CN102286862A - Sample duplication process of polyster fiber dyeing - Google Patents
Sample duplication process of polyster fiber dyeing Download PDFInfo
- Publication number
- CN102286862A CN102286862A CN2011102247490A CN201110224749A CN102286862A CN 102286862 A CN102286862 A CN 102286862A CN 2011102247490 A CN2011102247490 A CN 2011102247490A CN 201110224749 A CN201110224749 A CN 201110224749A CN 102286862 A CN102286862 A CN 102286862A
- Authority
- CN
- China
- Prior art keywords
- heating
- sample
- cup
- dyeing
- dye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sample duplication process of polyster fiber dyeing, which comprises the following steps: (1) dropping dye into a dyeing cup according to a formula, and adding an additive and a weighed fabric sample according to a bath ratio; (2) putting the dyeing cup in a sample jar at the pre-set temperature, and heating the dyeing cup; (3) heating the dyeing cup to 80 DEG C and then insulating for 2 minutes, then insulating for 5 minutes after heating to 110 DEG C, and finally insulating for 30-40 minutes after heating to 130 DEG C; and (4) taking the fabric sample in the heated dyeing cup out of the jar and performing aftertreatment. By the sample duplication process of polyster fiber dyeing in the invention, accurate color of mass goods in plant can be ensured, and the sample duplication time is effectively accelerated, thereby reducing cost and increasing the enterprise income to a certain degree.
Description
Technical field
The present invention relates to a kind of duplicate sample technology of polyster fibre dyeing.
Background technology
Terylene is that technology is the simplest a kind of in the three big synthetic fiber, and price is also relatively more cheap, and adding it has durable, good springiness, not yielding, corrosion-resistant, insulation, characteristics such as well-pressed, quick-drying washable, by people are liked.But along with the raising of people's living standard, people are more and more higher to the requirement of lining, except requiring to have the functional requirement of comfortableness, also require lining to have diversity, aesthetic property.Functional and perfect adaptation aesthetic property is the ultimate pursuit of weaving face fabric industry.
Before dyeing is handled in the weaving face fabric industry at present, all need to carry out duplicate sample.Specifically, be exactly that the client takes a sample to give manufacturer, require manufacturer to do according to sample, but manufacturer in order to be afraid of because technological level, quality etc. can not be in full accord with the sample that the other side provides,, the sample that manufacturer provides according to the client confirms Here it is duplicate sample so duplicating a sample to the other side.
The dyestuff of confirming with the embryo cloth of customer order bulk production and client carries out duplicate sample with reference to the manufacturing condition in workshop, and the color that the contrast client confirms finds a correct dye formulation to offer the workshop to carry out bulk production production.But existing duplicate sample technology generally will be carried out 4-10 time adjustment, and duplicate sample technology wants each 8-12 hour time to go to finish, like this time of duplicate sample longer, and cost height.
Summary of the invention
The object of the present invention is to provide a kind of duplicate sample technology of polyster fibre dyeing, can guarantee the accurate of workshop bulk production color, effectively carried soon the time of duplicate sample, thereby reduced cost to a certain extent, increased the income of enterprise.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of duplicate sample technology of polyster fibre dyeing is provided, has comprised the steps:
(1) dying a good colourant in the cup according to prescription earlier, according to bath raio adding additive and the sample cloth that weighs up;
(2) under preset temperature, will dye cup and put in the sample cylinder, will dye cup and heat;
(3) at first dye the cup the temperature of heating rise to 80 ℃ after the insulation 2 minutes, after the temperature of heating then rises to 110 ℃ the insulation 5 minutes, after the temperature of heating at last rises to 130 ℃ the insulation 30-40 minute;
(4) will be incubated sample cloth in the after stain cup goes out cylinder and does post processing.
In a preferred embodiment of the present invention, described additive is water, wash levelling agent, acetic acid, sodium acetate.
In a preferred embodiment of the present invention, describedly will dye cup to put into the preset temperature of heating in the sample cylinder be 35 ℃.
In a preferred embodiment of the present invention, described will to dye the speed of heating put into when heating to 80 ℃ in the sample cylinder of cup be 3 ℃ of per minutes.
In a preferred embodiment of the present invention, described will to dye the speed of heating put into when heating to 110 ℃ in the sample cylinder of cup be 1.5 ℃ of per minutes.
In a preferred embodiment of the present invention, described will to dye the speed of heating put into when heating to 80 ℃ in the sample cylinder of cup be 2 ℃ of per minutes.
