CN102304282A - Flame-retardant silicone rubber and preparation method thereof - Google Patents
Flame-retardant silicone rubber and preparation method thereof Download PDFInfo
- Publication number
- CN102304282A CN102304282A CN201110009695A CN201110009695A CN102304282A CN 102304282 A CN102304282 A CN 102304282A CN 201110009695 A CN201110009695 A CN 201110009695A CN 201110009695 A CN201110009695 A CN 201110009695A CN 102304282 A CN102304282 A CN 102304282A
- Authority
- CN
- China
- Prior art keywords
- silicone rubber
- weight parts
- minutes
- flame
- fire prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses flame-retardant silicone rubber, which consists of polyether diols, isocyanate, an aminosilane crosslinking agent and a flame retardant in a certain ratio. A preparation method for the flame-retardant silicone rubber comprises the following steps of: performing heat treatment on the polyether diols in vacuum for 30 to 60 minutes, exhausting, adding the isocyanate, performing chemical reaction for 60 to 180 minutes; adding the aminosilane crosslinking agent, and continuously reacting for 30 to 60 minutes; and adding the flame retardant, fully dispersing, and dehydrating and extracting. The flame-retardant silicone rubber can be cured at room temperature without being heated, has the advantages of convenience for use, no smell or toxicity, oxidation ageing resistance, light ageing resistance, high temperature and severe cold resistance and the like, has good elasticity, strength, electric insulativity and excellent flame retardancy, and can be widely applied to the fields with high flame-retardant requirements, such as construction joint stopping, cable hole sealing, oil and gas pipeline plugging, telecommunication base stations, steel industry and the like.
Description
Technical field
The present invention relates to a kind of silicone rubber and preparation method thereof, specifically, relate to a kind of fire prevention silicone rubber and preparation method thereof, belong to building material technical field.
Background technology
In numerous synthetic rubber, silicone rubber is outstanding person wherein, and it has tasteless nontoxic, is not afraid of high temperature and the characteristics of resisting severe cold, and " keeping cool ", " remaining calm " when 300 degree Celsius and subzero 90 are spent are not still lost original intensity and elasticity.Silicone rubber also has excellent electric insulating, oxytolerant resistance to deterioration, fast light resistance to deterioration and mildew resistance, chemical stability etc., can be widely used in building fields such as slit shutoff, cable cavern shutoff, oil and gas pipes shutoff, telecomm base station, steel industry.But existing silicone rubber flame retardant properties is not good enough, is not suitable for the higher field of fire protection requirement.
Summary of the invention
The purpose of this invention is to provide a kind of fire prevention silicone rubber and preparation method thereof,, satisfy the demand of existing market to overcome above-mentioned defective of existing in prior technology and deficiency.
For realizing the foregoing invention purpose, the technical scheme that the present invention adopts is following:
Fire prevention silicone rubber provided by the invention, its composition and composition proportioning are following:
Polyether Glycols 10～40 weight parts
Isocyanic ester 5～20 weight parts
Aminosilane linking agent 20～50 weight parts
Fire retardant 30～70 weight parts.
Described isocyanic ester is recommended as tolylene diisocyanate, diphenylmethanediisocyanate, hexa-methylene-1, any one or more than one the combination in the 6-vulcabond.
Described aminosilane linking agent is any one or more than one the combination in γ-An Bingjisanyiyangjiguiwan, phenylamino Union carbide A-162, γ-An Bingjisanjiayangjiguiwan, the diaminoethyl aminopropyl trimethoxysilane.
Described fire retardant is recommended as any one or more than one the combination in ammonium polyphosphate, white lake, magnesium hydroxide, the zinc borate.
The preparation method of fire prevention silicone rubber of the present invention is following:
At first with the thermal treatment 30～60 minutes under vacuum of the polyether Glycols of 10～40 weight parts, the isocyanic ester that the venting back adds 5～20 weight parts carried out chemical reaction 60～180 minutes; The aminosilane linking agent that adds 20～50 weight parts again continues reaction 30～60 minutes; The fire retardant that adds 30～70 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
The thermal treatment temp of said polyether Glycols is 40～105 ℃, and vacuum tightness is-0.1～0.05MPa.
Compared with prior art, the present invention has following advantage:
1, fire prevention silicone rubber provided by the invention is at room temperature curable, need not heating, has advantage easy to use.
2, fire prevention silicone rubber provided by the invention have tasteless nontoxic, oxytolerant resistance to deterioration, fast light resistance to deterioration, high temperature resistance and severe cold, and have good elasticity, intensity and electrical insulating property.
3, fire prevention silicone rubber provided by the invention also has excellent flame-retardant, and flame retardant rating reaches FV-0 level (GB/T 2408).
Embodiment
Below in conjunction with embodiment the present invention is done further detailed, complete explanation, but the present invention is not limited in following embodiment.
