CN102235953A - 交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法 - Google Patents
交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法 Download PDFInfo
- Publication number
- CN102235953A CN102235953A CN 201010154634 CN201010154634A CN102235953A CN 102235953 A CN102235953 A CN 102235953A CN 201010154634 CN201010154634 CN 201010154634 CN 201010154634 A CN201010154634 A CN 201010154634A CN 102235953 A CN102235953 A CN 102235953A
- Authority
- CN
- China
- Prior art keywords
- cable
- experiment
- cold
- sample
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法,具有试样预处理、低温弯曲实验、局部放电实验、交流电压实验和静置实验五个步骤,经过本发明的五个步骤的耐寒冷实验,可以确定电缆是否具有良好的耐寒冷性能:如达到每一步的要求,说明电缆耐寒冷性能良好,在寒冷地带能够正常使用;反之,说明电缆不具有良好的耐寒冷性能,就不能在寒冷地带正常使用。
Description
技术领域
本发明涉及一种电缆的耐寒冷实验方法,尤其是交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法。
背景技术
在寒冷地带(如我国的东北、西北地区)敷设的电力电缆,每年有3-5个月处于0℃以下的环境中。在这种寒冷的环境中敷设的电力电缆必需具有良好的耐寒冷性能,才能保证电缆的护套不会冻裂、电缆的绝缘性能不会下降、电缆正常使用的寿命不会减少。因此,产品在出厂前必需进行耐寒冷实验,以确定电缆良好的耐寒冷性能,保证电缆在寒冷地带的正常使用。交联聚乙烯绝缘耐寒电力电缆是常用在寒冷地带的一种电缆,然而,目前在电力电缆生产企业或研究单位还没有交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法,也就无法确定电缆良好的耐寒冷性能,也不能保证电缆在寒冷地带能否正常使用。
发明内容
为了确定交联聚乙烯绝缘耐寒电力电缆是否具有良好的耐寒冷性能,本发明提供一种交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法,通过这种实验方法可以确定电缆是否具有良好的耐寒冷性能。
本发明提供的一种交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法,具有试样预处理、低温弯曲实验、局部放电实验、交流电压实验和静置实验五个步骤,每个步骤的实验内容如下:
一、试样预处理:将交联聚乙烯绝缘耐寒电力电缆的试样在温度-15±3℃的实验环境中放置不少于24小时;
二、低温弯曲实验:在温度-15±3℃的实验环境中将试样在圆柱体表面正向绕不少于3圈后松开展直,再反向绕不少于3圈后松开展直,重复正、反向绕不少于10次,圆柱体的直径应为:对单芯电缆实验时为20(D+d)±5%毫米,对三芯电缆实验时为15(D+d)±5%毫米,其中D为电缆试样实测直径,d为电缆内的导体的实测直径;低温弯曲实验结束后,电缆护套表面目测应无可见的裂纹;
三、局部放电实验:应按国标GB/T 3048.12-2007第6部分第6.2条进行局部放电实验,实验灵敏度应为5pC或更优;三芯电缆的所有绝缘线芯都应实验,电压施加于每一根导体和金属屏蔽之间;实验电压应逐渐升高到2U0并保持10秒,然后缓慢降到1.73U0;在1.73U0时,应无任何由被试电缆产生的超过实验灵敏度的放电;这里的U0为电缆的任一绝缘导体和电缆的金属屏蔽或周围介质之间的电压;
四、交流电压实验:应按国标GB/T 3048.8-2008第6部分第6.2条、第6.3条进行交流电压实验,实验电压和持续时间见表1:
表1
交流电压实验结束时,电缆的绝缘应无击穿:
