CN102276987A - Solvent-free addition type liquid silicon resin - Google Patents
Solvent-free addition type liquid silicon resin Download PDFInfo
- Publication number
- CN102276987A CN102276987A CN2011101397749A CN201110139774A CN102276987A CN 102276987 A CN102276987 A CN 102276987A CN 2011101397749 A CN2011101397749 A CN 2011101397749A CN 201110139774 A CN201110139774 A CN 201110139774A CN 102276987 A CN102276987 A CN 102276987A
- Authority
- CN
- China
- Prior art keywords
- solvent
- type liquid
- parts
- silicone resin
- vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to solvent-free addition type liquid silicon resin. The solvent-free addition type liquid silicon resin is characterized by comprising the following components in part by weight: 100 to 130 parts of vinyl silicon oil with vinyl content weight ratio of 0.3 percent and viscosity of 10,000 to 50,000 cs, 38 to 58 parts of gas phase method silicon dioxide with grain size of 10 to 20 nm and specific surface area of 160 to 300 m<2>/g, 5 to 10 parts of hexamethyl silazane, 0.5 to 2 parts of vinyl triethoxysilane, 0.5 to 2 parts of dimethyl diethoxysilane, 2 to 5 parts of water, 0.06 to 0.09 part of release agent stearic acid, 0.001 to 0.003 part of inhibitor methylbutynol and 0.6 to 0.8 part of crosslinking agent hydrogen-containing silicon oil, wherein the hexamethyl silazane, the vinyl triethoxysilane and the dimethyl diethoxysilane are treating agents. The solvent-free addition type liquid silicon resin is prepared by an addition type preparation method. The solvent-free addition type liquid silicon resin solves the problems that the liquid silicon resin serving as the surface coating of materials such as glass fiber sleeves, silica gel tubes, glass fiber cloth and the like does not have excellent properties and are not stable in storing.
Description
Technical field
The present invention relates to silicone resin and preparation method thereof, especially relate to a kind of solvent-free add-on type liquid silicone resin that is used for material surface coatings such as fiberglass sleeve, silicone tube, glasscloth and preparation method thereof.
Background technology
In polysiloxane molecule, the ratio of organic substituent (R) and Siliciumatom (Si) is the important parameter of decision product form.When R/Si＜2, product is a silicone resin; During R/Si ≈ 2, be the rubber of high viscous plasticity attitude, i.e. silicon rubber; When R/Si＞2, be low-molecular-weight oily matter, claim silicone oil.Silicone resin is highly cross-linked cancellated organopolysiloxane, normally use the various mixtures of METHYL TRICHLORO SILANE, dimethyldichlorosilane(DMCS), phenyl-trichloro-silicane, diphenyl dichlorosilane or dichloromethyl phenylsilane, in the presence of organic solvent such as toluene, add water decomposition at a lower temperature, obtain the acidic hydrolysis thing.The initial product of hydrolysis is cyclic, line style and mixture cross-linked polymer, also contains considerable hydroxyl usually.Hydrolyzate removes disacidify through washing, and neutral condensation polymer thermooxidizing or further polycondensation in the presence of catalyzer in air just forms highly cross-linked cubic network structure at last.Feed rate in the hydrolytic process, temperature of reaction, stirring intensity etc., all influential to resin property.
Silicone resin molecule side group mainly is a methyl, introduces phenyl and can improve thermo-elasticity and cementability, and the compatibility of improvement and organic polymer and pigment is introduced ethyl, propyl group or chain alkyl and can be improved organic affinity, and improves hydrophobic nature; Introduce vinyl and hydrogen base, can use platinum catalytic addition reaction and superoxide to cause crosslinking reaction; Introduce the carbon official can machine then can with more organic compound reactions, improve cementability to base material.
