CN102231247A - Logistics identifier for metal hot-dipped part and preparation method for logistics identifier - Google Patents
Logistics identifier for metal hot-dipped part and preparation method for logistics identifier Download PDFInfo
- Publication number
- CN102231247A CN102231247A CN2011101587230A CN201110158723A CN102231247A CN 102231247 A CN102231247 A CN 102231247A CN 2011101587230 A CN2011101587230 A CN 2011101587230A CN 201110158723 A CN201110158723 A CN 201110158723A CN 102231247 A CN102231247 A CN 102231247A
- Authority
- CN
- China
- Prior art keywords
- logistics
- metal hot
- sign
- groove
- protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a logistics identifier for a metal hot-dipped part and a preparation method for the logistics identifier. The logistics identifier for the metal hot-dipped part comprises a microcrystalline glass sheet and a protective body, wherein bar codes are printed on the surface of the microcrystalline glass sheet; the protective body is made of a high-temperature resistant and impact-resistant material; a groove is formed on the protective body; and the microcrystalline glass sheet is arranged in the groove. The method for preparing the logistics identifier for the metal hot-dipped part comprises the following steps of: performing crystallization heat treatment on the glass sheet printed with the bar codes in a thermal treatment furnace under controlled conditions, and fusing the bar codes on the surface of the microcrystalline glass sheet; preparing the protective body with a dimension matched with that of the microcrystalline glass sheet by using the high-temperature resistant and impact-resistant material; and etching a groove on the protective body and putting the microcrystalline glass sheet into the groove. By the logistics identifier and the preparation method thereof, the identification efficiency of the logistics identifier in the processing process of the metal hot-dipping industry is greatly improved, the identification error rate of the identifier is reduced, the material consumption of the identifier is greatly reduced, and the production cost is reduced.
Description
Technical field
The present invention relates to metal hot dipping industry processing technique field, be specifically related to logistics sign of plating piece in the metal hot dipping process and preparation method thereof.
Background technology
Because under its special processing technology and working environment of metal hot dipping industry, original plating piece identification technology is to adopt the sign of printing workpiece on the irony thin plate, it is hung over the technological process of carrying out hot-dip on the workpiece with workpiece again.Because this method not only will consume a large amount of irony thin plate starting material, the printing degree of depth to sign has certain requirement simultaneously, sign after hot-dip is finished is covered by coating, therefore the identification of sign has certain difficulty, and rely on the identification manually finish sign fully, its error rate height, inefficiency.And because the starting material of sign are disposable uses, therefore, the consumption height of material.Particularly the galvanizing by dipping at shipbuilding industry pipe fitting is big in batches, and each root pipe fitting all has the uniqueness requirement, it is big to join workload through the identification of galvanizing by dipping rear tubular member and collection, has consumed great amount of manpower and go-no-go cycle, becomes the bottleneck problem in the sector pipe fitting manufacture process.
Summary of the invention
Technical matters to be solved by this invention provides a kind of logistics sign of metal hot dipping plating piece, overcomes the logistics sign identification error rate height of existing metal hot dipping plating piece, the defective that the consumption of material is high.
For solving the problems of the technologies described above, the logistics sign of metal hot dipping plating piece provided by the invention is characterized in that, described logistics sign comprises microcrystalline glass, and described microcrystalline glass is printed on bar code on the surface.Devitrified glass has anti-strong acid, alkali corrosion, and the characteristic of high temperature resistant chilling can not be carried out displacement reaction with metal, and therefore, bar code is not covered by metal in the metal hot dipping process.
Further, also comprise the protective that high temperature resistant and high impact material is made, described protective is provided with groove, and described microcrystalline glass places in the described groove.
More optimal, cover plate high temperature resistant and that high impact material is made is installed on the described groove, have window on the described cover plate, the information of described bar code can be read by the bar code fetch equipment by described window.
The edge of described protective is provided with the drop hole.
The present invention also provides the preparation method of the logistics sign of above-mentioned metal hot dipping plating piece simultaneously, it is characterized in that, may further comprise the steps:
The special-purpose bar coded sticker that suitable glass is fired is printed on the glass sheet, then described glass sheet is inserted the crystallization and thermal treatment that has in the heat-treatment furnace under the control condition, bar code fused into the devitrified glass surface after thermal treatment was finished, and had formed an integral body with devitrified glass.
Make and the microcrystalline glass protective of suitable size mutually with shock-resistant with exotic material, on protective, carve groove then, microcrystalline glass is inserted in the groove.
With exotic material and the shock-resistant cover plate of making, carve window on the cover plate then, be fixedly mounted on the groove of described protective, microcrystalline glass is protected in the protective, the bar code mark of microcrystalline glass is emerging in the window, is convenient to reading of bar code.
The logistics that machines plating piece is identified at the edge brill drop hole of its protective, will identify with plating piece by iron wire tying up board hole to be tied.
This sign can be by repeatedly the use batch carried out of hot dipping plating piece, after each batch hot dipping plating piece is finished, the plating piece information that provides according to the sign bar code identifies dislocation, after dislocation is finished, the sign bar code can redefine with next batch plating piece information, uses in the plating piece product of next batch.
