CN102277523A - Fe-X-C crystal grain refiner and preparation method thereof - Google Patents
Fe-X-C crystal grain refiner and preparation method thereof Download PDFInfo
- Publication number
- CN102277523A CN102277523A CN2011101611422A CN201110161142A CN102277523A CN 102277523 A CN102277523 A CN 102277523A CN 2011101611422 A CN2011101611422 A CN 2011101611422A CN 201110161142 A CN201110161142 A CN 201110161142A CN 102277523 A CN102277523 A CN 102277523A
- Authority
- CN
- China
- Prior art keywords
- grain
- melt
- refining agent
- crystal grain
- grain refiner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an Fe-X-C crystal grain refiner and a preparation method thereof, belonging to the technical field of metallic materials. The Fe-X-C crystal grain refiner comprises the following components in percentage by weight: 35-99.4% of Fe, 0.1-15% of C and 0.5-50% of X, wherein X is one or a plurality of Ti, V and Nb. The preparation method of the Fe-X-C crystal grain refiner comprises the following steps: 1. mixing Fe-C alloy with metal X, or mixing pure iron and graphite with the metal X, and then melting a mixture in an intermediate frequency induction furnace in vacuum, wherein in the mixture, Fe accounts for 35-99.4%, C accounts for 0.1-15%, and Fe is balance; 2. when the temperature of a melt is 1550-1650DEG C, introducing argon into the melt for 10s-3h; and 3. stopping introducing the argon, and carrying out outage to obtain the Fe-X-C crystal grain refiner. The Fe-X-C crystal grain refiner is simple to prepare. When the crystal grain refiner is added into a steel melt, steel crystal grains can be refined, and thus the equiaxed crystal zone ratio of billet casting state structure is improved to be above 60%.
Description
The present invention by number of patent application is: 200910307631.7, name of patent application is: " Fe-X-C grain-refining agent and preparation method thereof ", patent application is artificial: Shanghai Communications University, Baoshan Iron ﹠ Steel Co., Ltd, patent application day is: the patent on September 24th, 2009 is divided an application.
Technical field
The present invention relates to grain-refining agent of a kind of metallic substance technical field and preparation method thereof, specifically is a kind of Fe-X-C grain-refining agent and preparation method thereof.
Background technology
The weave construction of steel determines its performance, especially intensity and toughness.Crystal grain is thin more, and the intensity of steel and toughness are just high more.In the casting process, if only from exterior cooling, the speed of cooling of generous inside steel billet is slow, and the forming core core is few, with mainly growing in the mode of column crystal, causes defectives such as crystal grain is thick, center segregation, is easy to generate limit portion crackle when subsequent hot rolled.The key that addresses this problem is molten steel to be carried out forming core handle, and enlarges strand equiax crystal district ratio, crystal grain thinning.Controlling metal solidification texture by the interpolation nucleating agent is the crystal fining method of using always, and purpose is the formation that reduces dendrite interval, promotion equiax crystal, the growth that suppresses column crystal.The forming core core mainly contains two kinds of sources: external forming core particle and Nei Sheng forming core particle.Wherein, mainly be to point in the melt to add grain-refining agent by increasing the method that external forming core particle reaches the refinement purpose.
Find through literature search prior art, kingdom holds, Fang Keming, Wang Tieming etc. " add the research of the super particulate of titanium nitride in the high temperature pure iron melt "; steel vanadium titanium; 2006,27 (2): 21~25 " in following content has been described: adopt in the pure iron melt, to add TiN particulate method refined cast structure.But, because the TiN particle is more tiny, be difficult to it be added in the melt with the method for winding-up, hello silk, and poly-partially easily.The technical problem to be solved in the present invention is: a kind of grain-refining agent of new steel is provided, and this grain-refining agent preparation is simple, easy to use.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of Fe-X-C grain-refining agent and preparation method thereof is provided.Grain-refining agent preparation of the present invention is simple; In steel melt, add the Fe-X-C grain-refining agent, but the crystal grain of refinement steel is brought up to more than 60% steel billet as-cast structure equiax crystal district ratio.
