CN102241053B - Production method of zirconium gem weichi box cover - Google Patents
Production method of zirconium gem weichi box cover Download PDFInfo
- Publication number
- CN102241053B CN102241053B CN 201110168245 CN201110168245A CN102241053B CN 102241053 B CN102241053 B CN 102241053B CN 201110168245 CN201110168245 CN 201110168245 CN 201110168245 A CN201110168245 A CN 201110168245A CN 102241053 B CN102241053 B CN 102241053B
- Authority
- CN
- China
- Prior art keywords
- counterdie
- internal mold
- lid
- patrix
- tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a production method of a zirconium gem weichi box cover and a weichi box cover mold. The production method of the zirconium gem weichi box cover is characterized by comprising the following steps of: uniformly feeding yttrium oxide stable granulating powder with the granularity of less than 0.5-5mum into a special mold; carrying out isostatic press forming at the pressure of 50-300Mpa and maintaining the pressure for 10-30 minutes; demolding to obtain a zirconium gem weichi box cover blank; and sintering and polishing to obtain the zirconium gem weichi box cover. The zirconium gem weichi box cover has the advantages of high strength, high toughness and long service life and is suitable for industrial production.
Description
Technical field
The present invention relates to a kind of preparation method and go lid mould of zirconium jewel go lid, belong to the structural ceramics preparing technical field.
Background technology
Zirconium jewel go lid normally adopts plastics, agate, timber etc. to make, and the go box gloss and the color and luster that adopt plastics, timber to make are poor, and the go box gloss and the color and luster school of adopting agate to make are good, but consumes a large amount of natural agates, and cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of preparation method that can overcome the good zirconium jewel go lid of above-mentioned defective, ornamental performance.Its technical scheme is:
Go lid mould is internal mold rubber tube (1), internal mold tube (2), upper and lower mould anchor clamps (3), die clamper (4) in the counterdie, counterdie (5), counterdie rubber tube (6), patrix (7), patrix rubber liner (8), feeding mouth (9) and feeding mouth rubber stopper (10) are formed, with granularity is that 0.5~5 μ m content is that the zirconia mist projection granulating of 3~5mol% stabilized with yttrium oxide is prepared into granulation powder (11), evenly pack into then in the go box mould, at pressure isostatic compaction and pressurize 10~30 minutes under the pressure of 50~300Mpa., zirconium jewel go lid base substrate is made in the demoulding then, fire for 1450~1650 ℃ and burnt till in 3~6 hours, make zirconium jewel go lid through polishing.
The preparation method of described zirconium jewel go lid and go lid mould, internal mold tube (2), counterdie (5) and patrix (7) be make greater than the stainless steel material of 0.5mm by thickness and be evenly equipped with the through hole that many apertures are 1mm.
The preparation method of described zirconium jewel go lid and go lid mould, during compacting, earlier internal mold rubber tube (1) is sleeved on the internal mold tube (2), be set with counterdie rubber tube (6) and counterdie (5) then thereon, by die clamper in the counterdie (4) that counterdie (5) and internal mold tube (2) is fixing, again with patrix (7) liner patrix rubber liner (8), by upper and lower mould anchor clamps (3) upper and lower mould is fixed, by feeding mouth (9) the granulation powder (11) of evenly packing into, then with feeding mouth rubber stopper (10) jam-pack, put into isostatic pressing machine, hydraulic oil is by internal mold tube (2) during pressurization, the through hole that the last many apertures of counterdie (5) and patrix (7) are 1mm affacts internal mold rubber tube (1), counterdie rubber tube (6), patrix rubber liner (8) passes to the granulation powder with pressure.
The present invention compared with prior art, its advantage is:
1, the present invention produces zirconium jewel go lid uniform microstructure, intensity height, global reliability height;
2, it is relatively good that the present invention produces zirconium jewel go lid feel, gloss and color and luster.
Description of drawings
Fig. 1 is the structural representation of go lid embodiment;
Fig. 2 is a go lid mould structure schematic diagram.
Among the figure: 1, internal mold rubber tube, 2, the internal mold tube, 3, the upper and lower mould anchor clamps, 4, die clamper in the counterdie, 5, counterdie, 6, counterdie rubber tube, 7, patrix, 8, the patrix rubber liner, 9, feeding mouth, 10, feeding mouth rubber stopper, 11, the granulation powder, 12, tubular zirconium-oxide, 13, zirconia spherical crown body.
