaO, Ca
2C is as sweetening agent, and purpose is to reduce the desulfurization consumption of magnesium, is beneficial to high-sulphur molten iron in low Kg, the low rare-earth nodularizer processing.Guarantee that promptly nodularization eliminates spoken parts in traditional operas again, simultaneously CaF
2Have effect of tangible elimination subsurface porosity and poly-slag effect.
Compound spheroidizing inoculant of the present invention is applicable to the molten iron spheroidizing of 1400~1520 ℃ of temperature, sulphur content 0.015~0.06%.According to molten iron temperature, sulphur content situation, the proportioning and the size-grade distribution of spheroidizing inoculant closed in adjustable reduction.
Compound spheroidizing inoculant of the present invention is compared with the nodulizing agent of present use, has following several respects advantage aborning:
1, reacting balance, magnesium absorption rate height.
For the hot metal ladle of 1~1.5t, the reaction times is 60~100 seconds, and flue dust, magnesium light obviously reduce.Magnesium absorption rate can reach more than 70%.
2, nodularization steady quality, metallographic structure is superior, and comprehensive mechanical performance is good.
With the foundry goods that this spheroidizing inoculant is handled, stokehold nodularization rate reaches more than 2 grades, and number of graphite ball increases more than 30%, and it is good that sphere diameter can reach 6~7 grades, roundness, and cast ferrite content reaches more than 80%.Comprehensive mechanical performance is good, and its mechanical property is:
Tensile strength 460~550N/mm
2
Unit elongation 15~25%
Hardness HB143~156
3, the anti-ageing ability of moving back is strong
In antifading test, the molten iron of handling through this compound spheroidizing inoculant is during at 20 minutes, and rapid detection nodularization rate still reaches 2 grades.
4, because of compound spheroidizing inoculant silicon content of the present invention lower (below 30%), can in the spheroidizing process, relax pregnant amount, and can improve magnesium iron foundry returns and high trade mark pig iron utilization ratio.
Magnesium vapor stirring molten iron is spread in the molten iron sweetening agent during 5, owing to spheroidizing reacion, reaches the Pneumatic desulphurization effect, thereby need not use whipping device, has saved the sweetener investment.
6, compound spheroidizing inoculant cost of the present invention is lower than the nodulizing agent of present use.
The embodiment of the invention is as follows:
Embodiment 1
Produce the QT450-10 magnesium iron with following molten iron (low-sulfur):
Elements C Si Mn
Content % 3.60~3.80 1.0~1.7 0.2~0.3
P S
0.03~0.04 0.015~0.027
1450~1500 ℃ of temperature
Adopt following compound spheroidizing inoculant material mixture ratio and size-grade distribution
Title material proportioning size-grade distribution
<7mm45%
Re-si-mg alloy 80% 7~13mm55%
Graphite 15%<1mm35%
1~3mm65%
CaF
25% 0.5~2mm
Embodiment 2
Produce the QT450-10 magnesium iron with following molten iron (high-sulfur):
Elements C Si Mn
Content % 3.62~3.84 1.0~1.7 0.2~0.3
P S
0.03~0.06 0.03~0.054
1450~1500 ℃ of temperature
Adopt following compound spheroidizing inoculant material mixture ratio and size-grade distribution
Title material proportioning size-grade distribution
<7mm55%
Re-si-mg alloy 75% 7~13mm45%
Graphite 15%<1mm55%
1~3mm45%
CaF
2+CaO 5%+5% 0.5~2mm
The mechanical property of the handled magnesium iron of the foregoing description reaches:
Tensile strength 460~610N/mm
2
Unit elongation 12~25%
Hardness HB143~160
The proportioning size distribution
(percentage by weight)
Nodulizer<7mm 45~55%
(re-si-mg alloy) 65~80% 7~13mm 45~55%
Deceleration, inovulant 10~20%<1mm 30~45%
(graphite) 1~3mm 55~70%
Desulfurizing agent
(CaF
2Or CaO, Ca2C) 5~10% 0.5~2mm
Composition title proportioning size distribution
(percentage by weight)
Nodulizer 65~80%<7mm45~55%
(re-si-mg alloy) 7~13mm45~55%
Deceleration, inovulant 10~20%<1mm30~45%
(graphite) 1~3mm55~70%
Desulfurizing agent 5~10% 0.5~2mm
(CaF
2Or CaO, Ca2C)
Claims (1)
1, a kind of compound spheroidizing inoculant that contains re-si-mg alloy, it is characterized in that with graphite be slow down, nucleating agent, with CaF
2Or CaO, Ca
2C is that sweetening agent is made by adding to descend size-grade distribution and proportioning to mix through physical mechanical with the re-si-mg alloy nodulizing agent:
(table is seen the literary composition back)
Wherein, the chemical ingredients of re-si-mg alloy is:
Re 0.5~3%
Ca 1~4%
Mg 8~13%
Si 38~42%
The Fe surplus