CN102286245A - 塑胶地板弹性层 - Google Patents
塑胶地板弹性层 Download PDFInfo
- Publication number
- CN102286245A CN102286245A CN2011102341793A CN201110234179A CN102286245A CN 102286245 A CN102286245 A CN 102286245A CN 2011102341793 A CN2011102341793 A CN 2011102341793A CN 201110234179 A CN201110234179 A CN 201110234179A CN 102286245 A CN102286245 A CN 102286245A
- Authority
- CN
- China
- Prior art keywords
- elastic layer
- raw material
- component raw
- plastic floor
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种塑胶地板弹性层,由下列原料制备而成:第一组分原料(kg):聚醚多元醇240:850-950;聚醚多元醇330:250-350;滑石粉:2100-2500;色浆:14-18;甲苯:220-240;第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:100-110;二月硅酸二丁基锡:0.717;白炭黑:22;加工步骤为:将第一组分原料投入反应罐内搅拌、升温至130℃脱水;保温1小时;93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,85-90℃保温3.5小时,降温至50℃出料。本发明绿色环保,无毒无害,使塑胶地板硬度弹性适当、性能稳定。
Description
技术领域
本发明涉及一种塑胶地板弹性层
背景技术
塑胶地板具有一定的弹性、抗紫外线和耐老化能力,是国际上公认的最佳运动场地坪材料。
如塑胶跑道的优点有:
全天候使用:任何季节及温差,均能维持高水准的品质,雨后更能立即使用,增加利用时间,提高场地使用率。
弹性:具有适度的弹性及反弹力,可减少体力的消耗,增进竞赛成绩。
冲击力吸收:适度吸收脚部冲击力,减少运动伤害,长期练习及比赛均适宜。
耐候性:不会因紫外线、臭氧、酸雨的污染而褪色、粉化或软化,并能长期保持
其鲜艳的色彩。
耐磨性:耐磨耗性小于2.5%,满足各级学校长时间,高使用频率的需要。
耐压缩性:不会因为田径器材的重压而无法恢复弹性。
抗钉力:在受力最大使用最频繁的百米起跑点,也不会受到钉鞋或起跑架破坏。
耐冲击性:具有强韧的弹性层及缓冲层,可吸收强劲的冲击,表面不会受损。
平坦性:施工时使用自流平材料,表面平坦,能符合特别平坦的比赛场地要求。
粘接性:特殊施工处理,粘接力强,可压制水份上升,无起泡、剥离等现象。
安全性:可防止跌倒所发生的运动伤害。
经济:维护方便、节省管理费用。
色彩:专用高弹性EPDM和PU颗粒,表面颜色柔和,颗粒状表层,防止刺眼
光线的反射,美观耐久,并可采用多色彩搭配。
目前体操场馆用地垫多采用塑胶地垫,这类地垫大多数是PVC材料或PE高发泡聚乙烯材料制成。PVC(即聚氯乙烯)地垫,一般由软质的PVC制成,软PVC具有柔韧性,但手感粘,用过一段时候后在屈折处会出现白化现象。尤其是体操运动员在练习的时候,经常会对地面有较大力量的冲击,使用这类地垫表面出现折痕。PE(即高发泡聚乙烯)材料的地垫比较软,摸起来有蜡质感,耐磨。
还有一些地垫是采用EVA树脂制成,它是乙烯-醋酸乙烯共聚物,一般醋酸乙烯(VA)含量在5%~40%。与聚乙烯相比,EVA由于在分子链中引入了醋酸乙烯单体,从而降低了高结晶度,提高了柔韧性、抗冲击性、填料相溶性和热密封性能,被广泛应用于发泡材料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。它是一种比较常见的化工材料,通常经过一次发泡有一定的缓冲作用。
如何提高塑胶地板的安全性和弹性,开发出健康环保的塑胶地板,是塑胶地板业的一个新的课题。
发明内容
本发明需要解决的技术问题就在于克服现有技术的缺陷,提供一种塑胶地板弹性层,它绿色环保,无毒无害,施工方便,使塑胶地板抗压强度高、平整度好、硬度弹性适当、性能稳定,用于塑胶跑道等有利于运动员速度的发挥和技术的提高。
为解决上述问题,本发明采用如下技术方案:
本发明提供了一种塑胶地板弹性层,所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:850-950;聚醚多元醇330:250-350;滑石粉:2100-2500;色浆:14-18;甲苯:220-240;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:100-110;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温至130℃脱水;保温1小时;93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
优选的,本发明所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:890;聚醚多元醇330:300;滑石粉:2300;色浆:16;甲苯:230;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:104;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温脱水,升温温度为130℃;保温1小时,93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
