Summary of the invention
The present invention is directed to the deficiency of above-mentioned prior art existence and a kind of better anti-corrosion treatment process of nipple rust-proof effect for reservoir is provided.For this reason, the present invention adopts following technical scheme:
A kind of anti-corrosion treatment process to the reservoir nipple is characterized in that, this anti-corrosion treatment process may further comprise the steps:
The first step is coated in antirust solution on the nipple for the first time;
In second step, the nipple of reservoir is carried out phosphatization handle;
In the 3rd step, carry out plastic-blasting and handle;
In the 4th step, carry out baking processing;
In the 5th step, for the second time antirust fluid is coated on the nipple;
The 6th step, left standstill 24 hours, obtain finished product.
As to technique scheme further replenish and perfect, the present invention also comprises following supplementary technology scheme:
Described phosphatization is handled available spray mode and is handled, and the time accomplished in 0.5~3 minute;
Described phosphatization is handled the also available phosphorus mode of soaking and is handled, and the time accomplished in 1~5 minute;
It can be the zinc-iron based phosphatization liquid that said phosphatization is handled used phosphatization liquid;
It can also be the without phosphorus Chrome-free agent of nanometer that said phosphatization is handled used phosphatization liquid;
Described spray treatment is to spray with black powder, evenly distributes, do not have foaming, bright and clean up to the product surface coating;
The used black powder of said spray treatment can be a black plastic-blasting powder;
Temperature during said baking processing is controlled within 200~220 ℃, and the time was controlled within 20~40 minutes.
Compare with the anti-corrosion treatment process of the nipple of existing reservoir, use the present invention can reach following beneficial effect:
Use treatment process of the present invention, the product of gained long deposit or haulage time in be not easy to get rusty.After product was handled through phosphatization, product surface had formed layer protecting film, and this diaphragm can prevent that to a certain extent metal is corroded; On nipple, apply after the antirust solution; Spray again, plastic-blasting handles, and then advances the baking oven baking, after toasting; The antirust solution that is coated in the nipple surface has played further rust inhibition; In bake process, there is part content to infiltrate the nipple metal surface, improves the adhesion of antirust solution and metal, and make diaphragm firmer; The antirust processing second time is carried out on the new designs of threaded joints surface again, makes the metal surface corrosion resistance play duplicate protection.
The specific embodiment
Embodiments of the invention disclose a kind of anti-corrosion treatment process to the reservoir nipple.The embodiment of the following stated will be elaborated to the present invention:
Embodiment 1:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple to reservoir carries out the phosphatization processing, and adopts the spray mode to handle, and the time accomplished in 2 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 200 ℃, and the baking processing time is 40 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Embodiment 2:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple to reservoir carries out the phosphatization processing, and adopts the spray mode to handle, and the time accomplished in 2.5 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 220 ℃, and the baking processing time is 20 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Embodiment 3:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple to reservoir carries out the phosphatization processing, and adopts the spray mode to handle, and the time accomplished in 3 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 210 ℃, and the baking processing time is 30 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Embodiment 4:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple of reservoir is carried out phosphatization handle, and adopt and soak the phosphorus mode and handle, the time accomplished in 3 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 200 ℃, and the baking processing time is 40 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Embodiment 5:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple of reservoir is carried out phosphatization handle, and adopt and soak the phosphorus mode and handle, the time accomplished in 4 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 220 ℃, and the baking processing time is 20 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Embodiment 6:
The nipple of reservoir is handled according to following steps:
The first step: for the first time antirust solution is coated on the nipple;
Second step: the nipple of reservoir is carried out phosphatization handle, and adopt and soak the phosphorus mode and handle, the time accomplished in 5 minutes, and used phosphatization liquid is the without phosphorus Chrome-free agent of zinc-iron based phosphatization liquid or nanometer;
The 3rd step: when carrying out the plastic-blasting processing, spray, evenly distribute, do not have foaming, bright and clean up to the product surface coating with black plastic-blasting powder;
The 4th step: carry out baking processing: temperature is controlled at 210 ℃, and the baking processing time is 30 minutes;
The 5th step: for the second time antirust fluid is coated on the nipple;
The 6th step: left standstill 24 hours, and obtained finished product.
Preferable antirust according to the product of the foregoing description gained, product long deposit or haulage time in be not easy to get rusty.