Silicone resin is a kind of heat cured plastics, and one of performance that it is the most outstanding is excellent thermo-oxidative stability.250 ℃ of heating are after 24 hours, and silicone resin weightlessness only is 2～8%.Another outstanding performance of silicone resin is excellent electrical insulation capability, and it all can keep its good insulation performance performance in wide temperature and range of frequency.Silicone resin is broadly divided into several big classes such as organic silicon insulating varnish, organosilicon coating, silicone plastics and silicone adhesive by its main application and crosslinking method.Silicone resin has good resistance to elevated temperatures and outstanding dielectricity.It has good anti-corona, arc resistance, and dielectric loss angle tangent is low, these be other synthetic resins can't be obtained.Silicone resin can be made anti-180 ℃ electric motor insulating material, as varnished glass cloth, glass cloth laminated board, mica tape, impregnating varnish, enamel paint etc.Anti-500 ℃ of life-time service, the anti-1000 ℃ high-temperature coatings of instantaneous use be can be made into after afterwards both add aluminium powder, application jet engine jet pipe, metal chimney etc. are used for.With the moulding compound that glass fibre or asbestos reinforcement are made, can be used as the material of making anti-strong current, high-tension anti-arc switch.Silicone resin (being commonly called as silicone glass resin) so that methyl trialkoxysilane makes can make it that good brightness and wear resistance be arranged in order to treatment paper, plastics, metallic surface.Silicone resin can be used as the good outdoor use coating of weathering resistance after modification (as with Synolac etc.).
Because silicone resin raw materials for production, technology difference cause the silicone resin kind numerous and diverse.As Chinese patent 98101493.3 with regard to manufacture method of disclosed a kind of transparent liquid silicone resin and products thereof, selecting the organic oxirane that contains unsaturated alkyl, poly-diorganosiloxane and Diphenylsilanediol for use is raw material, its mole ratio is 1: 1-5: 5-1, adding anionic catalyst is the 0.005-0.04% of raw material gross weight, be to reduce pressure polycondensation 1-3 hour under 140-180 ℃ the condition in temperature, generate transparent liquid solvent-free silicone resin.A kind of organosilicon resin composition is disclosed as Chinese patent 200710027914.7.By: methyl vinyl silicon kautschuk, methylvinyl-polysiloxane, methyl ethylene silicone resin, linking agent, catalyzer and inhibitor mixed form, and its mass ratio is: 100 parts of methyl vinyl silicon kautschuks, 50～400 parts of methylvinyl-polysiloxane, 50～400 parts of methyl ethylene silicone resins, linking agent 5-50 part, 0.1～2 part of catalyzer, 0.05～2 part in inhibitor; Manufacture craft and flow process are that elder generation adds mixing and stirring in proportion with methyl vinyl silicon kautschuk, methylvinyl-polysiloxane, methyl ethylene silicone resin, linking agent and inhibitor, adds catalyzer then and stir to get final product.A kind of nano solidifiable silicone impression material is disclosed again as Chinese patent 200910305628.1, form by basic paste and catalyzer paste two portions, the basis paste comprise 0.2% ethenyl blocking polydimethylsiloxane, have at least 3 SiH base polymethyl hydrogen siloxane polydimethylsiloxanes, polyethet surfactant, diameter nano silicon, coloring agent, superfine talcum powder, light calcium carbonate, inhibitor 3-methyl isophthalic acid-butine-3-alcohol less than 30nm; The component of catalyzer paste comprises polydimethylsiloxane, polydimethylsiloxane, ethylene methacrylic radical siloxane coordinate platinum catalyst, the nano silicon of 0.2% ethenyl blocking.After basis paste and catalyzer paste two portions are the mediation of 1: 1 or 5: 1 with volume ratio, under room temperature, be cured as silicone elastomer in 3-5 minute.
This shows how to select suitable feedstock, also generate liquid silicone resin by suitable technology, product is not only wanted excellent property, and shelf-stable; Technology has short, power savings advantages of time spent; With its product of making or handling have not xanthochromia, do not ftracture, shrinking percentage is little, and pliability, intensity, glossiness are preferably arranged, self-extinguishing and dielectricity are good.These all are the directions of silicone resin research and development.
Summary of the invention
The purpose of this invention is to provide a kind of solvent-free add-on type liquid silicone resin, solve the problem that performance is excellent inadequately, storage is stable inadequately that the existing liquid silicone resin that is used for material surface coatings such as fiberglass sleeve, silicone tube, glasscloth exists.
