CN102321356A - 聚碳酸亚丙酯树脂用隔离剂 - Google Patents
聚碳酸亚丙酯树脂用隔离剂 Download PDFInfo
- Publication number
- CN102321356A CN102321356A CN201110200719A CN201110200719A CN102321356A CN 102321356 A CN102321356 A CN 102321356A CN 201110200719 A CN201110200719 A CN 201110200719A CN 201110200719 A CN201110200719 A CN 201110200719A CN 102321356 A CN102321356 A CN 102321356A
- Authority
- CN
- China
- Prior art keywords
- separant
- poly
- resin
- propylene carbonate
- carbonate resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚碳酸亚丙酯树脂用隔离剂,其由脂肪族酰胺类、液体石蜡和甲基硅油组成,其组成按质量百分比计为:脂肪族酰胺类90-95%,液体石蜡1-5%,甲基硅油1-5%。所述隔离剂在聚碳酸亚丙酯树脂中的用量按质量计为1-5%。本发明制成的聚碳酸亚丙酯树脂用隔离剂的少量掺用既起到有效的隔离作用,又不会对聚碳酸亚丙酯树脂性能产生影响,且没有毒副作用。
Description
技术领域
本发明涉及一种聚碳酸亚丙酯树脂用隔离剂,用于聚碳酸亚丙酯包装储存过程中树脂粒子之间起隔离作用。
技术背景
随着塑料用量的与日俱增,废弃塑料所造成的“白色污染”已成为世界性公害,开发可降解塑料已成为世界范围的研究热点。其发展不仅扩大了塑料的功能,而且在一定程度上缓解了环境矛盾,对日益枯竭的石油资源是一个补充,因此降解塑料的研究开发和推广应用,无论从地球环境保护的实际角度或从取之不尽的可再生资源,还是从合成功能性高分子的学术角度都具有重要的意义。
聚碳酸亚丙酯是一类降解塑料,因其原料主要利用二氧化碳,制成品又具有可降解性,正愈来愈受到重视。聚碳酸亚丙酯树脂是一种非晶材料,而且其玻璃化温度仅35-40度左右, 当储存运输温度较高时,树脂粒子之间会相互粘连结块,给使用带来不便。目前解决高分子材料相互粘连结块的方法是使用无机粉体如碳酸钙、滑石粉等,但聚碳酸亚丙酯使用无机粉体会影响制品的透明性,所以寻找一种隔离剂,用于聚碳酸亚丙酯包装储存过程中树脂粒子之间起隔离作用就显得很有意义。
发明内容
本发明的目的在于对聚碳酸亚丙酯包装储存过程中树脂粒子之间的粘连性能进行改性,提供一种隔离剂配方,工艺简单,适应范围广。
为实现上述目的,本发明采用的技术方案是:一种聚碳酸亚丙酯树脂隔离剂,其特征在于:它是由按质量百分比计的以下原料构成:
脂肪族酰胺类 90-95%
液体石蜡 1-5%
甲基硅油 1-5%。
所述脂肪族酰胺类为油酸酰胺或芥酸酰胺或硬脂酸酰胺。
本发明所述的聚碳酸亚丙酯树脂用隔离剂,其在聚碳酸亚丙酯树脂中的用量,按质量计为1-5%。
本发明所公开的聚碳酸亚丙酯树脂用隔离剂所具的优点一是,由于配方选择及配比合理,在硬度低、表面张力低的聚碳酸亚丙酯颗粒表面,分散效果好,覆盖均匀,高温放置涂层不消失,隔离效果显著;二是,无毒无害,对聚碳酸亚丙酯树脂的性能以及后续加工无不良影响;三是,工艺简单,无腐蚀性,不腐蚀设备,性价比高。
下面通过试验来说明隔离剂的效果:隔离剂的隔离效果评价是在50度烘箱中进行的,将聚碳酸亚丙酯树脂纯料和纯料质量3%的隔离剂分别装入塑料包装袋中,包装袋上方加载砝码,砝码重量按其与包装袋接触面积计算,使包装袋承受压力为1N/cm2,恒温保压24小时后检查树脂粒子之间是否粘连。
表1 聚碳酸亚丙酯树脂隔离剂的隔离效果
实施例 | 结块现象(50℃) |
纯聚碳酸亚丙酯树脂 | 有 |
加入含油酸酰胺成份的隔离剂 | 无 |
加入含芥酸酰胺成份的隔离剂 | 无 |
加入含硬脂酸酰胺成份的隔离剂 | 无 |
隔离剂的隔离效果如表1所示。从表1可看出,三种不同组成的隔离剂均有较好的隔离效果。
具体实施方式
下面用实施例进一步描述本发明。这些实例是本发明优先的实施方案,不构成对本发明的限制。
实施例1
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
油酸酰胺 95%
液体石蜡 2%
甲基硅油 3%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为3%。
实施例2
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
油酸酰胺 90%
液体石蜡 5%
甲基硅油 5%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为1%。
实施例3
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
油酸酰胺 93%
液体石蜡 3%
甲基硅油 4%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为5%。
实施例4
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
芥酸酰胺 95%
液体石蜡 2%
甲基硅油 3%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为3%。
实施例5
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
芥酸酰胺 90%
液体石蜡 5%
甲基硅油 5%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为1%。
实施例6
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
芥酸酰胺 93%
液体石蜡 4%
甲基硅油 3%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为5%。
实施例7
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
硬脂酸酰胺 95%
液体石蜡 2%
甲基硅油 3%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为3%。
实施例8
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
硬脂酸酰胺 90%
液体石蜡 5%
甲基硅油 5%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为1%。
实施例9
聚碳酸亚丙酯树脂用隔离剂由按质量百分比计的以下原料构成:
硬脂酸酰胺 93%
液体石蜡 4%
甲基硅油 3%
聚碳酸亚丙酯树脂用隔离剂在聚碳酸亚丙酯树脂中的用量,按质量计为5%。
Claims (3)
1.一种聚碳酸亚丙酯树脂用隔离剂,其特征在于:其是由按质量百分比计的以下原料构成:
脂肪族酰胺类 90-95%
液体石蜡 1-5%
甲基硅油 1-5% 。
2.由权利要求1所述的聚碳酸亚丙酯树脂用隔离剂,其特征在于:所述脂肪族酰胺类为油酸酰胺或芥酸酰胺或硬脂酸酰胺。
3.由权利要求1或2所述的聚碳酸亚丙酯树脂用隔离剂,其特征在于:其在聚碳酸亚丙酯树脂中的用量,按质量计为1-5%。