CN102345072A - High-strength cast steel for coal cutter rocking arm and heat treatment process thereof - Google Patents
High-strength cast steel for coal cutter rocking arm and heat treatment process thereof Download PDFInfo
- Publication number
- CN102345072A CN102345072A CN2011102846995A CN201110284699A CN102345072A CN 102345072 A CN102345072 A CN 102345072A CN 2011102846995 A CN2011102846995 A CN 2011102846995A CN 201110284699 A CN201110284699 A CN 201110284699A CN 102345072 A CN102345072 A CN 102345072A
- Authority
- CN
- China
- Prior art keywords
- foundry goods
- heat treatment
- insulation
- cast steel
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a high-strength cast steel for a coal cutter rocking arm and a heat treatment process thereof. The high-strength cast steel comprises the following chemical components in part by weight: 0.30-0.37 part of C, 0.45-0.60 part of Si, 0.90-1.10 part of Mn, 1.40-1.60 part of Cr, 1.40-1.60 parts of Ni, 0.20-0.30 part of Mo, not more than 0.020 part of P and not more than 0.020 part of S. The heat treatment process of the high-strength cast steel for the coal cutter rocking arm comprises the steps of: carrying out diffusion annealing at 1,040-1,060 DEG C; and then sequentially carrying out normalizing at 890-910 DEG C and tempering at 590-610 DEG C. In the invention, because the technical scheme is adopted, the mechanical property of the product is improved, meanwhile the wearing resistance is favorable, the surface rigidity reaches HB260-285, the surface wearing capability is improved, the service life of the product is prolonged, the deformation in the use process is reduced, and the operation reliability of a device is enhanced.
Description
Technical field
The present invention relates to the rocker arm of coal mining machine high-strength cast steel, and thermal treatment process.
Background technology
Rocker arm of coal mining machine adopts ZG270-500, ZG30Mn2 and ZG25MnNi cast steel more at present, and tensile strength of mechanical property is not high, is generally 550MPa, thereby easy deformation influences inner transmission in the use, influences the works better of coalcutter; And its wear resistance is not enough, and surface hardness HB~170 are caused wearing and tearing easily and influenced works better.
Summary of the invention
The object of the present invention is to provide the rocker arm of coal mining machine high-strength cast steel, it is characterized in that: the chemical ingredients that comprises following mass parts:
C:0.30~0.37;
Si:0.45~0.60;
Mn:0.90~1.10;
Cr:1.40~1.60;
Ni:1.40~1.60;
Mo:0.20~0.30;
P≤0.020;
S≤0.020。
Be used for the thermal treatment process of above-mentioned rocker arm of coal mining machine, it is characterized in that: carry out 1040~1060 ℃ " diffusion annealing " earlier, carry out 890~910 ℃ " normalizing " and 590~610 ℃ " tempering " more successively with high-strength cast steel.
Further, " diffusion annealing " technology is warmed up to 1040~1060 ℃ for to heat up with 110~130 ℃ of speed hourly; Press the wall thickness of foundry goods, per 20~30mm insulation was incubated in 2.5~3.5 hours, after waiting to be incubated completion; Stop heating, foundry goods is at the heat treatment furnace internal cooling.
Further; Said " normalizing and tempering " technology is for to heat up with 110~130 ℃ of speed hourly; Be warmed up to 890~910 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 1.5~2.5 hours; After treating that insulation is accomplished, open fire door, foundry goods is pulled out in heat treatment furnace; Carry out air cooling; To be cooledly again foundry goods is put into heat treatment furnace, be warmed up to 590~610 ℃ again to 190~210 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 1~2 hour; After treating that insulation is accomplished, stop heating, make foundry goods at the heat treatment furnace internal cooling.
The present invention makes product mechanics tensile strength reach 804~902Mpa owing to adopted technique scheme, has improved the mechanical property of product, and wear resistance is good simultaneously, and surface hardness reaches HB260~285, increases the surface abrasion resistance ability; And improve product work-ing life, reduce the distortion of use, increase the equipment serviceability.Technology of the present invention is easy, and cost is low, remarkable in economical benefits.
Embodiment
The invention discloses the rocker arm of coal mining machine high-strength cast steel, comprise the chemical ingredients of following mass parts: C:0.30~0.37; Si:0.45~0.60; Mn:0.90~1.10; Cr:1.40~1.60; Ni:1.40~1.60; Mo:0.20~0.30; P≤0.020; S≤0.020.
Be used for the thermal treatment process of above-mentioned rocker arm of coal mining machine, carry out 1040~1060 ℃ " diffusion annealing " earlier, carry out 890~910 ℃ " normalizing " and 590~610 ℃ " tempering " more successively with high-strength cast steel.
" diffusion annealing " technology is warmed up to 1040~1060 ℃ for to heat up with 110~130 ℃ of speed hourly, presses the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 2.5~3.5 hours; After treating that insulation is accomplished, stop heating, foundry goods is at the heat treatment furnace internal cooling." normalizing and tempering " technology is for to heat up with 110~130 ℃ of speed hourly; Be warmed up to 890~910 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 1.5~2.5 hours; After treating that insulation is accomplished; Open fire door; Foundry goods is pulled out in heat treatment furnace, carry out air cooling, to be cooled to 190~210 ℃; Again foundry goods is put into heat treatment furnace; Again be warmed up to 590~610 ℃, be incubated in 1~2 hour, after waiting to be incubated completion by the wall thickness of foundry goods, per 20~30mm insulation; Stop heating, make foundry goods at the heat treatment furnace internal cooling.
Only be specific embodiment of the present invention below, but technical characterictic of the present invention is not limited thereto.Any is the basis with the present invention, for realizing essentially identical technique effect, has done the ground simple change, has been equal to replacement or modification etc., all is covered by among protection scope of the present invention.
Claims (4)
1. rocker arm of coal mining machine high-strength cast steel is characterized in that: the chemical ingredients that comprises following mass parts:
C:0.30~0.37;
Si:0.45~0.60;
Mn:0.90~1.10;
Cr:1.40~1.60;
Ni:1.40~1.60;
Mo:0.20~0.30;
P≤0.020;
S≤0.020。
2. be used for the thermal treatment process of the described rocker arm of coal mining machine of claim 1, it is characterized in that: carry out 1040~1060 ℃ " diffusion annealing " earlier, carry out 890~910 ℃ " normalizing " and 590~610 ℃ " tempering " more successively with high-strength cast steel.
3. thermal treatment process according to claim 2; It is characterized in that: said " diffusion annealing " technology is for to heat up with 110~130 ℃ of speed hourly; Be warmed up to 1040~1060 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 2.5~3.5 hours; After treating that insulation is accomplished, stop heating, foundry goods is at the heat treatment furnace internal cooling.
4. thermal treatment process according to claim 2; It is characterized in that: said " normalizing and tempering " technology is for to heat up with 110~130 ℃ of speed hourly; Be warmed up to 890~910 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 1.5~2.5 hours; After treating that insulation is accomplished, open fire door, foundry goods is pulled out in heat treatment furnace; Carry out air cooling; To be cooledly again foundry goods is put into heat treatment furnace, be warmed up to 590~610 ℃ again to 190~210 ℃; Press the wall thickness of foundry goods; Per 20~30mm insulation was incubated in 1~2 hour; After treating that insulation is accomplished, stop heating, make foundry goods at the heat treatment furnace internal cooling.