Further purpose of the present invention provides a kind of preparation method of solvent-free add-on type liquid silicone resin, solves existing liquid silicone resin preparation method and has the problem that the time spent is long, energy consumption is high.
The principle of foundation of the present invention: the add-on type silicone resin is different from condensed type or superoxide initiation type silicone resin is curing mechanism.Add-on type silicone resin curing mechanism system is by the siloxanes and the siloxanes (linking agent) that contains ≡ Si-H group of tool ≡ Si-CH=CH2 group, under the platinum catalyst effect hydrosilylation addition reaction takes place and crosslinked.
The add-on type silicone resin has and does not contain solvent, and the condition of cure gentleness does not have low molecule by product and advantage such as emits.Therefore as impregnant, coating, casting material and when sealing material and using, can not produce bubble and sand holes, and have good interior dryness, thermal conductivity, corona resistance and resistance to sudden heating.Add-on type silicone resin synthesis technique more complicated, cost is also higher.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of solvent-free add-on type liquid silicone resin is characterized in that, in weight part, comprises following component: the ethylene content weight ratio is 0.3%, viscosity is vinyl silicone oil 100-130 part of 10000-50000cs; Fumed silica 38-58 part (particle diameter 10～20nm, specific surface area 160-300m
2/ g); Treatment agent comprises hexa methyl silazane 5-10 part, vinyltriethoxysilane 0.5-2 part, dimethyldiethoxysilane 0.5-2 part; And water 2-5 part; Stearic acid release agent 0.06-0.09 part; Inhibitor methylbutynol 0.001-0.003 part, linking agent containing hydrogen silicone oil 0.6-0.8 part; Adopt the add-on type preparation method to make.
A kind of preparation method of solvent-free add-on type liquid silicone resin gets all the each starting material ready by the said ratio component, comprises the steps:
1. adopt D4 (prestox tetrasiloxane) or DMC monomer in reactor process dehydration polymerization, heat up 180 ℃, add the vinyl double-seal head, remove lower-molecular substance again, discharging gets that the ethylene content weight ratio is 0.3%, viscosity is the vinyl silicone oil of 10000-50000cs;
2. partly measure vinyl silicone oil and the silicon-dioxide with gross weight drops into kneader, add hexamethyldisilazane (surface treatment again, its mechanism of action is with silazine link and the condensation of silicon hydroxyl), vinyltriethoxysilane (is used for synthesizing organo-silicon intermediate and macromolecular compound, as silane coupling agent) dimethyldiethoxysilane (is used for structure control, chainextender during organosilicon product is synthetic), water (destatic, explosion-proof), stearic acid (releasing agent), mediates 2 hours must sizing material;
3. the banburying that kneaded sizing material heated up in the vacuum Banbury mixer, the material temperature control vacuumizes in the time of 150 ℃ at 130-200 ℃ of degree, adds the surplus vinyl silicone oil again, banburying 6-8h, discharging, places 12-24 hour must the banburying material;
Banburying material physicals detect qualified after, grind and remove its block material, add the inhibitor methylbutynol again, the linking agent containing hydrogen silicone oil stirs 2h, after the press filtration liquid silicone resin.
Further, also the aluminium hydroxide that can add high temperature resistant auxiliary agent weight ratio 1-2 part at the whipping step of the kneading of above-mentioned steps 2 or step 4 improves flame retardant resistance, self-extinguishing.
The above-mentioned solvent-free add-on type liquid silicone resin that makes is joined chloroplatinic acid catalyst and is dispatched from the factory, and uses for the user.
In addition, silicone resin molecule side group mainly is a methyl, introduces phenyl and can improve thermo-elasticity and cementability, and the compatibility of improvement and organic polymer and pigment is introduced ethyl, propyl group or chain alkyl and can be improved organic affinity, and improves hydrophobic nature; Introduce vinyl and hydrogen base, can use platinum catalytic addition reaction and superoxide to cause crosslinking reaction; Introduce the carbon official can machine then can with more organic compound reactions, improve cementability to base material.
