CN102321401A - Multi-functional coating and preparation method thereof - Google Patents
Multi-functional coating and preparation method thereof Download PDFInfo
- Publication number
- CN102321401A CN102321401A CN201110196723A CN201110196723A CN102321401A CN 102321401 A CN102321401 A CN 102321401A CN 201110196723 A CN201110196723 A CN 201110196723A CN 201110196723 A CN201110196723 A CN 201110196723A CN 102321401 A CN102321401 A CN 102321401A
- Authority
- CN
- China
- Prior art keywords
- nano
- multifunctional coating
- bamboo charcoal
- boron carbide
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multi-functional coating and a preparation method thereof; the mass percentage of the raw material composition of the multi-functional coating is that: 1 percent to 5 percents of nano bamboo charcoal, 1 percent to 5 percents of nano boron carbide, 1 percent to 5 percents of compatilizer, and the rest is a base material; the preparation method comprises the steps that: the nano bamboo charcoal and the nano boron carbide are dissolved in the compatilizer ethanol and are continuously stirred until being fully dissolved, and a functional material is obtained; and the functional material is mixed with the base material, and a final product, i.e. the multi-functional coating is obtained. The multi-functional coating provided by the invention contains nano boron carbide, has a larger thermal neutron capture cross section and very good neutron absorption and anti-radiation performance, contains nano bamboo charcoal, and has absorption and environmental purification functions.
Description
[technical field]
The present invention relates to technical field of coatings, specifically, is a kind of multifunctional coating and preparation method thereof.
[background technology]
Antiradiation material has become a big problem of current material subject, and along with the appearance and the widespread use of various high radiation devices, the research of antiradiation material has caused people's common concern.The Fukushima Nuclear power plants crisis that the Fukushima, Japan earthquake on March 11st, 2011 is caused has also caused the worry of people to radioprotective; And various source of radiation exist in people's life, also force the attention of people to antiradiation material; Radiation is classified as the fourth-largest environomental pollution source after water source, atmosphere, noise by the World Health Organization, becomes the healthy stealth " killer " of harm humans, and the protection radiation has become the task of top priority.
What adopt mostly for radiation shielding coating at present is in coating composition, to add heavy metal or rare metal powder and oxide compound thereof, especially contains metallic compounds such as Ba, Pb, U, Lu, perhaps adopts composite deposite; Defectives such as but must also bring constructional difficulties, sticking power is not enough, and the while function is not enough; Thereby the radiation shielding coating Application Areas is also only at some special industries and special dimension, and less in people's field product application such as life, when therefore exploitation has shielding property concurrently; The additional properties that have other again; Satisfying the basic function of coating, widening its Application Areas, meeting also that coating is multi-functional, the requirement of multi-field development.The utility model adopts the Win 40350 loaded with nano PbSO of high-temperature activation
4, BaSO
4, cooperate silicone compounds, catalyzer and other auxiliary agents again, prepare with the method for gel-sol have radioprotective, the coating of fire-retardant and anti-microbial effect; It is many to have function, applied range, and preparation technology is simple; Characteristics such as execution conditions are convenient, and are environment friendly and pollution-free.
[summary of the invention]
The objective of the invention is to overcome the deficiency of prior art, a kind of multifunctional coating and preparation method thereof is provided.
The objective of the invention is to realize through following technical scheme:
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described bamboo charcoal nano mass percent most preferably is 3% for being preferably 2～4%;
Described nano boron carbide mass percent most preferably is 3% for being preferably 2～4%;
Described base-material can be for the coating of routine, such as the coating of usefulness or the like of whitewashing a wall.
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Compared with prior art, positively effect of the present invention is:
The present invention contains nano boron carbide, has bigger thermal-neutron capture cross-section, has fabulous intercept neutrons and radiation resistance;
The present invention contains nano-bamboo carbon, and the molecular structure of bamboo carbon is sexangle, and quality is hard, fine and closely woven porous, and high adsorption capacity is the optimum feed stock of gac, voidage is high, has the absorption function, and environmental purification function is arranged; This and bamboo carbon popularize rapidly with it simple and easy, be widely used, efficiently have direct relation; Bamboo carbon also is good purifying water treating agent, electromagnetic shielding agent, obnoxious flavour sorbent material.The bamboo charcoal whole body all is precious, is " Boart " by good name; Bamboo carbon is to be resource with abundant old bamboo, adopts the high temperature pyrolysis technology, lasts more than 20 day, fires meticulously to form; Because its carbonaceous is fine and close, than great, hole is many; Content of mineral substances is abundant, and surface-area is up to 700 meters squared per gram, and it has stronger absorption resolving power; Hygroscopic desiccation, performances such as smelly antibiotic and negative ion penetration disappear. and adopt felt class cloth with import cloth, middlely make packing layer with the high-quality particle; Form pure making by hand, refining forming through intensively and carefully working out something; Melt manufacturability, comfortableness, ventilation property, health care function, its product has and suppresses fungi procreation, moisture absorption, deodorizes, antipruritic, detumescence and promoting granulation, prevents and treats in one, integrates health, pleasant property, wholesomeness.Bamboo charcoal has cool in summer and warm in winter; The antibacterial and deodorizing effect; Can produce excellent far infrared rays effect and assemble when bamboo charcoal 300 grams-500 restrain, HUMAN HEALTH and brain cell activation are highly profitable, can produce anion air (similar polyphenol powde effect) in addition to promote the national life quality.
[embodiment]
The embodiment of a kind of multifunctional coating of the present invention and preparation method thereof below is provided.
Embodiment 1
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material can be the coating of routine,
Consisting of of base-material:
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Embodiment 2
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material can be the coating of routine,
Consisting of of base-material:
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Embodiment 3
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material can be the coating of routine,
The raw materials quality per-cent of base-material is:
Novolac epoxy is 55%; Filler is 44%; Auxiliary agent is 1%;
Described filler is selected from several kinds in permanent white, silicon powder, the mica powder;
Described auxiliary agent is selected from Vestolen PP 7052 flow agent powder auxiliary or aerosil thixotropic agent.
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Embodiment 4
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material can be polyurethane aqueous lacquer.
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Embodiment 5
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material is the aqueous woodware paint of staple with the synthetics of vinylformic acid and urethane.
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
Embodiment 6
A kind of multifunctional coating, its raw material are formed mass percent and are done,
Described base-material is an interior wall coating, makes in the composition and is made up of water, pigment, emulsion, weighting agent and various auxiliary agent basically.
A kind of preparation method of multifunctional coating, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.
The above only is a preferred implementation of the present invention; Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the present invention's design; Can also make some improvement and retouching, these improvement and retouching also should be regarded as in protection scope of the present invention.
Claims (6)
1. multifunctional coating, its raw material are formed mass percent and are done, it is characterized in that,
2. a kind of multifunctional coating as claimed in claim 1 is characterized in that, described bamboo charcoal nano mass percent is 2～4%.
3. a kind of multifunctional coating as claimed in claim 2 is characterized in that, described bamboo charcoal nano mass percent is 3%.
4. a kind of multifunctional coating as claimed in claim 1 is characterized in that, described nano boron carbide mass percent is 2～4%.
5. a kind of multifunctional coating as claimed in claim 4 is characterized in that, described nano boron carbide mass percent is 3%.
6. the preparation method of a multifunctional coating is characterized in that, with bamboo charcoal nano, nano boron carbide is dissolved in the compatilizer ethanol, and constantly stirs, and until dissolving fully, obtains function material; Function material is mixed with base-material, obtain final product multifunctional coating.