CN102330366A - Printing paint and preparation method for the same - Google Patents
Printing paint and preparation method for the same Download PDFInfo
- Publication number
- CN102330366A CN102330366A CN201110213780A CN201110213780A CN102330366A CN 102330366 A CN102330366 A CN 102330366A CN 201110213780 A CN201110213780 A CN 201110213780A CN 201110213780 A CN201110213780 A CN 201110213780A CN 102330366 A CN102330366 A CN 102330366A
- Authority
- CN
- China
- Prior art keywords
- organic pigment
- printing coating
- printing
- coating
- printing paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a printing paint and a preparation method for the same. Raw material of the printing paint is composed of the following components by mass percentages: 25-40% of organic pigment, 5-8% of maleic anhydride-acrylic polymer used as dispersing agent, 5-8% of polyoxyethylene polyoxypropylene butyl ether used as wetting agent butyl, 5-10% of polyvinyl alcohol, and water (the rest). The printing paint is prepared by mixing the components, and grinding the mixture into slurry with organic pigment grain size of 0.1-2 micrometers.
Description
Technical field
The invention belongs to field of textiles, and be particularly related to a kind of printing coating.
Background technology
COAT PRINTING is exactly to print on the fabric with suitable macromolecular compound and coating; Through handling; On fiber, form have certain elasticity, wear-resisting transparent resin film, with the printing method on the fiber that anchors at of paint machine, this macromolecular compound is in adhesive.Coating claims that also pigment is the chromogen in the print paste, mainly is divided into two big types of organic pigment and inorganic pigments, and the COAT PRINTING of fabric mainly adopts organic pigment, and its heat resistance is good, adapts to high temperature and bakes or decatize, and chromatogram is also comparatively complete.
Coating direct printing painted principle on fiber is different with general dyestuff, and its nationality adhesive anchors at insoluble granules of pigments on the textiles.The environmental protection of COAT PRINTING technology need not washing, and little to the restriction of fabric, technology is simple, and colorant match is convenient, and coloured light is easy to adjustment and control, and the pattern profile of printing is clear, well arranged, be rich in third dimension.It is good not enough that but the problem that present pigment printing paste exists mainly is exactly COLOR FASTNESS and friction, the soaping fastness of coating behind the stamp.
Summary of the invention
The present invention the invention provides a kind of printing coating and preparation method thereof in order to overcome the defective of existing printing coating washability difference, and washability improves greatly.
Technical scheme of the present invention is: a kind of printing coating, raw material consist of by percentage to the quality:
Organic pigment 25～40%,
Dispersant copolymer of maleic anhydride and acrylic acid 5～8%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 5～8%,
Polyvinyl alcohol 5 ~ 10%,
Water surplus;
Described organic pigment molecular structural formula is,
Also comprise 1 ~ 5% propylene glycol.
Also comprise 0.05 ~ 0.5 polydimethyl siloxane fluid.
Prepare described printing coating for textile fabrics, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.
Beneficial effect
1. coating of the present invention has good rub resistance and the anti-fastness of washing by rubbing with the hands.
2. coating of the present invention has good fast light, weather, heat resistance.
3. the present invention does not contain harmful substances such as formaldehyde, heavy metal and organotin, environmental protection, health.
The specific embodiment
Further explain in the face of the present invention down.
A kind of printing coating, raw material consist of by percentage to the quality:
Organic pigment 25～40%,
Dispersant copolymer of maleic anhydride and acrylic acid 5～8%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 5～8%,
Polyvinyl alcohol 5 ~ 10%,
Water surplus;
Described organic pigment molecular structural formula is,
Available from Zhejiang Province Longsheng Group Co., Ltd.
Also comprise 1 ~ 5% propylene glycol.
Also comprise 0.05 ~ 0.5 polydimethyl siloxane fluid.
Prepare described printing coating, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.
Embodiment 1
A kind of printing coating, raw material consist of by percentage to the quality:
Organic pigment 30%,
Dispersant copolymer of maleic anhydride and acrylic acid 6%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 6%,
Polyvinyl alcohol 8%,
Propylene glycol 2%,
Polydimethyl siloxane fluid 0.25%,
Water surplus;
Described organic pigment molecular structural formula is,
Prepare described printing coating, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.
Embodiment 2
A kind of printing coating, raw material consist of by percentage to the quality:
Organic pigment 40%,
Dispersant copolymer of maleic anhydride and acrylic acid 8%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 8%,
Polyvinyl alcohol 10%,
Water surplus,
Propylene glycol 5%,
Polydimethyl siloxane fluid 0.5.
Described organic pigment molecular structural formula is,
Prepare described printing coating, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.
Embodiment 3
A kind of printing coating, raw material consist of by percentage to the quality:
Organic pigment 25%,
Dispersant copolymer of maleic anhydride and acrylic acid 5%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 5%,
Polyvinyl alcohol 5%,
Water surplus,
Described organic pigment molecular structural formula is,
Prepare described printing coating, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.
Embodiment 4
Coating to embodiment 1 ~ 3 is tested, and adopts printing coating to be mixed with behind 5% the print paste concentrator with 15% stereoplasm composition, adopts this material to carry out stamp then,
1. fast light test: shine 20h with carbon arc lamp after the heat treatment, wherein the fastness rate rank is 0-8;
2. heat resistant test: 180 ℃ of hot-air seasoning 30s, heat-resisting rank is 0-5;
3. solvent-resistance test: add tetrachloro-ethylene after the heat treatment, with 40 ℃ of emerge in worm water 30min, anti-solvent rank is 0-5,
4. the anti-test of soaping: add ground caustic after the heat treatment, in 70 ℃ of warm water, wash 45min, the anti-rank of soaping is 0-5;
Table 1 The performance test results
| ? | Fast light test | Heat resistant test | Solvent-resistance test | The anti-test of soaping |
| Embodiment 1 | 7 | 4 | 4 | 4 |
| Embodiment 2 | 8 | 5 | 5 | 5 |
| Embodiment 3 | 6 | 3 | 3 | 3 |
Claims (4)
1. a printing coating is characterized in that, raw material consists of by percentage to the quality:
Organic pigment 25～40%,
Dispersant copolymer of maleic anhydride and acrylic acid 5～8%,
Wetting agent polyoxyethylene polyoxypropylene monobutyl ether 5～8%,
Polyvinyl alcohol 5 ~ 10%,
Water surplus;
Described organic pigment molecular structural formula is,
。
2. printing coating as claimed in claim 1 is characterized in that, also comprises 1 ~ 5% propylene glycol.
3. printing coating as claimed in claim 1 is characterized in that, also comprises 0.05 ~ 0.5 polydimethyl siloxane fluid.
4. preparation claim 1 ~ 3 arbitrary described printing coating is characterized in that, the slurry that is milled to the organic pigment particle diameter after each component is mixed and is 0.1 ~ 2 micron promptly gets.