The specific embodiment
In the embodiment shown in Fig. 1-2: the go lid is made up of the tubular zirconium-oxide (12) of certain altitude and wall thickness and certain altitude and wall thickness zirconia spherical crown body (13).Go lid mould is that die clamper (4), counterdie (5), counterdie rubber tube (6), patrix (7), patrix rubber liner (8), feeding mouth (9) and feeding mouth rubber stopper (10) are formed in internal mold rubber tube (1), internal mold tube (2), upper and lower mould anchor clamps (3), the counterdie.During compacting, earlier internal mold rubber tube (1) is sleeved on the internal mold tube (2), be set with counterdie rubber tube (6) and counterdie (5) then thereon, by die clamper in the counterdie (4) that counterdie (5) and internal mold tube (2) is fixing, again with patrix (7) liner patrix rubber liner (8), by upper and lower mould anchor clamps (3) upper and lower mould is fixed, by feeding mouth (9) the granulation powder (11) of evenly packing into, then with feeding mouth rubber stopper (10) jam-pack, put into isostatic pressing machine, hydraulic oil is by internal mold tube (2) during pressurization, counterdie (5), the through hole that the last many apertures of patrix (7) are 1mm affacts internal mold rubber tube (1), counterdie rubber tube (6), patrix rubber liner (8) passes to the granulation powder with pressure, reaches the purpose of moulding.
With granularity for being the yttria-stabilized zirconia powder of 3mol% less than 3 μ m content, mix with 40: 0.5: 59.5 weight ratio with polyvinyl alcohol, distilled water and to be prepared into ceramic size, be prepared into the yttria-stabilized zirconia mist projection granulating powder of 0.1mm then by the mist projection granulating tower, dress mould and the forming under the pressure of 50Mpa and pressurize 10 minutes, zirconium jewel go lid base substrate is made in the demoulding then, fired 3 hours at 1650 ℃, make zirconium jewel go lid blank, zirconium jewel go lid is made in polishing then.
The purity of testing used proportion material is technical pure.
With granularity for being the yttria-stabilized zirconia powder of 4.5mol% less than 0.5 μ m, yittrium oxide content, mix with 50: 0.3: 49.7 weight ratio with polyvinyl alcohol, distilled water and to be prepared into ceramic size, be prepared into the yttria-stabilized zirconia mist projection granulating powder of 0.2mm then by the mist projection granulating tower, the dress mould was the forming under the pressure of 200Mpa and pressurize 20 minutes, zirconium jewel go lid base substrate is made in the demoulding then, fired 4 hours at 1550 ℃, make zirconium jewel go lid blank, zirconium jewel go lid is made in polishing then.The purity of testing used proportion material is technical pure.
With granularity for being the yttria-stabilized zirconia of 5mol% less than 5 μ m, yittrium oxide content, mix with 60: 0.1: 39.9 weight ratio with polyvinyl alcohol, distilled water and to be prepared into ceramic size, be prepared into the yttria-stabilized zirconia mist projection granulating powder of 0.5mm then by the mist projection granulating tower, the dress mould was the forming under the pressure of 300Mpa and pressurize 30 minutes, zirconium jewel go lid base substrate is made in the demoulding then, fired 6 hours at 1450 ℃, make zirconium jewel go lid blank, zirconium jewel go lid is made in polishing then.
The purity of testing used proportion material is technical pure.
Claims (3)
1. the preparation method of a zirconium jewel go lid, it is characterized in that: go lid mould is by internal mold rubber tube (1), internal mold tube (2), upper and lower mould anchor clamps (3), die clamper (4) in the counterdie, counterdie (5), counterdie rubber tube (6), patrix (7), patrix rubber liner (8), feeding mouth (9) and feeding mouth rubber stopper (10) are formed, with granularity is that 0.5~5 μ m content is that the zirconia mist projection granulating of 3~5mol% stabilized with yttrium oxide is prepared into granulation powder (11), evenly pack into then in the go lid mould, at pressure isostatic compaction and pressurize 10~30 minutes under the pressure of 50~300Mpa., zirconium jewel go lid base substrate is made in the demoulding then, fire at 1450~1650 ℃ and to burn till in 3~6 hours, through polishing, make zirconium jewel go lid.
2. the preparation method of zirconium jewel go lid according to claim 1 is characterized in that: internal mold tube (2), counterdie (5) and patrix (7) be make greater than the stainless steel material of 0.5mm by thickness and be evenly equipped with the through hole that many apertures are 1mm.
3. the preparation method of zirconium jewel go lid according to claim 1 and 2, it is characterized in that: during compacting, earlier internal mold rubber tube (1) is sleeved on the internal mold tube (2), be set with counterdie rubber tube (6) and counterdie (5) then thereon, by die clamper in the counterdie (4) that counterdie (5) and internal mold tube (2) is fixing, again with patrix (7) liner patrix rubber liner (8), by upper and lower mould anchor clamps (3) upper and lower mould is fixed, by feeding mouth (9) the granulation powder (11) of evenly packing into, then with feeding mouth rubber stopper (10) jam-pack, put into isostatic pressing machine, hydraulic oil is by internal mold tube (2) during pressurization, the through hole that the last many apertures of counterdie (5) and patrix (7) are 1mm affacts internal mold rubber tube (1), counterdie rubber tube (6) and patrix rubber liner (8) pass to the granulation powder with pressure.