本发明中,聚醚多元醇为无色至淡黄色粘稠液体,用作聚氨酯弹性体、涂料、黏合剂、涂饰剂、密封胶,化学合成中间体。用于本发明弹性层的配方中,使本发明塑胶地板具有抗压强度高、平整度好、硬度弹性适当、性能稳定的特性,有利于运动员速度的发挥和技术的提高。
本发明施工快速、简便,可以全天候使用,保养、维修简便,耐用寿命长,有助于实现最佳经济效益。
本发明做作的塑胶地板弹性适中稳定,弹性层提供绝对的安全性、回弹性,使地板更加具有附着力,令鞋底时刻紧贴地面,防滑且能随心所欲传递强劲动力。良好的弹性对运动员的腿部关节能起到很好的保护作用,有效地避免了运动伤害,耐磨性强防滑性更佳,具有稳定场地尺寸、延长使用寿命的作用,使地板永不收缩,性能更加稳定,能更好地发挥运动员的水平。
本发明制造的动地板运动特征极佳,运动系数为最佳值,使运动员的能力尽情展现,为起动、蹬跳、滑步、制动等各种动作提供有力保障。
本发明的优点有:
1、绿色环保,无毒无害,无放射性污染,属绿色环保产品,可资源回收利用。
2、耐磨,高分子耐磨层使用寿命长。因为超级的耐磨性,所以在人流量较大的商场、超市、交通工具等,塑胶地板越来越受到欢迎。
3.防滑,止滑性强,遇水发涩,可解除老人,儿童的后顾之忧。塑胶地板质地较软所以弹性很好,在重物的冲击下有着良好的弹性恢复,所以能大大减少人员的滑到摔伤,同时对于重物冲击破坏也有很强的弹性恢复。不会造成损坏。
4.质量轻,轻型建材,能大幅度减轻楼层承重。
5.花色新颖,多种花色可供选择,色彩绚丽,自然逼真,任意拼组花色造型,突出个性色彩。
6.吸音降噪,,不但不产生噪音,而且还消除杂音,达到静音效果,能创造一个舒适的工作生活环境。
7.安全性高,绝缘,阻燃,耐腐蚀,耐酸碱,表面无异状。防火:塑胶地板可以达到b1级防火,这也是建材防火的最高标准。
8.防潮,遇水不变形。
9.脚感舒适,有弹性。塑胶地板表层的耐磨层有特殊的防滑性,而且与普通的地面材料相比,塑胶地板在粘水的情况下脚感更涩,更不容易滑到。
10.抗冲击力,有韧性使用期长。
11.施工方便快捷,缩短工期。
12、打扫方便。此外墙脚踢脚线也可以用同该地板滚边,方便墙角卫生打扫,免打蜡,减少后期维护成本。
具体实施方式
实施例1
本发明所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:890;聚醚多元醇330:300;滑石粉:2300;色浆:16;甲苯:230;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:104;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温脱水,升温温度为130℃;保温1小时,93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
实施例2
本发明提供了一种塑胶地板弹性层,所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:850;聚醚多元醇330:350;滑石粉:2100;色浆:18;甲苯:220;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:100;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温至130℃脱水;保温1小时;93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
实施例3
本发明提供了一种塑胶地板弹性层,所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:950;聚醚多元醇330:250;滑石粉:2500;色浆:14;甲苯:240;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:110;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温至130℃脱水;保温1小时;93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
最后应说明的是:显然,上述实施例仅仅是为清楚地说明本发明所作的举例,而并非对实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明的保护范围之中。
Claims (2)
1.一种塑胶地板弹性层,其特征在于,所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:850-950;聚醚多元醇330:250-350;滑石粉:2100-2500;色浆:14-18;甲苯:220-240;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:100-110;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温至130℃脱水;保温1小时;93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。
2.如权利要求1所述的塑胶地板弹性层,其特征在于,所述塑胶地板弹性层由下列原料制备而成:
第一组分原料(kg):聚醚多元醇240:890;聚醚多元醇330:300;滑石粉:2300;色浆:16;甲苯:230;
第二组分原料(kg):二苯基二氯硅烷:0.484;MDI:104;二月硅酸二丁基锡:0.717;白炭黑:22;
所述弹性层加工步骤为:将第一组分原料投入反应罐内搅拌、升温脱水,升温温度为130℃;保温1小时,93℃先加入二苯基二氯硅烷,在90℃时,再加入MDI,90℃以下时加入二月硅酸二丁基锡,在85-90℃进行保温3.5小时,降温至50℃出料,得弹性层涂料。