CN102260779A - Quenching method for 20CrNiMo material drill bit - Google Patents
Quenching method for 20CrNiMo material drill bit Download PDFInfo
- Publication number
- CN102260779A CN102260779A CN2011102038264A CN201110203826A CN102260779A CN 102260779 A CN102260779 A CN 102260779A CN 2011102038264 A CN2011102038264 A CN 2011102038264A CN 201110203826 A CN201110203826 A CN 201110203826A CN 102260779 A CN102260779 A CN 102260779A
- Authority
- CN
- China
- Prior art keywords
- drill bit
- 20crnimo
- material drill
- time
- 20crnimo material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a quenching method for a 20CrNiMo material drill bit. The method comprises the following: a first quenching step, which comprises the steps of heating up a drill bit workpiece after being carburized, heat preserving, discharging from a furnace and oil cooling, washing with clear water, first tempering, heat preserving for at least three hours, naturally cooling, and discharging from the furnace and air cooling to the room temperature; and a second quenching step, which comprises the steps of second heating up the drill bit, heat preserving, discharging from the furnace and second oil cooling, extracting oil, washing with clear water, second tempering, and discharging from the furnace and air cooling to the room temperature. Due to the adoption of the two-time quenching process and a display of detected data from a test, the hardness of the workpiece of the 20CrNiMo material drill bit is uniformly distributed, the hardness value of the workpiece of the 20CrNiMo material drill bit reaches to Rockwell hardness 58-61, and the metallurgical structure of the workpiece of the 20CrNiMo material drill bit is further refined; moreover, the invention has the advantages of prolonging the service life of the 20CrNiMo material drill bit, increasing economic benefit, reducing replacement times and reducing production cost.
Description
Technical field
The present invention relates to heat treating method, specifically belong to a kind of quenching method of the 20CrNiMo of being used for material drill bit object.
Background technology
At present, the drill bit product of 20CrNiMo material all adopts disposable quenching, its quenching temperature is 830～850 ℃, and under 830～850 ℃ of conditions, be incubated 2 hours, carry out low-temperaturetempering after adopting the quenching oil cooling then, tempering temperature is 150～180 ℃, is incubated 4 hours, come out of the stove then and air cooling to room temperature.The deficiency of its existence: can not eliminate the infiltration layer carbide network fully, the tissue of drill bit heart portion that can not refinement 20CrNiMo material, thereby cause hardness problem inhomogeneous and on the low side after heat treatment, its durometer level is at HRC45-60, and drill bit is when running up, because its hardness value fluctuation range is big, bearing arrangement occurs losing efficacy and whole drill bit can't be used, its life cycle is short, influences working efficiency, increases production cost.
Summary of the invention
The drill bit that the objective of the invention is to solve present 20CrNiMo material adopts the existing deficiency of disposable quenching, provides a kind of drill bit hardness of the 20CrNiMo of making material even, can improve the quenching method that is used for 20CrNiMo material drill bit of its life cycle.
Realize the technical measures of above-mentioned purpose:
A kind of quenching method that is used for 20CrNiMo material drill bit, its step:
Carrying out the first time quenches:
1) heat behind the 20CrNiMo material drill bit workpiece carbonization, heating and temperature control is 868～872 ℃;
2) be incubated 1.5～2 hours down at 868～872 ℃;
3) come out of the stove and oil cooling for the first time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 100～200 ℃;
4) clear water of 20CrNiMo material drill bit workpiece with 60～75 ℃ cleaned;
5) carry out the tempering first time, tempering temperature is controlled to be 595～605 ℃;
6) be incubated at least 3 hours down at 595～605 ℃;
7) carry out the nature cooling: 20CrNiMo material drill bit workpiece is with most 490～510 ℃ of process furnace nature temperature drops;
8) come out of the stove and air cooling to room temperature;
Carrying out the second time quenches:
9) 20CrNiMo material drill bit workpiece is carried out the heating second time, Heating temperature is 818～822 ℃;
10) be incubated 1.5～2 hours down at 818～822 ℃;
11) come out of the stove and carry out the oil cooling second time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 100～200 ℃;
12) adopt behind oil cooling to 100～200 ℃ fuel-displaced to 20CrNiMo material drill bit workpiece;
13) fuel-displaced back clear water with 60～75 ℃ cleans 20CrNiMo material drill bit workpiece;
14) under 150～160 ℃, carry out the tempering second time, tempering time at least 4 hours;
15) come out of the stove and air cooling to room temperature.
The present invention is owing to adopt twice quenching technology, the data that detect from test as can be known, 20CrNiMo material drill bit workpiece hardness is evenly distributed, hardness value reaches HRC 58-61, its metallographic structure obtains further refinement, thereby has prolonged the work-ing life of 20CrNiMo material drill bit, the corresponding economic benefit that improved, reduce and change number of times, reduced production cost.