Beneficial effect of the present invention: owing in vinyl silicone oil, add an amount of fumed silica strengthening agent, add the hexamethyldisilazane surface treatment agent again, vinyltriethoxysilane is used for structure control as silane coupling agent, dimethyldiethoxysilane; And adopting two-step approach to add vinyl silicone oil, water destatics, explosion-proof; Make silicone resin molecule tridimensional network appropriateness, silicone resin has good electrical insulation property, heatproof and good waterproof effect.And weathering resistance is better than general organic resin.Therefore, in the coating on heatproof, heat-resisting and anti-wet treatment protection top layer, be all desirable material.
Below with reference to embodiment, the present invention is carried out comparatively detailed explanation.
Embodiment
The preparation of vinyl silicone oil of embodiment 1, liquid silicone resin
Adopt D4 (prestox tetrasiloxane) or DMC monomer at reactor through the dehydration polymerization, heats up 180 ℃, adding vinyl double-seal head removes lower-molecular substance again, discharging gets that the ethylene content weight ratio is 0.3%, viscosity is the vinyl silicone oil of 10000-50000cs.
Embodiment 2, a kind of solvent-free add-on type liquid silicone resin preparation
In weight part, prepare following raw material: 100 parts of the vinyl silicone oils that the ethylene content weight ratio is 0.3%, viscosity is 10000-50000cs; Fumed silica 38 parts of (particle diameter 10～20nm, specific surface area 160-300m
2/ g); Treatment agent comprises 5 parts of hexa methyl silazanes, 0.5 part of vinyltriethoxysilane, 0.5 part of dimethyldiethoxysilane; And 2 parts in water; 0.06 part of stearic acid release agent; 0.001 part of inhibitor methylbutynol, 0.6 part of linking agent containing hydrogen silicone oil; Adopt the add-on type preparation method to make.The preparation method comprises the steps:
1. the vinyl silicone oil (embodiment 1 product) of partly measuring with gross weight drops into kneader with silicon-dioxide, adds hexamethyldisilazane, vinyltriethoxysilane, dimethyldiethoxysilane, water, stearic acid again, mediates and gets sizing material in 2 hours;
2. the banburying that kneaded sizing material heated up in the vacuum Banbury mixer, the material temperature control vacuumizes in the time of 150 ℃ at 130-200 ℃ of degree, adds the surplus vinyl silicone oil again, banburying 6-8h, discharging, places 12-24 hour must the banburying material;
Banburying material physicals detect qualified after, grind and remove its block material, add the inhibitor methylbutynol again, the linking agent containing hydrogen silicone oil stirs 2h, after the press filtration liquid silicone resin.
Embodiment 3, a kind of solvent-free add-on type liquid silicone resin preparation
In weight part, prepare following raw material: 130 parts of the vinyl silicone oils that the ethylene content weight ratio is 0.3%, viscosity is 10000-50000cs; Fumed silica 58 parts of (particle diameter 10～20nm, specific surface area 160-300m
2/ g); Treatment agent comprises 10 parts of hexa methyl silazanes, 2 parts of vinyltriethoxysilanes, 2 parts of dimethyldiethoxysilanes; And 5 parts in water; 0.09 part of stearic acid release agent; 0.003 part of inhibitor methylbutynol, 0.8 part of linking agent containing hydrogen silicone oil; The aluminium hydroxide that high temperature resistant auxiliary agent is 2 parts adopts the add-on type preparation method to make.The preparation method comprises the steps:
1. partly measure vinyl silicone oil and the silicon-dioxide with gross weight drops into kneader, adds hexamethyldisilazane, vinyltriethoxysilane, dimethyldiethoxysilane, aluminium hydroxide, water, stearic acid again, mediates 2 hours must sizing material;
2. the banburying that kneaded sizing material heated up in the vacuum Banbury mixer, the material temperature control vacuumizes in the time of 150 ℃ at 130-200 ℃ of degree, adds the surplus vinyl silicone oil again, banburying 6-8h, discharging, places 12-24 hour must the banburying material;
Banburying material physicals detect qualified after, grind and remove its block material, add the inhibitor methylbutynol again, the linking agent containing hydrogen silicone oil stirs 2h, after the press filtration liquid silicone resin.
Owing to add high temperature resistant auxiliary agent aluminium hydroxide, improved flame retardant resistance, self-extinguishing.
