CN102250529A - Ultralow-temperature cured epoxy powder coating and preparation method thereof - Google Patents
Ultralow-temperature cured epoxy powder coating and preparation method thereof Download PDFInfo
- Publication number
- CN102250529A CN102250529A CN2011101397448A CN201110139744A CN102250529A CN 102250529 A CN102250529 A CN 102250529A CN 2011101397448 A CN2011101397448 A CN 2011101397448A CN 201110139744 A CN201110139744 A CN 201110139744A CN 102250529 A CN102250529 A CN 102250529A
- Authority
- CN
- China
- Prior art keywords
- powder coating
- ultralow
- preparation
- cured epoxy
- temperature cured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of powder coating, in particular to an ultralow-temperature cured epoxy powder coating and a preparation method thereof. The formula of the powder coating comprises the following components in percentage by weight: 47-65% of bisphenol A epoxy, 3-6% of organic urea curing agent, 0.2-0.5% of benzoin, 8.8-19.5% of rutile type titanium dioxide and 20-30% of precipitated barium sulfate. The ultralow-temperature cured epoxy powder coating and the preparation method thereof are applied to surface coating of thermosensitive base materials, such as plastic products, paper, paperboards, wood and the like. The ultralow-temperature cured epoxy powder coating has the characteristics of excellent mechanical performance. Meanwhile, the ultralow-temperature cured epoxy powder coating can be quickly cured and is easy to popularize and apply, production cost is lowered, and energy is saved.
Description
Technical field
The present invention relates to a kind of technical field of powder coating, especially a kind of cryogenic curing epoxide powder coating and preparation method thereof.
Background technology
Powder coating is no matter be thermoplasticity or thermoset, and generally needing in temperature be more than 180 ℃, and the time is to toast under the condition of 20min, make it use resistant substrates such as only being confined to metal, be difficult to be applied to the thermo-sensitivity base material, range of application is narrow, bad mechanical property wastes energy easily.
Summary of the invention
Original powder coating range of application is narrow in order to overcome, bad mechanical property and the deficiency that wastes energy easily, the invention provides a kind of cryogenic curing epoxide powder coating and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is: a kind of cryogenic curing epoxide powder coating, the prescription of this powder coating is as follows by weight percentage: bisphenol-A epoxy 47% ~ 65%, organic ureas solidifying agent 3% ~ 6%, st-yrax 0.2% ~ 0.5%, rutile titanium white powder 8.8% ~ 19.5% and process white 20% ~ 30%.
According to another embodiment of the invention, comprise that further the concrete proportioning of prescription of this powder coating is as follows by weight percentage: bisphenol-A epoxy 56.6%, organic ureas solidifying agent 5%, st-yrax 0.4%, rutile titanium white powder 12% and process white 26%.
A kind of preparation method of cryogenic curing epoxide powder coating, this method may further comprise the steps:
A) bisphenol-A epoxy 47% ~ 65%, organic ureas solidifying agent 3% ~ 6%, st-yrax 0.2% ~ 0.5%, rutile titanium white powder 8.8% ~ 19.5% and process white 20% ~ 30% are put into container by proportioning and carry out batch mixing, mix;
B) get the material that mixes in the steps A through coarse reduction-fine powder broken-after sieving, promptly make finished product.
The invention has the beneficial effects as follows: this cryogenic curing epoxide powder coating and preparation method thereof is used the surface coatings of heat-sensitive substrate materials such as plastics, paper, cardboard and timber, has excellent mechanical property, have quick-setting characteristics simultaneously, reduced production cost, saved the energy, be easy to apply.
Embodiment
The prescription of this cryogenic curing epoxide powder coating is as follows by weight percentage:
Bisphenol-A epoxy 47% ~ 65%;
Organic ureas solidifying agent 3% ~ 6%;
St-yrax 0.2% ~ 0.5%;
Rutile titanium white powder 8.8% ~ 19.5%;
Process white 20% ~ 30%.