Embodiment
The invention will be further described below in conjunction with specific embodiment:
Embodiment 1
A kind of quenching method that is used for 20CrNiMo material drill bit, its step:
Carrying out the first time quenches:
1) heat behind the 20CrNiMo material drill bit workpiece carbonization, heating and temperature control is 868 ℃;
2) be incubated 1.5 hours down at 868 ℃;
3) come out of the stove and oil cooling for the first time, 20CrNiM o material drill bit workpiece surface temperature is cooled to 100～110 ℃;
4) clear water of 20CrNiMo material drill bit workpiece with 60 ℃ cleaned;
5) carry out the tempering first time, tempering temperature is controlled to be 595 ℃;
6) be incubated 3 hours down at 595 ℃;
7) carry out the nature temperature drop: 20CrNiMo material drill bit workpiece is with most 490～495 ℃ of process furnace nature temperature drops;
8) come out of the stove and air cooling to room temperature;
Carrying out the second time quenches:
9) 20CrNiMo material drill bit workpiece is carried out the heating second time, Heating temperature is 818 ℃;
10) be incubated 1.5～2 hours down at 818 ℃;
11) come out of the stove and carry out the oil cooling second time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 150～160 ℃;
12) fuel-displaced back clear water with 60 ℃ cleans 20CrNiMo material drill bit workpiece;
13) under 150 ℃, carry out the tempering second time, tempering time 4 hours;
14) come out of the stove and air cooling to room temperature.
Embodiment 2
A kind of quenching method that is used for 20CrNiMo material drill bit, its step:
Carrying out the first time quenches:
1) heat behind the 20CrNiMo material drill bit workpiece carbonization, heating and temperature control is 870 ℃;
2) be incubated 1.5 hours down at 870 ℃;
3) come out of the stove and oil cooling for the first time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 150～165 ℃;
4) clear water of 20CrNiMo drill bit workpiece with 70 ℃ cleaned;
5) carry out the tempering first time, tempering temperature is controlled to be 600 ℃;
6) be incubated 3.5 hours down at 600 ℃;
7) carry out the nature temperature drop: 20CrNiMo material drill bit workpiece is with most 495～500 ℃ of process furnace nature temperature drops;
8) come out of the stove and air cooling to room temperature;
Carrying out the second time quenches:
9) 20CrNiMo material drill bit workpiece is carried out the heating second time, Heating temperature is 820 ℃;
10) be incubated 2 hours down at 820 ℃;
11) come out of the stove and carry out the oil cooling second time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 100～110 ℃;
12) fuel-displaced back clear water with 68 ℃ cleans 20CrNiMo material drill bit workpiece;
13) carry out the tempering second time under 155 ℃, tempering time is 4.5 hours;
14) come out of the stove and air cooling to room temperature.
Embodiment 3
A kind of quenching method that is used for 20CrNiMo material drill bit, its step:
Carrying out the first time quenches:
1) heat behind the 20CrNiMo material drill bit workpiece carbonization, heating and temperature control is 872 ℃;
2) be incubated 1 hour 45 minutes down at 872 ℃;
3) come out of the stove and oil cooling for the first time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 185～200 ℃;
4) clear water of 20CrNiMo material drill bit workpiece with 75 ℃ cleaned;
5) carry out the tempering first time, tempering temperature is controlled to be 605 ℃;
6) be incubated 4 hours down at 600 ℃;
7) carry out the nature temperature drop: 20CrNiMo material drill bit workpiece is with most 505～510 ℃ of process furnace nature temperature drops;
8) come out of the stove and air cooling to room temperature;
Carrying out the second time quenches:
9) 20CrNiMo material drill bit workpiece is carried out the heating second time, Heating temperature is 822 ℃;
10) be incubated 1 hour 45 minutes down at 822 ℃;
11) come out of the stove and carry out the oil cooling second time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 190～200 ℃;
12) fuel-displaced back clear water with 75 ℃ cleans 20CrNiMo material drill bit workpiece;
13) carry out the tempering second time under 155 ℃, tempering time is 4.5 hours;
14) come out of the stove and air cooling to room temperature.
Table 1 is back hardness value after testing and the tabulation of drill bit workpiece surface hardness situation statistics of each embodiment
Find out that from the detection of table 1 the present invention makes drill bit workpiece surface hardness fluctuations scope very little, expression drill bit workpiece surface hardness is even, drill bit workpiece centre hardness fluctuation good uniformity, the metallographic structure of drill bit workpiece heart portion in order, thereby can improve its life cycle.
Claims (1)
1. quenching method that is used for 20CrNiMo material drill bit, its step:
Quench for the first time:
1) heat behind the 20CrNiMo material drill bit workpiece carbonization, heating and temperature control is 868～872 ℃;
2) be incubated 1.5～2 hours down at 868～872 ℃;
3) come out of the stove and oil cooling for the first time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 100～200 ℃;
4) clear water of 20CrNiMo material drill bit workpiece with 60～75 ℃ cleaned;
5) carry out the tempering first time, tempering temperature is controlled to be 595～605 ℃;
6) be incubated at least 3 hours down at 595～605 ℃;
7) carry out the nature temperature drop: 20CrNiMo material drill bit workpiece is with most 490～510 ℃ of process furnace nature temperature drops;
8) come out of the stove and air cooling to room temperature;
Quench for the second time:
9) 20CrNiMo material drill bit workpiece is carried out the heating second time, Heating temperature is 818～822 ℃;
10) be incubated 1.5～2 hours down at 818～822 ℃;
11) come out of the stove and carry out the oil cooling second time, 20CrNiMo material drill bit workpiece surface temperature is cooled to 100～200 ℃;
12) fuel-displaced back clear water with 60～75 ℃ cleans 20CrNiMo material drill bit workpiece;
13) under 150～160 ℃, carry out the tempering second time, tempering time at least 4 hours;
14) come out of the stove and air cooling to room temperature.