CN102285296A - Ceramic perfume handicraft and manufacturing method thereof - Google Patents
Ceramic perfume handicraft and manufacturing method thereof Download PDFInfo
- Publication number
- CN102285296A CN102285296A CN201110191235XA CN201110191235A CN102285296A CN 102285296 A CN102285296 A CN 102285296A CN 201110191235X A CN201110191235X A CN 201110191235XA CN 201110191235 A CN201110191235 A CN 201110191235A CN 102285296 A CN102285296 A CN 102285296A
- Authority
- CN
- China
- Prior art keywords
- perfume
- main body
- ceramic
- ceramic main
- handicraft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramic perfume handicraft and a manufacturing method thereof. The method comprises the following specific steps of: molding a ceramic body, wherein the water permeability of the ceramic body is required to be controlled to be 0.01-0.10 percent; glazing the ceramic body; and finally, fully infiltrating perfume into micropores of the ceramic body. Since the perfume is infiltrated into the body of the ceramic handicraft by using porosity of the ceramic handicraft, a container for holding the perfume is not required to be specially arranged, and the set position of an opening part of the container is not required to be considered; and thus, a ceramic product has a more random and flexible shape, and the creative idea is not limited.
Description
Technical field
A kind of perfume handicraft of the present invention is meant a kind of ceramic perfume handicraft and manufacture method thereof especially.
Background technology
At present, ceramics that can be scentetd mostly, mainly be that a container that is used for splendid attire perfume is set in ceramics, and the peristome of this container is opened in the outer surface of this handicraft, stopper by opening of container or other structure and scentetd to the outside, and the moulding that cooperates handicraft itself is to reach the effect that handicraft is furnished that causes.
The ceramics that adopts said structure must be considered the position that is provided with of this opening of container when shape-designing, therefore limited the moulding intention of ceramics greatly.
Summary of the invention
The purpose of this invention is to provide a kind of ceramic perfume handicraft and manufacture method thereof, need not the built-in container that is used for splendid attire perfume in the ceramics, need not to consider the position that is provided with of opening of container when moulding, thereby make the moulding of ceramics more flexible, intention is unrestricted.
For achieving the above object, solution of the present invention is:
A kind of ceramic perfume handicraft, wherein the ceramic main body of this ceramics is to be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% by fineness, fires to form under the temperature of 1000 ° of C-1800 ° of C; Unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%, this is fired, and infiltration has perfume in the micropore of the ceramic main body that forms.
A kind of manufacture method of ceramic perfume handicraft comprises following several steps:
Step 1, be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% with fineness, be fired into the ceramic main body blank under the temperature of 1000 ° of C-1800 ° of C, its unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%;
Step 2, with this ceramic main body blank glazing;
In step 3, the ceramic main body immersion perfume pond, perfume is infiltrated through in the micropore of ceramic main body fully with first-class glaze;
Step 4, will fully permeate and have the ceramic main body of perfume normal temperature to dry, or under 30 ° C to 80 ° C temperature, dry.
In step 3, there is the ceramic main body of perfume further to place 0.100mpa infiltration to the pressure environment between the 0.852mpa.
A kind of manufacture method of ceramic perfume handicraft comprises following several steps:
Step 1, be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% with fineness, be fired into the ceramic main body blank under the temperature of 1000 ° of C-1800 ° of C, its unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%;
Step 2, with this ceramic main body blank glazing;
Step 3, the ceramic main body that glazing is good are placed in the secret room of vacuum, and perfume is discharged in this secret room, and perfume is infiltrated through in the micropore of ceramic main body fully;
Step 4, will fully permeate and have the ceramic main body of perfume normal temperature to dry, or under 30 ° C to 80 ° C temperature, dry.
Described vacuum secret room is pressurization vacuum secret room.
Above-mentioned step 4 is directly to have the ceramic main body of perfume to approach to execute permeable wax or the silica gel that goes out fragrance of one deck outward in abundant infiltration.
The present invention utilizes the gas porosity of ceramics itself and with perfume infiltration wherein, the position that is provided with that need not to be provided for the container of splendid attire perfume specially and consider opening of container, the moulding that makes ceramic product more arbitrarily, flexibly, intention is unrestricted.