The above-mentioned solvent-free add-on type liquid silicone resin that makes is joined chloroplatinic acid catalyst and is dispatched from the factory, and uses for the user.
Embodiment 4, a kind of solvent-free add-on type liquid silicone resin preparation
In weight part, prepare following raw material: 120 parts of the vinyl silicone oils that the ethylene content weight ratio is 0.3%, viscosity is 10000-50000cs; Fumed silica 48 parts of (particle diameter 10～20nm, specific surface area 160-300m
2/ g); Treatment agent comprises 8 parts of hexa methyl silazanes, 1 part of vinyltriethoxysilane, 1 part of dimethyldiethoxysilane; And 3 parts in water; 0.08 part of stearic acid release agent; 0.002 part of inhibitor methylbutynol, 0.7 part of linking agent containing hydrogen silicone oil; 1 part in aluminium hydroxide adopts the add-on type preparation method to make.The preparation method comprises the steps:
1. partly measure vinyl silicone oil and the silicon-dioxide with gross weight drops into kneader, adds hexamethyldisilazane, vinyltriethoxysilane, dimethyldiethoxysilane, water, stearic acid again, mediates 2 hours must sizing material;
2. the banburying that kneaded sizing material heated up in the vacuum Banbury mixer, the material temperature control vacuumizes in the time of 150 ℃ at 130-200 ℃ of degree, adds the surplus vinyl silicone oil again, banburying 6-8h, discharging, places 12-24 hour must the banburying material;
Banburying material physicals detect qualified after, grind and remove its block material, add the inhibitor methylbutynol again, linking agent containing hydrogen silicone oil, aluminium hydroxide stir 2h, after the press filtration liquid silicone resin.
The above-mentioned solvent-free add-on type liquid silicone resin that makes is joined chloroplatinic acid catalyst and is dispatched from the factory, and uses for the user.
Embodiment silicate resinous product and currently available products performance perameter comparison sheet:
As can be seen above-mentioned, the embodiment silicate resinous product promotes greatly than currently available products performance perameter.
Claims (3)
1. a solvent-free add-on type liquid silicone resin is characterized in that, in weight part, comprises following component: the ethylene content weight ratio is 0.3%, viscosity is vinyl silicone oil 100-130 part of 10000-50000cs; Particle diameter is that 10～20nm, specific surface area are 160-300m
2Fumed silica 38-58 part of/g; Treatment agent comprises hexa methyl silazane 5-10 part, vinyltriethoxysilane 0.5-2 part, dimethyldiethoxysilane 0.5-2 part; And water 2-5 part; Stearic acid release agent 0.06-0.09 part; Inhibitor methylbutynol 0.001-0.003 part, linking agent containing hydrogen silicone oil 0.6-0.8 part; Adopt the add-on type preparation method to make.
2. solvent-free add-on type liquid silicone resin as claimed in claim 1 is characterized in that: described preparation method, get all the each starting material ready by the described component of claim 1, and comprise the steps:
1) adopt D4 or DMC monomer at reactor through the dehydration polymerization, heats up 180 ℃, adding vinyl double-seal head removes lower-molecular substance again, discharging gets that the ethylene content weight ratio is 0.3%, viscosity is the vinyl silicone oil of 10000-50000cs;
2) partly measure vinyl silicone oil and the silicon-dioxide with gross weight drops into kneader, adds hexamethyldisilazane, vinyltriethoxysilane, dimethyldiethoxysilane, water, stearic acid again, mediates 2 hours must sizing material;
3) kneaded sizing material is heated up in vacuum Banbury mixer banburying, the material temperature control vacuumizes in the time of 150 ℃ at 130-200 ℃ of degree, adds the surplus vinyl silicone oil again, banburying 6-8h, discharging, places 12-24 hour must the banburying material;
4) banburying material physicals detect qualified after, grind and remove its block material, add the inhibitor methylbutynol again, the linking agent containing hydrogen silicone oil stirs 2h, after the press filtration liquid silicone resin.
3. solvent-free add-on type liquid silicone resin as claimed in claim 1 is characterized in that: adding weight ratio in the step of described step 2 of claim 2 or step 4 is the aluminium hydroxide stirring of 1-2 part.