五、静置实验:将整根试样电缆围绕在实验圆柱体上,圆柱体的直径应符合第二步低温弯曲实验要求,然后静置在温度更低的环境中,环境温度和静置时间为:护套材料为聚乙烯的电缆试样,环境温度-76℃,静置时间24小时;护套材料为聚氯乙烯的电缆试样,环境温度-40℃,静置时间24小时;然后,每种电缆试样应反方向绕在实验圆柱体上后重复此过程,静置实验结束时,护套表面目测应无可见的裂纹;
上述五个步骤应连续进行,即每一个步骤结束应立即进入下一个步骤的实验。
本发明的有益效果是:经过本发明的五个步骤的耐寒冷实验,可以确定电缆是否具有良好的耐寒冷性能:如达到每一步的要求,说明电缆耐寒冷性能良好,在寒冷地带能够正常使用;反之,说明电缆不具有良好的耐寒冷性能,就不能在寒冷地带正常使用。
具体实施方式
本发明具体实施时按试样预处理、低温弯曲实验、局部放电实验、交流电压实验和静置实验五个步骤进行,每个步骤的实验内容如下:
一、试样预处理:将交联聚乙烯绝缘耐寒电力电缆的试样在温度-15±3℃的实验环境中放置不少于24小时;
二、低温弯曲实验:在温度-15±3℃的实验环境中将试样在圆柱体表面正向绕不少于3圈后松开展直,再反向绕不少于3圈后松开展直,重复正、反向绕不少于10次,圆柱体的直径应为:对单芯电缆实验时为20(D+d)±5%毫米,对三芯电缆实验时为15(D+d)±5%毫米,其中D为电缆试样实测直径,d为电缆内的导体的实测直径;低温弯曲实验结束后,电缆护套表面目测应无可见的裂纹;
三、局部放电实验:应按国标GB/T 3048.12-2007第6部分第6.2条进行局部放电实验,实验灵敏度应为5pC或更优;三芯电缆的所有绝缘线芯都应实验,电压施加于每一根导体和金属屏蔽之间;试验电压应逐渐升高到2U0并保持10秒,然后缓慢降到1.73U0;在1.73U0时,应无任何由被试电缆产生的超过实验灵敏度的放电;这里的U0为电缆的任一绝缘导体和电缆的金属屏蔽或周围介质之间的电压;
四、交流电压实验:应按国标GB/T 3048.8-2008第6部分第6.2条、第6.3条进行交流电压实验,实验电压和持续时间见表1:
表1
交流电压实验结束时,电缆的绝缘应无击穿;
五、静置实验:将整根试样电缆围绕在实验圆柱体上,圆柱体的直径应符合第二步低温弯曲实验要求,然后静置在温度更低的环境中,环境温度和静置时间为:护套材料为聚乙烯的电缆试样,环境温度-76℃,静置时间24小时;护套材料为聚氯乙烯的电缆试样,环境温度-40℃,静置时间24小时;然后,每种电缆试样应反方向绕在实验圆柱体上后重复此过程,静置实验结束时,护套表面目测应无可见的裂纹;
上述五个步骤应连续进行,即每一个步骤结束应立即进入下一个步骤的实验。
Claims (1)
1.一种交联聚乙烯绝缘耐寒电力电缆的耐寒冷实验方法,其特征在于该方法具有试样预处理、低温弯曲实验、局部放电实验、交流电压实验和静置实验五个步骤,每个步骤的实验内容如下:
一、试样预处理:将交联聚乙烯绝缘耐寒电力电缆的试样在温度-15±3℃的实验环境中放置不少于24小时;
二、低温弯曲实验:在温度-15±3℃的实验环境中将试样在圆柱体表面正向绕不少于3圈后松开展直,再反向绕不少于3圈后松开展直,重复正、反向绕不少于10次,圆柱体的直径应为:对单芯电缆实验时为20(D+d)±5%毫米,对三芯电缆实验时为15(D+d)±5%毫米,其中D为电缆试样实测直径,d为电缆内的导体的实测直径;低温弯曲实验结束后,电缆护套表面目测应无可见的裂纹;
三、局部放电试验:应按国标GB/T 3048.12-2007第6部分第6.2条进行局部放电试验,实验灵敏度应为5pC或更优;三芯电缆的所有绝缘线芯都应试验,电压施加于每一根导体和金属屏蔽之间;试验电压应逐渐升高到2U0并保持10秒,然后缓慢降到1.73U0;在1.73U0时,应无任何由被试电缆产生的超过试验灵敏度的放电;这里的U0为电缆的任一绝缘导体和电缆的金属屏蔽或周围介质之间的电压;
四、交流电压实验:应按国标GB/T 3048.8-2008第6部分第6.2条、第6.3条进行交流电压实验,实验电压和持续时间见表1:
表1
交流电压实验结束时,电缆的绝缘应无击穿;
五、静置实验:将整根试样电缆围绕在实验圆柱体上,圆柱体的直径应符合第二步低温弯曲试验要求,然后静置在温度更低的环境中,环境温度和静置时间为:护套材料为聚乙烯的电缆试样,环境温度-76℃,静置时间24小时;护套材料为聚氯乙烯的电缆试样,环境温度-40℃,静置时间24小时;然后,每种电缆试样应反方向绕在实验圆柱体上后重复此过程,静置实验结束时,护套表面目测应无可见的裂纹;
上述五个步骤应连续进行,即每一个步骤结束应立即进入下一个步骤的实验。