The present invention relates to a kind of Fe-X-C grain-refining agent, its component and mass percent are: Fe 35~99.4%, and C 0.1~15%, and X 0.5~50%; Wherein, X is Ti, one or more among V and the Nb.
Density 〉=10000 of XC in the described Fe-X-C grain-refining agent/mm
3
Described Fe-X-C grain-refining agent, its component and mass percent are: Fe 99.4%, and C 0.1%, and Ti 0.5%.
Described Fe-X-C grain-refining agent, its component and mass percent are: Fe 35%, and C 15%, and Ti 0.5%, and Nb 25%.
Described Fe-X-C grain-refining agent, its component and mass percent are: Fe 67.5%, and C 7.5%, and Ti 10%, and Nb 10%, and V 5%.
The invention still further relates to a kind of preparation method of above-mentioned Fe-X-C grain-refining agent, comprise the steps:
Step 1 is got the Fe-C alloy, mixes with metal X;
Perhaps, get pure iron and graphite, mix with metal X afterwards;
Afterwards mixture is frequently felt in a vacuum melt in the stove melt;
Step 2 when the temperature of melt is 1550~1650 ℃, feeds argon gas in melt, the time is 10s~3h;
In the step 2, described feeding argon gas, flow are 100~1000ml/min.
The present invention will contain Fe, and the mixture of C and X is put into the fusing of intermediate frequency vacuum induction furnace crucible internal heating, and ventpipe is inserted in the alloy melt, after ventilation reaches the scheduled time, extract ventpipe out, and the outage casting promptly obtains the grain-refining agent of steel.For preventing alloy oxidization burning loss in fusion process, the melting of alloy is carried out under vacuum, adopt the stirring of the method realization of insertion gas blow pipe blowing argon gas in melt simultaneously, improve the disperse in grain-refining agent of TiC, VC, the NbC second phase particle and distribute melt.
Compared with prior art, the present invention has following beneficial effect: grain-refining agent preparation of the present invention is simple, with low cost; The second phase pellet density reaches 10000/mm at least in the Fe-X-C grain-refining agent that the present invention prepares; In steel melt, add the Fe-X-C grain-refining agent, but the crystal grain of refinement steel is brought up to more than 60% steel billet as-cast structure equiax crystal district ratio.
Description of drawings
Fig. 1 is a Fe-X-C grain-refining agent preparation facilities synoptic diagram;
Fig. 2 is not for adding the 409L ferritic stainless steel macrograph figure of fining agent;
Fig. 3 is 409L ferritic stainless steel macrograph figure behind the interpolation 2wt% fining agent.
Embodiment
Following example will the invention will be further described in conjunction with the accompanying drawings.Present embodiment has provided detailed embodiment and process being to implement under the prerequisite with the technical solution of the present invention, but protection scope of the present invention is not limited to following embodiment.The experimental technique of unreceipted actual conditions in the following example, usually according to normal condition, or the condition of advising according to manufacturer.
Fig. 1 is a Fe-X-C grain-refining agent preparation facilities synoptic diagram, and this device comprises: ball valve 1, argon flow amount meter 2, argon bottle 3, ruhmkorff coil 4, temperature measurer 5, crucible 6, thermopair 7, ventpipe 9, its Center Vent tube 9 is communicated with argon bottle 3, ball valve 1 is positioned on the ventpipe 9 with argon flow amount meter 2, temperature measurer 5 links to each other with thermopair 7, and ventpipe 9 and thermopair 7 extend in the crucible 6, and ruhmkorff coil 4 is positioned at around the crucible 6.To contain Fe, the mixture of C and X is put into the fusing of intermediate frequency vacuum induction furnace crucible 6 internal heating, and described X is one or more among Ti, V or the Nb.Adopt thermocouple temperature measuring apparatus 5,7 on-line measurement temperature, make melt temperature remain on 1550~1650 ℃; Open ball valve 1, regulate the air-flow that argon flow amount meter 2 makes argon bottle 3 outputs; Ventpipe 9 is inserted in the alloy melt 10; After ventilation reaches 10s~3h, extract ventpipe 9 out, the outage casting promptly obtains the grain-refining agent of steel.
