CN102304287A - 一种硅太阳能电池银浆用有机粘合剂组合物及制备方法 - Google Patents

一种硅太阳能电池银浆用有机粘合剂组合物及制备方法 Download PDF

Info

Publication number
CN102304287A
CN102304287A CN201110200620A CN201110200620A CN102304287A CN 102304287 A CN102304287 A CN 102304287A CN 201110200620 A CN201110200620 A CN 201110200620A CN 201110200620 A CN201110200620 A CN 201110200620A CN 102304287 A CN102304287 A CN 102304287A
Authority
CN
China
Prior art keywords
solar cell
silicon solar
organic binder
binder bond
silver slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110200620A
Other languages
English (en)
Inventor
朱万超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Irico Group Corp
Original Assignee
Irico Group Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Irico Group Corp filed Critical Irico Group Corp
Priority to CN201110200620A priority Critical patent/CN102304287A/zh
Publication of CN102304287A publication Critical patent/CN102304287A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种硅太阳能电池银浆用有机粘合剂组合物，按质量份由以下原料组成：5-13％的聚酰胺树脂、8-25％的松香树脂或酚醛改性萜烯树脂、65-80％的有机溶剂、0-1％的湿润分散剂。本发明所述的有机粘合剂组合物在银浆中作为载体或分散介质存在，赋予浆料合适的流体性能，能充分润湿银浆中银粉及无机粘合剂粉末，能与其它助剂混溶。

Description

一种硅太阳能电池银浆用有机粘合剂组合物及制备方法
技术领域
本发明涉及硅太阳能电池领域，特别是涉及一种硅太阳能电池银浆用有机粘合剂组合物及其制备方法
背景技术
太阳能电池是一种能将太阳能转换成电能的半导体器件，在光照条件下太阳能电池内部会产生光生电流，通过电极可直接将电能输出。
为了将太阳能电池产生的光生电流引出，必须在太阳能电池的表面制作出正反电极。常用的电极制作工艺有磁控溅射、真空蒸镀和丝网印刷烧结等，但是磁控溅射、真空蒸镀方法的生产成本太高，经济性差。目前，在太阳能电池生产企业中，普遍使用太阳能电池导电银浆，通过丝网印刷、低温烘干、高温烧结工艺制成太阳能电池的电极。现有导电银浆由银粉、玻璃粘合剂、有机粘合剂等原材料按不同配比制备而成。其中有机粘合剂主要起分散和包裹作用，将银粉颗粒均匀的包裹起来，使得导电银浆不容易产生沉淀和氧化。并且能够让银浆有更好的印刷效果。导电银浆的质量直接影响太阳能电池的串联电阻和电池光电转换效率，它是太阳能电池生产中的一个非常关键的技术要点。而采用好的有机粘合剂能够使银浆在印刷时有更好的适印性，并且提升银浆线条的高宽比，这样就会让导电性能更佳，从而提高电池的光电转化效率。
发明内容
本发明的目的是提供一种本发明的目的是提供一种硅太阳能电池银浆用有机粘合剂组合物及其制备方法，使印刷的银浆线条在保持银线宽度的同时达到一定的高度，来提升电池的光电转化效率。
为实现上述目的，本发明提供的技术方案如下：
一种硅太阳能电池银浆用有机粘合剂组合物，所述有机粘合剂组合物按质量份组成为：聚酰胺树脂5-13％，松香树脂或酚醛改性萜烯树脂8-25％，有机溶剂65-80％，湿润分散剂0-1％，总量100％；所述有机溶剂包括但不限于丁基卡必醇、DBE、丁基卡必醇醋酸酯中的一种或几种，所述湿润分散剂包括但不限于BYK-163，BYK-P104S，BYK-110中的至少一种。
上述硅太阳能电池银浆用有机粘合剂的制备方法，依据上述有机粘合剂的组成，按以下步骤制备：按质量百分比称取5-13％的聚酰胺树脂、8-25％的松香树脂或酚醛改性萜烯树脂、65-80％的有机溶剂、及0-1％的湿润分散剂投入到反应釜内，使用水浴加热至70-90℃，并使用电动搅拌机搅拌，搅拌速度100-200转/分，当升温之后恒温4-6小时，直至反应釜内树脂全部溶解，各组分呈均一相。冷却之后用丝网过滤，得到晶体硅太阳能电池银浆用有机粘合剂组合物。
本发明有机粘合剂具有良好的分散和包裹作用，可将银粉颗粒均匀的包裹起来，使得导电银浆不容易产生沉淀和氧化。本发明有机粘合剂具有很好的触变性，高触变性能可以保证浆料印刷时候的成形效果，能够尽量保证印刷图形不变形，使印刷图形具有立体感。因此，使用本发明中的有机粘合剂能够使银浆在印刷时有更好的适印性，并且提升银浆线条的高宽比，这样就可以增加银浆线条的电导率，提升银浆的导电性能，从而提高电池的光电转化效率。
具体实施方式
以下通过实施例来说明本发明的具体实施。
利用实施例中的有机粘合剂组合物制备的太阳能电池银浆包含的成分以及各成分的质量配比为：玻璃组合物1-3％；银粉80-85％；上述的有机粘合剂组合物5-8％；溶剂8-12％；无机添加剂1-3％。其中玻璃组合物所包含的成分以及各成分的质量配比又分别为：Bi2O3，65-75％；SiO2，5-10％；B2O3，6-8％；A12O3，0-2％；ZnO，8-10％；无机添加剂包括ZrO2，ZnO，B2O3中的一种或几种；有机溶剂包括丁基卡必醇、DBE、丁基卡必醇醋酸酯中的一种或几种。
实施例1
有机粘合剂组合物的各组分的质量份数为：聚酰胺树脂UNI-REZ26655％，松香树脂AQUATAC 608525％，丁基卡必醇醋酸酯70％。
上述有机粘合剂组合物的制备步骤：将上述组分投入到反应釜内，使用水浴加热至80℃，并使用电动搅拌机搅拌，搅拌速度100转/分，当升温之后恒温4小时，直至反应釜内树脂全部溶解，各组分呈均一相。所得有机粘合剂组合物冷却之后，用400目丝网过滤，得到硅太阳能电池铝浆用有机粘合剂成品。
实施例2
有机粘合剂组合物的各组分的质量份数为：聚酰胺树脂VERSAMID 97211％，酚醛改性萜烯树脂SYLVARES TP 20408％，丁基卡必醇80％，湿润分散剂BYK-P104S 1％。上述有机粘合剂组合物的制备步骤：将各组分投入到反应釜内，使用水浴加热至70℃，并使用电动搅拌机搅拌，搅拌速度150转/分，当升温之后恒温5小时，直至反应釜内树脂全部溶解，各组分呈均一相。所得有机粘合剂组合物冷却之后，用400目丝网过滤，得到硅太阳能电池铝浆用有机粘合剂成品。
实施例3
有机粘合剂组合物的各组分的质量份数为：聚酰胺树脂VERSAMID 94013％，松香树脂SYLVALITE RE 100F 21％，丁基卡必醇65％，湿润分散剂BYK-P1101％。
上述有机粘合剂组合物的制备步骤：将各组分投入到反应釜内，使用水浴加热至85℃，并使用电动搅拌机搅拌，搅拌速度150转/分，当升温之后恒温5小时，直至反应釜内树脂全部溶解，各组分呈均一相。所得有机粘合剂组合物冷却之后，用400目丝网过滤，得到硅太阳能电池铝浆用有机粘合剂成品。
以上所述非本发明全部或唯一的实施方式，本领域普通技术人员通过阅读本发明说明书而对本发明技术方案采取的任何等效的变换，均为本发明的权利要求所涵盖。