The specific embodiment
The present invention has disclosed a kind of ceramic perfume handicraft, wherein the ceramic main body of this ceramics is to be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% by fineness, fires to form under the temperature of 1000 ° of C-1800 ° of C; Unit volume proportion is 2.0g-4.0g/cm
3The water permeability is 0.01%-0.10%, and this is fired, and infiltration has perfume in the micropore of the ceramic main body that forms.
A kind of manufacture method of ceramic perfume handicraft specifically comprises following step:
Step 1, be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% with fineness, be fired into the ceramic main body blank under the temperature of 1000 ° of C-1800 ° of C, its unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%;
Step 2, with this ceramic main body blank glazing;
In step 3, the ceramic main body immersion perfume pond, perfume is infiltrated through in the micropore of ceramic main body fully with first-class glaze;
Step 4, will fully permeate and have the ceramic main body of perfume normal temperature to dry, or under 30 ° C to 80 ° C temperature, dry.
Can also in above-mentioned steps 3, further infiltration there be the ceramic main body of perfume to place 0.100mpa to the pressure environment between the 0.852mpa.
The mode of described step 3 ceramic main body infiltration perfume also has:
The ceramic main body that glazing is good is placed in the secret room of vacuum, perfume is discharged in this secret room, perfume is infiltrated through in the micropore of ceramic main body fully, this vacuum secret room also can be pressurization vacuum secret room.
Described step 4 can also be in abundant infiltration thin permeable wax or the silica gel that goes out fragrance of one deck of executing of the ceramic main body of perfume to be arranged outward, with the prolongation dispensation of fragrance time.
The present invention utilizes the gas porosity of ceramics itself and with perfume infiltration wherein, the position that is provided with that need not to be provided for the container of splendid attire perfume specially and consider opening of container, the moulding that makes ceramic product more arbitrarily, flexibly, intention is unrestricted.
The above, it only is preferred embodiment of the present invention, be not that technical scope of the present invention is imposed any restrictions, so every foundation technical spirit of the present invention all still belongs in the scope of technical solution of the present invention any trickle modification, equivalent variations and modification that above embodiment did.
Claims (6)
1. ceramic perfume handicraft, wherein the ceramic main body of this ceramics is to be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% by fineness, fires to form under the temperature of 1000 ° of C-1800 ° of C; Unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%, this is fired, and infiltration has perfume in the micropore of the ceramic main body that forms.
2. the manufacture method of a kind of ceramic perfume handicraft according to claim 1 is characterized in that comprising following several steps:
Step 1, be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% with fineness, be fired into the ceramic main body blank under the temperature of 1000 ° of C-1800 ° of C, its unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%;
Step 2, with this ceramic main body blank glazing;
In step 3, the ceramic main body immersion perfume pond, perfume is infiltrated through in the micropore of ceramic main body fully with first-class glaze;
Step 4, will fully permeate and have the ceramic main body of perfume normal temperature to dry, or under 30 ° C to 80 ° C temperature, dry.
3. the manufacture method of a kind of ceramic perfume handicraft according to claim 2 is characterized in that: in step 3, have the ceramic main body of perfume further to place 0.100mpa to the pressure environment between the 0.852mpa infiltration.
4. the manufacture method of a kind of ceramic perfume handicraft according to claim 1 is characterized in that comprising following several steps:
Step 1, be quartzy 30-60% of 325 purpose kaolin 20-60%, 220 purposes and 200 purpose feldspar 10-20% with fineness, be fired into the ceramic main body blank under the temperature of 1000 ° of C-1800 ° of C, its unit volume proportion is 2.0g-4.0g/cm
3, the water permeability is 0.01%-0.10%;
Step 2, with this ceramic main body blank glazing;
Step 3, the ceramic main body that glazing is good are placed in the secret room of vacuum, and perfume is discharged in this secret room, and perfume is infiltrated through in the micropore of ceramic main body fully;
Step 4, will fully permeate and have the ceramic main body of perfume normal temperature to dry, or under 30 ° C to 80 ° C temperature, dry.
5. the manufacture method of a kind of ceramic perfume handicraft according to claim 3 is characterized in that: described vacuum secret room is pressurization vacuum secret room.
6. according to the manufacture method of claim 2,4 described any ceramic perfume handicrafts, it is characterized in that: above-mentioned step 4 is directly to have the ceramic main body of perfume to approach to execute permeable wax or the silica gel that goes out fragrance of one deck outward in abundant infiltration.