Table 1
Embodiment 1
As shown in table 1, the present embodiment preparation process comprises the steps:
Step 1 is mixed the Fe-C alloy with metal Ti, with mixture frequently melt in the induction furnace in a vacuum melt; Described mixing need make the mass percent of each element in the mixture that obtains be: Fe 99.4%, and Ti 0.5%, and C 0.1%;
Step 2 when the temperature of melt is 1650 ℃, feeds argon gas in melt, the flow of argon gas is 1000ml/min, and the time is 3h;
Present embodiment prepares that the TiC particle size mainly concentrates on 0.5~5 μ m in the gained grain-refining agent, and TiC density is 10
4Individual/mm
3
With the 409L ferritic stainless steel in a vacuum frequently behind the induction furnace internal heating to 1530 ℃, the molten steel casting.Do not add fining agent the 409L steel macrostructure as shown in Figure 2, equiax crystal district grain-size: 2000 microns, equiax crystal district ratio 34.1%.The 409L ferritic stainless steel in a vacuum after induction furnace internal heating to the 1530 ℃ fusing frequently, is added the fining agent of the present embodiment of 2wt% in molten steel, cast after being incubated for 10 seconds.To the foundry goods cross section polish, burn into observes and to learn that equiax crystal district proportion is not increased to 83% by adding 34.1% before the fining agent, and equiax crystal district grain-size is reduced to 500 microns by 2000 microns that do not add before the fining agent, as shown in Figure 3.
Embodiment 2
As shown in table 1, the present embodiment preparation process comprises the steps:
Step 1 is mixed the Fe-C alloy with metal Ti, metal V and metal Nb, with mixture frequently melt in the induction furnace in a vacuum melt; Described mixing need make the mass percent of each element in the mixture that obtains be: Fe 35%, and Ti 25%, and Nb 25%, and C 15%;
Step 2 when the temperature of melt is 1600 ℃, feeds argon gas in melt, the flow of argon gas is 500ml/min, and the time is 1.5h;
Present embodiment prepares that the XC pellet density is 10 in the gained grain-refining agent
7Individual/mm
3But present embodiment prepares the crystal grain of gained grain-refining agent refinement steel, and steel billet as-cast structure equiax crystal district ratio is improved.
As shown in table 1, the present embodiment preparation process comprises the steps:
Step 1, with pure iron, graphite mixes with metal Ti, metal V and metal Nb, with mixture frequently melt in the induction furnace in a vacuum melt; Described mixing need make the mass percent of each element in the mixture that obtains be: Fe 67.5%, and Ti 10%, and V 5%, and Nb 10%, and C 7.5%;
Step 2 when the temperature of melt is 1550 ℃, feeds argon gas in melt, the flow of argon gas is 100ml/min, and the time is 10s;
Present embodiment prepares that XC density is 10 in the gained grain-refining agent
8Individual/mm
3But present embodiment prepares the crystal grain of gained grain-refining agent refinement steel, and steel billet as-cast structure equiax crystal district ratio is improved.
Claims (4)
1. a Fe-X-C grain-refining agent is characterized in that, component and mass percent are: Fe 35%, and C 15%, and Ti 25%, and Nb 25%, and wherein X is Ti element and Nb element.
2. Fe-X-C grain-refining agent according to claim 1 is characterized in that, the density of XC 〉=10000/mm
3
3. the preparation method of a Fe-X-C grain-refining agent as claimed in claim 1 is characterized in that, comprises the steps:
Step 1 is got the Fe-C alloy, mixes with metal X;
Perhaps, get pure iron and graphite, mix with metal X afterwards;
Afterwards mixture is frequently felt in a vacuum melt in the stove melt;
Step 2 when the temperature of melt is 1550~1650 ℃, feeds argon gas in melt, the time is 10s~3h;
Step 3 stops to feed argon gas, and outage gets the Fe-X-C grain-refining agent.
4. the preparation method of Fe-X-C grain-refining agent according to claim 3 is characterized in that, in the step 2, described feeding argon gas, flow are 100~1000ml/min.