CN102248718A - Explosion cladding rolled double-sided stainless steel composite thin strip - Google Patents
Explosion cladding rolled double-sided stainless steel composite thin strip Download PDFInfo
- Publication number
- CN102248718A CN102248718A CN2011101200336A CN201110120033A CN102248718A CN 102248718 A CN102248718 A CN 102248718A CN 2011101200336 A CN2011101200336 A CN 2011101200336A CN 201110120033 A CN201110120033 A CN 201110120033A CN 102248718 A CN102248718 A CN 102248718A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- strip
- rolling
- thin strip
- sided
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a composite thin strip, in particular to an explosion cladding rolled double-sided stainless steel composite thin strip, which belongs to the field of strips. An explosion cladding rolled double-sided stainless steel composite thin strip production process provided by the invention comprises the following steps of: compounding stainless steel on the two sides of a substrate of carbon steel; and rolling to obtain a double-sided stainless steel composite plate strip with any thickness, so that expensive stainless steel materials are saved, and prices are reduced. The mechanical properties of the materials are higher than those of pure stainless steel plates; and when the strip is used, the structural design thickness of the strip can be reduced or the structural operating stress of the strip can be improved. Simultaneously, the strip has the corrosion resistance, abrasion resistance and aesthetic appearance of the stainless steel, the yieldingness of a common steel plate and high plasticity and reduces the friability of the stainless steel.
Description
Technical field
The present invention relates to the THIN COMPOSITE band, relate in particular to the compound thin strip of the two-sided stainless steel of a kind of blast composite rolling, it belongs to the band field.
Background technology
As everyone knows, the steel of common name are meant the cold and hot various rolled steels such as strip material, pipe, shaped steel that roll, and it can be divided into carbon steel, steel alloy, stainless steel three major types by material.Wherein stainless steel material is widely used in industries such as oil, chemical industry, generating, water conservancy, light industry, food, building, and it has corrosion resistance, aesthetic property and can not be replaced by other steel, but stainless steel material price height, is 6～10 times of straight carbon steel price.
For many years, some experts and scholars are devoted to the research work that composite replaces the stainless steel material aspect, and have done a large amount of work, but produce little effect.60～seventies of twentieth century, China is special industry--the needs of shipbuilding, warship, ship, and the compound carbon steel of explosion--the research of stainless steel composite material has been carried out in investment, has obtained success.But because this composite is the single-side stainless steel material, and without rolling and directly use, can only limited several aspect use, do not form scale, can not replace stainless steel.China's this composite annual production less than is 20,000 tons at present.Thereby, a kind ofly can replace stainless material imperative.
Summary of the invention
In order to solve the problem that above-mentioned prior art exists, the invention provides the compound thin strip of the blast two-sided stainless steel of composite rolling, it adopts with the carbon steel plate slab is base material, behind two-sided composite stainless steel coating, through the technology of the strip material of hot rolling, cold rolling moulding, reached the purpose that replaces stainless steel material again.
The technical solution adopted for the present invention to solve the technical problems is: the compound thin strip of the blast two-sided stainless steel of composite rolling, it is by first corrosion resistant plate, second corrosion resistant plate and carbon steel sheet, the one side of carbon steel sheet is provided with first corrosion resistant plate, another side is provided with second corrosion resistant plate,, hot rolling compound through exploding, the cold rolling rolling ply-metal band that forms.
The technical process that the compound thin strip of the two-sided stainless steel of described blast composite rolling is produced is: adopt the method for explosive welding, make compound base, plate or hot rolled coil in becoming through hot rolling are then through cold rolling one-tenth cold-strip.
Described strip thickness after cold rolling is 0.5mm.
Linkage interface between described corrosion resistant plate and the carbon steel sheet combines by interatomic key.
The compound thin strip production technology of the two-sided stainless steel of the blast composite rolling two-sided composite stainless steel on the substrate of carbon steel that provides of the present invention, and through the two-sided stainless steel clad sheet material of rolling acquisition any thickness, its superiority is:
A. save the expensive stainless steel material, reduce price.
B. the mechanical performance of material is better than pure corrosion resistant plate, in use, can reduce the applied stress of structural design thickness or raising structure.Existing stainless corrosion resistance, wearability, aesthetic property have the flexibility of general steel plate again, and have reduced stainless fragility simultaneously, have good plasticity.
C. two-sided stainless steel metal composite board can carry out cold and hot working and be shaped, and has good solderability, and range of application is wide.
D. stainless steel clad sheet is compared with pure stainless steel, stainless steel clad plate magnetic conduction, and simple corrosion resistant plate magnetic conduction not, so it has application widely than simple stainless steel material.
What e. the thermal conductivity of stainless steel clad plate will be good than simple corrosion resistant plate is many, and the heat conductivity of composite plate approximately is simple stainless 6～8 times, and therefore, in some special application fields, it is much better than simple corrosion resistant plate.
Description of drawings
Fig. 1 is a profile of the present invention;
Among the figure: 1, first corrosion resistant plate, 2, carbon steel sheet, 3, second corrosion resistant plate.
The specific embodiment
The compound thin strip of the blast two-sided stainless steel of composite rolling, it is by first corrosion resistant plate 1, second corrosion resistant plate 3 and carbon steel sheet 2, the one side of carbon steel sheet 2 is provided with first corrosion resistant plate 1, another side is provided with second corrosion resistant plate 3,, hot rolling compound through exploding, the cold rolling rolling ply-metal band that forms.
The technical process that the compound thin strip of the two-sided stainless steel of described blast composite rolling is produced is: adopt the method for explosive welding, make compound base, plate or hot rolled coil in becoming through hot rolling are then through cold rolling one-tenth cold-strip; Strip thickness after cold rolling is 0.5mm; Linkage interface between corrosion resistant plate and the carbon steel sheet combines by interatomic key.
Claims (4)
1. the blast two-sided stainless steel of composite rolling compound thin strip, it is by first corrosion resistant plate, second corrosion resistant plate and carbon steel sheet, it is characterized in that: the one side of carbon steel sheet is provided with first corrosion resistant plate, another side is provided with second corrosion resistant plate,, hot rolling compound through exploding, the cold rolling rolling ply-metal band that forms.
2. according to the compound thin strip of the claim 1 two-sided stainless steel of described blast composite rolling, it is characterized in that: the technical process that the compound thin strip of the two-sided stainless steel of described blast composite rolling is produced is: the method that adopts explosive welding, make compound base, through plate or hot rolled coil in the hot rolling one-tenth, then through cold rolling one-tenth cold-strip.
3. according to the compound thin strip of the claim 1 two-sided stainless steel of described blast composite rolling, it is characterized in that: described strip thickness after cold rolling is 0.5mm.
4. according to the compound thin strip of the claim 1 two-sided stainless steel of described blast composite rolling, it is characterized in that: the linkage interface between described corrosion resistant plate and the carbon steel sheet combines by interatomic key.