CN102336585A - 复合泡沫混凝土及浮床 - Google Patents

复合泡沫混凝土及浮床 Download PDF

Info

Publication number
CN102336585A
CN102336585A CN2011102921801A CN201110292180A CN102336585A CN 102336585 A CN102336585 A CN 102336585A CN 2011102921801 A CN2011102921801 A CN 2011102921801A CN 201110292180 A CN201110292180 A CN 201110292180A CN 102336585 A CN102336585 A CN 102336585A
Authority
CN
China
Prior art keywords
foamed concrete
floating bed
concrete
composite foam
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102921801A
Other languages
English (en)
Other versions
CN102336585B (zh
Inventor
高斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110292180 priority Critical patent/CN102336585B/zh
Publication of CN102336585A publication Critical patent/CN102336585A/zh
Application granted granted Critical
Publication of CN102336585B publication Critical patent/CN102336585B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种复合泡沫混凝土及浮床,将水泥与水搅拌成水泥浆,发泡剂加水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;按体积比向每立方米泡沫混凝土中加入40-90%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入10-60%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。本发明充分利用了陶粒和聚苯乙烯两种材料的各自优点,又是利用水泥作胶凝材料,使它的浮力强度、重量都达到了良好的状态,具有浮力大、稳定性好的特点,使用寿命长;即使浮床遭到了意外破坏,也可将其破碎后加入一定的泡沫水泥将其重新浇注使用,避免了二次污染,大大降低了浮床的使用成本,对大面积推广使用浮床提供了先决条件。

Description

复合泡沫混凝土及浮床
技术领域
本发明涉及一种复合泡沫混凝土的制备,本发明还涉及用这种复合泡沫混凝土制成的用于栽培植物的浮床。
背景技术
浮床是发展“水体农业”及“水体生态”修复技术的载体。目前,国内外主要是采用高分子聚合材料及聚苯乙烯等制作而成,少部分利用木、竹及植物纤维材料制作,以上材料虽然在试验实践中都取得了很好的效果,但要进行大面积的推广应用,仍存在很多问题:主要是制作成本高,使用年限短,载体稳定性差,同时还存在着二次污染。
发明内容
本发明提供一种浮力大、稳定性好,在不人为破坏的情况下,可长期使用,也不会造成二次污染的复合泡沫混凝土浮床。
本发明的目的是这样实现的:一种复合泡沫混凝土,将水泥与水搅拌成水泥浆,发泡剂加水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入40-90%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入10-60%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
所述的陶粒为堆积密度在500kg/m3以下的人造轻骨料。
聚苯乙烯的加入量为泡沫混凝土体积的50-70%。
陶粒的加入量为泡沫混凝土体积的30-50%。
利用复合泡沫混凝土制成的浮床,浮床由床体和床体上栽培孔构成,栽培孔底部设有通气孔,栽培孔填充有陶粒,浮床采用复合泡沫混凝土制成。
栽培孔填充的陶粒直径10毫米以下,堆积密度在600-700kg/m3之间。
本发明提供的复合泡沫混凝土浮床,充分利用了陶粒和聚苯乙烯两种材料的各自优点,又是利用水泥作胶凝材料,使它的浮力强度、重量都达到了良好的状态,具有浮力大、稳定性好的特点,在不人为破坏的情况下,可永久性使用;即使浮床遭到了意外破坏,也可将其破碎后加入一定的泡沫水泥将其重新浇注使用,避免了二次污染,大大降低了浮床的使用成本,对大面积推广使用浮床提供了先决条件。
附图说明
下面结合附图和实施例对本发明作进一步说明。
图1是本发明的结构示意图。
具体实施方式
复合泡沫混凝土制备:
实施例1:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入40%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入60%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
实施例2:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入50%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入50%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
实施例3:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入60%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入40%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
实施例4:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入70%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入30%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
实施例5:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入80%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入20%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
实施例6:将水泥与水搅拌成水泥浆,每Kg水泥加水450-550Kg;发泡剂入25-35倍水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入90%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入10%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
 上述实施例中所采用的陶粒为堆积密度在500kg/m3以下的人造轻骨料。
上述实施例得到的复合泡沫混凝土用于生产复合泡沫混凝土浮床。
复合泡沫混凝土浮床的结构如如图1所示,浮床由床体1和床体1上栽培孔2构成,栽培孔2底部设有通气孔3,栽培孔2填充有陶粒,浮床1采用复合泡沫混凝土制成。在种植植物时,向栽培孔中填充陶粒,直径10毫米以下,选用5-10毫米均可,陶粒堆积密度在600-700kg/m3之间。

Claims (6)

1.一种复合泡沫混凝土,其特征在于:将水泥与水搅拌成水泥浆,发泡剂加水制成泡沫,与水泥浆充分搅拌均匀,得到泡沫混凝土,备用;
按体积比向每立方米泡沫混凝土中加入40-90%聚苯乙烯,与水泥浆充分混合;再按体积比向立方米泡沫混凝土中加入10-60%的陶粒,充分搅拌均匀,得到复合泡沫混凝土。
2.根据权利要求1所述的复合泡沫混凝土,其特征在于:所述的陶粒为堆积密度在500kg/m3以下的人造轻骨料。
3.根据权利要求1所述的复合泡沫混凝土,其特征在于:聚苯乙烯的加入量为泡沫混凝土体积的50-70%。
4.根据权利要求1所述的复合泡沫混凝土,其特征在于:陶粒的加入量为泡沫混凝土体积的30-50%。
5.利用权利要求1所述复合泡沫混凝土制成的浮床,其特征在于:浮床由床体(1)和床体(1)上栽培孔(2)构成,栽培孔(2)底部设有通气孔(3),栽培孔(2)填充有陶粒,浮床(1)采用复合泡沫混凝土制成。
6.根据权利要求5所述的复合泡沫混凝土制成的浮床,其特征在于:所采用的陶粒直径10毫米以下,堆积密度在600-700kg/m3之间。
CN 201110292180 2011-10-02 2011-10-02 复合泡沫混凝土浮床 Expired - Fee Related CN102336585B (zh)