The concrete proportioning of the prescription of this cryogenic curing epoxide powder coating is as follows by weight percentage:
Bisphenol-A epoxy 56.6%;
Organic ureas solidifying agent 5%;
St-yrax 0.4%;
Rutile titanium white powder 12%;
Process white 26%.
The present invention adds a kind of organic ureas low temperature curing agent; Condition of cure: 130 ℃/8min.
This cryogenic curing epoxide powder coating being sprayed at heat-sensitive substrate materials such as plastics, paper, cardboard and timber and forming and film, is 130 ℃ in temperature, and the time is baking-curing under the condition of 8min.
This cryogenic curing epoxide powder coating being sprayed at heat-sensitive substrate materials such as plastics, paper, cardboard and timber and forming and film, is 140 ℃ in temperature, and the time is baking-curing under the condition of 4min.
A kind of preparation method of cryogenic curing epoxide powder coating, this method may further comprise the steps:
A) bisphenol-A epoxy 56.6%, organic ureas solidifying agent 5%, st-yrax 0.4%, rutile titanium white powder 12% and process white 26% are put into container by proportioning and carry out batch mixing, mix;
B) get the material that mixes in the steps A through coarse reduction-fine powder broken-after sieving, promptly make finished product.
Further specify component of the present invention and content below by embodiment:
Embodiment 1
Prepare raw material, bisphenol-A epoxy: 56.6; Organic ureas solidifying agent: 5; Process white: 26; Rutile titanium white powder: 12; St-yrax: 0.4, above-mentioned raw materials is carried out batch mixing through proportioning, melt extrude, the cooling compressing tablet, fragmentation is sieved the back electrostatic spraying on heat-sensitive substrate material, baking back film forming under the condition of 130 ℃/8min or 140 ℃/4min.
Embodiment 2
Prepare raw material, bisphenol-A epoxy: 47; Organic ureas solidifying agent: 3; Process white: 30; Rutile titanium white powder: 19.5; St-yrax: 0.5, above-mentioned raw materials is carried out batch mixing through proportioning, melt extrude, the cooling compressing tablet, fragmentation is sieved the back electrostatic spraying on heat-sensitive substrate material, baking back film forming under the condition of 130 ℃/8min or 140 ℃/4min.
Embodiment 3
Prepare raw material, bisphenol-A epoxy: 65; Organic ureas solidifying agent: 6; Process white: 20; Rutile titanium white powder: 8.8; St-yrax: 0.2, above-mentioned raw materials is carried out batch mixing through proportioning, melt extrude, the cooling compressing tablet, fragmentation is sieved the back electrostatic spraying on heat-sensitive substrate material, baking back film forming under the condition of 130 ℃/8min or 140 ℃/4min.
This cryogenic curing epoxide powder coating and preparation method thereof is used the surface coatings of heat-sensitive substrate materials such as plastics, paper, cardboard and timber, have excellent mechanical property, have quick-setting characteristics simultaneously, reduced production cost, saved the energy, be easy to apply.
Claims (3)
1. cryogenic curing epoxide powder coating, it is characterized in that: the prescription of this powder coating is as follows by weight percentage: bisphenol-A epoxy 47% ~ 65%, organic ureas solidifying agent 3% ~ 6%, st-yrax 0.2% ~ 0.5%, rutile titanium white powder 8.8% ~ 19.5% and process white 20% ~ 30%.
2. cryogenic curing epoxide powder coating according to claim 1 is characterized in that: the concrete proportioning of this powder coating prescription is as follows by weight percentage: bisphenol-A epoxy 56.6%, organic ureas solidifying agent 5%, st-yrax 0.4%, rutile titanium white powder 12% and process white 26%.
3. the preparation method of a cryogenic curing epoxide powder coating, it is characterized in that: this method may further comprise the steps:
A) bisphenol-A epoxy 47% ~ 65%, organic ureas solidifying agent 3% ~ 6%, st-yrax 0.2% ~ 0.5%, rutile titanium white powder 8.8% ~ 19.5% and process white 20% ~ 30% are put into container by proportioning and carry out batch mixing, mix;
B) get the material that mixes in the steps A through coarse reduction-fine powder broken-after sieving, promptly make finished product.