Claims (4)

1.一种硅太阳能电池银浆用有机粘合剂组合物，其特征在于：按质量百分比由以下组分组成：5-13％的聚酰胺树脂、8-25％的松香树脂或酚醛改性萜烯树脂、65-80％的有机溶剂、及0-1％的湿润分散剂。
2.根据权利要求1所述的硅太阳能电池银浆用有机粘合剂组合物，其特征在于：所述有机溶剂包括丁基卡必醇、DBE、丁基卡必醇醋酸酯中的一种或几种的混合物。
3.根据权利要求1所述的硅太阳能电池银浆用有机粘合剂组合物，其特征在于：所述湿润分散剂包括毕克分散剂BYK-163、BYK-P104S、BYK-110中的至少一种。
4.一种硅太阳能电池银浆用有机粘合剂组合物的制备方法，其特征在于：按质量百分比称取5-13％的聚酰胺树脂、8-25％的松香树脂或酚醛改性萜烯树脂、65-80％的有机溶剂、及0-1％的湿润分散剂投入到反应釜内，使用水浴加热至70-90℃，并使用电动搅拌机搅拌，搅拌速度100-200转/分，当升温之后恒温4-6小时，直至反应釜内树脂全部溶解，各组分呈均一相，冷却之后用丝网过滤，得到硅太阳能电池银浆用有机粘合剂组合物。
CN201110200620A 2011-07-19 2011-07-19 一种硅太阳能电池银浆用有机粘合剂组合物及制备方法 Pending CN102304287A (zh)