The duplicate sample technology of polyster fibre dyeing of the present invention can guarantee the accurate of workshop bulk production color, has effectively carried soon the time of duplicate sample, thereby has reduced cost to a certain extent, has increased the income of enterprise.
Description of drawings
Accompanying drawing 1 is washed the flow chart of duplicate sample technology one preferred embodiment of polyster fibre dyeing for the present invention.
The specific embodiment
Below in conjunction with accompanying drawing preferred embodiment of the present invention is described in detail, thereby protection scope of the present invention is made more explicit defining so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that.
Please refer to Fig. 1, Fig. 1 is the flow chart of duplicate sample technology one preferred embodiment of polyster fibre dyeing of the present invention.The duplicate sample technology that this washs polyster fibre dyeing comprises the steps:
(1) dying a good colourant in the cup according to prescription earlier, according to bath raio adding additive and the sample cloth that weighs up;
(2) under preset temperature, will dye cup and put in the sample cylinder, will dye cup and heat;
(3) at first dye the cup the temperature of heating rise to 80 ℃ after the insulation 2 minutes, after the temperature of heating then rises to 110 ℃ the insulation 5 minutes, after the temperature of heating at last rises to 130 ℃ the insulation 30-40 minute;
(4) will be incubated sample cloth in the after stain cup goes out cylinder and does post processing.
Additive in the above-mentioned technology is water, wash levelling agent, acetic acid, sodium acetate.To dye cup, to put into the preset temperature of heating in the sample cylinder be 35 ℃.To dye glass speed of putting into when heating to 80 ℃ in the sample cylinder of heating is 3 ℃ of per minutes; To dye glass speed of putting into when heating to 110 ℃ in the sample cylinder of heating is 1.5 ℃ of per minutes; To dye glass speed of putting into when heating to 80 ℃ in the sample cylinder of heating is 2 ℃ of per minutes.
What a the duplicate sample technology of a kind of polyster fibre dyeing of announcement of the present invention prepared earlier and dyed cup, adds dyestuff by prescription in dying cup, according to bath raio add entry, wash levelling agent, acetic acid, sodium acetate, put into the cloth specimen that weighs up at last.Preset temperature be 35 ℃ will dye down that cup is put in the sample cylinder and be warming up to 80 ℃ with the speed of 3 ℃ of per minutes after insulation 2 minutes, insulation is 5 minutes after being warming up to 110 ℃ with the speed of 1.5 ℃ of per minutes again, be warming up to 130 ℃ with the speed of 2 ℃ of per minutes again after insulation go out cylinder after 30-40 minute and do post processing.Duplicate sample technology of washing polyster fibre dyeing of the present invention can guarantee the accurate of workshop bulk production color, has effectively carried soon the time of duplicate sample, thereby has reduced cost to a certain extent, has increased the income of enterprise.
The specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the disclosed technical scope of the present invention, and variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (6)
1. the duplicate sample technology of a polyster fibre dyeing is characterized in that, comprises the steps:
(1) dying a good colourant in the cup according to prescription earlier, according to bath raio adding additive and the sample cloth that weighs up;
(2) under preset temperature, will dye cup and put in the sample cylinder, will dye cup and heat;
(3) at first dye the cup the temperature of heating rise to 80 ℃ after the insulation 2 minutes, after the temperature of heating then rises to 110 ℃ the insulation 5 minutes, after the temperature of heating at last rises to 130 ℃ the insulation 30-40 minute;
(4) will be incubated sample cloth in the after stain cup goes out cylinder and does post processing.
2. the duplicate sample technology of polyster fibre according to claim 1 dyeing is characterized in that, described additive is water, wash levelling agent, acetic acid, sodium acetate.
3. the duplicate sample technology of polyster fibre according to claim 1 dyeing is characterized in that, describedly will dye cup to put into the preset temperature of heating in the sample cylinder be 35 ℃.
4. the duplicate sample technology of polyster fibre according to claim 1 dyeing is characterized in that, described will to dye the speed of heating that cup puts into when heating to 80 ℃ in the sample cylinder be 3 ℃ of per minutes.
5. the duplicate sample technology of polyster fibre according to claim 1 dyeing is characterized in that, described will to dye the speed of heating that cup puts into when heating to 110 ℃ in the sample cylinder be 1.5 ℃ of per minutes.
6. the duplicate sample technology of polyster fibre according to claim 1 dyeing is characterized in that, described will to dye the speed of heating that cup puts into when heating to 80 ℃ in the sample cylinder be 2 ℃ of per minutes.