Embodiment 1
At first with the polyether Glycols of 10 weight parts-0.005MPa, 65 ℃ of following pre-treatment 30 minutes, the tolylene diisocyanate that the venting back adds 10 weight parts carried out chemical reaction 100 minutes; The phenylamino Union carbide A-162 that adds 20 weight parts again continues reaction 60 minutes; The magnesium hydroxide that adds 50 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 2
At first with the polyether Glycols of 20 weight parts-0.1Mpa, 45 ℃ of following pre-treatment 40 minutes, the diphenylmethanediisocyanate that the venting back adds 5 weight parts carried out chemical reaction 120 minutes; The diaminoethyl aminopropyl trimethoxysilane that adds 30 weight parts again continues reaction 120 minutes; The ammonium polyphosphate that adds 60 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 3
At first with the polyether Glycols of 30 weight parts 0.05Mpa, 105 ℃ of following pre-treatment 50 minutes, the venting back adds the hexa-methylene-1 of 15 weight parts, the 6-vulcabond carried out chemical reaction 180 minutes; The γ-An Bingjisanjiayangjiguiwan that adds 40 weight parts again continues reaction 110 minutes; The white lake that adds 30 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 4
At first with the polyether silicone dibasic alcohol of 40 weight parts-0.07Mpa, 60 ℃ of following pre-treatment 60 minutes, the venting back adds the hexa-methylene-1 of 20 weight parts, the 6-vulcabond carried out chemical reaction 130 minutes; The γ-An Bingjisanyiyangjiguiwan that adds 40 weight parts again continues reaction 140 minutes; The zinc borate that adds 70 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 5
At first with the end hydroxy polyether dibasic alcohol of 15 weight parts-0.08Mpa, 50 ℃ of following pre-treatment 45 minutes, the tolylene diisocyanate that the venting back adds 12 weight parts carried out chemical reaction 140 minutes; The phenylamino Union carbide A-162 that adds 50 weight parts again continues reaction 160 minutes; Add the magnesium hydroxide of 45 weight parts and the ammonium polyphosphate of 15 weight parts then, promptly get described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 6
At first with the polyether Glycols of 25 weight parts 0.01MPa, 85 ℃ of following pre-treatment 35 minutes, the diphenylmethanediisocyanate that the venting back adds 6 weight parts carried out chemical reaction 110 minutes; The γ-An Bingjisanyiyangjiguiwan that adds 40 weight parts again continues reaction 100 minutes; The zinc borate that adds 40 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Embodiment 7
At first with the polyether Glycols of 35 weight parts-0.03pa, 70 ℃ of following pre-treatment 30 minutes, the venting back adds the hexa-methylene-1 of 8 weight parts, the 6-vulcabond carried out chemical reaction 60 minutes; The diaminoethyl aminopropyl trimethoxysilane that adds 30 weight parts again continues reaction 180 minutes; The ammonium polyphosphate that adds 30 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
Fire prevention silicone rubber of the present invention is seen shown in the table 1 by the The performance test results that GB/T5574-2008 and GB/T2408-1996 carry out.
The The performance test results of table 1 fire prevention silicone rubber of the present invention
| Test item | Test result | Test item | Test result |
| Outward appearance | The black Hookean body | Thermal conductivity (J/msK) | 5.1×10 -4 |
| Proportion (g/cm 3) | 1.40 | Volume resistivity (Ω cm) | 3.4×10 13 |
| Hardness (Shao Shi A) | 40 | Shearing resistance (MPa) | 0.49 |
| Elongation at break (%) | 200 | Combustionproperty | Meet the FV-0 rank |
The performance test results by table 1 is visible: fire prevention silicone rubber proportion provided by the invention is lighter; Favorable elasticity and, heat insulation, insulation and flame retardant properties are arranged, can be widely used in building the higher fields of fire protection requirement such as slit shutoff, cable cavern shutoff, oil and gas pipes shutoff, telecomm base station, steel industry.
Claims (6)
1. a fire prevention silicone rubber is characterized in that, its composition and composition proportioning are following:
Polyether Glycols 10～40 weight parts
Isocyanic ester 5～20 weight parts
Aminosilane linking agent 20～50 weight parts
Fire retardant 30～70 weight parts.
2. fire prevention silicone rubber according to claim 1 is characterized in that: described isocyanic ester is tolylene diisocyanate, diphenylmethanediisocyanate, hexa-methylene-1, any one or more than one the combination in the 6-vulcabond.
3. fire prevention silicone rubber according to claim 1 is characterized in that: described aminosilane linking agent is any one or more than one the combination in γ-An Bingjisanyiyangjiguiwan, phenylamino Union carbide A-162, γ-An Bingjisanjiayangjiguiwan, the diaminoethyl aminopropyl trimethoxysilane.
4. fire prevention silicone rubber according to claim 1 is characterized in that: described fire retardant is any one or more than one the combination in ammonium polyphosphate, white lake, magnesium hydroxide, the zinc borate.
5. the preparation method of the described fire prevention silicone rubber of claim 1; It is characterized in that: be at first with the thermal treatment 30～60 minutes under vacuum of the polyether Glycols of 10～40 weight parts, the isocyanic ester that the venting back adds 5～20 weight parts carried out chemical reaction 60～180 minutes; The aminosilane linking agent that adds 20～50 weight parts again continues reaction 30～60 minutes; The fire retardant that adds 30～70 weight parts then promptly gets described fire prevention silicone rubber through the dehydration extraction after fully disperseing.
6. the preparation method of fire prevention silicone rubber according to claim 5 is characterized in that: the thermal treatment temp of said polyether Glycols is 40～105 ℃, and vacuum tightness is-0.1～0.05MPa.