CN102329139A - Integrally cast calcium carbide furnace door - Google Patents
Integrally cast calcium carbide furnace door Download PDFInfo
- Publication number
- CN102329139A CN102329139A CN201110206858A CN201110206858A CN102329139A CN 102329139 A CN102329139 A CN 102329139A CN 201110206858 A CN201110206858 A CN 201110206858A CN 201110206858 A CN201110206858 A CN 201110206858A CN 102329139 A CN102329139 A CN 102329139A
- Authority
- CN
- China
- Prior art keywords
- granularity
- calcium carbide
- parts
- plate diamond
- furnace door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an integrally cast calcium carbide furnace door which is prepared from the following raw materials in parts by weight: 40-80 parts of slaty corundum of which the granularity is 8-0mm, 10-25 parts of slaty corundum of which the granularity is 120-180 meshes, 5-15 parts of silicon carbide of which the granularity is 120-200 meshes, 5-10 parts of alpha-Al2O3 micropowder of which the granularity is lower than 5 mu m, 5-8 parts of pure calcium sodium aluminate cement and 4-7 parts of water. Slaty corundum and other refractory materials are integrally cast into the calcium carbide furnace door, and thus, the calcium carbide furnace door can resist the high temperature of higher than 1800 DEG C, does not have weakness, has high thermal stability, and can avoid the phenomena of electric leakage and stony edema.
Description
Technical field
The present invention relates to a kind of furnace of calcium carbide fire door, be specifically related to a kind of integrated poured furnace of calcium carbide fire door.
Background technology
Furnace of calcium carbide is the method with the electrode melting, produces calcium carbide solution, and temperature is up to 2200 ℃, and fire door is the key position of furnace of calcium carbide, requires the erosion performance of existing anti-preferably calcium carbide water and slag thereof, and anti-thermal shock stability is preferably arranged again.For a long time, the furnace of calcium carbide fire door uses high performance composite corundum brick to build by laying bricks or stones, the weak part of the mortar joint stone water phenomenon of often leaking electricity, influence safety in production.
Summary of the invention
The technical problem that the present invention will solve is that the furnace of calcium carbide fire door uses high performance composite corundum brick to build by laying bricks or stones, and the weak part of the mortar joint stone water phenomenon of often leaking electricity provides a kind of integrated poured furnace of calcium carbide fire door.
Technical scheme of the present invention is: a kind of integrated poured furnace of calcium carbide fire door, and it is to be processed by the raw material of following parts by weight:
Granularity is the plate diamond spar 40-80 of 8-0 mm
Granularity is 120-180 purpose plate diamond spar 10-25
Granularity is 120-200 purpose silit 5-15
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
5-10
Pure sodium aluminate calcium cement 5-8
Water 4-7.
Integrated poured furnace of calcium carbide fire door, preferably process by the raw material of following parts by weight:
Granularity is the plate diamond spar 50-70 of 8-0 mm
Granularity is 120-180 purpose plate diamond spar 12-20
Granularity is 120-200 purpose silit 8-12
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
6-8
Pure sodium aluminate calcium cement 6-8
Water 5-7.
Integrated poured furnace of calcium carbide fire door, optimum is processed by the raw material of following parts by weight:
Granularity is the plate diamond spar 60 of 8-0 mm
Granularity is a 120-180 purpose plate diamond spar 15
Granularity is a 120-200 purpose silit 10
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
7
Pure sodium aluminate calcium cement 7
Water 6.
The invention has the beneficial effects as follows: the present invention adopts refractory material casting materials such as plate diamond spar, and the furnace of calcium carbide fire door is poured into an integrated entity, and there is not weak link in anti-high temperature more than 1800 ℃, Heat stability is good, the stone water phenomenon of can avoiding leaking electricity.
Embodiment
Embodiment 1
A kind of integrated poured furnace of calcium carbide fire door, it is to be processed by following raw material: granularity is that plate diamond spar 60 kg, the granularity of 8-0 mm is that 120 purpose plate diamond spars, 15 kg, granularity are that 120 purpose silit, 10 kg, granularity are the α-Al below the 5 μ m
2O
3Micro mist 7 kg, pure sodium aluminate calcium cement 7 kg, water 6 kg.
After the above-mentioned raw materials mixing, integrated poured is the furnace of calcium carbide fire door, the back of condensing.
Embodiment 2
A kind of integrated poured furnace of calcium carbide fire door, it is to be processed by following raw material:
Granularity is that plate diamond spar 80 kg, the granularity of 8-0 mm is that 180 purpose plate diamond spars, 25 kg, granularity are that 200 purpose silit, 15 kg, granularity are the α-Al below the 5 μ m
2O
3Micro mist 10 kg, pure sodium aluminate calcium cement 8 kg, water 7 kg.
Embodiment 3
A kind of integrated poured furnace of calcium carbide fire door, it is to be processed by following raw material:
Granularity is that plate diamond spar 40 kg, the granularity of 8-0 mm is that 160 purpose plate diamond spars, 10 kg, granularity are that 180 purpose silit, 5 kg, granularity are the α-Al below the 5 μ m
2O
3Micro mist 5 kg, pure sodium aluminate calcium cement 5 kg, water 4 kg.
Embodiment 4
A kind of integrated poured furnace of calcium carbide fire door, it is to be processed by following raw material:
Granularity is that plate diamond spar 70 kg, the granularity of 8-0 mm is that 140 purpose plate diamond spars, 20 kg, granularity are that 160 purpose silit, 12 kg, granularity are the α-Al below the 5 μ m
2O
3Micro mist 8 kg, pure sodium aluminate calcium cement 8 kg, water 7 kg.
Embodiment 5
A kind of integrated poured furnace of calcium carbide fire door, it is to be processed by following raw material:
Granularity is that plate diamond spar 50 kg, the granularity of 8-0 mm is that 120-180 purpose plate diamond spar 12 kg, granularity are that 120-200 purpose silit 8 kg, granularity are the α-Al below the 5 μ m
2O
3Micro mist 6 kg, pure sodium aluminate calcium cement 6 kg, water 5 kg.
Claims (3)
1. an integrated poured furnace of calcium carbide fire door is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the plate diamond spar 40-80 of 8-0 mm
Granularity is 120-180 purpose plate diamond spar 10-25
Granularity is 120-200 purpose silit 5-15
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
5-10
Pure sodium aluminate calcium cement 5-8
Water 4-7.
2. integrated poured furnace of calcium carbide fire door according to claim 1 is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the plate diamond spar 50-70 of 8-0 mm
Granularity is 120-180 purpose plate diamond spar 12-20
Granularity is 120-200 purpose silit 8-12
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
6-8
Pure sodium aluminate calcium cement 6-8
Water 5-7.
3. integrated poured furnace of calcium carbide fire door according to claim 2 is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the plate diamond spar 60 of 8-0 mm
Granularity is a 120-180 purpose plate diamond spar 15
Granularity is a 120-200 purpose silit 10
Granularity is the α-Al below the 5 μ m
2O
3Micro mist
7
Pure sodium aluminate calcium cement 7
Water 6.