The invention has the beneficial effects as follows, improved the recognition efficiency of the logistics sign in the metal hot dipping industry process greatly, and the error rate that reduces sign identification, thereby improve logistic efficiency and accuracy rate in the sector process, also significantly reduced simultaneously the consumption of marking materials, reduced production costs.
Description of drawings
Below in conjunction with the drawings and specific embodiments technical scheme of the present invention is further described in detail.
Fig. 1 is a front view of the present invention.
Fig. 2 is a side view of the present invention.
Embodiment
Shown in Fig. 1,2, protective 1 is provided with groove, and the microcrystalline glass 2 that the surface is printed on bar code 6 is positioned in the groove, and the edge of protective is drilled with drop hole 5.Cover plate 3 is installed on the groove, is had window 4 on the cover plate 3, the information of bar code 6 can be read by the bar code fetch equipment by window 4.
Devitrified glass is as the carrier material of identification barcode.Devitrified glass can satisfy the anti-strong acid of hot-dip industry, highly basic, and the requirement of high temperature chilling, also satisfies in the hot-dip process simultaneously not covered by coating.Bar code printing is after the crystallite high-temperature firing forms one in addition, and therefore, the sign after printing is fired should not be worn and torn and come off by burn into.
Simultaneously, devitrified glass bears a little less than the impact ability of metal, and protective adopts high temperature resistant and high impact material, and as stainless steel, microcrystalline glass places in the protective, is protected the protecting against shock protection of body.
The preparation method of the logistics sign of metal hot dipping plating piece of the present invention may further comprise the steps:
By identifying the glass-cutting one-tenth sign body required size glass sheet that the required size requirement will be added with the nucleus agent or not add nucleus agent specific composition, and will be fit to the special-purpose bar coded sticker that glass fires and be printed on this glass sheet, then this glass sheet is inserted the crystallization and thermal treatment that has in the heat-treatment furnace under the control condition, bar code fused into the devitrified glass surface after thermal treatment was finished, and had formed an integral body with devitrified glass.
Cut into and the microcrystalline glass protective of suitable size mutually with high impact material stainless steel etc. is high temperature resistant, on protective, mill out groove then, and be drilled with aperture at the edge of protective; Microcrystalline glass is inserted in the groove.
Select the high temperature resistant platelet suitable with groove size with the high impact material making; carve a window on the platelet; make cover plate; cover plate is fixed on the groove of protective in modes such as welding, riveted joints; microcrystalline glass is protected in the protective; the bar code mark of microcrystalline glass is emerging in the window simultaneously, is convenient to reading of bar code.Promptly finish the logistics sign processing of plating piece.
Sign strong alkali-acid resistance of the present invention, high temperature resistant chilling, the impact of anti-metal, and prevent that the zinc behind the galvanizing by dipping from going up problem such as should not discern attached to sign, satisfy recycling of identifying simultaneously to reduce production costs.This sign has improved logistics management efficient and the accuracy rate in the metal hot dipping industry technological process process greatly, uses good.
It should be noted last that, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can make amendment or be equal to replacement technical scheme of the present invention, and not breaking away from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of the claim scope of the present invention.
Claims (8)
1. the logistics of metal hot dipping plating piece sign is characterized in that comprise microcrystalline glass, described microcrystalline glass is printed on bar code on the surface.
2. the logistics sign of metal hot dipping plating piece according to claim 1 is characterized in that also comprise the protective that high temperature resistant and high impact material is made, described protective is provided with groove, and described microcrystalline glass places in the described groove.
3. the logistics sign of metal hot dipping plating piece according to claim 2, it is characterized in that, cover plate high temperature resistant and that high impact material is made is installed on the described groove, is had window on the described cover plate, the information of described bar code can be read by the bar code fetch equipment by described window.
4. according to the logistics sign of claim 2 or 3 described metal hot dipping plating pieces, it is characterized in that the edge of described protective is provided with the drop hole.
5. the preparation method of the logistics of the described metal hot dipping plating piece of claim 1 sign is characterized in that, may further comprise the steps:
The special-purpose bar coded sticker that suitable glass is fired is printed on the glass sheet, then described glass sheet is inserted the crystallization and thermal treatment that has in the heat-treatment furnace under the control condition, bar code fused into the devitrified glass surface after thermal treatment was finished, and had formed an integral body with devitrified glass.
6. according to the preparation method of the logistics of the described metal hot dipping plating piece of claim 5 sign; it is characterized in that; further comprising the steps of: as to make and the microcrystalline glass protective of suitable size mutually with shock-resistant with exotic material; on protective, carve groove then, microcrystalline glass is inserted in the groove.
7. according to the preparation method of the logistics of the described metal hot dipping plating piece of claim 6 sign; it is characterized in that; further comprising the steps of: with exotic material and the shock-resistant cover plate of making; carve window on the cover plate then; be fixedly mounted on the groove of described protective; microcrystalline glass is protected in the protective, and the bar code mark of microcrystalline glass is emerging in the window, is convenient to reading of bar code.
8. according to the preparation method of the logistics of the described metal hot dipping plating piece of claim 7 sign, it is characterized in that, further comprising the steps of: in the edge boring of described protective.